• Restorative Dentistry and Endodontics
• /
• 제25권1호
• /
• pp.109-115
• /
• 2000

This study was designed to evaluate the microhardness of restorative composite resin and dual-cured composite resin cement which were light cured through the 1.5mm thickness composite overlay. For restorative materials, Z100 and Tetric Ceram were used. For dual cured composite cements, Variolink II((VL II) of three consistency (low, high, ultra high) were used. To determine the optimal microhardness of Z100, Tetric Ceram and Variolink II, each material was packed into the 1mm thickness teflon mold without composite overlay and light cured for 60 seconds. Then the microhardnesses of each sample were measured, averaged and regarded as optimal hardness of each material. To evaluate the microhardness of restorative composite resin and dual-cured composite resin cement which were light cured through the 1.5mm thickness composite overlay, the composites were packed into 1mm thickness teflon mold, coverd with celluloid strip, and then precured composite overlay which was made of Targis(Ivoclar/Vivadent, Liechtenstein) was positioned. 2 types of visible light curing machine, the power density of one of which was 400$mW/cm^2$ and the other was 900$mW/cm^2$, and one type of argon laser were used to cure the restorative composite and dual cured cement. For each group, 10 sample were assigned. The light curing tip was positioned over the composite overlay and light cured for 1min., 2min. or 3min with visible light curing machine or 15sec, 30 sec, 45sec, and 60 sec with argon laser. The Vickers hardnesses of upper and lower surface of Z100, Tetric Ceram, and 3 types of VL II cement were measured. When the 900 $mW/cm^2$ curing light was used, 2min. was needed for optimal curing of Z100 and Tetric Ceram. Variolink II did not be cured optimally even though the curing time was extended to 3min. When 400$mW/cm^2$ curing light was used, 3min. was necessary for Z100, whereas 3min. was not enough for Tetric Ceram. Variolink II was not cured optimally even though the curing time was extended to 3min. When argon laser was used, Z100, Tetric Ceram and Variolink II were not cured optimally in 60 seconds.

• 대한치과보철학회지
• /
• 제29권1호
• /
• pp.91-109
• /
• 1991

The purpose of this study were to comfirm the effects of the thickness and kinds of porcelain, etchants, illumination time, elapsed time for the measurement, and chemical cure component to the bond strength of porcelain laminate and composite resin cement, and to compare the effects between the light cured resin and the dual cured resins. The etched porcelain surface, the sectioned surface crossing porcelain and resin after bonding, and the debonded surfaces were observed by the SEM. One product of laminate porcelain powder, one light cured resin and two dual cured resins were selected. Each resin cements are lightened through the thin porcelain disc which was cut from cylindrical porcelain specimen by the diamond saw, and by the light through the porcelain disc they were bonded. Changes of thickness and kinds of porcelain, etchants, illumination time, and the elapsed time for the measurement were considered as variables for the bond strength. And the bond strength of porcelain and dual cured resins under the conditions of autopolymerization or the removal of chemical cure component were measured and compared. Bond strength were measured by shear stress. The etched surface, the cross-sectioned surface, and the debonded surface of porcelain or resin were observed by SEM. On the summary of this study, the following conclusions can be stated; 1. Bond strength of light cured resin was decreased inversely by the thickened porcelain laminate and showed the lowest value to the masking dentin porcelain among 4 kinds of porcelain powder. 2. Bond strength of autopolymerization of dual cured resin without illumination in dark chamber were from 75% to 98% to the data of dual cured resin with illumination. 3. Bond strength of dual cured resin used without chemical cured components were same to them of light cured resin. 4. Cross-sectioned surface treated by silane did not show the gap between the porcelain and resin. 5. Illumination over 80 seconds did not make the significant increase of bond strength on all kinds of resin.

• Restorative Dentistry and Endodontics
• /
• 제25권1호
• /
• pp.17-40
• /
• 2000

Resin cements are used for cementing indirect esthetic restorations such as resin or porcelain inlays. Because of its limitations in curing of purely light cured resin cements due to attenuation of the curing light by intervening materials, dual cured resin cements are recommended for cementing restorations. The physical properties of resin cements are greatly influenced by the extent to which a resin cures and the degree of cure is an important factor in the success of the inlay. The purpose of this study was to evaluate the influence of porcelain thickness and exposure time on the polymerization of resin cements by measuring the microhardness and the degree of conversion, to investigate the nature of the correlation between two methods mentioned above, and to determine the exposure time needed to harden resin cements through various thickness of porcelain. The degree of resin cure was evaluated by the measurements of microhardness [Vickers Hardness Number(VHN)] and degree of conversion(DC), as determined by Fourier Transform Infrared Spectroscopy(FTIR) on one light cured composite resin [Z-100(Z)] and three dual cured resin cements [Duo cement(D), 3M Resin cement(R), and Dual cement(DA)] which were cured under porcelain discs thickness of 0mm, 1mm, 2mm, 3mm with light exposure time of 40sec, 80sec, 120sec, and regression analysis was performed to determine the correlation between VHN and DC. In addition, to determine the exposure time needed to harden resin cements under various thickness of porcelain discs, the changes of the intensity of light attenuated by 1mm, 2mm, and 3mm thickness of porcelain discs were measured using the curing radiometer. The results were obtained as follows ; 1. The values of microhardness and the degree of conversion of resin cements without intervening porcelain discs were 31~109VHN and 51~63%, respectively. In the microhardness Z was the highest, followed by R, D, DA. In the degree of conversion, D and DA was significantly greater than Z and R(p<0.05). 2. The microhardness and the degree of conversion of the resin cements decreased with increasing thickness of porcelain discs, and increased with increasing exposure time, D and R showed great variation with inlay thickness and exposure time, whereas, DA showed a little variation. 3. The intensity of light through 1mm, 2mm, and 3mm porcelain inlays decreased by 0.43, 0.25, and 0.14 times compared to direct illumination, and the respective needed exposure times are 53 sec, 70 sec, and 93 sec. In D and R, 40 sec of light irradiation through 2mm porcelain disc and 80 sec of light irradiation through 3mm porcelain disc were not enough to complete curing. 4. The microhardness and the degree of conversion of the resin cements showed a positive correlationship(R=0.791~0.965) in the order of R, D, Z, DA. As the thickness of porcelain discs increased, the decreasing pattern of microhardness was different from that of the degree of conversion, however.

• 구강회복응용과학지
• /
• 제23권4호
• /
• pp.283-292
• /
• 2007

Two-step or one-step bonding systems generally inhibit curing process of dual-cured core build-up resin composite for their adhesive acidity. In addition this dual-cured core build-up resin composite can be applied to dentin of pulp chamber and root at the time that complete the endodontic treatment. The purpose of this investigation was to determine the influence of sodium hypochlorite on rnicrotensile bond strength of dual-cured core build-up resin composite. Extracted human molars were horizontally sectioned with 1mm thickness using low speed diamond saw. After the sectioned specimens were divided into 8 groups, adhesive systems (Clearfil SE-Bond, Prime&Bond NT[2-step, 1-step], Adper Prompt L-Pop) were then applied with or without sodium hypochlorite pretreatment. The treated specimen was filled with dual-cured core build-up resin composite (Luxacore, DMG corp., German). Then light cured for 40 seconds and soaked in $37^{\circ}C$ water bath for 24 hours. After the treated specimen was grinded with 1mm width and measured rnicrotensile bond strength by testing machine. Additionally 8 teeth were prepared for SEM evaluation. The results were as follows. : NaOCl treated groups generally had lower rnicrotensile bond strength but did not show any difference statistically except Adper Prompt L-Pop. When the teeth were treated by NaOCl, though the difference of applied adhesive system, it had no statistically significant difference within the NaOCl treated groups except the relation of between ClearFil SE-Bond adhesive system and Adper Prompt L-Pop adhesive system. In the SEM evaluation, NaOCl treated groups presented relatively long resin tags and incomplete hybrid layer formation generally.

• 대한치과보철학회지
• /
• 제44권1호
• /
• pp.1-9
• /
• 2006

Purpose: The purpose of this study was to evaluate the efficacy and substitute possibility of a newly developed flowable composite resins as a luting cement for translucent fiber post. Material & Method: Two kinds of 12 mm translucent fiber Post (D.T. Light-Post (Bisco, USA) and FRC Postec (Ivoclar vivadent, Liechtenstein) was inserted into the teflon mold (7 mm diameter, 9 mm long) and Filtek-Flow (3M ESPE. USA), a light activated flowable composite resin, was polymerized for 60 seconds through the post. Also, the post was cut from the tip to 9 mm, 6 mm, 3 mm, and Filtek-Flow was light cured according to each length. For comparison, 60 seconds light-cured and 24 hours self-cured two dual cured resin cement (Duo-cement (Bisco, USA) and 2 Panavia-F (Kuraray, Japan)) samples were prepared as control group. Also cavities (1 mm in width, 1 mm in depth and 12 mm in length) were prepared using acrylic plate and aluminum bar, and flowable composite resin was flied and light cured by the diffused light from the fiber post's side wall. The degree of polymerization was measured according to the distance from curing light using Vickers' hardness test. Result: Within the limitation of this study, the following conclusions were drawn: 1. Vickers' hardness of light cured dual cured resin cement and flowable composite resin decreased from Panavia-F, Filtek-Flow and Duo-cement accordingly (p<0.05). In the dual curing resin cement, light curing performed group showed higher surface hardness value than self cured only group (p<0.05). 2. Surface hardness ratio (light cured through fiber post /directly light cured) of D.T. Light-Post using Filtek-Flow showed about 70% in the 6 mm deep and about 50% in the 12 mm deep FRC Postec showed only 40% of surface hardness ratio. 3. Surface hardness ratio by diffused light from the post's side wall showed about 50% at 6 mm and 9 mm deep, and about 40% at 12 mm deep in D.T. Light-Post. However, FRC Postec showed about 40% at 6 mm deep, and almost no polymerization in 9 mm and 12 mm deep.

• 대한치과보존학회:학술대회논문집
• /
• 대한치과보존학회 2001년도 추계학술대회(제116회) 및 13회 Workshop 제3회 한ㆍ일 치과보존학회 공동학술대회 초록집
• /
• pp.595-595
• /
• 2001

As the interest for esthetic restoration is increasing, the usage of composite resin is increasing. The usage of composite resin is not limited to anterior teeth but is spreading to posterior area using direct ＆ indirect methods. Generally, dual or chemical cure resin cement has been used for setting composite or porcelain inlay restoration. However, chemical cure resin cement has limited working time and it's difficult to remove excess cement from the tooth and the restoration. The dual cured composite is also difficult to remove from the tooth surface.(omitted)

• Restorative Dentistry and Endodontics
• /
• 제34권5호
• /
• pp.383-389
• /
• 2009

이 연구의 목적은 이중 중합복합레진과 수평 포스트를 이용하여 수복한 치관-치근 복합파절 치아의 수직파절 저항성을 알아보기 위한 것이다. 48개의 발치된 사람의 소구치에 실험적으로 치관-치근 복합파절을 일으킨 후 대조군 및 3개의 실험군에 (n=12) 각각 할당하였다. 대조군에서는 치아 파절편을 레진시멘트를 이용하여 접착한 후 근관치료를 시행하고, 근관와동을 이중중합 복합레진을 사용하여 충전하였다. 실험군에서는, 각각의 치아에 근관치료를 시행한 후 레진-포스트 군에서는 근관와동을 수평 포스트 및 이중중합 복합레진을사용하여 충전하였다. 레진 군에서는 근관와동을 포스트 없이 이중중합 복합레진만 사용하여 수복하였으며 아말감 코어 군에서는 근관와동을 접착 아말감을 사용하여 수복하였다. 이렇게 수복된 치아를 처음과 같은 방법으로 다시 치관-치근 복합파절을 유도하여 이때의 파절 저항성을 기록하고 이 값과 처음 파절을 유도하였을 때의 파절 저항성의 비를 계산하고 각 군별로 차이가 있는 지 검증하기 위해 Kruskal-Wallis test를 시행하였다. 수복된 치아의 파절저항성은 레진-포스트군, 대조군, 레진군, 접착 아말감 순으로 높았으며, 이 실험결과로 볼 때,치관-치근 복합파절 치아의 수복 시 수평 포스트를 사용하는 것이 재파절 방지를 위해 효과적 일 것으로 사료된다.

• Restorative Dentistry and Endodontics
• /
• 제32권1호
• /
• pp.1-8
• /
• 2007

본 연구는 자가 산부식 접착제를 적용한 법랑질에 광중합과 이원중합 복합레진을 접착시켜 접착제와 복합레진의 종류에 따른 미세전단 결합강도를 상호 비교하기 위하여 시행하였다. 발거된 상 하악 대구치를 근, 원심 방향으로 1 mm 두께가 되도록 절단하여 사용된 접착제의 종류에 따라 Xeno 군 (Xeno III), Adper 군 (Adper Prompt L-Pop), AQ 군(AQ Bond)으로 분류하였다. 각 시편의 법랑질 표면에 각 군에 해당하는 접착제를 적용한 후 Tygon tube를 이용하여 광중합형 복합레진 (Z 250)이나 이원중합 복합레진 (Luxacore)을 접착하였다. 실온의 증류수에 24시간 동안 보관한 후. universal testing machine을 이용하여 각 시편의 복합레진과 법랑질의 접착계면이 파절될 때가지 분당 1 mm의 crosshead speed를 가하여 미세전단 결합강도를 측정 한 후 통계학적으로 분석하여 다음과 같은 결과를 얻었다. 1. 동일 접착제로 결합된 광중합과 이원중합 복합레진의 법랑질에 대한 미세인장 결합강도는 광중합 복합레진에서 통계학적으로 높게 나타났다 (p<0.05). 2. Z 250을 접착시킨 각 군의 미세전단 결합강도는 Xeno군에서 $7.73{\pm}2.01\;MPa$, Adper군에서 $6.74{\pm}1.80\;MPa$, AQ 군에서 $9.59{\pm}2.51\;MPa$를 나타내어 AQ 군이 Adper군 보다 통계학적으로 높게 나타났다 (p<0.05). 3. Luxacore를 접착시킨 각 군의 미세전단 결합강도는 Xeno군에서 $5.19{\pm}1.32\;MPa$, Adper 군에서 $3.41{\pm}1.19\;MPa$, AQ군에서 $4.50{\pm}0.96\;MPa$를 나타내어 Xeno군이 Adper군 보다 통계학적으로 높게 나타났다(p<0.05).

• Restorative Dentistry and Endodontics
• /
• 제32권5호
• /
• pp.445-458
• /
• 2007

단일과정 접착제를 이용함에 있어 복합레진과의 부적합성을 개선하고자 중간레진이 결합에 영향을 미칠 것으로 사료된다. Experimental single step system (Bisco Ltd., Schaumburg, IL)을 대조군으로 하고 6종의 중간레진을 접착제의 중합여부, 복합레진의 광중합-자가중합 여부로 분류하였다. 상아질에 대한 광중합 또는 자가중합형 복합레진의 결합강도를 측정하고 접착계면에 대한 투과전자현미경 관찰하여 다음과 같은 결론을 얻었다. 1. 중간레진의 적용은 광중합형 복합레진의 결합강도를 증가시키지 않았다. 2. 자가중합형 복합레진의 결합강도는 중간레진을 적용할 경우 증가하였다. 3. 중간레진의 적용 전 접착제의 중합여부는 결합강도의 변화에 영향을 미치지 않았다. 4. 중간레진이 친수성일 때 소수성 중간레진을 적용할 때 보다 높은 결합강도를 나타냈으나 통계적 유의차는 없었다. 광중합형 복합레진의 수복 시 단일과정 접착제를 사용하는 것은 초기 결합강도에 영향을 미치지 않으며, 자가중합형 복합레진을 단일과정 접착제와 사용할 때는 접착층의 투과도를 감소시키는 소수성의 중간레진을 적용하여 부적합성을 해소할 수 있을 것이다.

• Restorative Dentistry and Endodontics
• /
• 제32권3호
• /
• pp.169-179
• /
• 2007

이 연구의 목적은 2단계 자가산부식 접착제를 이용하여 법랑질에 대한 광중합과 화학중합 복합레진의 결합강도 차이를 비교하고, 또한 현미경적 인 관찰을 통하여 2단계 자가 산부식 접착제가 법랑질에서 화학중합 복합레진과 비적합성을 나타내는가를 알아보기 위해 시행하였다. 미세전단 결합강도를 측정하기 위하여 Isomet Low Speed Saw를 이용하여 발거한 대구치를 근, 원심 방향으로 1 mm두께가 되도록 절단하여 여러 개의 절편을 만들었다. 치아의 절편들을4개의 군으로 분류한 후, 사용된 접착제에 따라 SE Bond 군, AdheSE 군, Tyrian 군 Contax 군으로 분류하였다. 각 군의 접착제를 각 절편의 법랑질 표면에 적용한 후, Tygon tube를 이용하여 광중합형 복합레진 (Filtek Z250) 또는 화학중합 복합레진 (Luxacore Smartmix Dual)을 접착하였다. 실온의 증류수에 24시간 동안 보관한 후, universal testing machine을 이용하여 각 시편의 복합레진과 법랑질의 접착계면이 파절될 때까지 분당 1 mm의 crosshead speed를 가하여 미세전단 결합강도를 측정하였다. 각 군의 미세전단 결합강도치에 대한 유의성 검증은 two-way ANOVA와 Tukey HSD검정 및 독립표본 t 검정을 이용하여 p = 0.05 유의수준에서 분석하였다. 주사전자 현미경 관찰을 위해 발거한 대구치의 협면이나 설면의 법랑질 일부를 Isomet Low Speed Saw로 절단한 후 각 군의 접착제와 광중합 복합레진 또는 화학중합 복합레진을 축조하여 각 군당 2개의 시편을 제작하였다. 주사전자 현미경 하에서 법랑질과 접착제 및 복합레진 계면을 관찰하여 다음과 같은 결과를 얻었다. 1. 광중합과 화학중합 복합레진 모두에서 SE Bond 군의 법랑질에 대한 미세전단 결합 강도는 다른 3개의 군보다 통계학적으로 높게 나타났다 (p < 0.05). 2. 광중합과 화학중합 복합레진 모두에서 AdheSE 군, Tyrian 군 Contax군의 법랑질에 대한 미세 전단 결합 강도는 통계학적으로 유의한 차이를 나타내지 않았다. 3. 동일한 접착제를 사용한 경우, 모든 군에서 법랑질에 대한 광중합 복합레진의 미세전단 결합강도는 화학중합 복합레진보다 통계학적으로 높게 나타났다 (p < 0.05). 4. 모든 접착제와 법랑질 계면은 긴밀한 접합을 나타내어 화학중합 복합레진과 접착제 간에 비적합성이 나타나지 않았다.