• Proceedings of KOSOMES biannual meeting
• /
• 2005.05a
• /
• pp.161-165
• /
• 2005

Recently, it is on the increase interest for Al alloy with new material for ship application to substitute for FRP ship. The reason is thatAl alloy ship has beneficial characteristics such as high sea speed, increase of loadage and easy to recycle compared with FRP ship. In this paper, mechanical and electrochemical properties are investigated by slow strain rate test experiment in various applied potential condition. These results will provide as reference data to design ship by deciding optimum protection potential regard to hydrogen embrittlement and stress corrosion cracking. In general, Al and Al alloys are not corroded with forming film which has the corrosion resistance property in neutral solution. However, it was observed that formation and destruction of passive film by $Cl^-$ ion in sea water environment. At comparison of current density after 1200 sec in potentiostatic experiment, the current density in the potential range of -0.68 $\~$-1.5 V is shown low value. The low current density means protection potential range. Elongation in applied potential of 0 V was high. However, the corrosion protection application in this condition is impossible potential because the toughness is low value by decreasing strength by active dissolution reaction at parallel part of specimen. The film composed with $CaCO_3$ and $Mg(OH)_2$ has a corrosion resistance property. However, the uniform electrodeposition coating at below -1.6 V potential is not formed since the time to form the uniform electrodeposition coating is short. Therefore, it is concluded that mechanical property is poor because effect by hydrogen gas generation is larger than that of electrodeposition coating. It is concluded that the optimum protection potential range from comparison of_maxim urn tensile strength, elongation and time to fracture is -1.3$\~$0.7 V (SSCE).

• Korean Journal of Materials Research
• /
• v.12 no.7
• /
• pp.573-579
• /
• 2002

Stoichiometric mullite ($3Al_2$$O_3$. $2SiO_2$) precursor sol has been prepared by sol-gel method. The effects of the precursor pH and sintering temperature on the synthesizing behavior and morphology of mullite have been studied. Mullite precursor sol was prepared by dissolution of aluminum nitrate enneahydrate (Al($NO_3$)$_3$.9H$_2O) into the mixture of silica sol. Precursor pH of the sols was controlled to acidic condition ($PH\leq$ 1~1.5) and to basic condition ($pH\geq$8.5~9). The synthesized aluminosilicate sols were formed under 20 MPa pressure after drying at $150^{\circ}C$ for 24 hours, and then sintered for 3hours in the temperature range of $1100~1600^{\circ}C$. From TGA/DTA analysis, total weight loss in the aluminosilicate gel of the acidic sample was (equation omitted) 56% and that of the basic sample was (equation omitted) 85%, indicating that the synthesizing temperature of mullite phase for acidic and basic samples was above $1200^{\circ}C$ and $1300^{\circ}C$, respectively. The morphologies of the synthesized mullite were fine and needle-like (or rod-like) for acidic sample, and granular for basic sample that has been sintered above $1300^{\circ}C$. It was found that the morphology of mullite particle was predominantly governed by precursor pH and sintering temperature.

• Journal of the Korean Society for Heat Treatment
• /
• v.34 no.5
• /
• pp.233-238
• /
• 2021

The mechanical, anti-tarnishing, and corrosion characteristics of Yuggi (Cu-22wt%Sn) alloy are greatly affected by fraction of constituent phases according to heat treatment method. The Yuggi heat-treated at 750℃ has a β1' phase of 98% or more, which is a high-temperature disordered beta phase, on the other hand, cast Yuggi that Sn is solid-solutioned into Cu consists with α-phase over 60v/o. This difference of constituent phases of Yuggi may cause a difference in dissolution of Cu under antimicrobial test condition. Nonetheless, few studies have been conducted on the effect of fraction of constituent phases and constituent phases in antimicrobial activity. In addition, few studies have also been conducted on the suitable method measuring the antimicrobial activity of Yuggi. Hence, the purpose of this study is to provide an optimum measurement method of antimicrobial activity, and to evaluate quantitatively the effect of constituent phases on antimicrobial activity.

• Resources Recycling
• /
• v.30 no.2
• /
• pp.53-60
• /
• 2021

Leaching experiments from single metal and metallic mixtures were conducted to develop a process for the recovery of cobalt, copper, and nickel in spent lithium ion batteries. Inorganic and organic acid solutions without oxidizing agents were employed. No copper was dissolved in the absence of an oxidizing agent in the leaching solutions. The leaching condition to completely dissolve single metal of cobalt and nickel was determined based on acid concentration, reaction temperature and time, and pulp density. The leaching condition to dissolve all of cobalt and nickel from the metallic mixtures was also obtained. Leaching of the metallic mixture with methanesulfonic acid led to selective dissolution of cobalt at low temperatures.

• Korean Journal of Metals and Materials
• /
• v.47 no.4
• /
• pp.223-227
• /
• 2009

The precipitates, hardness, and tensile properties of Al-6.2Si-2.9Cu AC2B alloy were investigated with respect to solution treatment time at $500^{\circ}C$. $Al(Cu)-Al_2Cu$ eutectic, Si, ${\theta}-(Al_2Cu)$, and $Q-(Al_5Cu_2Mg_8Si_6)$ phases were observed in the as-cast specimen. With increasing the solution treatment time at $500^{\circ}C$, the $Al(Cu)-Al_2Cu$ eutectic and ${\theta}-(Al_2Cu)$ phases were gradually reduced and finally almost disappeared in 5 h. The mechanical properties, such as hardness, tensile strength, and elongation, were improved with solution treatment time until about 5 h due to the dissolution of the $Al_2Cu$ particles. With further holding time, the mechanical properties did not change much. The solution treated specimens for over 5 h at $500^{\circ}C$ exhibit almost the same tensile properties even after aging at $250^{\circ}C$ for 3.5 h. Accordingly, the optimal solution treatment condition of the Al-Si-Cu AC2B alloy is considered to be 5 h at $500^{\circ}C$.

• Journal of the Korean Electrochemical Society
• /
• v.24 no.1
• /
• pp.7-12
• /
• 2021

In this study, we investigated the formation of the metal oxide nanostructure by anodization of aluminum 3104H18 alloy. The anodization was performed in pyrophosphoric acid (H4P2O7) electrolyte. By the control of anodization condition such as concentration of electrolyte, anodization temperature and applied voltage, nanoporous or nanofiber structures were obtained. The optimal anodization condition to form nanofiber structures are 75 wt% of H4P2O7 at 30 V and 20℃. When anodization was performed at over 40 V, nanoporous structures were formed due to accelerated dissolution reaction rate of nanofiber structures or increasing thickness of channel wall.

• Corrosion Science and Technology
• /
• v.20 no.6
• /
• pp.373-383
• /
• 2021

The effect of Cr addition to high Mn steel on flow-accelerated corrosion (FAC) behavior in a neutral aqueous environment was evaluated. For comparison, two types of conventional ferritic steels (API X70 steel and 9% Ni steel) were used. A range of experiments (electrochemical polarization and impedance tests, weight loss measurement, and metallographic observation of corrosion scale) were conducted. This study showed that high Mn steel with 3% Cr exhibited the highest resistance to FAC presumably due to the formation of a bi-layer scale structure composed of an inner Cr enriched Fe oxide and an outer Mn substituted partially with Fe oxide on the surface. Although the high Mn steels had the lowest corrosion resistance at the initial corrosion stage due to rapid dissolution kinetics of Mn elements on their surface, the kinetics of inner scale (i.e. Cr enriched Fe oxide) formation on Cr-bearing high Mn steel was faster in dynamic flowing condition compared to stagnant condition. On the other hand, the corrosion scales formed on API X70 and 9% Ni steels did not provide sufficient anti-corrosion function during the prolonged exposure to dynamic flowing conditions.

• Journal of Electrochemical Science and Technology
• /
• v.13 no.2
• /
• pp.213-226
• /
• 2022

In the present study, the corrosion behavior of aluminum Al-7075 tempered (T-6 condition) alloy was evaluated by immersion testing and electrochemical testing in 1.75% and 3.5% NaCl environment at acidic, neutral and basic pH. The data obtained by both immersion tests and electrochemical corrosion tests (potentiodynamic polarization and electrochemical impedance spectroscopy tests) present that the corrosion rate of the alloy specimens is minimum for the pH=7 condition of the solution due to the formation of dense and well adherent thin protective oxide layer. Whereas the solutions with acidic and alkaline pH cause shift in the corrosion behavior of aluminum alloy to more active domains aggravated by the constant flux of acidic and alkaline ions (Cl^- and OH^-) in the media which anodically dissolve the Al matrix in comparison to precipitated intermetallic phases (cathodic in nature) formed due to T6 treatment. Consequently, the pitting behavior of the alloy, as observed by cyclic polarization tests, shifts to more active regions when pH of the solutions changes from neutral to alkaline environment due to localized dissolution of the matrix in alkaline environment that ingress by diffusion through the pores in the oxide film. Microscopic analysis also strengthens the results obtained by immersion corrosion testing and electrochemical corrosion testing as the study examines the corrosion behavior of this alloy under a systematic evaluation in marine environment.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.5 no.4
• /
• pp.273-281
• /
• 2007

Hyperalkaline groundwater formed by groundwater-cement components and its reaction with bedrock in a nuclear waste repository were simulated by geochemical modeling. The result of groundwater-cement components reaction showed that the pH of water was 13.3 and the precipitated minerals were Brucite, Katoite, Calcium Silicate Hydrate(CSH1.1), Ettringite, Hematite, and Portlandite. The result of interaction between such minerals and groundwater sampled in Gyeongju area also showed that the pH of groundwater reached 12.4. Interaction between such hyperalkaline groundwater and granite was simulated by kinetic model during $10^3$ years. This result showed that the final pH of groundwater reached 11.2 and the variation of pH was controlled by dissolution/precipitation of silicate and CSH minerals. Groundwater quality was also determined by dissolution/precipitation of silicate, CSH, oxide minerals. Our results show that geochemical modeling of long-term hyperalkaline groundwater and rock interaction can contribute to the safety assessment of engineered barrier by predicting geochemical condition in repository site.

• Journal of Life Science
• /
• v.9 no.2
• /
• pp.194-200
• /
• 1999

Grinding aid is a necessary unit operation when the raw materials are handled in solid form, and the purpose is to improve the bioavailability by reducing the particle size. For the particle design of pefloxacin, the dry planetary ball-mill was used. With the drying process, 330 g of zirconia ball with its size of 2 mm in diameter and 10 g of pefloxacin were transferred to the pot and mixed well. The mixture was ground at 112 rpm (60 Hz) for 15, 30, and 60 min, respectively. The most satisfactory grinding products were generated at 15 min of grinding time for their particle size. The volume mean diameter $\X_50$ of the grinding products was 2.97 $\mu$m. X-ray diffraction (XRD), differential scanning calorimeter (DSC), and infrared spectroscopy (IR) patterns were relatively unchanged before pulverizing pefloxacin and in the progress of grinding. Thus, these results suggest that this pulverizing method can be used for grinding products without evident effect on stability of the drug pefloxacin. Dissolution test was carried out to set up the optimal detective condition against residual antibacteria of fish by HPLC. The grinding pefloxacin for 15 min is most effective in dissolution test.