• Journal of Welding and Joining
• /
• v.32 no.4
• /
• pp.26-33
• /
• 2014

The metallurgical and mechanical characteristics, toughness and corrosion resistance of dissimilar welds between super duplex stainless steel UNS S32750 and carbon steel ASTM A516Gr.70 have been evaluated. Three heat inputs of 21.12, 24.00, 26.88kJ/cm were employed to make joints of dissimilar metals with flux cored arc welding(FCAW). Based on microstructural examination, vermicular ferrite was formed in the first layer of weld at low heat input(21.12kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.61 while acicular ferrite was formed in last layer of weld at high heat input(26.88kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.72. Ferrite percentage in dissimilar welds was lowest in the first layer of weld regardless of heat inputs and it gradually increased in the second and third layers of weld. Heat affected zone showed higher hardness than the weld metal although reheated zone showed lower hardness than weld metal due to the formation of secondary austenite. Tensile strengths of dissimilar welds increased with heat input and there was 100MPa difference. The corrosion test by ferric chloride solution showed that carbon steel had poor corrosion resistance and pitting corrosion occurred in the first layer(root pass) of weld due to the presence of reheated zone where secondary austenite was formed. The salt spray test of carbon steel showed that the surface only corroded but the amount of weight loss was extremely low.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.189-194
• /
• 2003

It is important to evaluate strength of dissimilar weld zone to use dissimilar materials safely. This study examines mechanical characteristics of dissimilar weld zone between low alloy steel and austenitic stainless steel that satisfies welding related requirements of ASME Code, experimentally reviews metallurgical and mechanical properties at and adjacent to weld interface. It is confirmed that hardness singularity occurs at the weld interface, and that optimum buttering thickness is more than 5㎜ from view points of tensile & yield strength. From a macroscopic view, brittle fracture characteristics is observed in buttering weld zone by tensile test.

• Journal of Welding and Joining
• /
• v.34 no.3
• /
• pp.61-68
• /
• 2016

Characteristics of dissimilar metal welds between alloy steel ASTM A387 Gr. 91 and carbon steel ASTM A516 Gr.70 made with Flux cored arc welding(FCAW) have been evaluated in terms of microstructure, mechanical strength, chemical analysis by EDS as well as corrosion test. Three heat inputs of 15.0, 22.5, 30.0kJ/cm were employed to make joints of dissimilar metals with E91T1-B9C wire. Post-weld heat treatment was carried out at $750^{\circ}C$ for 2.5 h. Based on microstructural examination, tempered martensite and lower bainite were formed in first layer of weld metal. The amount of tempered martensite was decreased and the amount of lower bainite was increased with increasing heat input and layer. Heat affected zone of alloy steel showed the highest hardness due to the formation of tempered Martensite and lower Bainite. Tensile strengths of dissimilar welds decreased with increasing heat inputs. Dissimilar welds seemed to have a good hot cracking resistance due to the low HCS index below 4. The salt spray test of dissimilar metals showed that the corrosion rate increased with increasing heat inputs due to the increase of the amount of lower Bainite.

• Korean Journal of Materials Research
• /
• v.7 no.2
• /
• pp.162-170
• /
• 1997

This study has evaluated the dissimialr weldability of Incoloy 825 Ni base alloy with a mild steel(SS41). Further a compatibility study of wrveral Ni base filler metals with the dissimilar joint between the two alloys was also included. The dissimilar weldability of Incoloy 825 with mild steel is strongly dependent upon the type of the filler metal used. Among the filler metals, ENiCrFe which has a chemical comosition similar to that of Incoloy 825 was found to be most compatible to the joint. In addition, a filler metal which showed a good cracing resistance in one dissimiar alloy combination was not necessarily graranteed to other combination. Microstructural examination with SEM, TEM and Auger revealed that the solidification cracking resestance of the dissimilar joint. between Incoloy 835 and SS41 was closely with the Ti+Nb content and with the content of a low melting eutectic phase of Laves relatibve to that of MC type phase.

• Proceedings of the KSME Conference
• /
• 2001.06e
• /
• pp.436-443
• /
• 2001

In order to investigate the mixing of dissimilar grades during the arbitrary grade transition in bloom caster, a computational model has been developed. The model is fully transient and consists of two sub models, which account for mixing in the bloom tundish, mixing in the strand. The developed model was verified using concentration histories measured on 1 : 1 scale bloom tundish water model. The result of numerical model showed good agreement with the experimental results of water model. By using this numerical model, the mixing of dissimilar grades in bloom caster has been simulated. As that result, the characteristics of the steel mixing in the bloom tundish and strand was showed and the amount of the intermixed grade bloom was predicted.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.155-157
• /
• 2007

The Friction spot dissimilar welding of galvanized steel/Al6061-T6 was performed to investigate the mechanical characteristics of the joints. The presence of thin film of aluminum oxide on the surface and melting of zinc in the coating, made substandard joint characteristics for dissimilar Friction spot joining(FSJ) performed with out removing the coating. Where as, for dissimilar FSJ of galvanized steel/Al6061-T6 after removing the coating, superior agitation and welding quality has been obtained for a configuration of galvanized steel as the upper plate and Al6061-T6 as lower plate. The results from tensile tests and microscopic examination for various combinations of the welding parameters have been presented.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.18 no.4
• /
• pp.68-73
• /
• 2010

Welding conditions in process of spot welding must become optimum and need to guarantee stability and reliability of vehicle body considering dynamic load history. Because welding parameters in process of spot welding are various, it is difficult that the quality of spot weldment was included in the optimum levels. In this paper, we found the optimum welding conditions satisfying KS spot welding qualities using genetic algorithm and spot welding experiments of high tensile strength steel and galvanized steel. Those experiments were dissimilar weld and 2-lap spot welding. Genetic algorithm created random welding condition after that, selected optimum individuals by probability concept.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.244-249
• /
• 2007

In several locations of the pressurized water reactors, dissimilar metal welds using inconel welding wires are used to join the low alloy steel nozzles to stainless steel pipes. To evaluate the integrity and design the dissimilar welds, tensile and fracture properties variations are needed. In this study, dissimilar metal welds composed of SA508 Gr.3 LAS, inconel 82/182 weld, and TP316 stainless steel were prepared by gas tungsten arc welding and shielded metal arc welding technique. Microstructures were observed using optical and electron microscopes. Different tensile and fracture properties were observed depending on the specimen sampling position at room temperature and $320^{\circ}C,$ and that was discussed based on the microstructure characteristics. It was found that the strength at the bottom of weld was greater than at the top of the weld. Also, from the test data using small punch specimen, more detailed tensile property variations were evaluated.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2002.05a
• /
• pp.33-38
• /
• 2002

Nowdays, related with vehicle weight reduction, many automotive maker are trying to develop spaceframe. If aluminum member and steel member are applied together in constructing spaceframe, there will be many advantages in aspect of inclosing strength and saving weight of automotive. In this case, joining method of aluminum and steel members has to be proposed. For this method, electomagnetic joining has many advantages compared to welding. In this paper, joining of aluminum tube and steel tube using eletomagnetic pressure was studied and strength of joint was evaluated through commission test.

• Korean Journal of Metals and Materials
• /
• v.49 no.1
• /
• pp.64-72
• /
• 2011

The spot weldability of dissimilar metal joints between austenitic stainless steels (STS316)/IF steels and ferritic stainless steels (STS430)/IF steels was investigated. This study was aimed to determine the spot welding parameters for a dissimilar metal joint and to evaluate the dissimilar metal joint's weldability, including its welding nugget shape, tensile-shear strength, hardness, and microstructure. The comparison of these results was described in terms of fracture behavior. Compared with the weld lobe of similar metal joints, dissimilar metal joints (STS430/IF) had reduced weld current range. However, the weld lobe of STS316/IF steel joint showed increased weld current range. This is because the dilution of chemical composition in the molten weld pool suppressed the heat input being caused by Joule heat with current flow through the samples. The microstructure of the fusion zone was fully martensite and mixture of ferrite and martensite for austenitic stainless steel/IF steel and ferritic stainless steel/IF steel combination, respectively. The experimental results showed that the shape of nugget was asymmetric, in which the fusion zone of the austenitic and ferritic stainless steel sheet was larger due to the higher bulk-resistance. The predicted microstructure by using the Schaeffler diagram was well matched with experimental results. After peel test, the fracture was initiated from heat affected zone of ferritic stainless steel sheet side, however the final fracture was propagated into the IF steel sheet side due to its lower strength.