• Journal of the Korean Wood Science and Technology
• /
• v.47 no.5
• /
• pp.557-566
• /
• 2019

Radial and tangential water diffusion in Eucalyptus globulus wood was investigated using three mature trees from a forest in Khemis Sahel (North Morocco). Absorption and desorption kinetics experiments were conducted at ambient temperature ($25^{\circ}C$) and $30^{\circ}C$, respectively, and a relative humidity of 60%. The diffusion coefficients in the two directions were determined under imposed hygrothermal conditions; they were greater in the radial direction for the absorption as well as desorption processes. Convective drying under load, preceded by reconditioning and followed up by balancing, revealed the drying conditions that corresponded to the appropriate drying schedules for E. globulus wood. This was verified by measuring the cracks and bowsbefore and after drying of boards.

• Transactions of Materials Processing
• /
• v.13 no.1
• /
• pp.72-77
• /
• 2004

An Fe-25Cr steel was oxidized in Ar atmosphere at 973K with and without applying external stress of 30∼35 MPa. A 0.1$\mu\textrm{m}$ thick $Cr_2O_3$ scales formed during pre-treatment in Ar atmosphere. Initiation of cracking on the oxide scales took place at grain boundaries during the end of second creep stage, in which cracks were found nearly perpendicular to the tensile directions. On the contrary, a scale developed in $N_2$-0.1%$SO_2$ displaced a poor adherence on the metal substrate. In this sample, a fast grown of scales was observed during creep deformation, and the strength of materials was much lower than in Ar. The creep strain rate of $1.5{\times}10^{-7}/s$ and $5.8{\times}10^{-7}/s$ was determined in Ar and in $N_2$-0.1%$SO_2$ under 30MPa, respectively.

• Journal of Welding and Joining
• /
• v.20 no.6
• /
• pp.99-99
• /
• 2002

In order to evaluate the proper fracture strength of microstructures in a steel weldment, smaller size loading ball than used for a conventional small punch(CSP) testing is required due to regional limitation on constitutive structures. In this study, the minimized loading ball(φ 1.5mm) and bore diameter of lower die(φ 3mm) were designed for an advanced small punch(ASP) test. The results obtained from the ASP test were compared with those from a CSP testing for a X20CrMoV121 steel weldment. It was found that the ASP test clearly showed the microstructural dependance on fracture strength and ductile-brittle transition behavior of the weldment. In the ASP test, especially, the cracks tend to initiate for various directions within hemispherical indentation region of an objective structure in SP test. This indicates that the evaluation of more proper fracture strength for F.L+CGHAZ, FGHAZ and ICHAZ can be performed by means of the ASP test in a steel weldment.

• Journal of Welding and Joining
• /
• v.20 no.6
• /
• pp.823-829
• /
• 2002

In order to evaluate the proper fracture strength of microstructures in a steel weldment, smaller size loading ball than used for a conventional small punch(CSP) testing is required due to regional limitation on constitutive structures. In this study, the minimized loading ball(${\varphi}1.5mm$) and bore diameter of lower die(${\varphi}3mm$) were designed for an advanced small punch(ASP) test. The results obtained from the ASP test were compared with those from a CSP testing for a X20CrMoV121 steel weldment. It was found that the ASP test clearly showed the microstructural dependance on fracture strength and ductile-brittle transition behavior of the weldment. In the ASP test, especially, the cracks tend to initiate for various directions within hemispherical indentation region of an objective structure in SP test. This indicates that the evaluation of more proper fracture strength for F.L+CGHAZ, FGHAZ and ICHAZ can be performed by means of the ASP test in a steel weldment.

• Journal of the Korea Concrete Institute
• /
• v.12 no.2
• /
• pp.63-69
• /
• 2000

This study investigates a new method of using a concrete disk to calculate stress intensity factor (SIF) for mixed mode cases. The results indicate that the disk method is more accurate than three point bending test (TPB) in obtaining correct SIF values for mixed mode fracture propagation. Stress intensity factors $K_{I}$ and $K_{II}$ are calculated using a center notched disk subjected to splitting load. The notch angle is calculated by finite element (FEM). Fracture toughness $K_\textsc{k}$ of the concrete is obtained from the load intensities at the initiation of crack propagation. According to the finite element analysis(FEA) and disk test, the results show that mode I and mixed mode cracks propagate toward the directions of crack face and loading point, respectively. The results from FEA with maximum stress theory compare well with the experimental date. Unlike TPB method where an accurate fracture toughness value is difficult to obtain due to the irregular shape of load deflection curve and delayed final crack propagation (following slow stable cracking). fracture toughness value is easily measured in the disk test from the crack initial load. Therefore, it is safe to conclude that disk method is more advantageous than TPB method in analyzing combined mode fracture problems.

• The Journal of the Convergence on Culture Technology
• /
• v.9 no.2
• /
• pp.569-574
• /
• 2023

For maintenance of concrete structures, it is necessary to identify and maintain various defects. With the current method, there are problems with efficiency, safety, and reliability when inspecting large-scale social infrastructure, so it is necessary to introduce a new inspection method. Recently, with the development of deep learning technology for images, concrete defect classification research is being actively conducted. However, studies on contamination and spalling other than cracks are limited. In this study, a variety of concrete defect type classification models were developed through transfer learning on a pre-learned deep learning model, factors that reduce accuracy were derived, and future development directions were presented. This is expected to be highly utilized in the field of concrete maintenance in the future.

• Composites Research
• /
• v.32 no.6
• /
• pp.327-334
• /
• 2019

The delamination is a special mode of failure occurring in composite laminates. Several numerical studies with finite element analysis have been carried out on the delamination behavior of unidirectional composite laminates. On the other hand, the fracture for the multi-directional composite laminates may occur not only along the resin-fiber interface between plies known as interply or interlaminar fracture but also within a ply known as interyarn or intralaminar fracture accompanied by matrix cracking and fiber bridging. In addition, interlaminar and intralaminar cracks appear at irregular proportions and intralaminar cracks proceeded at arbitrary angle. The probabilistic analysis method for the prediction of crack growth behavior within a layer is more advantageous than the deterministic analysis method. In this paper, we analyze the crack path when the mode I load is applied to the cross-ply carbon/epoxy composite laminates and collect and analyze the probability data to be used as the basis of the probabilistic analysis in the future. Two criteria for the theoretical analysis of the crack growth direction were proposed by analyzing the stress field at the crack tip of orthotropic materials. Using the proposed method, the crack growth directions of the cross-ply carbon/epoxy laminates were analyzed qualitatively and quantitatively and compared with experimental results.

• Composites Research
• /
• v.37 no.3
• /
• pp.209-214
• /
• 2024

Graphene oxide (GO), known for its high stiffness, thermal conductivity, and electrical conductivity, is being utilized as a reinforcement in nanocomposite materials. This study evaluates the mechanical properties of epoxy nanocomposites incorporating GO and edge modified GO (E-GO), which has hydroxyl groups substituted only on its edges. GO/E-GO was uniformly dispersed in epoxy resin using ultrasonic dispersion, and mechanical properties were assessed through tensile testing. The results showed that the addition of nanoparticles increased both tensile strength and toughness. The tensile strength of the epoxy without nanoparticles was 74.4 MPa, while the highest tensile strength of 90.7 MPa was observed with 0.3 wt% E-GO. Additionally, the modulus increased from 2.55 GPa to 3.53 GPa with the addition of nanoparticles. Field emission scanning electron microscopy of the fracture surface revealed that the growth of cracks was impeded by the nanoparticles, preventing complete fracture and causing the cracks to split in multiple directions. E-GO, with surface treatment only on the edges, exhibited higher mechanical properties than GO due to its superior dispersion and surface treatment effects. These results highlight the importance of nanoparticle surface treatment in developing high-performance nanocomposite materials.

• Journal of Korean Society of Occupational and Environmental Hygiene
• /
• v.19 no.1
• /
• pp.39-50
• /
• 2009

This study is for the occurrence types of asbestos within 2 serpentinite mines, Baekdong and Kwangsi, Chungnam. They were exploited as serpentinite mines for several decades and closed in the 1980's. Asbestos with associated minerals were collected from the serpentinite bodies. They were examined with microscopes and FESEM, and analysed with EPMA, XRD and EDX to confirm for the types and/or compositions of the minerals. The serpentinites contain asbestos and nonasbestos minerals. Asbestos include chrysotile, tremolite and actinolite. The chrysotiles occur as veins of several mm to cm thickness with random directions. The tremolite and actinolite occur along cracks and fractures of several cm to ten cm thickness. They show mineralogical characteristics showing common asbestos under the microscope. Non-asbestos including chrysotile, lizardite, antigorite, tremolite and actinolite were also found within the serpentinite. The serpentines form pseudomorphic mesh textures, and also show hourglass or ribbon textures. The tremolite and actinolite were formed from the alterations of the pyroxenes and amphiboles, and plot between tremolite and magnesio hornblende. Tremolitic grains are colorless and occur as commonly elongated grains whereas the magnesio hornblende grains mainly show light green and occur as subhedral to euhedral grains. Overall results suggest that three types of asbestos are found in the Baekdong and Kwangsi serpentinite mines with varieties of the occurrences. Based on the occurrence types for the asbestos, additional studies are required for the asbestos of the top soil and the air.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.6 no.2
• /
• pp.20-27
• /
• 2010

In order to prevent the corrosion of component contacted primary water designed alloy 600 material in the nuclear power plant. But the primary water stress corrosion cracking(PWSCC) of alloy 600 and weld area occurs continuously due to the residual stress. The leakage accident resulted from PWSCC in the drain nozzle of the steam generator of domestic power plants. Heater sleeves of the pressurizer are welded with alloy 600 weld material and therefore exposed to the primary water environment. PWSCC occurred in heater sleeve material and weld area of many foreign power plants. The current issue of domestic nuclear power plants are consequently concentrated to PWSCC of similar material. In order to improve the detection and the sizing of the PWSCC in the welding sleeve of the pressurizer, the automatic UT system and multi-directions probe sets have been developed. The experimental studies have been performed using the mock-up block containing artificial reflectors(ID connected EDM notch) and semi-artificial cracks made from thermal fatigue. The automatic UT System is applied in the detection and the length sizing of the ID/OD on the tube and the J-groove weld area of the artificial reflectors and results of the detection and the sizing are compared respectively. Also, the developed automatic UT system is successfully accomplished to inspect the heater sleeve and the J-groove weld area on the pressurizer for the detection of PWSCC.