• Journal of Welding and Joining
• /
• v.32 no.4
• /
• pp.10-14
• /
• 2014

Laser aided Direct Metal Tooling(DMT) process is a kind of Additive Manufacturing processes (or 3D-Printing processes), which is developed for using various commercial steel powders such as P20, P21, SUS420, H13, D2 and other non-ferrous metal powders, aluminum alloys, titanium alloys, copper alloys and so on. The DMT process is a versatile process which can be applied to various fields like the mold industry, the medical industry, and the defense industry. Among of them, the application of DMT process to the mold industry is one of the most attractive and practical applications since the conformal cooling channel core of injection molds can be fabricated at the slightly expensive cost by using the hybrid fabrication method of DMT technology compared to the part fabricated with the machining technology. The main objectives of this study are to provide various characteristics of the parts made by DMT process compared to the same parts machined from bulk materials and prove the performance of the injection mold equipped with the conformal cooling channel core which is fabricated by the hybrid method of DMT process.

• Corrosion Science and Technology
• /
• v.17 no.4
• /
• pp.166-175
• /
• 2018

In this study, the electrochemical properties of CP-Ti (commercially pure titanium) and Ti-64 (Ti-6Al-4V) were evaluated and the effect of hydrofluoric acid on corrosion resistance and electrochemical properties was elucidated. Additive manufactured materials were made by DMT (Directed Metal Tooling) method. Samples were heat-treated for 1 hour at $760^{\circ}C$ and then air cooled. Surface morphologies were studied by optical microscope and SEM. Electrochemical properties were evaluated by anodic polarization method and AC-impedance measurement. The oxide film formed on the surface was analyzed using an XPS. The addition of HF led to an increase in the passive current density and critical current density and decreased the polarization resistance regardless of the alloys employed. Based on the composition of the oxide film, the compositional difference observed by the addition of HF was little, regardless of the nature of alloys. The Warburg impedance obtained by AC-impedance measurement indicates the dissolution of the constituents of CP-Ti and Ti-64 through a porous oxide film.

• Corrosion Science and Technology
• /
• v.17 no.1
• /
• pp.20-29
• /
• 2018

Ti and its alloys show the excellent corrosion resistance to chloride environments, but they show less corrosion resistance in HCl, $H_2SO_4$, NaOH, $H_3PO_4$, and especially HF environments at high temperature and concentration. In this study, we used the commercially pure titanium and Ti-6Al-4V alloy, and evaluated the effect of the manufacturing process on the electrochemical properties. We used commercial products of rolled and forged materials, and made additive manufactured materials by DMT (Directed Metal Tooling) method. We annealed each specimen at $760^{\circ}C$ for one hour and then air cooled. We performed anodic polarization test, AC impedance measurement, and Mott-Schottky plot to evaluate the electrochemical properties. Despite of the difference of its microstructure of CP-Ti and Ti-6Al-4V alloys by the manufacturing process, the anodic polarization behavior was similar in 20% sulfuric acid. However, the addition of 0.1% hydrofluoric acid degraded the electrochemical properties. Among three kinds of the manufacturing process, the electrochemical properties of additive manufactured CP-Ti, and Ti-6Al-4V alloys were the lowest. It is noted that the test materials showed a Warburg impedance in HF acid environments.