• Journal of the Korean Ceramic Society
• /
• v.51 no.4
• /
• pp.337-343
• /
• 2014

A single layer ultrafiltration(UF) ceramic membrane was prepared using boehmite sol. Boehmite was synthesized using a typical sol-gel process with optimization of the viscosity, pH, molar ratio of aluminum isopropoxide(AIP) and $HNO_3$. Boehmite sol was coated on a microfiltration(MF) support using the dip-coating method. MF support was dipped into the boehmite sol with a withdrawal speed of 5 mm/s and was maintained for 10 s in the boehmite sol, resulting in a uniform UF membrane layer of $10{\mu}m$ thickness. The porosity of the obtained membrane was measured and found to be 41.2%; the pore size was found to range from 80~100 nm, corresponding to the pore size of the UF membrane. The flux of the obtained membrane was initially 540 $L/m^2h$ and approximately 85% of the initial flux was recovered using a periodic back-flushing process.

• Journal of Integrative Natural Science
• /
• v.4 no.4
• /
• pp.311-314
• /
• 2011

Application of self-assembled monolayers (SAMs) to the fabrication of organic thin film transistor has been recently reported very often since it can help to provide ohmic contact between films as well as to form simple and effective electrode pattern. Accordingly, quality of these ultra-thin films is becoming more imperative. In this study, in order to manufacture a high quality SAM pattern, a hydrophobic alkylsilane monolayer and a hydrophilic aminosilane monolayer were selectively coated on $SiO_2$ surface through the consecutive procedures of a micro-contact printing (${\mu}CP$) and dip-coating methods under extremely dry condition. On a SAM pattern cleaned with SC1 solution immediately after ${\mu}CP$, poly(3,4-ethylenedioxythiophene) (PEDOT) source and drain electrode array were very selectively and nicely vapour phase polymerized. On the other side, on a SC1-untreated SAM pattern, PEDOT array was very poorly polymerized. It strongly suggests that the SC1 cleaning process effectively removes unwanted contaminants on SAM pattern, thereby resulting in very selective growth of PEDOT electrode pattern.

• Membrane Journal
• /
• v.25 no.5
• /
• pp.422-430
• /
• 2015

The present study announces that the pH value of seed coating solution makes a significant effect on the microstructure of silicalite-1 zeolite layer formed on ${\alpha}$-alumina support. Seed with an average diameter of 75 nm was dispersed in ethanol to prepare three kinds of seed coating solutions with different pH values, and dip-coated on the support. The pH value was controlled to be 2.2, 7.0, and 9.3, respectively. In the secondary growth process, pH 7 seed solution resulted an uniform, 3 to $4{\mu}m$ thick, completely covered, and 100 nm grained silicalite-1 zeolite separation layer. The uniformity and completeness were explained by a uniform, closely packed, multi-layered, and completely covered seed coating in the pH 7 condition. In the condition, ${\alpha}$-alumina support and seed are oppositely charged: support is positively charged (8.4 mV) and seed, negatively (-1.7 mV). The opposite charging induced a strong electrostatic attraction between seed and support, which made the good seed coating state. On the other hand, pH 2.2 and pH 9.3 seed solutions resulted non-uniform, partially covered, and around $1{\mu}m$ grained zeolite separation layer, since seed and support are the same sign charged in the conditions. The same sign charging induced a strong electrostatic repulsion between seed and support which caused a low coverage of seed. It could be concluded that the pH value of seed coating solution is a key parameter to determine the microstructure of silicalite-1 zeolite separation layer.

• Clean Technology
• /
• v.28 no.3
• /
• pp.218-226
• /
• 2022

As a result of the recent social transformation towards a hydrogen economy and carbon-neutrality, the demands for hydrogen energy have been increasing rapidly worldwide. As such, eco-friendly hydrogen production technologies that do not produce carbon dioxide (CO₂) emissions are being focused on. Among them, ammonia (NH₃) is an economical hydrogen carrier that can easily produce hydrogen (H₂). In this study, Ru/Al₂O₃ catalyst coated onmetallic monolith for hydrogen production from ammonia was prepared by a dip-coating method using a catalyst slurry mixture composed of Ru/Al₂O₃ catalyst, inorganic binder (alumina sol) and organic binder (methyl cellulose). At the optimized 1:1:0.1 weight ratio of catalyst/inorganic binder/organic binder, the amount of catalyst coated on the metallic monolith after one cycle coating was about 61.6 g L^-1. The uniform thickness (about 42 ㎛) and crystal structure of the catalyst coated on the metallic monolith surface were confirmed through scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. Also, a numerical optimization regression equation for NH3 conversion according to the independent variables of reaction temperature (400-600 ℃) and gas hourly space velocity (1,000-5,000 h^-1) was calculated by response surface methodology (RSM). This model indicated a determination coefficient (R²) of 0.991 and had statistically significant predictors. This regression model could contribute to the commercial process design of hydrogen production by ammonia decomposition.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.332-332
• /
• 2010

We have successfully demonstrated the inkjet printing method to create $Al_2O_3$ films withouWe have successfully demonstrated the inkjet printing method to create $Al_2O_3$ films without a high temperature sintering process. In order to remove the coffee ring effect in the ink drop, we have introduced a co-solvent system in order to create Marangoni flow in the ink drop, which leads to the dense packing of ceramic powders on the substrate during inkjet process. The packing density of the Inkjet-printed $Al_2O_3$ films is around 60% (max. 70%) which is very high compared to the value obtained from the same material films by other conventional methods such as film casting, dip coating process, etc. The voids inside the films (which are around 40% of the entire film volume) are filled with the polymer resin (Cyanate ester) by the infiltration process. This resin infiltration is also implemented by the inkjet printing process right after the Ah03 film ink-jetting process. The microstructures of the printed $Al_2O_3$ films are investigated by Scanning Electron Microscope (SEM) to understand the degree of packing density in the printed films. The inkjet-printed $Al_2O_3$ films have been characterized to investigate its thickness and roughness. Quality factor of the printed $Al_2O_3$ film is also measured to be over 300 at 1MHz.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.5
• /
• pp.254-259
• /
• 2003

In the fabrication process of transparent conducting thin films of the ATO (antimony-doped tin oxide) on a soda lime glass substrate by a sol-gel dip coating method, the effects of the $SiO_2$ buffer layer formed on the substrate and $N_2$ annealing treatment were investigated by XPS (X-ray photoelectron spectroscopy) analysis. Optical transmittance and electrical resistivity of the 400 nm-thick ATO thin films which were deposited on $SiO_2$ buffer layer/soda lime glass and then annealed under nitrogen atmosphere were 84 % and $5.0\times 10^{-3}\Omega \textrm{cm}$ respectively. The XPS analysis confirmed that a $SiO_2$ buffer layer inhibited Na ion diffusion from the substrate, resulting in prohibiting the formation of a secondary phase such as $Na_2SnO_3$ and SnO and increasing Sb ion concentration and ratio of $Sb^{5+}/Sb^{3+}$ in the film. And it was also found that $N_2$ annealing treatment leads to the reduction of $Sn^{4+}$as well as $Sb^{5+}$ however the reduction of $Sn^{4+}$ is more effective and therefore consequently results in decrease in the electrical resistivity to produce an excellent electrical properties of the film.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.12 no.8
• /
• pp.3532-3540
• /
• 2011

In order to improve flux of PTMSP/PDMS dense membrane, PTMSP/PDMS-PEI composite membrane with PEI support was prepared by phase inversion process and dip coating. These membranes were evaluated in terms of the removal of volatile organic compounds such as PCE, TCE, chloroform, 1,1,1-trichloroethane from wastewater by pervaporation. The selectivity and flux of PTMSP/PDMS dense membranes was in the range of 216.2 to 2394.4 and 244.3 to 428.2g/m2h, respectively. And pervaporation property of PTMSP/PDMS-PEI composite membrane was in the range of 215.5 to 2404.2 and 390.4 to 728.6g/m2h, respectively. PTMSP/PDMS-PEI composite membrane has remarkably greater flux than dense membranes with similar selectivity. It was possible for polymeric membranes used in this study to remove PCE selectively which is dissolved small quantity in water among other separable solutes. PTMSP/PDMS-PEI composite membrane showed the best performances among the silicone polymeric membranes, and has better durability and mechanical strength than dense membranes. PTMSP/PDMS-PEI composite membrane should be a useful candidate for the removal of volatile organic compounds dissolved in wastewater.

• Journal of Ocean Engineering and Technology
• /
• v.25 no.1
• /
• pp.32-38
• /
• 2011

Galvanized steel has gone through a chemical process to keep it from corroding. The steel gets coated in layers of zinc because rust will not attack this protective metal. For countless outdoor, marine, or industrial applications, galvanized steel is an essential fabrication component. The reduction of the corrosion rate of zinc is an important topic. In the past, a very popular way to reduce the corrosion rate of zinc was to use chemical conversion layers based on $Cr^{+6}$. However, a significant problem that has arisen is that the use of chromium salts is now restricted because of environmental protection legislation. Therefore, it is very important to develop new zinc surface treatments that are environmentally friendly to improve the corrosion resistance of zinc and adhesion with a final organic protective layer. In this study, a Urethane solution (only Urethane 20 wt.%; S-700) and an organic/inorganic solution with Si (Si polysilicate 10 wt.% + Urethane 10 wt.%; LRO-317) are used. Based on the salt spray test of 72 h, S-700 and LRO-317 had a superior effect for the corrosion resistance on EGI and HDGI, respectively.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.137-137
• /
• 2003

Optical amplificator have been used to compensate the losses in the optical signal transmission and processing. Today, there has been increasing demand for the very low cost optical amplifier. Sol-gel offers considerable potential both low cost manufacture, and for great flexibility in materials composition and structure. In addition, the sol-gel process is a very attractive method for producing porous materials with controlled structure. In this work, we present the potoluminescence properties of Er doped A1$_2$O$_3$/SiO$_2$ films. Erbium doped alumina nano sol was prepared by Al(NO$_3$)$_3$.9$H_2O$ and Er(NO$_3$)$_3$.5$H_2O$ through hydrolysis and peptization, and then GPS (3-Glycidoxypropyltrimethoxysilane) was added into Er doped alumina nano sol for organic- inorganic hybridization. Er doped A1$_2$O$_3$/SiO$_2$ film was obtained by spin coating, dip coating and thermal treatment from 30$0^{\circ}C$~120$0^{\circ}C$, and there were crack-free after thermal treatment. The thickness of film was measured SEM, and the porosity of film was characterized by BET and TGA. The crystal phase of Er doped A1$_2$O$_3$/SiO$_2$ were determined by XRD. Finally, the photoluminescence properties of Er doped A1$_2$O$_3$/SiO$_2$ films will be discuss with the consideration of porosity and crystallity.

• Polymer(Korea)
• /
• v.34 no.5
• /
• pp.405-409
• /
• 2010

New sol-gel precursors having the ability to protect iron against corrosion were synthesized and used to prepare organic-inorganic hybrid coatings based on epoxy. Bisphenol A epoxy was modified with 3-isocyanatopropyltriethoxysilane to improve the compatibility, and water and HCl were used as catalysts for sol-gel process. Various coating formulations were prepared depending on the type of sol-gel precursors and the amount of each ingredient, and cast on iron substrates by dip-coating and thermally cured. Corrosion protection properties of coated iron were studied by a salt spray test and electrochemical impedance spectroscopy under 0.1 M NaCl electrolyte. Hybrid coatings containing anticorrosive functional group exhibited excellent corrosion protection on iron, compared to that of typical hybrid coatings. From electrochemical impedance spectroscopy, the hybrid coatings containing anticorrosive functional group could maintaine the initial impedance after 500 h, while the impedance of hybrid coatings without them started to decrease after 24 h.