• Polymer(Korea)
• /
• v.33 no.1
• /
• pp.39-44
• /
• 2009

Polymer substrates were fabricated by using poly (phenylene ether) as a base resin, N,N'-m-phenylenedimaleimide (PDMI) as a crosslinking agent and decabromodiphenylethane as a flame retardant. The effects of crosslinking agent and flame retardant on physical properties such as dielectric property of the substrate were investigated. Thermal curing feature of PDMI with or without an initiator was analyzed by DSC, and then, PPE-PDMI test compositions were designed based on this result. Composite sheets were cast by film coater, laminated under vacuum and pressure, and then, the changes of dielectric constant, dielectric loss, peel strength, solder heat resistance and inflammability according to increasing amount of PDMI and flame retardant were evaluated, Dielectric constant and dielectric loss showed increasing trend with increasing amount of PDMI and flame retardant, but solder heat resistance and inflammability were improved. Peel strength was obtained higher than 1 kN/m when PDMI above 10 wt% was added, but slightly decreased as the amount of flame retardant increased. From the measured gel contents, the reaction mechanism of PPE-PDMI system was deduced to the formation of network structure by crosslinking PDMI with PPE rather than the formation of semi-IPN structure. In conclusion, the polymer composite substrate materials with dielectric constant of 2.52$\sim$2.65 and dielectric loss below 0.002 at 1 GHz were obtained and they will be proper for high frequency applications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.04a
• /
• pp.229-232
• /
• 1997

A free space transmission method using standard gain horn antennas in the frequency range from 9.0 to 10.5GHz is applied to determine the dielectric properties of grain such as rough rice, brown rife and barley. The dielectric constant and loss factor, which depend on the moisture content of the wetted grain are obtained from the measured attenuation and phase shift by vector network analyzer. The effect of density fluctuation, which is an important parameter governing the dielectric properties of grain, on the dielectric constant and loss factor is presented. A new density-independent model in terms of measured attenuation and moisture density is proposed for reducing the effects of density fluctuation on the moisture content measurement.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.549-552
• /
• 2002

$(SrBi_2Nb_2O_9)_{0.5}-(Bi_3TiNbO_9)_{0.5}$ ceramics were fabricated by the mixed-oxide method, and the structural and electrical properties with variation of ball-milling time were investigated. All SBN-BTN specimens showed the typical polycrystalline X-ray diffraction patterns without the presence of the second phase. The SBN-BTN specimen sintered at $1200^{\circ}C$ and ball-milled for 168h showed the average grain size of $16{\mu}m$. The dielectric constant and dielectric loss of the SBN-BTN specimen sintered at $1150^{\circ}C$ and ball-mill for 72h were 225, 0.4% at 1KHz, respectively.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.3
• /
• pp.38-46
• /
• 1996

The purpose of this study is to develop the miniaturized duplexer filter for mobile communications using high dielectric constant (${\varepsilon}$r > 100, 180) ceramic resonators. Duplexer filter was ocmposed of ceramic resonators which has been developed using BNT system and SCT system, respectively. Developed duplexer filter was formed to have Tx frequency band at 836.5 (($\pm$12.5)MHz and Rx frequency band at 881.5 ($\pm$12.5)MHz. Insertion loss at Tx frequency band was 1.41dB and 1.46dB, insertion loss at Rx frequency band was 3.49dB and 3.65dB, respectively. Especially, duplexer filters using dielectric cermaics with ${\varepsilon}$r = 180 were 8% smaller than commercially manufactured duplexer filters using dielectric ceramics with ${\varepsilon}$r = 90 by murata.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.309-310
• /
• 2005

Generally, the dielectric constant and loss tangent are gotten by resonators. This paper presents analysis of the comparing the dielectric constant and loss tangent from the Ring, T and series gap structures. The T structure can be analyzed easily at wideband characteristic with simple design. the Ring can ignore the radiation loss from the open-ended effect. the Series gap can get more accurate permittivity than a Ring structure. The Used materials were dupont9599 LTCC ceramic and daeju0086 Ag.

• Electrical & Electronic Materials
• /
• v.7 no.6
• /
• pp.534-542
• /
• 1994

Microstructures and dielectric properties of (Sr$_{1-x}$ .Ca$_{x}$)TiO$_{3}$+0.006Nb$_{2}$O$_{5}$ (0.05.leq.x.leq.0.2) ceramic were investigated. The specimens fired in a reducing atmosphere(N$_{2}$) were painted on the surface with CuO paste, and then annealed at 1100.deg. C for 2 hr. SEM and EDAX revealed that CuO penetrated rapidly into the bulk along the grain boundaries during the annealing. Grain size increased with increasing Ca content up to 15[mol%], but decreased with further addition. In the specimens with 10-15[mol%l of Ca, excellent dielectric properties were obtained as follows; dielectric constant <25000, dielectric loss(tan .delta[%]) <0.3[%] and capacitance change rate with temperature <.+-.[%], respectively. All the specimens in this study exhibited dielectric relaxation with frequency as a function of the temperature. The dispersive frequency was over 10$^{6}$ [Hz].z].

• Proceedings of the KIEE Conference
• /
• 2004.07c
• /
• pp.1621-1623
• /
• 2004

The $Pb(Zr_{0.52}Ti_{0.48})O_3/(Ba_{0.6}Sr_{0.4})TiO_3$ [PZT(52/48)/BST(60/40)] heterolayered thin films were deposited on Pt/Ti/$SiO_2$/Si substrates by using the RF sputtering method with RF powers of 60,70,80,90[W]. All thin films showed the peaks of the tetragonal phase. Increasing the RF power, dielectric constant and loss of the PZT(52/48)/BST(60/40)] heterolayered thin films were decreased. The thickness ratio of PZT and BST thin films was 1/1. The relative dielectric constant and the dielectric loss of the PZT(52/48)/ BST(60/40) heterolayered thin films were 562 and 13%, respectively.

• 전기의세계
• /
• v.30 no.10
• /
• pp.639-644
• /
• 1981

PVC is a kind of electric insulation polymer. But we get some deteriorations in electrical characteristics of the PVC, when it is used on the radioactive field. In order to find out the cause of the deterioration, we investigate the surface-resistance, volume-resistance, dielectric constant and dielectric loss angle of the soft and hard PVC which is irradiated by the Co$^{60}$ .gamma. radioactivity. From the experiment, we can conclude the followings 1. Radio-activity proof characteristic in the soft PVC is stronger than in the hard PVC. 2. The resistance of PVC which is irradiated by the radio-activity decrease exponentially. 3. The dielectric constant and the dielectric loss angle of PVC irradiated by Co$^{60}$ .gamma.ray reach maximum value in first few time.

• Journal of the Korean Ceramic Society
• /
• v.30 no.8
• /
• pp.671-677
• /
• 1993

Effects of PbTiO3 addition on dielectric properties and extent of PbO loss in Nd-doped Pb(Mg1/3Nb2/3)O3 system were investigated. As the proportion of dopping increased, the phase transition temperature shifted to low region, and the dielectric constant at room temperature decreased rapidly. But as the proportion of PbTiO3 increased, the phase transition temperature shifted to high retion, and the dielectric constant at room temperature increased. The substitution of Nd3+ for Pb2+ decreased the amount of PbO evaporation, therefore the sample sintered well in case of only 1 mole% adding excess PbO.

• Journal of Soil and Groundwater Environment
• /
• v.9 no.3
• /
• pp.1-11
• /
• 2004

To evaluate the applicability of dielectric constant measurement method on the geoenvironmental investigation of subsurface contaminated by landfill leachate, the analysis on dielectric characteristics of sand containing contaminated pore water by landfill leachate was performed. The separate real and imaginary parts of dielectric constant were investigated in the frequency range of 75kHz to 12MHz. The real part of dielectric constant increased at the lower frequency wherea the real part of dielectric constant decreased at the higher frequency as the concentration of leachate increased. These results can be explained by the frequency dependence of space charge polarization and orientation polarization. The imaginary part of dielectric constant on the contaminated sand with leachate increased with their concentration for whole frequency range. These results are caused by the increase of energy loss due to the enhancement of conduction in soil with leachate concentration. The results in this study indicate that the dielectric constant measurement method has potential in evaluating the contaminated soil and pore water by landfill leachate.