Five different composition UV-cured poly(urethane acrylate-co-acrylic acid) (PU-co-AA) films have been prepared by reacting isophorone diisocyanate(IPDI), polycaprolactone triol(PCLT), 2-hydroxyethyl acrylate(HEA), and different weight ratio trimethylolpropane triacrylate(TMPTA) and acrylic acid(AA) as diluents, and characterized using a Fourier transform infrared spectroscopy(FT-IR). The adhesion properties onto the stainless steel, morphology, mechanical hardness, and electrical property of UV-cured PU-co-AA films were investigated as a function of acrylic acid(AA) content. All the PU-co-AA films are structure-less and the molecular ordering and packing density decreased with increasing content of AA due to the flexible structure and -COOH side chains in AA. The crosscut test showed that PU-co-AA films without AA and with low content of AA showed 0% adhesion(0B) and the adhesion of PU-co-AA films in the range of 40-50% AA increased dramatically as the content of AA increases. The pull-off measurements showed that the adhesion force of PU-co-AA films to stainless steel substrate varied from 6 to 31 kgf /$cm^2$ and increased linearly with increasing AA content. The mechanical hardness also decreased as the content of AA increases. This may come from relatively linear and flexible structure in AA and low crystallinity in PU-co-AA films with higher content of AA. The higher AA-containing PU-co-AA films showed higher dielectric constant due to the increase of polarization by introducing AA monomer. In conclusion, the physical properties of UV-cured PU-co-AA films are strongly dependent upon the content of AA and the incorporation of AA in polyurethane acrylate is very useful way to increase the adhesion strength of UV-curable polymers on the stainless steel substrate.

• Journal of Sensor Science and Technology
• /
• v.7 no.3
• /
• pp.154-162
• /
• 1998

A planar Bi-Sb multijunction thermal converter with high thermal sensitivity and small ac-dc transfer error has been fabricated by preparing the bifilar thin film Pt-heater and the hot junctions of thin film Bi-Sb thermopile on the $Si_{3}N_{4}/SiO_{2}/Si_{3}N_{4}$-diaphragm, which functions as a thermal isolation layer, and the cold junctions on the dielectric membrane supported with the Si-substrate, which acts as a heat sink, and its ac-dc transfer characteristics were investigated with the fast reversed dc method. The respective thermal sensitivities of the converter with single bifilar heater were about 10.1 mV/mW and 14.8 mV/mW in the air and vacuum, and those of the converter with dual bifilar heater were about 5.1 mV/mW and 7.6 mV/mW, and about 5.3 mV/mW and 7.8 mV/mW in the air and vacuum for the inputs of inside and outside heaters, indicating that the thermal sensitivities in the vacuum, where there is rarely thermal loss caused by gas, are higher than those in the air. The ac-dc voltage and current transfer difference ranges of the converter with single bifilar heater were about ${\pm}1.80\;ppm$ and ${\pm}0.58\;ppm$, and those of the converter with dual bifilar heater were about ${\pm}0.63\;ppm$ and ${\pm}0.25\;ppm$, and about ${\pm}0.53\;ppm$ and ${\pm}0.27\;ppm$, respectively, for the inputs of inside and outside heaters, in the frequency range below 10 kHz and in the air.

• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.3
• /
• pp.33-38
• /
• 2021

Recently, rollable and foldable displays are attracting great attention in the flexible display market due to their excellent form factor. To predict and prevent the mechanical failure of the display panels, it is essential to accurately understand the mechanical properties of brittle SiN_x thin films, which have been used as an insulating film in flexible displays. In this study, tensile properties of the ~130 nm- and ~320 nm-thick SiN_x thin films were successfully measured by coating a ~190 nm-thick organic nano-support-layer (PMMA, PS, P3HT) on the fragile SiN_x thin films and stretching the films as a bilayer state. Young's modulus values of the ~130 nm and ~320 nm SiN_x thin films fabricated through the controlled chamber pressure and deposition power (A: 1250 mTorr, 450 W/B: 1000 mTorr, 600 W/C: 750 mTorr, 700 W) were calculated as A: 76.6±3.5, B: 85.8±4.6, C: 117.4±6.5 GPa and A: 100.1±12.9, B: 117.9±9.7, C: 159.6 GPa, respectively. As a result, Young's modulus of ~320 nm SiN_x thin films fabricated through the same deposition condition increased compared to the ~130 nm SiN_x thin films. The tensile testing method using the organic nano-support-layer was effective in the precise measurement of the mechanical properties of the brittle thin films. The method developed in this study can contribute to the robust design of the rollable and foldable displays by enabling quantitative measurement of mechanical properties of fragile thin films for flexible displays.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.33 no.2
• /
• pp.83-90
• /
• 2023

The β-Ga₂O₃ has the most thermodynamically stable phase, a wide band gap of 4.8~4.9 eV and a high dielectric breakdown voltage of 8MV/cm. Due to such excellent electrical characteristics, this material as a power device material has been attracted much attention. Furthermore, the β-Ga₂O₃ has easy liquid phase growth method unlike materials such as SiC and GaN. However, since the grown pure β-Ga₂O₃ single crystal requires the intentionally controlled doping due to a low conductivity to be applied to a power device, the research on doping in β-Ga₂O₃ single crystal is definitely important. In this study, various source powders of un-doped, Sn 0.05 mol%, Sn 0.1 mol%, Sn 1.5 mol%, Sn 2 mol%, Sn 3 mol%-doped Ga₂O₃ were prepared by adding different mole ratios of SnO₂ powder to Ga₂O₃ powder, and β-Ga₂O₃ single crystals were grown by using an edge-defined Film-fed Growth (EFG) method. The crystal direction, crystal quality, optical, and electrical properties of the grown β-Ga₂O₃ single crystal were analyzed according to the Sn dopant content, and the property variation of β-Ga₂O₃ single crystal according to the Sn doping were extensively investigated.

• Journal of the Korean Vacuum Society
• /
• v.15 no.5
• /
• pp.527-533
• /
• 2006

Spinel $LiNi_xMn_{2-x}O_4$ thin films were synthesized up to x = 0.9 by a sol-gel method employing spin-coating. The Ni-substituted films were found to maintain cubic structure at low x but to exhibit tetragonal structure for $x{\geq}0.6$. Such cubic-tetragonal phase transition indicates that $Ni^{3+}(d7)$ ions with low-spin $(t_{2g}^6,e_g^1)$ state occupy the octahedral sites of the compound, thus being subject to the Jahn-Teller distortion. By x-ray photoelectron spectroscopy both $Ni^{2+}$ and $Ni^{3+}$ ions were detected. Optical properties of the $LiNi_xMn_{2-x}O_4$ films were investigated by spectroscopic ellipsometry (SE) in the visible?ultraviolet range. The measured dielectric function spectra by SE mainly consist of broad absorption structures attributed to charge-transfer (CT) transitions, $O^{2-}(2p){\rightarrow}Mn^{4+}(3d)$ for 1.9 $(t_{2g})$ and $2.8{\sim}3.0$ eV $(e_g)$ structures and $O^{2-}(2p){\rightarrow}Mn^{3+}(3d)$ for 2.3 $(t_{2g})$ and $3.4{\sim}3.6$ eV $(e_g)$ structures. Also, sharp absorption structures were observed at about 1.6, 1.7, and 1.9 eV, interpreted as due to d-d crystal-field transitions within the octahedral $Mn^{3+}$ ion. The strengths of these absorption structures are reduced by the Ni substitution. Rapid reduction of the CT transition strength involving the eg states for x = 0.6 is attributed to the reduced wavefunction overlap between the $e_g$ and the $O^{2-}(2p)$ states due to the tetragonal extension of the lattice constant by the Jahn-Teller effect.