Graphite and MoS2 were added respectively as a lubricant to improve the cutting efficiency of micro blades which contains diamond abrasive. Strength, fracture toughness, and life span of micro-blades were observed to decrease with the increase in diamond abrasive and lubricant content. Wearing mode of micro-blades and the cutting efficiency were also found to be affected by the content of diamond abrasive and the addition of lubricants.

• Journal of the Korean institute of surface engineering
• /
• v.45 no.1
• /
• pp.37-42
• /
• 2012

$WS_2$ powder was added to the Cu/Sn bond metal of diamond micro-blades for machining of semi-conductor and IC chips to improve cutting efficiency. The effect of $WS_2$ additive on cutting efficiency was investigated and compared with the micro-blades with $MoS_2$ developed in previous research. Flexural strength, frictional coefficient, and wear resistance of blades decreased with $WS_2$ but wear depth increased. It was found that the blades including $WS_2$ consumed less momentary energy than the blades containing $MoS_2$ during dicing test. Micro-blades containing $WS_2$ exhibited lower flexural strength than the blades with $MoS_2$ resulting from higher amount of sintering defects relevant to the less effectiveness of $WS_2$ on fluidity. The effect of $WS_2$ and $MoS_2$ on fluidity during sintering was analyzed in terms of mismatching degree between the longitudinal direction of lubricant particles and the perpendicular direction to the compact loading. The blade with 8.1 vol.% of $WS_2$ showed the best cutting efficiency.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.1
• /
• pp.41-45
• /
• 2010

The effect of $MoS_2$ and graphite content on wear resistance and mechanical properties of Cu/Sn bonded diamond micro blades was comparatively investigated in terms of volume and weight fraction. For the evaluation of endurance and cutting performance, instantaneous electric power consumption and cumulative wear loss during cutting glass work piece at constant velocity were measured with the micro blades of the wide range of lubricant content. The energy consumption of blades for glass cutting decreased with the content of lubricants. Wear amount of blade in volume increased with the amount of lubricant addition. It was found to be relevant to the decrease in flexural strength and hardness with the amount of lubricants. With the same amount of lubricant content in volume fraction $MoS_2$ showed superiority in mechanical properties and cutting performance than graphite while graphite could result in stronger effect on lowering electric consumption during cutting work piece for the same weight percent fraction than $MoS_2$ because of lower density.

• Journal of the Korean institute of surface engineering
• /
• v.46 no.1
• /
• pp.22-28
• /
• 2013

$WS_2$ particles were added to micro-diamond blades with Cu/Sn binding metal as lubricants to improve cutting efficiency. It was found in previous works that the added $WS_2$ lubricant could reduce remarkably the momentary energy consumption during dicing tests but increased wear rate slightly owing to weak bonding between lubricant particles and bond metals. In the present work, the surface of $WS_2$ lubricant particles were etched for activating the surface of $WS_2$ particles that provide even distribution of particles during powder mixing process and improvement of wetting at the interfaces between $WS_2$ particles and molten Cu/Sn bond metals during pressurized sintering so that could provide the improved strength of micro-blades and result in extended life. Chipping behavior of workpiece with the types of micro-blades including $WS_2$ were compared because it is important in semiconductor and micro-packaging industries to control average roughness and straightness of sliced surface which is closely related with quality.

• Journal of Industrial Technology
• /
• v.27 no.B
• /
• pp.137-144
• /
• 2007

Sintering condition and various chemical composition of bond materials for micro-blades were studied. The methods mixing of pure powders and using pre-alloyed powders for compaction and sintering were compared and optimized in terms of the evaluation of bending strength and fractographic study. The effect of the amount of graphite as a lubricant and diamond abrasive on the strength of sintered bond materials and fracture toughness was investigated. The strength decreased with increasing the amount of graphite and diamond abrasive.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.6
• /
• pp.335-340
• /
• 2008

Cutting performance and wear behavior were studied with the diamond micro-blade of Cu/Sn bond materials containing various amount of lubricant materials such as graphite and $MoS_2$. Measurement of instantaneous electric power consumption for cutting glass workpiece at the constant velocity was conducted and proposed as a method to assess cutting efficiency. The energy consumption of micro-blade for glass cutting decreased with the content of graphite and $MoS_2$ while wear amount of blade in volume increased with the amount of lubricant addition during the dicing test. It is because that hardness, flexural strength, and fracture toughness ($K_{IC}$) reduced with the amount of lubricant addition. Blades with $MoS_2$ additive showed higher mechanical properties than those with graphite additives when the same amount of the lubricant additive in wt.% was added. Due to the lower density of graphite than $MoS_2$, higher volume fraction of graphite could result in stronger effect on lowering electric power consumption by reducing the friction between blade and work piece however increasing wear rate due to the reduction in strength and fracture toughness. Adhesive wearing mode of micro blade could be remarkably improved by the addition of graphite as well as $MoS_2$.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.1
• /
• pp.16-22
• /
• 2019

The structural change of DLC coatings during long-term wear test and dicing test under the low loading condition was investigated. DLC coatings were applied for the precision injection molds of a modified SNCM steel for the extension of life and the micro-diamond blades for the high cutting efficiency and the increase in life. A ball-on-disc wear tests in the mold steel and a dicing tests in the micro-diamond blades were conducted to understand degradation of DLC coatings. The degradation of DLC coatings for the injection mold steel and the micro-diamond blades during the wear and dicing tests were studied with Raman Spectroscopy. Raman peaks were divided two bands(D band and G band) to study the degradation process of DLC structure. By the wear test, polished condition of wear marks were observed to be maintained until 10 hrs of wear test period is given, but small striation marks appeared in 20 hours wear test. It was observed that $I_D/I_G$ ratios changed as the degradation of DLC coatings is proceeded during the wear tests and the dicing tests. It is suggested that the change in $I_D/I_G$ value possibly reflected from the composition of $sp^2$ and $sp^3$ bondings in DLC layers relevant to the change in mechanical and physical property.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.144-145
• /
• 2012

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.200-201
• /
• 2014

다이아몬드 마이크로 블레이드의 절삭 효율을 향상시키고 절삭 과정에서의 블레이드 측면 경질 박막이 절삭 성능에 미치는 영향을 연구하기 위해 Cu/Sn 금속 결합재에 $MoS_2$와 $WS_2$ 고체 윤활제를 각각 동일 분율 첨가한 후 PAPVD법으로 DLC 박막을 블레이드의 측면에 증착하였다. 실착 절삭 시험을 위해 마이크로 블레이드 시편을 제조하여 충분한 드레싱 과정 후 절삭 시험을 행하였으며 절삭 중 순간 소모 전력과 블레이드의 마모량을 비교 평가하였다. DLC 코팅은 절삭 중 측면에 안정적으로 존재하며 측면 지립의 돌출을 억제하고 마찰을 감소시켜 절삭 효율이 향상되었으며 결과적으로 수명이 증가하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.324-325
• /
• 2012

다이아몬드 마이크로 블레이드의 절삭 효율을 향상시키고 소결 공정 중 윤활제의 유동성과 젖음성이 다이아몬드 마이크로 블레이드의 물성에 미치는 영향을 연구하기 위해 Cu/Sn 금속 결합재에 표면을 부식시킨 $WS_2$와 부식을 시키지 않은 $WS_2$ 윤활제를 각각 동일한 체적 분율로 첨가하였다. 윤활제의 표면 개질에 따른 마이크로 블레이드 결합재의 내마모성과 굽힘 강도 시험을 행하였고, 실착 절삭 시험을 위한 마이크로 블레이드 시편을 제작하여 수명 및 효율을 평가하였다. Cu/Sn 금속 결합재 파면에서의 $WS_2$ 입자 방향 분석을 통해 표면 개질 과정을 거친 $WS_2$가 압축소결 공정 중 압축 방향에 수직하게 위치하려는 경향이 크게 나타났으며, 이는 소결체의 강도와 경도를 향상시켰다. 마이크로 블레이드의 절삭 효율 및 수명을 평가하기 위한 실착 절삭 시험 결과, 윤활제 표면 부식처리는 처리하지 않은 경우에 비하여 절삭성능은 비슷하게 관찰되었으나 결합재와의 계면 결함을 줄이므로써 블레이드의 수명을 연장시킬 수 있었다.