• Journal of Korean Academy of Oral and Maxillofacial Radiology
• /
• v.26 no.2
• /
• pp.133-145
• /
• 1996

Aspirating or swallowing foreign bodies is a common occurrence. If they are wholly or partly radiopaque, their localization in and progress through the gastrointestinal tract can be more effective. Of the dental origin foreign materials swallowed, the most common things are fragments of anterior maxillary partial denture. But the radiopacity of denture base resins is not sufficient to determine the location of the objects. The purpose of this study was to develop a radiopaque dental acrylic resin, which has clinically detectible radiopacity with minimal change of mechanical properties and color. The radiopacity, color change(CIE 6..E) and microhardness of acrylic resins were determined after mixing barium sulfate or iodide compound. Thermocycling course was conducted to determine the change of characteristic of resins after using for a long time in the mouth. Five or ten percent of barium sulfate to total weight of cured material was mixed with heat curing dental acrylic resin or chemically curing orthodontic resin. In the case of iodide compound, the mixing ratio was two or three percent. After mixing the high radiopaque materials, resin was cured to 20×20×2 mm plate, polished with #600 sand paper and finally polished with Microcloth(Buehler). The specimens were thermocycled in 5 and 55 t distilled water for 2,000 times, and the measurement of radiopacity, color and Vickers hardness was repeated every 500 times thcrmocycling. The radiopacity of specimens on the X -ray films was measured with densitometer(X-rite). The color change was detennined with differential colorimeter(Model TC-6FX, Tokyo Denshoku), and the Vickers hardness number was measured with microhardness tester(Mitsuzawa). The following results were obtained : 1. All the three variables, the kinds of acrylic resins, the mixing or the kinds of high radiopaque materials and thermocycling, had combined effect on the radiopacity of the dental acrylic resins(p<0.0l). 2. The two variables, the mixing or the kinds of high radiopaque materials and thermocycling, influenced on the radiopacity of the dental acrylic resins(p<0.01). But the kinds of acrylic resins did not influence on the color change of mixed dental acrylic resins(p>0.05). 3. Each of the three variables, the kinds of acrylic resins, the mixing or the kinds of high radiopaque materials and thermocycling, influenced on the radiopacity of dental acrylic resins(p<0.0l). 4. The high radiopaque materials used in this study did not yield clinically usable radiopacity, and the color change was great after mixing those materials.

• The Journal of Korean Academy of Prosthodontics
• /
• v.54 no.3
• /
• pp.286-290
• /
• 2016

Recently, flexible removable prosthesis with thermoplastic resin clasp has increasingly become popular. In comparison with conventionally used acrylic resin, thermoplastic resin has lower flexural strength and elastic modulus. Thus, flexible removable prosthesis has low risk of fracture, so denture base can be made thin and light, increasing patient comfort. Also, it can passively sit at tooth undercut during rest, so abutment teeth need minimum or no preparation. In this case report, a 44 year old female patient with mild velopharyngeal insufficiency was treated with a palatal lift prosthesis made of polyester thermoplastic resin. Since the patient had no missing tooth and desired conservative treatment, the flexible removable prosthesis provided relatively satisfactory results.

• The korean journal of orthodontics
• /
• v.17 no.1
• /
• pp.135-148
• /
• 1987

To investigate the relationship between craniofacial growth and bone maturity of the hand wrist in normal occlusion, the author took cephalogram and handwrist radiogram of 391 students (male 192, female 199) and assessed the measurements of cephalogram according to skeletal maturity stages of the hand and wrist. In this study, four skeketal stages and 36 linear, angular measurements of the cephalometrics were selected. In hand-wrist X-ray the bones used to determine skeletal maturity were the middle phalanges of the third finger, and distal epiphysis of the radius. In cephalogram, the landmark used to measure the angle and length were N, S, Po., Ar., Go., Me., Gn., Pog., Point B, Point A, ANS, PNS, Or., U1, L1, U6, L6 etc.. The results were as follows, 1. The table of mean, standard deviation, p-value from measurements were made in each group and both sex. 2. The increased measurements according to skeletal maturity were anterior cranial bese length, posterior cranial base length, ramus height, anterior facial height, posterior facial height, L1 to mandibular plane (mm), facial plane angle. In contrast to, decreased measurements were genial angle, facial cnvexity and facial plane angle. 3. Denture pattern measurements (IMPA, FMIA, occlusal plane to Go-Gn, interincisal angle, U1 to SN plane, U1 to SN plane, U1 to facial plane, L1 to facial plane etc.) .had nothing to do with skeletal maturity. 4. Skeletal maturity had close relationship with craniofacial growth, but had little to do with tooth development.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.6
• /
• pp.589-598
• /
• 2001

The fracture of acrylic resin dentures remains an unsolved problem. Therefore, many investigations have been performed and various approaches to strengthening acrylic resin, for example, the reinforcement of heat-cured PMMA resin using glass fibers, have been suggested over the years. The aim of the present study was to investigate the effect of short glass fibers treated with silane coupling agent on the transverse strength of heat-polymerized PMMA denture base resin. To avoid fiber bunching and achieve even fiber distribution, glass fiber bundles were mixed with PMMA powder in conventional mixer whose blade was modified to be blunt. Composite of glass fiber($11{\mu}m$ diameter, 3mm & 6mm length, silane treated) and PMMA resin was made. Transverse strength and Young's modulus were estimated. Glass fibers were incorporated with 1%, 3%, 6% and 9% by weight. Plasticity and workability of dough was evaluated. Fracture surface of specimens was investigated by SEM. The results of this study were as follows 1. 6% and 9% incorporation of 3mm glass fibers in the PMMA resin enhanced the transverse strength of the test specimens(p<0.05). 2. 6% incorporation of 6mm glass fibers in the PMMA resin increased transverse strength, but 9% incorporation of it decreased transverse strength(p<0.05). 3. When more than 3% of 3mm glass fibers and more than 6% of 6mm glass fibers were incorporated, Young's modulus increased significantly(p<0.05). 4. Workability decreased gradually as the percentage of the fibers increased. 5. Workability decreased gradually as the length of the fibers increased. 6. In SEM and LM, there was no bunching of fibers and no shortening of fibers.

• Journal of Technologic Dentistry
• /
• v.42 no.2
• /
• pp.91-98
• /
• 2020

Purpose: This study is to compare the flexural strength and modulus by inserting a mesh and stick type fiberglass reinforcement into resin specimens. Methods: Wax specimens (length 64 mm, width 39 mm, thickness 5 mm) are prepared according to ISO 20795-1:2013. Mesh type and stick type glass fiber reinforcements were prepared. The prepared wax specimens were used plaster and flask for investment. The flask was separated and the wax was removed. The heat curing resin was injected into the flask, and then a mesh type and stick type fiberglass reinforcement were inserted. The prepared resin specimen was cut into three equal parts (length 64 mm, width 10 mm, thickness 3.3 mm). The mesh type glass fiber reinforcement (MT group) and the stick type glass fiber reinforcement (ST group) were classified into two groups. The prepared specimen was measured using a universal testing machine (UTM). The data were analyzed by Mann-Whitney U test, and the significance level was set to 0.05. Results: In the flexural strength, the ST group was higher than the MT group, and there was a significant difference between the two groups (p<0.05). In the flexural modulus, the ST group was higher than the MT group, and there was a significant difference between the two groups (p<0.05). Conclusion: The stick-type glass fiber inreased the flexural strength than the mesh-type glass fiber reinforcement.

• The Journal of Advanced Prosthodontics
• /
• v.8 no.4
• /
• pp.290-295
• /
• 2016

PURPOSE. The aim of this study was to evaluate the effect of paracetic acid (PAA) and ozone disinfection on the tensile bond strength (TBS) of silicone-based resilient liners to acrylic resins. MATERIALS AND METHODS. One hundred and twenty dumbbell shaped heat-polymerized acrylic resins were prepared. From the mid segment of the specimens, 3 mm of acrylic were grinded off and separated parts were reattached by resilient liners. The specimens were divided into 2 control (control1, control7) and 4 test groups of PAA and ozone disinfection (PAA1, PAA7, ozone1 and ozone7; n=10). While control groups were immersed in distilled water for 10 min (control1) and 7 days (control7), test groups were subjected to PAA (16 g/L) or ozone rich water (4 mg/L) for 1 cycle (10 min for PAA and 60 min for ozone) per day for 7 days prior to tensile tests. Measurements of the TBS were analyzed using 3-way ANOVA and Tukey's HSD test. RESULTS. Adhesive strength of Mollosil decreased significantly by application of ozone disinfection. PAA disinfection had no negative effect on the TBS values of Mollosil and Molloplast B to acrylic resin. Single application of ozone disinfection did not have any negative effect on TBS values of Molloplast B, but prolonged exposure to ozone decreased its adhesive strength. CONCLUSION. The adhesion of resilient liners to acrylic was not adversely affected by PAA disinfection. Immersion in ozonated water significantly decreased TBS of Mollosil. Prolonged exposure to ozone negatively affects adhesion of Molloplast B to denture base materials.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.2
• /
• pp.98-107
• /
• 2015

PURPOSE. The aim of this study was to appraise the some mechanical properties of polymethyl methacrylate based denture base resin polymerized by copolymerization mechanism, and to investigate the cytotoxic effect of these copolymer resins. MATERIALS AND METHODS. 2-hydroxyethyl methacrylate (HEMA) and isobutyl methacrylate (IBMA) were added to monomers of conventional heat polymerized and injection-molded poly methyl methacrylate (PMMA) resin contents of 2%, 3%, and 5% by volume and polymerization was carried out. Three-point bending test was performed to detect flexural strength and the elasticity modulus of the resins. To determine the statistical differences between the study groups, the Kruskall-Wallis test was performed. Then pairwise comparisons were performed between significant groups by Mann-Whitney U test. Agar-overlay test was performed to determine cytotoxic effect of copolymer resins. Chemical analysis was determined by FTIR spectrum. RESULTS. Synthesis of the copolymer was approved by FTIR spectroscopy. Within the conventional heat-polymerized group maximum transverse strength had been seen in the HEMA 2% concentration; however, when the concentration ratio increased, the strength decreased. In the injection-molded group, maximum transverse strength had been seen in the IBMA 2% concentration; also as the concentration ratio increased, the strength decreased. Only IBMA showed no cytotoxic effect at low concentrations when both two polymerization methods applied while HEMA showed cytotoxic effect in the injection-molded resins. CONCLUSION. Within the limitations of this study, it may be concluded that IBMA and HEMA may be used in low concentration and at high temperature to obtain non-cytotoxic and durable copolymer structure.

• The Journal of Korean Academy of Prosthodontics
• /
• v.36 no.6
• /
• pp.858-866
• /
• 1998

Soldering is the usual method used to correct an unstable fixed partial denture framework at patient's try-in; However, presoldering base metal alloys is technique-sensitve and results are unstable because it is difficult to maintain uniform heat distribution and to prevent oxidation of an alloy. A cast-joining technique has been developed by Weiss and Munyon for repair, correction and addition to base metal framework. This joining technique eliminates the problem with presoldering of non-precious frameworks. The object of this study was to 1) compare the relative flexure strength and the joining effectiveness of Ni-Cr-Be cast in two pieces and 'pre-soldered' versus in two pieces and 'cast-joined'. 2) determine the effect of increasing the number of retentive grooves on the face of the cast and 3) determine the effect of the relative matched position of groove patterns on flexure strength. The joining effectiveness can be expressed by the ratio of the mean flexure stress of soldered or cast-joined specimens to that of one-piece cast. Resin rods 3mm in diameter were used as pattern of specimens for one-piece casted, presoldered, and cast-joined groups. Cast-joined specimens had two different patterns of retentive grooves on the joined faces. Type A had cross-shaped grooves 1mm in depth. 0.6mm in width. Type B was the same except for the addition of one more retentive groove. In the experiment connecting cast-joined specimens, half of specimens with type A pattern had their patterns on the faces of paired casts matched with each other as mirror image. With the rest pairs, it was proceeded that one of paired casts turned 45 degrees so that the patterns crossed. Half of specimens with type B pattern also had the patterns matched as mirror image; However, here, one of paired casts turned 90 degrees with the other pairs. Retentive groove in this study lacked the intentional undercuts, in contrast with the suggestion of Weiss and Munyon. The specimens were subjected to four-point flexural loading in an Instron testing machine. The midspan flexural stress was calculated at the point of initial plastic strain as determined from a strip-chart recorder or at the point of failure if this occured at a lower stress level. Within the scope of this study, the following results were obtained. 1. The presoldered group showed flexural strength at least 2 times higher than the cast-joined groups. Its joining effectiveness was 82%. 2. In cast-joined groups, the flexural strength of joints with type B patterns exhibited 1.5 times that of joints with type A patterns. Joining effectivenesses were 38% for type B patterns, 25-26% for type A patterns. 3. The relative matched position of groove patterns did not have any significant effect on flexural strength of the cast-joined specimens with either type A patterns or type B patterns(p>.05).

• The Journal of Korean Academy of Prosthodontics
• /
• v.58 no.3
• /
• pp.207-216
• /
• 2020

Purpose: To compare the polishing characteristics and their influence on Candida albicans adhesion to the recently introduced polyetherketoneketone (PEKK) and the conventional polymethylmethacrylate (PMMA) denture resin material. Materials and methods: Specimens from PEKK (Group E) and PMMA (Group M) were made in dimensions of 8 mm in diameter and 2 mm in thickness. The specimens were further divided into sub-groups according to the extent of polishing (ER, MR: rough; EP, MP: polished, N = 12 each). The specimens were polished using polishing machine and SiC foil. ER and MR group specimens were polished with 600 grit SiC foil only. EP and MP groups were further polished with 800, 1,000, 1,200 grit SiC foils sequentially. To measure the surface roughness values (Sa) of specimens, atomic force microscope (AFM) was used and scanning electron microscope (SEM) observation under 1,000, and 20,000 magnifications was performed to investigate surface topography. The polished specimens were soaked in C. albicans suspension for 2 hours with shaking to promote adhesion. The attached C. albicans were detached from the surface with 10 times of pipetting. The suspension of detached C. albicans was performed by serial dilution to 10³ times, and the diluted suspensions were inoculated on Sabouraud dextrose agar plates using spread plate method. After incubating the plate for 48 hours, colony forming unit (CFU)/plate of C. albicans was counted. Statistical analysis was performed using one-way ANOVA and Tukey HSD test to confirm significant difference between the groups (α=.05). Results: Average Sa value was significantly higher in MR group compared to other groups (P<.05), meaning that additional polishing steps reduced surface roughness effectively only in the PMMA specimens. There was no significant difference in Sa values between MP and EP groups. In SEM images, PEKK specimens showed numerous spikes of abraded material protruding from the surface and this phenomenon was more significant in EP group. The mean CFU/plate value was the highest in EP group and this was significant when it was compared to MP group (P<.05) which was the lowest. Conclusion: Polishing PEKK using serial SiC abrasive foil may result in higher adhesion of C. albicans. In clinic, this should be considered carefully.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.21 no.2
• /
• pp.95-103
• /
• 2005

Purpose: Recently, various metal primers have been developed, and these are known to increase the bond strength between metal and relining resin. In this study, the change in bond strength according to amount of thermocycling was evaluated. Materials and Methods: In this study, 216 specimens were fabricated. Tokuyama Rebase $II^{(R)}$(Tokuyama Corp., Japan) and $Kooliner^{(R)}$(GC America Inc., Japan) as relining material, and MR. $Bond^{(R)}$(Tokuyama Corp., Japan) and Alloy $Primer^{(R)}$(Kuraray Medical Inc., Japan) as a metal primers were used. Using Ni-Cr and various metal surface treatment methods, resin was bonded and the change in bond strength during thermocycling was measured. The data was analyzed by one-way ANOVA, t-test(p<.05 level of significance). Results: When comparing the groups with only sandblasting, rapid decrease in shear bond strength could be seen. In the groups using Tokuyama Rebase $II^{(R)}$, with the exception of the 1000 and 2000 cycle groups, each group showed statistically significant decrease in shear bond strength(p<0.05). In comparison according to relining materials, $Kooliner^{(R)}$ showed higher shear bond strength than Tokuyama Rebase $II^{(R)}$ in all groups. In groups using MR $bond^{(R)}$, $Kooliner^{(R)}$ had higher shear bond strength than Tokuyama Rebase $II^{(R)}$ but, there was no statistical significance(p<0.05). In the other groups, $Kooliner^{(R)}$ showed significantly higher shear bond strength(p<0.05). There was significant difference between groups with sandblasting and metal primer treatments(p<0.05). In comparison according to metal primer materials, Alloy $Primer^{(R)}$ showed the highest shear bond strength but there was no statistical significance(p>0.05). According to the number of thermocycling cycles, when using Tokuyama Rebase $II^{(R)}$, there were no significant differences between the 0, 1000 and 2000 cycle groups regardless of the type of metal primer. There were no differences between the 2000 and 3000 cycle groups. When using $Kooliner^{(R)}$, regardless of the type of metal primer, there were no significant differences between the 0, 1000, 2000 and 3000 cycle groups(p>0.05). Conclusion: The use of metal primers showed increase in bond strength, and the stability after to thermocycling has been authenticated. Thus, the use of metal primers in relining and rebasing of metal frameworks is essential. But when selecting the material various physical properties should be considered.