• Title/Summary/Keyword: Dentin shear bonding strength

Search Result 123, Processing Time 0.034 seconds

Comparison of the shear bond strength of self-etching dentin bonding agents to dentin (자가부식형 상아질 접착제와 상아질과의 전단결합강도 비교)

  • Noh, Su-Jeong;Kim, Bu-Sub;Chung, In-Sung
    • Journal of Technologic Dentistry
    • /
    • v.29 no.2
    • /
    • pp.141-150
    • /
    • 2007
  • The purpose of this study was to ascertain the bonding durability of self-etching dentin bonding agents to dentin by means of shear bonding strength. Several acid-etching dentin bonding system (ESPE Z100) and self-etching dentin bonding systems (DEN-FIL, GRADIA DIRET) were used. The occlusion surface of human molars were ground flat to expose dentin and treated with the etch bonding system according to manufactures instruction and followed by composite resin application. After 24hours of storage at 37$^{\circ}C$, the shear bonding strength of the specimens was measured in a universal testing machine with a 1mm/min crosshead speed. An one-way analysis of variance and the scheffe test were performed to identify significant differences (p<0.05). The bonded interfacial surfaces and treated dentin surfaces were examined using a SEM. Through the analysis of shear bond strength data and micro-structures of dentin-resin interfaces, following results are obtained. In dentin group, the shear bond strength of DEN-FIL showed statistical superiority in comparison to the other groups and followed by ESPE Z100 and GRADIA DIRECT (p<0.05).

  • PDF

STUDIES ON THE BOND BETWEEN COMPOSITE RESIN AND DENTIN TREATED BY DENTIN BONDING AGENTS (상아질 표면 처리에 의한 상아질과 복합레진의 결합에 관한 연구)

  • Youn, Dong-Ho;Park, Sang-Jin
    • Restorative Dentistry and Endodontics
    • /
    • v.17 no.1
    • /
    • pp.36-54
    • /
    • 1992
  • The purpose of this study was to compare the shear bond strengths to ground dentin surfaces of four dentinal bonding agents in 193 teeth. Various dentin surfaces treated with four dentin bonding agents were attached with two restorative composite resins. The effectiveness of the bonding were tested by the monitoring the shear bond strength. The shear bond strengths were measured after 2 hours and 24 hours after surface conditioning with four dentin bonding agents. Effects of EDTA, the additive illumination, and sealer treatments without primer on bond strength to dentin surfaces were assessed. In addition the effects of the thickness of specimens ranging from 0.65 mm to 1.95 mm and the ratio of catalyst and base paste on the bond strength of chemical cure composite resin were estimated. The shear bond strength was determined by testing specimens in the Instron universal testing machine (Model No. 1122) at a crosshead speed of 1.0 mm/min. Following condusions were drawn: 1. The highest mean shear bond strengths of chemical cure composite resin to dentin conditioning with dentin bonding agents aged 2 hours were obtained, and then that was decreased with time followed by EDTA treatment. 2. In light cure composite resin, the shear bond strength was increased following dentin conditioning with bonding agents with time, irradiation time and EDTA treatment except in SB group. 3. The thicker the composite resin specimen was, the less the shear bond strength in chemical cure composite resin was. 4. In light cure composite resin, there was a little change in shear bond strength following dentin conditioning with bonding agents. 5. In chemical cure composite resin, the shear bond strength was the highest in the ratio of 1/1 of catalyst and base part. 6. Without a dentin primer, shear bond strength to dentin conditioned only with UB sealer was the highest among four sealers in light cure composite resin.

  • PDF

SHEAR BOND STRENGTH OF THE ETCHED PORCELAIN TO ENAMEL AND DENTIN (법랑질(琺瑯質)과 상아질(象牙質)에 대한 Etched Porcelain의 전단접착강도(剪斷接着强度)에 관(關)한 연구(硏究))

  • Kang, Jeong-Min;Yang, Kyuo-Ho
    • Restorative Dentistry and Endodontics
    • /
    • v.15 no.1
    • /
    • pp.165-173
    • /
    • 1990
  • The purpose of this study was to measure the effect of two commercially available composite resin systems and GC dentin cement on the shear bond strength of the etched porcelain to enamel and dentin. The specimens were divided into six groups, and each group was as follows. Group I : etched enamel-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group II : etched enamel-Scotchbond 2-Silux-unfilled resin-silane-etched porcelain. Group III : dentin-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group IV : dentin-Scotchbond 2-Silux-unfilled resin-silane-etched porcelain Group V : dentin-GC dentin cement-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group VI : dentin-GC dentin cement-Scotchbond 2-Silux- unfilled resin-silane-etched porcelain Following polymerization. the specimens were stored in 100% humidity for 24 hours before testing. Shear bond strength was measured with Instron universal testing machine. The results obtained were as follows; 1. The shear bond strength of the etched porcelain to enamel was greater than that of the etched porcelain to dentin. 2. The shear bond strength of Silux-Scotchbond 2 to dentin was greater than that of CHOICE-dentin/enamel bonding agent. 3. There was no significant difference in shear bond strength to dentin between the groups lined with GC dentin cement. 4. The shear bond strength of Silux-Scotchbond 2 to dentin was greater than that of the groups lined with GC dentin cement. 5. There was no significant difference in shear bond strength to dentin between the groups lined with GC dentin cement and the group directly bonded with CHOICE-dentin/enamel bonding agent.

  • PDF

An effect of immediate dentin sealing on the shear bond strength of resin cement to porcelain restoration

  • Choi, Yu-Sung;Cho, In-Ho
    • The Journal of Advanced Prosthodontics
    • /
    • v.2 no.2
    • /
    • pp.39-45
    • /
    • 2010
  • PURPOSE. The aim of this study was to determine differences in shear bond strength to human dentin using immediate dentin sealing (IDS) technique compared to delayed dentin sealing (DDS). MATERIALS AND METHODS. Forty extracted human molars were divided into 4 groups with 10 teeth each. The control group was light-cured after application of dentin bonding agent ($Excite^{(R)}$ DSC) and cemented with $Variolink^{(R)}$. II resin cement. IDS/SE (immediate dentin sealing, $Clearfil^{TM}$ SE Bond) and IDS/SB (immediate dentin sealing, $Adapter^{TM}$ Single Bond 2) were light-cured after application of dentin bonding agent ($Clearfil^{TM}$ SE Bond and $Adapter^{TM}$ Sing Bond 2, respectively), whereas DDS specimens were not treated with any dentin bonding agent. Specimens were cemented with $Variolink^{(R)}$. II resin cement. Dentin bonding agent ($Excite^{(R)}$. DSC) was left unpolymerized until the application of porcelain restoration. Shear strength was measured using a universal testing machine at a speed of 5 mm/min and evaluated of fracture using an optical microscope. RESULTS. The mean shear bond strengths of control group and IDS/SE group were not statistically different from another at 14.86 and 11.18 MPa. Bond strength of IDS/SE group had a significantly higher mean than DDS group (3.14 MPa) (P < .05). There were no significance in the mean shear bond strength between IDS/SB (4.11 MPa) and DDS group. Evaluation of failure patterns indicates that most failures in the control group and IDS/SE groups were mixed, whereas failures in the DDS were interfacial. CONCLUSION. When preparing teeth for indirect ceramic restoration, IDS with $Clearfil^{TM}$ SE Bond results in improved shear bond strength compared with DDS.

REGIONAL MICRO-SHEAR BOND STRENGTH TO DENTIN:EFFECTS OF DENTINAL HARDNESS, POSITION, AND REMAINING DENTIN THICKNESS (상아질의 경도, 위치 및 잔존 상아질 후경이 상아질에 대한 부위별 미세 전단결합강도에 미치는 영향)

  • Hwang, Seon-Seong;Im, Mi-Kyung;Lee, Yong-Keun
    • Restorative Dentistry and Endodontics
    • /
    • v.23 no.1
    • /
    • pp.401-412
    • /
    • 1998
  • The aim of this study was to measure the regional micro-shear bond strength of dentin bonding agents to dentin, and to investigate the relationship between the micro-shear bond strength and two dentinal characteristics ; Vickers hardness and remaining dentin thickness. Twenty-four freshly extracted, noncarious human molars were selected for this study. The materials tested in this study consisted of two commercially available dentin bonding agents (MAC-BOND, ONE-STEP) and two restorative light-cured composite resins (AELITEFIL, Z100). The occlusal or side surface of tooth crown was sectioned to expose dentin, and the exposed surface was finally polished with # 600 sandpaper. Four groups of application methods were used combining the filling materials and the dentin bonding agents. The composite resin-attached tooth specimens were embeded in a cold cure acrylic resin, and were cut with a low speed diamond saw to the dimension of 1mm $\times$ 1mm. Nine specimens were obtained from each tooth. The cut specimens were divided into three groups depending on the position of the dentin bonding surface. The micro-shear bond strength, remaining dentin thickness, and dentinal hardness were measured. Experimental results were then statistically analyzed with ANOVA. t-test, Scheffe test, and regression analysis. From this experiment, the following results were obtained : 1. In the case of occlusal surface bonding, the pooled micro-shear bond strength of ONST-AELIT group (16.62 MPa) was significantly higher than that of MACB-AELIT group (9.91 MPa) (p<0.05). However, there was no significant difference in the micro-shear bond strength depending on the dentin position (p>0.05). 2. In the case of side surface bonding of crown, the pooled micro-shear bond strength of four different bonding groups was not significantly different among each other (p>0.05). However, in three of the test groups (ONST-AELIT, MACB-Z100, ONST-Z100), the micro-shear bond strength to the lower 1/3(III) position was significantly lower than that to middle 1/3(II) position of surface (p<0.05). 3. In the ONST-AELIT bonding group, the pooled micro-shear bond strength to the occlusal surface was significantly lower than that to the side surface of crown (p<0.05). 4. There was no significant correlation between the micro-shear bond strength and dentin hardness / remaining dentin thickness (p>0.05).

  • PDF

CHANGES OF THE DEGREE OF CONVERSION AND SHEAR BOND STRENGTH ACCORDING TO THE MONOMER RATIO OF EXPERIMENTAL BONDING RESINS (실험적 접착레진의 단량체 조성비에 따른 중합률 및 전단결합강도 변화에 관한 연구)

  • Moon, Anne-Jay;Kim, Byung-Hyun;Cho, Byeong-Hoon;Kwon, Hyuk-Choon
    • Restorative Dentistry and Endodontics
    • /
    • v.24 no.1
    • /
    • pp.26-39
    • /
    • 1999
  • Bis-GMA, the representative monomer of bonding resin, contributes to the rigidity of bonding layer. Hydrophilic monomer contributes to the permeability into dentin substrates while weaken the bonding layer due to its small molecular weight. The degree of conversion also contributes to the ultimate strength of the bonding layer. This study was performed for the correlation analysis of monomer ratio and dentin bonding strength via degree of conversion. 7 experimental bonding resins were prepared with Bis-GMA, ratio from 20% to 80% by 10% increment, and hydrophilic HEMA monomer. Their degree of conversion and shear bond strength to dentin were compared with Scotchbond Multi-Purpose adhesive, and the fractured surfaces were examined microscopically. The results were as follows; 1. The degree of conversion increased when, the ratio of Bis-GMA increased from 20% to 70%, whereas it decreased when the ratio of Bis-GMA was 80%. 2. Shear bond strengths of the experimental bonding resins of 80%, 70%, 60% ratio of Bis-GMA were significantly higher than those of the experimental bonding resin of 50% ratio of Bis-GMA and Scotchbond Multi-Purpose adhesive. Lower shear bond strengths were obtained with the experimental bonding resins of 40%, 30%, 20% ratio of Bis-GMA (p<0.05). 3. Adhesive fractures were associated with the bonding resins of the lower bond strength, while cohesive fractures within the bonding resin layer were associated with the bonding resins of higher bond strength. Bonding resins with shear bond strength higher than 18MPa showed some cohesive fractures within the composite resin or within the dentin. 4. Correlations between Bis-GMA ratio and the degree of conversion (r=0.826), between Bis-GMA ratio and shear bond strength (r=0.853), and between the degree of conversion and shear bond strength (r=0.786) were significant (p<0.05).

  • PDF

SHEAR BOND STRENGTH OF DENTIN BONDING AGENTS ON DENTIN SURFACE TREATED WITH EUGENOL (유지놀 처리된 상아질 표면의 상아질 접착제의 전단결합강도에 관한 연구)

  • Yu, Hwa-Sung;Choi, Gi-Woon;Choi, Kyung-Kyu;Park, Sang-Jin
    • Restorative Dentistry and Endodontics
    • /
    • v.25 no.4
    • /
    • pp.550-560
    • /
    • 2000
  • In this study, shear bond strength of two bonding systems were measured and appearance of dentin surfaces were observed with SEM according to the storage time of eugenol on dentin surface, thus evaluated the effect of eugenol on bond strength of two dentin bonding systems. Control groups were directly bonded to dentin surface with One Step, Prime & Bond 2.1. Experimental groups were divided into experimental I and II according to dentin bonding agents. After eugenol application, dentin surfaces were bonded with One Step and Prime & Bond 2.1 according to the each storage time of immediately, 3min, 24hour, 48hour and 1week, and then control and experimental groups were filled with light cured composite resin(Z-100). After 24 hours water storage at $37^{\circ}C$, all samples were subjected to a shear load to fracture at a cross head 1.0mm/min with Instron universal testing machine(No. 4467). Etched dentin surface storaged for each time of immediately, 3min, 24hour, 48hour and 1 week after eugenol application were observed under Scanning Electron Microscope(Hitachi S-2300) at 20kvp. The data were evaluated statistically with two-way ANOVA and Tukey's HSD. The results were as follows; 1. Shear bond strengths were higher in control groups than in the experimental groups. 2. As storage time was increased after eugenol application, the shear bond strengths were decreased in experimental groups. 3. In experimental I, II the shear bond strengths were the lowest in which storage time was 1 week after eugenol application. 4. As storage time was increased after eugenol application, etched dentin surfaces showed obstructed dentinal tubule.

  • PDF

SHEAR BOND STRENGTH OF LUTING CEMENTS TO DENTIN TREATED WITH RESIN BONDING AGENTS (레진접착제를 도포한 상아질에 대한 합착용 시멘트의 전단결합강도)

  • Kim, Kyo-Chul;Choi, Boo-Byung
    • The Journal of Korean Academy of Prosthodontics
    • /
    • v.36 no.1
    • /
    • pp.26-49
    • /
    • 1998
  • The purpose of this study was to confirm the formation of hybrid layer and resin tags in dentin tissue and the possibility of bonding between luting cements used for the prosthesis and the resinous surface coated with resin bonding agents to prevent the dentin hypersensitivity after abutment preparation. Some resin bonding agents, which may have the possibility of bonding with polyacrylic acid as a liquid ingredient of polycarboxylate and glass ionomer cements, were selected. All-Blond desensitizer containing NTG-GMA and BPDM, Scotch-Bond Multipurpose plus containing HEMA, and XR-bond containing organophosphate were selected as a coating agent. Dental cements were zinc phosphate, polycarboxylate, and glass ionomer cement. After the exposed dentin surface of premolars was ethced with 10% phosphoric acid and coated with resin bonding agents, the morphology of treated surfaces and the resin tags and hybrid layers on sectioned surfaces were observed by SEM. Shear bond strength between the resin bonding agents and 3 kinds of cements was measured 24 hours after bonding. On the debonded surfaces of the shear bond strength tested specimens, the cement tags and the bonding sites between the resin materials and cements were examined by SEM. Following conclusions were drawn : 1. Coating of dentin with resin bonding agents had no effect on the shear bond strength of zinc phosphate cement. 2. Both of polycarboxylate and glass ionomer cements showed the increased shear bond strength by the dentinal coating with Scotch-Bond Multipurpose plus containing HEMA. However, in the case of dentinal coating with some agents containing NTG-GMA and BPDM or organophosphate, polycarboxylate cement exhibited the lowered shear bond strength, and glass ionomer cement showed the unchanged shear bond strength. 3. Complete obstructions of dentinal tubules were observed on the dentin coated with All-Bond desensitizer or XR-bond, but distinct shape of the orifices of dentinal tubules was observed consistently on the dentin coated with Scotch-Bond Multipurpose plus. 4. The hybrid layer was thickest on the dentin coated with All-Bond desensitizer, and the length of resin tags was longest on the dentin coated with Scotch-Bond Multipurpose plus. 3. On the debonded specimens which had been bonded with polycarboxylate cement or glass ionomer cement after coating with Scotch-Bond Multipurpose plus, the cement tags and the bonding sites between the resinous surface and the cements could be examined.

  • PDF

AN EXPERIMENTAL STUDY FOR SHEAR BOND STRENGTH OF COMPOISTE RESIN USING SEVERAL DENTIN BONDING AGENTS AND LIGHT CURED GLASS IONOMER CEMENT (상아질 접착제를 사용한 광중합 복합레진과 Glass Ionomer Cement의 전단 결합력에 관한 연구)

  • Kwon, Byung-Ryul;Lee, Jae-Ho;Choi, Hyung-Jun;Lee, Jong-Gap
    • Journal of the korean academy of Pediatric Dentistry
    • /
    • v.23 no.2
    • /
    • pp.450-460
    • /
    • 1996
  • The purpose of this study was to compare shear bond strength of composite resin using several dentin bonding agents and light cured glass ionomer cement(Fuji II LC). 40 Bovine primary anterior teeth were used for this experiment. Labial surface of teeth were flattened. It were divided into four groups. Each group was composed of 10 teeth. The material used for this experiment were Scotchbond Multipurpose-Z-100, Allbond 2-Aelitefil, Gluma-Pekalux, light cured glass ionomer cement(Fuji II LC). Each of the materials was applied to the exposed surfaces of 10 teeth by insertion into a cylindrical shaped matrix which is 3mm diameter and 3mm in height. The completed specimens were stored at $37^{\circ}C$ under 100% humidity for 24 hours : the shear bond strength of each material to dentin surface were measured with INSTRON universal testing machine. The results were as follows : 1. Shear bond strength to dentin surface increased in order of light cured glass ionomer cement(Fuji II LC), Gluma, Allbond 2, Scotchbond Multipurpose. 2. Between shear bond strength of light cured glass ionomer cement(Fuji II LC) and Allbond 2, there was statistical significace(p<0.05) 3. Between shear bond strength of light cured glass ionomer cement(Fuji II LC) and Scotchbond Multipurpose, between shear bond strength of Gluma and Scotchbond Multipurpose, there was statistical significance.(p<0.01) The shear bond strength of dentin bonding agents were higher than light cured glass ionomer cement. The reason is that materials and quality of dentin bonding agent were enhanced. Further investigation is necessary to improve shear bond strength of light cured glass ionomer cement.

  • PDF

COMPARISON OF SHEAR BOND STRENGTHS OF FOUR DENTINAL ADHESIVES (네가지 상아질 접착제의 전단 결합 강도 비교)

  • Cho, Kyeong-Mee;Hur, Bock;Lee, Hee-Joo
    • Restorative Dentistry and Endodontics
    • /
    • v.21 no.1
    • /
    • pp.280-288
    • /
    • 1996
  • The purpose of this study was to assess comparatively the shear bond strength on dentin of four dentin bonding agents used in conjunction with light-curing composite resins. Clearfil New Bond, Scotchbond Multipurpose Dentin Adhesive, All-Bond 2 and X-R Bond were applicated on labial dentin surfaces just below dentin - enamel juction of bovine incisor teeth. After shear bond strength testing with the universal testing machine, the bonding interface of the specimens were observed under light stereomicroscope. Following results were obtained. 1. The shear bond strength was high in the order of B,C,D,A and group B Scotchbond Multipurpose Dentine Adhesive revealed greater bond strength than Clearfil New Bond and X-R Bond. (p<.001) 2. When using ANOVA and Duncan's multiple range test, there were statistical differences among the four groups, except between group Band C,group D and A. 3. There was no relationship between mode of failure and shear bond strength.

  • PDF