• Restorative Dentistry and Endodontics
• /
• v.38 no.4
• /
• pp.241-247
• /
• 2013

Objectives: The aim of this study was to determine the effect of epigallocatechin gallate (EGCG) on the shear bond strength of composite resin to bleached enamel. Materials and Methods: Ninety enamel surfaces of maxillary incisors were randomly divided into 9 groups as follows: G1: control (no bleaching); G2: bleaching; G3: bleaching and storage for seven days; G4 - 6: bleaching and application of 600, 800 and 1,000 ${\mu}mol$ of EGCG-containing solution for 10 minutes, respectively; G7 - 9: bleaching and application of 600, 800 and 1,000 ${\mu}mol$ of EGCG-containing solution for 20 minutes, respectively. The specimens were bleached with 30% hydrogen peroxide gel and a composite resin cylinder was bonded on each specimen using a bonding agent. Shear bond strength of the samples were measured in MPa. Data was analyzed using the two-way ANOVA and Tukey HSD tests (${\alpha}$ = 0.05). Results: The maximum and minimum mean shear bond strength values were observed in G1 and G2, respectively. Time and concentration of EGCG showed no significant effects on bond strength of the groups (p > 0.05). Multiple comparison of groups did not reveal any significant differences between the groups except for G2 and all the other groups (p < 0.05). Conclusions: There is a significant decrease in bond strength of composite resin to enamel immediately after bleaching. A delay of one week before bonding and the use of EGCG increased bond strength of composite resin to bleached enamel.

• Restorative Dentistry and Endodontics
• /
• v.36 no.5
• /
• pp.385-396
• /
• 2011

Objectives: This study evaluated the effects of adhesion variables such as the priming concepts of canal wall and the curing modes of adhesives on the sealing ability of a resin-based root canal filling system. Materials and Methods: Apical microleakage of the Resilon-RealSeal systems filled with 3 different combinations of adhesion variables was compared with the conventional gutta-percha filling using a dye penetration method. Experimental groups were SEDC, Resilon (Resilon Research LLC) filling with self-etch RealSeal (SybronEndo) primer and dual-cure RealSeal sealer; NELC, Resilon filling with no etching, Scotchbond Multi-Purpose (3M ESPE) primer application and light-curing adhesive; and TELC, Resilon filling with Scotchbond Multi-Purpose primer and adhesive used under total etch / wet bonding and lightcure protocols. GPCS, gutta-percha filling with conventional AH26 plus sealer, was the control group. Results: The median longitudinal dye penetration length of TELC was significantly shorter than those of GPCS and SEDC (Kruskal-Wallis test, p < 0.05). In the cross-sectional microleakage scores, TELC showed significant differences from other groups at 2 to 5 mm from the apical foramen (Kruskal-Wallis test, p < 0.05). Conclusions: When a resin-based root canal filling material was used, compared to the self-etching primer and the dual-cure sealer, the total etch/wet-bonding with primer and light-curing of adhesive showed improved apical sealing and was highly recommended.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.5
• /
• pp.392-399
• /
• 2015

PURPOSE. The aim of this study was to evaluate the effect of metal primers on the bonding of dental alloys and veneer resin. Polyvinylpyrrolidone solution's tarnish effect on bonding strength was also investigated. MATERIALS AND METHODS. Disk-shape metal specimens (diameter 8 mm, thickness 1.5 mm) were made from 3 kinds of alloy (Co-Cr, Ti and Au-Ag-Pd alloy) and divided into 4 groups per each alloy. Half specimens (n=12 per group) in tarnished group were immersed into polyvinylpyrrolidone solution for 24 hours. In Co-Cr and Ti-alloy, Alloy Primer (MDP + VBATDT) and MAC-Bond II (MAC-10) were applied, while Alloy Primer and V-Primer (VBATDT) were applied to Au-Ag-Pd alloys. After surface treatment, veneering composite resin were applied and shear bond strength test were conducted. RESULTS. Alloy Primer showed higher shear bond strength than MAC-Bond II in Co-Cr alloys and Au-Ag-Pd alloy (P<.05). However, in Ti alloy, there was no significant difference between Alloy Primer and MAC-Bond II. Tarnished Co-Cr and Au-Ag-Pd alloy surfaces presented significantly decreased shear bond strength. CONCLUSION. Combined use of MDP and VBATDT were effective in bonding of the resin to Co-Cr and Au-Ag-Pd alloy. Tarnish using polyvinylpyrrolidone solution negatively affected on the bonding of veneer resin to Co-Cr and Au-Ag-Pd alloys.

• The Journal of the Korean dental association
• /
• v.55 no.12
• /
• pp.850-860
• /
• 2017

Orthodontic treatment with premolar extraction is usually performed to correct bialveolar protrusion. These methods require the use of stiff rectangular working archwire which requires lengthy alignment and leveling before insertion. In this case report, interproximal reproximation was performed instead of extraction. To establish clearance between the archwire and resin domes fixing the archwire, an archwire was inserted into a water-soluble tube before fabricating resin domes. This tube is solved away by the saliva. During fabrication of resin domes, the archwire was deflected intentionally reflecting the displacement of teeth from their ideal position. This can be called as deflection-based bonding (DBB) technique. DBB is different from conventional method of positioning the brackets on its ideal position and then inserting an archwire to align the brackets. Because the orthodontic force of the archwire comes from its deflection from passive configuration, deflecting an archwire as needed can move the teeth more predictably than just bonding brackets on its ideal position. Also, areas with good alignment before orthodontic treatment can be maintained simply by not deflecting the archwire during bonding in these areas. After initial alignment, interproximal reproximation was performed to create 4.8 mm space in the maxillary arch and 4.2 mm space in the mandibular arch. These spaces were closed using orthodontic mini-implant anchorage thus retracting the maxillary incisors 4 mm posteriorly accompanied with 0.7 mm and 0.3 mm distal movement of right and left molars. By using interproximal reproximation and water-soluble tube with DBB, mild bialveolar protrusion was successfully treated without extraction.

• The Journal of Advanced Prosthodontics
• /
• v.16 no.2
• /
• pp.105-114
• /
• 2024

PURPOSE. This study aimed to evaluate the effect of pretreatment of three different universal adhesives (Single Bond Universal [SBU], All-Bond Universal [ABU], and Prime&Bond universal [PBU]) on the bonding durability of an adhesive (Panavia F 2.0, PF) and a conventional (Duo-Link, DL) resin cements to air-abraded zirconia. MATERIALS AND METHODS. Rectangular-shaped zirconia specimens were prepared. The chemical composition and surface energy parameters of the materials were studied by Fourier transform infrared spectroscopy and contact angle measurement, respectively. To evaluate resin bonding to the zirconia, all the bonding specimens were immersed in water for 24 h and the specimens to be aged were additionally thermocycled 10000 times before the shear bond strength (SBS) test. RESULTS. The materials showed different surface energy parameters, including the degree of hydrophilicity/hydrophobicity. While the DL/CON (no pretreatment) showed the lowest SBS and a significant decrease in the value after thermocycling (P < .001), the PF/CON obtained a higher SBS value than the DL/CON (P < .001) and no decrease even after thermocycling (P = .839). When the universal adhesives were used with DL, their SBS values were higher than the CON (P < .05), but the trend was adhesive-specific. In conjunction with PF, the PF/SBU produced the highest SBS followed by the PF/ABU (P = .002), showing no significant decrease after thermocycling (P > .05). The initial SBS of the PF/PBU was similar to the PF/CON (P = .999), but the value decreased after thermocycling (P < .001). CONCLUSION. The universal adhesive pretreatment did not necessarily show a synergistic effect on the bonding performance of an adhesive resin cement, whereas the pretreatment was beneficial to bond strength and durability of a conventional resin cement.

• Restorative Dentistry and Endodontics
• /
• v.37 no.1
• /
• pp.2-8
• /
• 2012

The limited durability of resin-dentin bonds severely compromises the longevity of composite resin restorations. Resin-dentin bond degradation might occur via degradation of water-rich and resin sparse collagen matrices by host-derived matrix metalloproteinases (MMPs). This review article provides overview of current knowledge of the role of MMPs in dentin matrix degradation and four experimental strategies for extending the longevity of resin-dentin bonds. They include: (1) the use of broadspectrum inhibitors of MMPs, (2) the use of cross-linking agents for silencing the activities of MMPs, (3) ethanol wet-bonding with hydrophobic resin, (4) biomimetic remineralization of water-filled collagen matrix. A combination of these strategies will be able to overcome the limitations in resin-dentin adhesion.

• Proceedings of the KACD Conference
• /
• 2008.05a
• /
• pp.213-223
• /
• 2008

The objective of this study was to compare dentin shear bond strength (DSBS) of dentin bonding agents (DBAs) cured with a plasma arc (PAC) light curing unit (LCU) and those cured with a light emitting diode (LED) LCU. Optical properties were also analyzed for Elipar freelight 2 (3M ESPE); LED LCU, Apollo 95E (DMT Systems); PAC LCU and VIP Junior (Bisco); Halogen LCU. The DBAs used for DSBS test were Scotchbond Multipurpose (3M ESPE), Singlebond 2 (3M ESPE) and Clearfil SE Bond (Kuraray). After DSBS testing, fractured specimens were analyzed for failure modes with SEM. The total irradiance and irradiance between 450 nm and 490 nm of the LCUs were different. LED LCU showed narrow spectral distribution around its peak at 462 nm whereas PAC and Halogen LCU showed a broad spectrum. There were no significant differences in mean shear bond strength among different LCUs (P > 0.05) but were significant differences among different DBAs (P < 0.001).

• Restorative Dentistry and Endodontics
• /
• v.33 no.3
• /
• pp.213-223
• /
• 2008

The objective of this study was to compare dentin shear bond strength (DSBS) of dentin bonding agents (DBAs) cured with a plasma arc (PAC) light curing unit (LCU) and those cured with a light emitting diode (LED) LCU. Optical properties were also analyzed for Elipar freelight 2 (3M ESPE); LED LCU, Apollo 95E (DMT Systems); PAC LCU and VIP Junior (Bisco); Halogen LCU. The DBAs used for DSBS test were Scotchbond Multipurpose (3M ESPE), Singlebond 2 (3M ESPE) and Clearfil SE Bond (Kuraray). After DSBS testing, fractured specimens were analyzed for failure modes with SEM. The total irradiance and irradiance between 450 nm and 490 nm of the LCUs were different. LED LCU showed narrow spectral distribution around its peak at 462 nm whereas PAC and Halogen LCU showed a broad spectrum. There were no significant differences in mean shear bond strength among different LCUs (P > 0.05) but were significant differences among different DBAs (P < 0.001)

• Journal of Technologic Dentistry
• /
• v.20 no.1
• /
• pp.91-98
• /
• 1998

Bonded lingual retained are divided into two common types; preformed retainers with attached mash pads, and those that are custom fabricated from standard round ir multi-standed wire. The clinician may encounter problems in the bonding process of both types of retainers because of an inability to accurtely place and temporarily stability the wire in the same position as it was adapted an a guide model. Because of these problems, a new fabrication technique of bonded lingual retainers which increase their accuracy and ease of placement and also increased their tretention was suggested by the author. Using a current model as a guide, this bonded lingual retainer was fabricated from $.028"{\sim}.032"$ standard round wire. The wire was formed with pliers for idel adapation to the lingual surfaces of the involved teeth. Right angle bends were placed in the retainer wire ends and custom "composite" bonding pads were added to the ends of the retainer wire. This bonded lingual retainer with custom "composite" bonding pads is easir to place because of the increased stability and the accuracy of placement is greatly increased. The increased insure that the retainer comforms ideally to the lingual surface of the teeth being retained.

• Journal of Technologic Dentistry
• /
• v.8 no.1
• /
• pp.23-29
• /
• 1986

One of the primary advantage of acrylic resin teeth is their ability to bond chemically to the denture base resins. But, occasionally, failure have been observed in which acrylic resin teeth break lose from the denture, indicating that chemical bonding does not always occur. The most probable explanation for this type of failure was the presence of a trace of wax remaining as a residue on the surfaces of the teeth after the boiling-out procedure which adgered to the tooth surface and prevented bonding. The purpose of this stdy was preparing the specimens of denture base resin with acrylic resin teeth that four treatment method to ridge lap portion of the tooth and investigated bond between the teeth and denture base resin with tensile strength. Compared results of tensile strength on test specimens were as follows: 1. The mean of strength among the four test groups showed the difference was significant enough(P 0.01). The order of its strength mean was methylene chloride treatment group, detergent solution treatment group, kerosene-ether treatment grgoup, boiling water only group. 2. In compared results between the wax eliminating method groups, there were significant difference between the boiling water only group and other groups(P 0.01), no significant difference were found in the wax eliminating method groups except boiling water only group(P 0.05).