• Journal of the Korean Ceramic Society
• /
• v.32 no.12
• /
• pp.1383-1391
• /
• 1995

Hexagonal $\delta$-FeOOH was coated with Ba-Sol, which was produced by hydrolizing Ba(OC2H5)2, Ba-Sol coated $\delta$-FeOOH spread on a stainless plate, dried at 8$0^{\circ}C$ and then heat-treated. In this way, Ba-ferrite fine particles were produced. although there was a difference in a degree of hydrolysis of Ba(OC2H5)2, crystalline phase of Ba-ferrite appeared around 617$^{\circ}C$, and Ba-ferrite single phase was obtained after heat treatment at 80$0^{\circ}C$ for 2 hr. When Ba-ferrite was made from Ba-Sol coated $\delta$-FeOOH, $\delta$-FeOOH was thermally decomposed to $\alpha$-Fe2O3 at $700^{\circ}C$, producing a porous structure which was observed by TEM photographs. But the porous structure was not observed at 80$0^{\circ}C$. Ba-ferrite, heat-treated at 80$0^{\circ}C$ for 2 hr, had mean particle size of 1000$\AA$, lattice parameter of a0=5.889243 $\AA$ and c0=23.214502 $\AA$, a saturation magnetization ($\sigma$8) of 45.3 emu/g and a coercive force (Hc) of 5200Oe.

• Journal of Welding and Joining
• /
• v.31 no.6
• /
• pp.8-16
• /
• 2013

As the energy consumption increases rapidly, power generation needs the high energy efficiency continuously. To achieve the high efficiency of power generation, the materials used have to endure the higher temperature and pressure. The 9-12%Cr steels possess good mechanical properties, corrosion resistance, and creep strength in high temperature due to high Cr contents. Therefore, the 9-12%Cr steels are widely used for the high-temperature components in power plants. Even though the steels usually have a fully martensitic microstructure, they are susceptible to the formation of ${\delta}$-ferrite specifically during the welding process. The formation of ${\delta}$-ferrite has several detrimental effects on creep, ductility and toughness. Therefore, it is necessary to avoid its formation. As the volume fraction of ${\delta}$-ferrite is less than 2% in microstructure, it has the isolated island morphology and causes no significant degradation on mechanical properties. For ${\delta}$-ferrite above 2%, it has a polygonal shape affecting the detrimental influence on the mechanical properties. The formation of ${\delta}$-ferrite is affected by two factors: a chemical composition and a welding heat input. The most effective ways to get a fully martensite microstructure are to reduce the chromium equivalent less than 13.5, to keep the difference between the chromium and nickel equivalent less than 8, and to reduce the welding heat input.

• Journal of the Korean Ceramic Society
• /
• v.38 no.11
• /
• pp.1015-1022
• /
• 2001

In this study, formation process of Ba-ferrite by using molten salt synthesis and its magnetic properties were investigated. Among starting materials, BaC $O_3$was only soluble in the molten salts, but other starting material such as $\delta$-FeOOH or F $e_2$ $O_3$was not soluble even at 105$0^{\circ}C$. It implies that the dissolved $Ba^{2+}$ diffused on surfaces of F $e_2$ $O_3$(or $\delta$-FeOOH), therefore, Ba-ferrtites were formed through surface reaction. However, the magnetic properties of Ba-ferrite prepared by two starting materials (F $e_2$ $O_3$and $\delta$-FeOOH) were not different. On the other hand, compared $\delta$-FeOOH with F $e_2$ $O_3$m, morphologies and dispersibility of Ba-ferrites prepared by using $\delta$-FeOOH were good and Ba-ferrites were obtaioned at lower temperature.

• Journal of Korea Foundry Society
• /
• v.35 no.5
• /
• pp.109-113
• /
• 2015

In this study, the measurement of FN (ferrite volume fraction) and the solution annealing ratio at a temperature of $1130^{\circ}C$ were determined with 15A elbow fittings of shell cast SSC13, and the corrosion resistance with and without austenitizing solution annealing were investigated in comparison with AISI304. The delta ferrite phase was observed in the material due to the slow cooling effect of the shell mold casting. However, the delta ferrite phase decreased gradually with the solution annealing at a temperature of $1130^{\circ}C$. The hardness generally decreased with a heat treatment; however, its corrosion resistance was improved with the heat treatment. In addition, when a passivation treatment was applied, its corrosion ratio showed the lowest value. The pattern of general corrosion decreased due to the decrease in the delta ferrite phase with the solution annealing treatment. Consequently, it is suggested that the corrosion resistance of SSC13 elbow fittings can be improved by increasing the ratio of any solution annealing treatment used and by decreasing the ferrite phase. The relationship between the ratio of solution annealing and delta ferrite is expressed as follows: SA (solution annealing ratio,%) = 98 - FN (ferrite volume fraction, %).

• Journal of the Korean Magnetics Society
• /
• v.19 no.1
• /
• pp.12-16
• /
• 2009

Z-type barium ferrite [($Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$, $Ba_{3+{\delta}}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$ ${\delta}$ = 3, 5, 7, 13 wt%. $Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24+{\delta}}O_{41}$ ${\delta}$ = 5, 7, 10 wt% )] were synthesized using co-precipitation method. The microstructure and magnetic properties of synthesized particles were investigated. In all prepared particles M-type Ba ferrite is identified with Z-type Ba ferrite together. It is found that particles having 7 wt% for Ba and 5 wt% for Fe excess addition revealed high saturation magnetization, respectively. All synthesized particles showed relatively high coercivity for device application. This result may be attributed to the contribution of M-type Ba ferrite. Ba and Fe excess addition was not affected to the structural change of CoZnZ Ba ferrite. The certain amount of excess additions of Ba and Fe and the 2 step heat-treatment may be beneficial to the improvement of soft magnetic properties of Z-type barium hexa-ferrite

• Korean Journal of Materials Research
• /
• v.14 no.6
• /
• pp.379-388
• /
• 2004

To investigate the effect of D-ferrite on the hot workability and surface defect of STS 304 billets containing 3 wt. % Cu, microstructure observations and high temperature mechanical properties test were carried out for the specimens extracted mainly from raw or oxidized billets. It was found that the total $\delta$-ferrite content has little influence on the hot workability, even though the fracture cracks due to high temperature tension or compression test were initiated and propagated mostly along $\delta$/${\gamma}$ boundary in the specimens. On the other hand, it was supposed that the direct causes of surface defects in the wire rolled from the as-continuously cast billet were the grain boundary embrittlement arose from the deep diffusion of oxygen into the grain boundary, and the oxidation of $\delta$-ferrite connected by a grain boundary to the surface during the billet reheating process as well.

• Journal of Welding and Joining
• /
• v.6 no.2
• /
• pp.40-46
• /
• 1988

The effect of heat input on the content of residual .delta.-ferrite and the hot cracking susceptibility in the austenitic stainless steel overlaid on the carbon steel was studied in the range of heat input from 7.5 to 15.1 KJ/cm. Present study shows that residual .delta.-ferrite content in the overlay is mainly determined by the dilution of the base metal (carbon steel) which is in turn affected by heat input, i.e. the amount of dilution decreases as heat input increase. Accordingly, higher heat input results in a substantial increase in Cr equivalent but a little increase in Ni equivalent due to the less dilution of carbon from base metal. This fact can explain the result obtained in this study, i, e, the higher content of .delta.-ferrite in the weld deposit made with higher heat input. This in turn causes more resistant overlaying weld metal to hot cracking.

• Journal of the Korean Ceramic Society
• /
• v.32 no.3
• /
• pp.394-402
• /
• 1995

Electrical conductivity and thermoelectric power of the ferrous ferrite system of (Mg0.29-yMnyFe0.71)3-$\delta$O4 have been measured as function of the thermodynamic variables, cationic composition(y), temperature(T) and oxygen partial pressure(Po2) under thermodynamic equilibrium conditions at elevated temperatures. On the basis of the electrical properties-phase stability correlation, the stability regions of the ferrite spinel and its neighboring phases have been subsequently located in the log Po2 vs. y and log Po2 vs. 1/T planes in the ranges of 0 y 0.29, 1100 T/$^{\circ}C$ 1400 and 10-14 Po2/atm 1. The stability region, Δlog Po2(y, 1/T), of the ferrite spinel single phase widens with increasing Mn-content(y) and the boundaries of each region are linear against 1/T with negative slopes.

• Journal of Welding and Joining
• /
• v.34 no.3
• /
• pp.69-76
• /
• 2016

Characteristics of dissimilar metal welds between ASTM Type 316L and carbon steel ASTM A516 Gr.70 made with FCAW were evaluated in terms of microstructure, ferrite content, EDS analysis, hardness, tensile strength, impact toughness and corrosion resistance. Three heat inputs of 10.4, 16.9, 23.4kJ/cm were employed to make joints of dissimilar metals with E309LMoT1-1 wire. Microstructure of dissimilar weld metals consisted of mostly vermicular type of ${\delta}$-ferrite and some lathy type of ${\delta}$-ferrite, and ${\delta}$-ferrite was transformed into globular type in reheated zone. In all conditions, weld metals were solidified on FA solidification mode. Based on the EDS analysis of weld metals, All Creq/Nieq values were in the range of FA solidification mode, and it was decreased with increasing heat inputs whereas it was increased with increasing layers. The amount of ${\delta}$-ferrite was decreased with increasing heat input due to the difference of cooling rate, and it was increased with increasing layers. Accordingly, hardness and tensile strength of dissimilar metals weld joints was decreased with increasing heat input while impact energy was increased with increasing heat input. Corrosion test of dissimilar metals weld joints showed that weight gain rate of heat input 10.4kJ/cm was the greatest, and that of three heat inputs became constant after certain time.

• Proceedings of the KWS Conference
• /
• 1998.05a
• /
• pp.150-154
• /
• 1998

The purpose of this paper is to investigate optimum welding conditions of STS 304 thin sheet by GTA welding and control 6 $\delta$--fenite which is harmful in mechanical processing, corrosion problem and can be formed brittle a phase in using long term at high temperature. One series of automatic welds was made using argon plus 10, 20, 30 % nitrogen to ensure a fully austenite deposit. Results obtained were summarized as follows: 1) 6 $\sigma$ferrite content in the weld metals is influenced largely by the nitrogen content. 2) Additions of nitrogen to the shielding gas can significantly reduce the amount of retained delta ferrite and result in an increase in hot cracking. 3) Bead width was increased when Ar + $N_2$ shielding gas was used and travel speed was increased. 4) Ar+$N_2$ shielding gas made weld metal ductile and reduce 6 -$\delta$-ferrite.