• Bulletin of the Korean Chemical Society
• /
• v.26 no.9
• /
• pp.1354-1358
• /
• 2005

Nano- and microstructured indium nitride crystals were synthesized by the reaction of indium oxide ($In_2O_3$) powder and its pellet with ammonia in the temperature range 580-700 ${^{\circ}C}$. The degree of nitridation of $In_2O_3$ to InN was very sensitive to the nitridation temperature. The formation of zero- to three-dimensional structured InN crystals demonstrated that $In_2O_3$ is nitridated to InN via two dominant parallel routes (solid ($In_2O_3$)-to-solid (InN) and gas ($In_2O$)-to-solid (InN)). The growth of InN crystals with such various morphologies was explained by the vapor-solid (VS) mechanism where the degree of supersaturation of In vapor determines the growth morphology and the vapor was mainly by the reaction of $In_2O$ with ammonia and partially by sublimation of solid InN. The pellet method was proven to be useful to obtain homogeneous InN nanowires.

• Textile Coloration and Finishing
• /
• v.15 no.3
• /
• pp.154-160
• /
• 2003

Polypropylene nonwoven fabrics were grafted with acrylic acid by a preirradiation method by using electron beam accelerator. The effect of irradiation dose, storage time, concentration of acrylic acid, reaction temperature, reaction time and Mohr's salt concentration on the degree of grafting were investigated in detail. The grafted Polypropylene nonwoven fabrics were characterized using IR spectroscopy and SEM. The results showed that the degree of grafting increased with increasing absorbed dose and the Mohr's salt in the acrylic acid solution promoted grafting efficiency.

• Journal of the Korean Chemical Society
• /
• v.27 no.2
• /
• pp.127-132
• /
• 1983

The catalytic activity of ZSM-5 catalyst for the disproportionation of toluene is dependent on the type of cation exchanged, the degree of ion-exchange and the reaction temperature. The activity increases in the order of alkaline-, alkali earth-, hydrogen, and rare-earth-exchanged ZSM-5 and decreases with increasing degree of cation exchange. Among the ion-exchanged ZSM-5 catalyst, only Cs-ZSM-5 shows predominant selectivity for p-xylene. The selectivity increases with increasing degree of $Cs^+$-exchange and decreasing reaction temperature. This phenomenon is interpreted in terms of shape selectivity arising from the partial blocking of channel intersections by large cesium ions.

• Journal of Magnetics
• /
• v.19 no.4
• /
• pp.333-339
• /
• 2014

Single crystal growth of $BaFe_{12}O_{19}$ by the solid state crystal growth method was attempted. Seed crystals of ${\alpha}-Fe_2O_3$ were pressed into pellets of $BaFe_{12}O_{19}$ + 2 wt% $BaCO_3$ and heat-treated at temperatures between $1150^{\circ}C$ and $1250^{\circ}C$ for up to 100 hours. Instead of single crystal growth taking place on the seed crystal, BaO diffused into the seed crystal and reacted with it to form a polycrystalline reaction layer of $BaFe_{12}O_{19}$. The microstructure, chemical composition and structure of the reaction layer were studied using scanning electron microscopy-energy dispersive spectroscopy (SEM-EDS), x-ray Diffraction (XRD) and micro-Raman scattering and confirmed to be that of $BaFe_{12}O_{19}$. XRD showed that the reaction layer shows a strong degree of orientation in the (h00)/(hk0) planes in the sample sintered at $1200^{\circ}C$. $BaFe_{12}O_{19}$ layers with a degree of orientation in the (hk0) planes could also be grown by heat-treating an ${\alpha}-Fe_2O_3$ seed crystal buried in $BaCO_3$ powder.

• Journal of Radiation Industry
• /
• v.6 no.2
• /
• pp.171-176
• /
• 2012

In this study, a crosslinked poly(styrene-butadiene-styrene) [SBS] block copolymers were prepared by using gamma ray irradiation method. The effects of various radiation doses on the degree of crosslinking, thermo property, and morphology of crosslinked SBS block copolymer were investigated. The degree of crosslinking of crosslinked SBS block copolymers were measured by gel-fraction and FT-IR. It was found that the degree of crosslinking of crosslinked SBS block copolymers increases with increase of the irradiation dose while the TGA result shows that the initial degradation temperature of irradiated SBS block copolymer was shifted to lower temperature with increasing irradiation dose. These results indicate that degradation reaction also occurs when SBS block copolymer is exposed to gamma ray irradiation for crosslinking reaction. The SAXS and FE-SEM results indicate that the phase separation of the styrene block and butadiene block was reduced with increasing irradiation dose.

• Journal of Environmental Health Sciences
• /
• v.27 no.1
• /
• pp.36-43
• /
• 2001

Chitosans were prepared from red crab chitin under various alkali treatment conditions(different alkali concentrations, reaction times and temperatures) and theirphysicochemical properties were investigated. The nitrogen content and deacetylation degree of red crab chitin were 6.15% and 22.17A%, respectively. By the IR spectra, red crab and reference chitin showed the sharp bands at 1650 $cm^{-1}$ / and 1550 $cm^{-1}$ /, which are characteristic of chitin. The nitrogen contents of prepared chitosans ranged from 6.19~7.48%. Thedeacetylation degree was increased from 63~76% and 48~78% with increasing reaction time and temperature, whereas viscosity was decreased. The nitrogen content and yield of red crab chitosan perpared from chitin with 50% NaOH, 1:25(w/v) for 3.0 hr at 120$cm^{-1}$ / were 7.26% and 85.0%, respectively. and viscosity, deacetylation degree and molecular weight, 67.0 mPa.s, 75.0% and 6.5$\times$10$^{5}$ Dalton, respectively. From the IR spectra, the amide absorption bands of red crab and reference chitosan became very weak, similarly. And at solid state $^{13}$ C-NMR spectra, C=O(carbonyl carbon) signals absent, whereas $CH_3$(methyl carbon) was residues. Chemical shift of $^{13}$ C-NMR spectra of red crab and reference chitosans were in good agreement with slight experimental deviation.

• Clean Technology
• /
• v.11 no.2
• /
• pp.105-116
• /
• 2005

Carboxymethylcellulose(CMC) which is water soluble at room temperature was manufactured from the cellulose material in this study. Experimental parameters were reaction temperature, time and concentration of NaOH and monochloroacetic acid. CMC was tested for solubility, degree of substitution(D.S.) and tensile strength. The surface structure of CMC fiber was tested using scanning electron microscope(SEM). CMC manufactured from viscose rayon was affected by the chemical concentration rather then the reaction time and temperature. Also, degree of substitution is closely related to the solubility of the CMC.

• Microbiology and Biotechnology Letters
• /
• v.22 no.3
• /
• pp.283-289
• /
• 1994

The production of maltose utilizing swollen extrusion starch seems to have many technical advantages, such as, high reaction rate and high yield, production of high purity concentrated maltose, and low energy consumption, over the conventional method utilizing liquefied starch. The characteristics of maltose formation in heterogeneous enzyme reaction system comtaining swollen extrusion starch was investigated using fungal $\alpha $-amylase. The influence of extrusion conditions on structure of extruded starch, such as, degree of gelatinization, water absorption index, and water solubility index was analyzed. The relationship between the structural features and maltose forming reaction was investigated, and the result was analyzed in terms of surface reaction of insoluble extruded swollen starch. The characteristics of maltose formation from swollen sxtrusion starch was compared using endo-type fungal $\alpha $-amylase and exo-type $\beta $anylase, and the structural trasformation of extruded starch was also observed to clarify the reaction mechanism.

• Polymer(Korea)
• /
• v.36 no.1
• /
• pp.65-70
• /
• 2012

Glycidyl methacrylate (GMA) was used to introduce epoxy groups on the surface of polypropylene (PP) plate, used as a substrate, through plasma-induced graft copolymerization. Emulsion polymerization was applied for graft copolymerization of GMA and was compared with conventional solution polymerization to confirm its effect. Plasma treatment conditions under one atmospheric pressure were fixed as follows; the RF power of 200 W, the treatment time of 30 sec, the Ar gas flow rate of 6 LPM, and the exposure time of treated PP samples in air of 5 min. For graft-copolymerization, GMA concentration, reaction temperature, and reaction time was optimized to maximize the grafting degree of GMA. The maximum grafting degree of GMA was obtained at the condition of 12%-GMA concentration, $90^{\circ}C$ reaction temperature, and 5 hr-reaction time. Analysis results supported that the emulsion polymerization was more effective than the solution polymerization for grafting more GMAs on the surface of PP plate under the same reaction conditions.

• Polymer(Korea)
• /
• v.26 no.2
• /
• pp.160-167
• /
• 2002

We synthesized HPP-g-GMA copolymer using pre-irradiation method by E-beam and aminated HPP-g-GMA using amination reaction. Degree of grafting increased with increasing GMA monomer concentration and showed the maximum value of 130% at 1.46 M of GMA. The degree of amination increased with increasing the degree of grafting. When the degree of grafting was 100%, degree of amination showed the maximum value of 37.4%. The ion exchange capacity of aminated HPP-g-GMA was about 3.78 meq/g, and it showed remarkable adsorption ability of hollow fiber ion exchanger. Through the BET analysis, the surface area of aminated HPP-g-GMA was 54.83 $\m^2/g$ and the mean pore size was $26\AA$. These showed the decrease of surface area and the slight increase of the mean pore size. SEM results show that the thickness of fiber increased after the step of reaction and there pore blocking phenomena was not observed. The aminated HPP-g-GMA was synthesized successfully and found to be suitable for the adsorption and separation of anion.