• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.1
• /
• pp.19-22
• /
• 1999

N-doped and low-hydrogenated DLC thin films were coated on the Mo-tip FEAs in order to improve the field emission performance and their electrical properties were evaluated. The fabricated devices showed improved field emission performance in terms of turn-on voltage, emission current and current fluctuation. This result might be caused both by the shift of Fermi level toward conduction band by N-doping and by the inherent stability of DLC material. Furthermore, the transconductance of the DLC-coated Mo-tip FEA and electrical conductivity and optical band-gap of the deposited DLC films were investigated.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.3
• /
• pp.127-131
• /
• 2010

Adhesion of DLC film is very significant property that exhibits wear resistance, chemical inertness and high hardness when being deposited to metal substrate. This study was considered that change adhesion of DLC film produced by Plasma Enhanced Chemical Vapor Deposition can be presented through inserting interlayer (Cr, Si-C:H). The thickness of interlayer was result of changing adhesion and residual stress. It was showed that the maximum 12 N of adhesion is on DLC film of Cr interlayer, and that a tendency is to be increased residual stress depend on the thickness. DLC film of Si-C:H interlayer represented 16 N of adhesion at $1{\mu}m$, whereas adhesion is decreased when the thickness is increased. For the interlayer at multi-layer, it was the best that adhesion of Cr/Si-C:H/DLC film was 33 N. Si-C:H interlayer at DLC film controled adhesion of the whole film. It was relaxed the internal stress of DLC film produced by inserting Cr, Si-C:H interlayer.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.1
• /
• pp.16-22
• /
• 2019

The structural change of DLC coatings during long-term wear test and dicing test under the low loading condition was investigated. DLC coatings were applied for the precision injection molds of a modified SNCM steel for the extension of life and the micro-diamond blades for the high cutting efficiency and the increase in life. A ball-on-disc wear tests in the mold steel and a dicing tests in the micro-diamond blades were conducted to understand degradation of DLC coatings. The degradation of DLC coatings for the injection mold steel and the micro-diamond blades during the wear and dicing tests were studied with Raman Spectroscopy. Raman peaks were divided two bands(D band and G band) to study the degradation process of DLC structure. By the wear test, polished condition of wear marks were observed to be maintained until 10 hrs of wear test period is given, but small striation marks appeared in 20 hours wear test. It was observed that $I_D/I_G$ ratios changed as the degradation of DLC coatings is proceeded during the wear tests and the dicing tests. It is suggested that the change in $I_D/I_G$ value possibly reflected from the composition of $sp^2$ and $sp^3$ bondings in DLC layers relevant to the change in mechanical and physical property.

• Korean Journal of Materials Research
• /
• v.21 no.3
• /
• pp.149-155
• /
• 2011

We investigated tribological characteristics of diamond-like carbon (DLC) in a condition with carbon nanotube (CNT) content of 1wt% in aqueous solution. Si-DLC films were deposited by radio frequency plasma enhanced chemical vapor deposition (RF-PECVD) process on Al6061 aluminum alloy. In this study, the deposition of DLC films was carried out in vacuum with a chamber pressure of 10-5 to 10-3 Torr achieved by mechanical pump followed by turbo molecular pump. The surface adsorbed oxygen on the Aluminum substrates was removed by passing Ar gas for 10 minutes. The RF power was maintained at 500W throughout the experiment. A buffer layer of HMDSO was deposited on the substrate to improve the adhesion of DLC coating. At this point CH4 gas was introduced in the chamber using gas flow controller and DLC coating was deposited on the buffer layer along with HMDSO for 50 min. The thickness of 1 ${\mu}m$ was obtained for DLC films on aluminum substrates The tribological properties of as synthesized DLC films were analyzed by wear test in the presence of dry air, water and lubricant such as CNT ink.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.4
• /
• pp.173-178
• /
• 2009

DLC film was synthesized on plastic injection mold(SKD11, $30\;mm\;{\times}\;19\;mm\;{\times}\;0.5\;mm$) and Si(100) wafer for 2 h at $130^{\circ}C$ under 6 mTorr using hybrid method of rf sputtering and ion source. The obtained film was analysed by Raman spectroscopy, AFM, TEM, Nano indenter and scratch tester, etc. The film was defined as an amorphous phase. In the Raman spectrum, broad peak of $sp^2$-bonded carbon attributed to graphite at $1550\;cm^{-1}$ were observed, and the ratio of ID($sp^3$ diamond intensity)/IG($sp^2$ graphite intensity) was approximately 0.54. The adhesion of DLC film was more than 80 N with scratch tester when $0.2\;{\mu}m$ thickness Cr was coated as interlayer. The micro-hardness was distributed at 35~37 GPa. The friction coefficient was 0.02~0.07, and surface roughness(Ra) was 0.34~1.64 nm. The lifetime of DLC coated plastic injection mold using as a connector part in computer was more than 2 times of non-coated mold.

• Journal of the Korean Ceramic Society
• /
• v.35 no.8
• /
• pp.813-818
• /
• 1998

A simple method to measure the elastic modulus E and Poisson's ratio v of diamod-like carbon (DLC) films deposited on Si wafer was suggested. Using the anisotropic etching technique of Si we could make the edge of DLC overhang free from constraint of Si substrate. DLC film is chemically so inert that we could not on-serve any surface damage after the etching process. The edge of DLC overhang free from constraint of Si substrate exhibited periodic sinusoidal shape. By measuring the amplitude and the wavelength of the sinu-soidal edge we could determine the stain of the film required to adhere to the substrate. Since the residual stress of film can be determine independently by measurement of the curvature of film-substrate com-posite we could calculated the biaxial elastic modulus E/(1-v) using stress-strain relation of thin films. By comparing the biaxial elastic modulus with the plane-strain modulus E/(1-{{{{ { v}^{2 } }}) measured by nano-in-dentation we could further determine the elastic modulus and Poisson's ratio independently. This method was employed to measure the mechanical properties of DLC films deposited by {{{{ { {C }_{6 }H }_{6 } }} rf glow discharge. The was elastic modulus E increased from 94 to 169 GPa as the {{{{ { V}_{ b} / SQRT { P} }} increased from 127 to 221 V/{{{{ {mTorr }^{1/2 } }} Poisson's ratio was estimated to be abou 0.16∼0.22 in this {{{{ { V}_{ b} / SQRT { P} }} range. For the {{{{ { V}_{ b} / SQRT { P} }} less than 127V/{{{{ {mTorr }^{1/2 } }} where the plastic deformation can occur by the substrate etching process however the present method could not be applied.

• Tribology and Lubricants
• /
• v.35 no.1
• /
• pp.1-8
• /
• 2019

Demand for plastic gears are increasing in many industries due to their low production cost, light weight, applicability without lubricant, corrosion resistance and high resilience. Despite these benefits, utilizing plastic gears is limited due to their poor material properties. In this work, DLC coating was applied to improve the tribological properties of polyamide66 gear. 0 V, 40 V, and 70 V of negative bias voltages were selected as a deposition parameter in DC magnetron sputtering system. Pin-on-disk experiment was performed in order to investigate the wear characteristics of the gears. The results of the pin-on-disk experiment showed that DLC coated polyamide66 with 40 V of negative bias voltage had the lowest friction coefficient value (0.134) and DLC coated PA66 with 0 V of negative bias voltage showed the best wear resistance ($9.83{\times}10^{-10}mm^3/N{\cdot}mm$) among all the specimens. Based on these results, durability tests were conducted for DLC coated polyamide66 gears with 0 V of negative bias voltage. The tests showed that the temperature of the uncoated polyamide66 gear increased to about $37^{\circ}C$ while the DLC coated gear saturated at about $25^{\circ}C$. Also, the power transmission efficiency of the DLC coated gear increased by about 6% compared to those without coating. Weight loss of the polyamide66 gears were reduced by about 73%.

• Journal of Satellite, Information and Communications
• /
• v.6 no.1
• /
• pp.28-31
• /
• 2011

In this paper, a new set of structural and sacrificial material that is diamond like carbon (DLC)/photoresist for high performance piezoelectric RF-MEMS switches which are actuated in d33 mode is suggested. To avoid curing problem of photoresist sacrificial layer, DLC structure layer is deposited at room temperature by radio frequency plasma enhanced chemical vapor deposition (RF-PECVD) method. And lead zirconate titanate (PZT) piezoelectric layer is deposited on structure layer directly at room temperature by rf magnetron sputtering system and crystallized by rapid thermal annealing (RTA) equipment. Particular attention is paid to the annealing of PZT film in order to crystallize into perovskite and the variation of mechanical properties of DLC layer as a function of annealing temperature. The DLC layer shows good performance for structure layer in aspect to Young's modulus and hardness. The fabrication becomes much simpler and cheaper with use of a photoresist.

• Journal of Powder Materials
• /
• v.17 no.6
• /
• pp.456-463
• /
• 2010

This paper describes the results of the application of Cr-Diamond-like carbon (DLC) films for efficiency improvement through surface modification of spur gear parts in the hydraulic gear pump. Cr-DLC films were successfully deposited on SCM 415 substrates by a hybrid coating process using linear ion source (LIS) and magnetron sputtering method. The characteristics of the films were systematically investigated using FE-SEM, nano-indentation, sliding tester and AFM instrument. The microstructure of Cr-DLC films turned into the dense and fine grains with relatively preferred orientation. The thickness formed in our Cr buffer layer and DLC coating layer were obtained the 487 nm and $1.14\;{\mu}m$. The average friction coefficient of Cr-DLC films considerably decreased to 0.15 for 0.50 of uncoated SCM415 material. The hardness and surface roughness of Cr-DLC films were measured 20 GPa and 10.76 nm, respectively. And then, efficiency tests were performed on the hydraulic gear pump to investigate the efficiency performance of the Cr-DLC coated spur gear. The experimental results show that the volumetric and mechanical efficiency of hydraulic gear pump using the Cr-DLC spur gear were improved up to 2~5% and better efficiency improvement could be attributed to its excellent microstructure, higher hardness, and lower friction coefficient. This conclusion proves the feasibility in the efficiency improvement of hydraulic gear pump for industrial applications.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.14 no.5
• /
• pp.22-27
• /
• 2015

Processing of low toughness graphite material requires high-speed machine tools and DLC coating. In this study, results of investigation of the tool wear and machining properties of the DLC coating according to the thickness, and the machining time of the tool used for the machining of graphite electrodes, were as follows. 1. DLC coating thickness shows a larger wear amount of the tool center in accordance with thickness; the wear amount of the tool increases in proportion to the machining time. 2. The difference between the amount of wear depending on the processing time shows edge portions larger than the tool wear amount in the center. This amount of wear of the tool edge is formed since the rotating torque is in contact with the graphite material surface significantly more than the central portion. 3. The thicker the DLC coating, the more the coating tool eliminated of the coating area by the interface between the cemented carbide tool being coated with an increased friction of the graphite material and the DLC coating area.