• Composites Research
• /
• v.18 no.4
• /
• pp.14-20
• /
• 2005

To determine the effect of chemical structure of aromatic amino curing agents on thermal and mechanical properties, standard epoxy resin DGEBF (diglycidylether of bisphenol F) was cured with diaminodiphenyl methane (DDM) and diaminodiphenyl sulphone (DDS) in a stoichiometrically equivalent ratio. From this work the effect of aromatic amino curing agents on the thermal and mechanical properties is significantly influenced by the chemical structure of curing agents. In contrast, the results show that the DGEBF/DDS system having the sulfone structure between the benzene rings had higher values in the thermal stability, density, shrinkage ($\%$), thermal expansion coefficient, tensile modulus and strength, flexural modulus and strength than the DGEBF/DDM system having methylene structure between the benzene rings, whereas the DGEBF/DDS system presented low values in maximum exothermic temperature, conversion of epoxide, and grass transition temperature. These results are caused by the relative effects of sulfone group having strong electronegativity and methylene group having (+) repulsive property. The result of fractography shows that the grain distribution of DGEBF/DDS system is more irregular than that of the DGEBF/DDM system.

• Composites Research
• /
• v.15 no.2
• /
• pp.40-47
• /
• 2002

The di-functional epoxy resins, i.e., diglycidylether of bisphenol A(DGEBA) and diglycidylethere of bisphenol F(DGEBF) were initiated by cationic catalyst, i.e., benzylquinoxalinium hexafluoroantimonate(BQH) using electron-beam(EB) technique. And the effect of structure of DGEBA and DGEBF on thermal stabilities and cure behaviors was investigated. According to the experimental results, the decomposed activation energy based on Horowitz-Metzger method was higher in the case of DGEBA, but intergral procedural decomposition temperature(IPDT) of DGEBA was lower than DGEBF. This could be interpreted in terms of high crosslink density resulted from hydroxyl bond of DGEBF backbone. It was confirmed in increasing the hydroxyl band at $7000\;cm^{-1}$ and $5235\;cm^{-1}$ using near-infrared spectroscopy(NIRS).

• Composites Research
• /
• v.17 no.6
• /
• pp.37-43
• /
• 2004

To determine the effect of chain length and chemical structure of linear amine curing agents on thermal and mechanical properties, a standard bifunctional linear DGEBF epoxy resin was cured with EDA and HMDA having amine group at the both ends of main chain in a stoichiometrically equivalent ratio in condition of preliminary and post cure. From this work, the effect of linear amine curing agents on the thermal and mechanical properties is significantly influenced by numbers of carbon atoms of main chain. In contrast, the results show that the DCEBF/EDA system having two carbons had higher values in the thermal stability, density, shrinkage (%), grass transition temperature, tensile modulus and strength, flexural modulus and strength than the DGEBF/HMDA system having six carbons, whereas the DGEBF/EDA cure system had relatively low values in maximum ekothermic temperature, maximum conversion of epoxide, thermal expansion coefficient than the DGEBF/HDMA cure system. These findings indicate that the packing capability (rigid property) in the EDA structure affects the thermal and mechanical properties predominantly. It shows that flexural fracture properties have a close relation to flexural modulus and strength.

• Korean Chemical Engineering Research
• /
• v.46 no.1
• /
• pp.200-204
• /
• 2008

The curing kinetics of diglycidyl ether of bisphenol F (DGEBF) with an asymmetric cycloaliphatic amine curing agent were examined by thermal analysis in both isothermal and dynamic curing conditions. From the residual curing of the samples partially cured in isothermal condition and from the dynamic curing with various heating rates, it was found that there exist two kinds of reactions such as at low temperature and at high temperature regions. It was thus also found that the cure parameters obtained from the isothermal curing kinetic model hardly estimate experimental results for a degree of cure larger than 0.6. The activation energies and frequency factors of these two kinds of reactions were obtained from the dynamic curing experiments with various heating rates. From the curing analysis, it was verified that the total cure kinetics for low degrees of cure is dominated by the cure reaction in the low temperature region.

• Composites Research
• /
• v.17 no.6
• /
• pp.44-51
• /
• 2004

To determine the effect of numbers of nitrogen atom bonded at ethyl group included in main chain of linear amine curing agents of epoxy-cure systems on the thermal and mechanical properties, standard epoxy resin DGEBF was cured with DETA, TETA and TEPA in a stoichiometrically equivalent ratio. From this work, the effect of curing agents of the DGEBF/amine systems oil the thermal and mechanical properties was significantly influenced by numbers of nitrogen atom of curing agents. The results showed that heat of reaction increased, and maximum exothermic temperature decreased with the decrease of numbers of nitrogen atom. In case of cured systems, density and maximum conversion(%) had no relation to numbers of nitrogen atom, but flexural modulus and tensile modulus increased with the decrease of numbers of nitrogen atom in main chain. Thermal stability, shrinkage(%), Tg, tensile and flexural strength showed irregular tendency having nothing to do with numbers of nitrogem atom at a sight. This findings imply that the differences in the maximum conversion(%) about the chain length of curing agents affect the thermal and mechanical properties.

• Polymer(Korea)
• /
• v.38 no.6
• /
• pp.787-790
• /
• 2014

In this work, the epoxy specimens were prepared from diglycidyl ether of bisphenol F (DGEBF) with silane coupling agents (3-glycidoxypropyl trimethoxysilane (GPTMS)) in different ratios. Thermal stability was studied in terms of polymer decomposition temperature (PDT), temperature of maximum rate of weight loss ($T_{max}$), integral procedural decomposition temperature (IPDT), and decomposition activation energy ($E_a$) using TGA analysis. Adhesion properties of epoxy composite specimens were measured by UTM (universal testing machine) at atmosphere temperature. In this result, the adhesion properties of DGEBF were improved by addition of silane coupling agents compared to non-treated epoxy resin. However, when the content of GPTMS agent is more than 10 phr, adhesion properties decreased with increasing GPTMS agent.

• Applied Chemistry for Engineering
• /
• v.22 no.3
• /
• pp.266-271
• /
• 2011

Single-walled carbon nanotube (SWCNT)/Epoxy composites were prepared for improving thermal conductivities and dispersion of SWCNTs in the epoxy matrix. Composites obtained different types of SWCNTs which are pristine and functionalized of the SWCNTs by acid and amine treatments. Three types of SWCNTs were dispersed in diglycidyl ether of bisphenol A (DGEBA) and bisphenol F (DGEBF). Enhanced interaction between functional groups on SWCNT and epoxy resins was evidenced by an improvement in the dispersion of the SWCNTs in the epoxy matrix. Thermal conductivity of composites containing acid SWCNTs were found to be much better than those containing pristine and amine treated SWCNTs.

• Applied Chemistry for Engineering
• /
• v.8 no.6
• /
• pp.960-966
• /
• 1997

The effects of epoxy resins and content of catalyst on the cure characteristics were studied by FT-IR, DSC and dynamic viscometer for the thermal properties and rheological properties of the catalytic (N-Benzylpyrazinium hexafluoroantimonate, BPH) epoxy thermosetting system. Compared with DSC results of DEGBF containing 0.5wt% BPH, the DSC thermograms of DGEBA containing 0.5wt% BPH indicated that the reaction was faster than that of DGEBF/BPH and the conversion rate of DGEBA/BPH was high in the initial stage of the reaction. As the concentration of BPH increases, the reaction and conversion rates show similar value in both the cases. The influence of hydroxyl group of epoxy resin on gel point defined from the crossover point of storage modulus (G') and loss modulus (G") could be explained by the formation of 3-dimensional network in the initial stage owing to the curing reaction between epoxides and hydroxyl groups of epoxy resin. This was consistent with the gel point obtained from DSC, FT-IR and moduli crossover. The activation energy (Et) obtained from the crossover point (G'/G"=1) are $31-39kJ.mol^{-1}$ for various BPH compositions in case of two epoxy systems.

• Polymer(Korea)
• /
• v.36 no.1
• /
• pp.22-28
• /
• 2012

Functionalized graphene/epoxy composites were prepared to miprove thermal conductivities of epoxy composites and to maintain electrical insulating property. Graphene oxide (GO) was prepared using Hummers method, and then GO was reacted with aluminum isopropoxide to functionalize $Al(OH)_3$ layer onto GO surface by a simple sol-gel method (Al-GO). GO and Al-GO were characterized by X-ray photoelectron spectroscopy, field emission scanning electron microscopy and transmission electron microscopy. The analyses confirm that GO was coated with a large and dense coverage of $Al(OH)_3$. GO and Al-GO (1 and 3 wt%) were embedded in bisphenol A (DGEBA) to investigate the effects of electrical insulating property. Electrical resistivity showed that Al-GO had better insulating property than GO. Further, the thermal conductivity of GO and Al-GO/epoxy composites was higher than that of neat epoxy resins. In particular, the thermal conductivity of Al-GO/bisphenol F (DGEBF) improved by 23.3% and Al-GO/DGEBA enhanced by 21.8% compared with pure epoxy resins.

• Polymer(Korea)
• /
• v.35 no.6
• /
• pp.548-552
• /
• 2011

Two functionalization methods, i.e., acid treatment and chemical amidation were performed to prepare the functionalized multi-walled carbon nanotubes (MWCNT), and the properties of epoxy/functionalized MWCNT composites were investigated and compared. Fourier transform infrared spectroscopy (FTIR) was used to confirm the surface functionality of the MWCNT obtained by the functionalization methods. The effects of the MWCNT functionalization on the interface and thermal conductivity were studied by zeta potential analyzer, scanning electron microscope and thermal conductivity analyzer. From these results, it was confirmed that the thermal conductivity of the epoxy/MWCNT composites could be increased by grafting with dodecylamine. This could be interpreted by relatively strong dispersion forces of the grafting MWCNT with dodecylamine in DGEBF epoxy resin. These results were in good agreement with the results that the zeta potential value of the grafting MWCNT with dodecylamine has a higher negative value than that of MWCNT with acid treatment.