• Journal of the Korean institute of surface engineering
• /
• 제20권2호
• /
• pp.60-73
• /
• 1987

For the purpose of improving the cyclic oxidation resistance of Ni-base superalloy, Inconel 600, aluminide coating methods are studied. The formation rate of aluminide coating layers is measured as a function of time and pack composition to find out the optimum coating condition. The evaluation of cyclic oxidation is established by the change in weight, the microphotography and EPMA of cross sectional area during $200^{\circ}C\;{\leftrightarrow}\;950^{\circ}C\;and\;200^{\circ}C\;{\leftrightarrow}\;1100^{\circ}C$, respectively. The thickness of coating layer and weight gains are parabolic behavior in propotion to time and Al contents. In pack of low aluminum contents, 2 wt%, however, weight gain is decreased when activator, $NH_4Cl$ is higher than 2 wt%. The cyclic oxidation resistance of the coating carried out at 1100$^{\circ}C$ are superior to those of the coating diffusion-treated after pack cementation at 800$^{\circ}C$. Aluminide oxide, which is formed in external scale, is barrier to the cyclic oxidation.

• Journal of the Korean institute of surface engineering
• /
• 제52권6호
• /
• pp.283-288
• /
• 2019

MCrAlY overaly coatings are used as oxidation barrier coatings to prevent degradation of the underlying substrate in high temperature and oxidizing environment of the hot section of gas turbines. Therefore, oxidation resistance in high temperature is important property of MCrAlY coatings. Also, coefficients of thermal expansion (CTE) of MCrAlY have middle value of that of Ni-based superalloys and oxides, which have the effect of preventing the delamination of the surface oxides. Cyclic oxidation test is one of the most useful methods for evaluating the high temperature durability of coatings used in gas turbines. In this study, NiCoCrAlY overlay coatings were formed on Inconel 792(IN 792) substrates by vacuum plasma spraying process. Vacuum plasma sprayed NiCoCrAlY coatings and IN 792 susbstrates were exposed to 1000℃ one-hour cyclic oxidation environment. NiCoCrAlY coatings showed lower weight gain in short-term oxidation. In long-term oxidation, IN 792 substrates showed higher weight loss due to delamination of surface oxide but NiCoCrAlY coatings showed lower weight loss. X-ray diffraction (XRD) analysis showed α-Al2O3 and NiCr₂O₄ was formed during the cyclic oxidation test. Through cross-section observation using scanning electron microscopy (SEM) and electron back scatter diffraction (EBSD) analysis, thermally grown oxide (TGO) layer composed of α-Al₂O₃ and NiCr₂O₄ was formed and the thickness of TGO increased during 1000℃ cyclic oxidation test. β phase in upper side of NiCoCrAlY coating was depleted due to oxidation of Al and outer beta depletion zone thickness also increased as the cyclic oxidation time increased.

• 연구논문집
• /
• 통권29호
• /
• pp.141-149
• /
• 1999

Brazing of Fe-Cr-Al alloy was carried out at $1200^{\circ}C$ in vacuum furnace using nickel-based filler metals : BNi-5 powder(Ni-Cr-Si-Fe base alloy} and MBF-50 foil (Ni-Cr-Si-B). The effect of boron content on the stability of oxide scale on the brazed joint was investigated by means of cyclic oxidation test performed at $1050^{\circ}C$ and $1200^{\circ}C$. Apparently, the joints brazed with MBF-50 containing boron showed relatively stable oxidation rates compared to boron-free BNi-5 at both temperatures. However, it was considered that the slower weight loss of MBF-50 brazed specimen wasn’t resulted from the low oxidation rate but from the spallation of oxide layer. The oxide layer consisted of thick spinel oxide on the surface and $Al_2 O_3$ internal oxide layer along the interface between mother alloy and braze, the mother alloy was also eroded seriously by the formation of spinel oxides such as $FeCr_2 O_4$ and $NiCr_2 O_4$ on the surface, likely to be induced by the change of oxide forming mechanism due to diffusion of boron from the braze. On the contrary, the joint brazed with BNi-5 showed the good oxidation resistance during the cyclic oxidation test. It seems that the oxidation can be retarded by the formation of stable $Al_2 O_3$ layer at the surface.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• 제24권4호
• /
• pp.151-157
• /
• 2014

The degradation mechanisms of thermal barrier coatings (TBCs) were investigated in different thermal fatigue condition in terms of microstructural analyses. The isothermal and cyclic oxidation tests were conducted to atmospheric plasma sprayed-TBCs on NIMONIC 263 substrates. The delamination occurred by the oxide layer formation at the interface, the Ni/Cr-based oxide was formed after Al-based oxide layer grew up to ${\sim}10{\mu}m$ in the isothermal condition. In the cyclic oxidation with dwell time, the failure occurred earlier (500 hr) than in the isothermal oxidation (900 hr) at same temperature. The thickness of Al-based oxide layer of the delaminated specimen in the cyclic condition was ${\sim}4{\mu}m$ and the interfacial cracks were observed. The acoustic emission method revealed that the cracks generated during the cooling step. It was considered that the specimens were prevented from the formation of the Al-based oxide by cooling treatment, and the degradation mode in the cyclic test was dominantly interfacial cracking by the difference of thermal expansion coefficients of the coating layers.

• Journal of the Korean institute of surface engineering
• /
• 제27권2호
• /
• pp.91-98
• /
• 1994

For the plasma sprayed as well as the EB-PVD thermal barrier coatings, the fracture paths within the oxidation products developed at the interface between the partially stabilized zirconia ceramic coating and NiCoCrAlY bond coat during cyclic thermal oxidation has been investigated. It was observed that the fracture in the oxidation products primarily took place within the oxide such as $Ni_{1-x}Co_3(Al_,Cr)_2O_4$ or at the interface between the oxide and $Al_2O_3$. It was found that Al2O3 developed first, followed by the Ni/Co/Cr rich oxides such as ,,$Ni_{1-x}Co_x(Al_,Cr)_2O_4$ $Cr_2O_3$and NiO at the interface between the ceramic coating and the bond coat in a cyclic high temperature environment. It was therfore concluded that the formation of the oxide containing Ni, Cr and Co was a life-limiting event for thermal barrier coatings during cyclic thermal oxidation.

• Journal of the Korean institute of surface engineering
• /
• 제39권4호
• /
• pp.147-152
• /
• 2006

Failure mechanisms of electron beam physical vapor deposited thermal barrier coatings(EB-PVD TBCs) that occur during thermal cyclic oxidation were investigated. The investigations include microstructural degradation of NiCrAIY bond coat, thermally grown oxides(TGOs) along the ceramic top coat-substrate interface and fracture path within TBCs. The microstructural degradation of the bond coat during cyclic oxidation created Al depleted zones, resulting in reduction of NiAl and ${\gamma}$-Ni solid solution phase. It was observed that the fracture took placed primarily within the TGOs or at the interfaces between TGOs and bond coat.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 한국정밀공학회 2009년도 춘계학술대회 논문집
• /
• pp.725-726
• /
• 2009

• Analytical Science and Technology
• /
• 제15권6호
• /
• pp.550-555
• /
• 2002

The oxidation mechanism of boratabenzene was studied. As a model compound the ferrocene analogue (${\eta}^6$-1-Methylboratabenzene)(${\eta}^5$-Pentamethylcyclopentadiennyl)iron 3 was chosen. The complex underwent irreversible oxidation in the presence of ortho proton on the ring and a methyl group on the boron atom in methanol medium. Chemical oxidations with $Hg(OAc)_2$, $HgSO_4$, $Cu(OH)_2$, $AgCF_3SO_3$ or $FeCl_3$ in MeOH gave, via a transition state [3], at first the derivates 6 and 7, which were converted to each 8 and 9.

• Journal of the Korean institute of surface engineering
• /
• 제32권1호
• /
• pp.49-60
• /
• 1999

The protective oxide scales and coatings formed on high temperature materials must be preserved in high temperature atmosphere. And the thermal stresses induced by thermal cycling and the growth stresses by the formation of oxide scales can cause the loss of adherence and spalling of the oxide scales and coated layers. Among the coating processes Al diffusion coating is favored due to thermochemical stability and superior adherence in an hostile atmosphere. In this study, protective oxide forming element, Al was coated on Ni, Inconel 600 and 690 by diffusion coating process varying coating temperature and time. And the surface stability and adherence of oxide scales formed on those Al diffusion coated materials were evaluated by thermal cycling test. Al diffusion coated specimens showed superior cyclic oxidation resistance compared to bare ones and specimens coated for longer period had better cyclic oxidation resistance, due to the abundant amount of Al in the coated layer. Meanwhile Al diffusion coated Inconel 600 and 690 showed improved cyclic oxidation resistance by the effect of Al in the coated layer and Cr in the substrate. Comparing both Al diffusion coated Inconel 600 and 690, Al diffusion coated Inconel 690 maintained better adhesion between coated layer and substrate by virtue of the bridging effect resulting from the segregation of Cr in the interdiffusion zone.

• Journal of the Korean institute of surface engineering
• /
• 제30권2호
• /
• pp.93-103
• /
• 1997

High temperature materials used in the elevated temperature and corrosive atmosphere must have the good oxidation resistance and preserve their own mechanical properties simultaneously. For the oxidation resistance, it is very important to form a protective oxide scale such as $Al_2O_3$ or $Cr_2O_3$ on the substrate. However, the additions of protective oxide forming elements such as Cr and Al in the alloy to enhance its oxidation resistance are limited due to the deleterious effects on their mechanical properties. PECVD(P1asma Enhanced Chemical Vapor Deposition) coating processes were employed to improve the oxidation resistance at high temperature. Cr and/or A1 were coated on the substrates of Ni and Inconel 600 at various temperatures of 400, 500, $600^{\circ}C$ and at different conditions of specimen surfaces. Then, coated specimens were exposed to isothermal and cyclic oxidation conditions in air at 1000 and $1100^{\circ}C$. In order to enhance the adhesion between the substrate and coated layer, heat treatments of the coated specimens were conducted in a vacuum. At isothermal oxidation experiments, Al-coated Ni specimen showed better oxidation resistance than pure Ni. At cyclic oxidation experiments at $1000^{\circ}C$. Cr and Al-coated specimen showed better oxidation resistance. Cr-coated Inconel 600 had also showed better oxidation resistance due to Cr in the substrate. By PECVD coating process, oxidation resistance could be improved, but it was not improved as expected due to the weakness of the adhesion between the substrate and the coated layer.