• Applied Chemistry for Engineering
• /
• v.5 no.2
• /
• pp.345-356
• /
• 1994

Each of the three cationized compounds synthesized previously, poly(OMA-co-DAMA)[PODC], poly(DMA-co-DAMA)[PDDC] and poly(EMA-co-DAMA)[PEDC] was blended with waxes, emulsifiers and cationized fatty carbamide(ODTCC) synthesized in this study for the preparation of some durable softening water-repellenting agents, PODCW, PDDCW and PEDCW. The results of washability, tearing strength, crease recovery and contact angle of the cotton fabrics treated with PODCW, PDDCW and PEDCW with and without textile finishing resin, showed remarkable improvement of the physical properties. Rating of water repellency of cotton fabric treated with PODCW was 80, but those treated with PDDCW and PEDCW were not high enough to use in industry. Proper curing temperature of the synthesized water-repelleting agents was $140^{\circ}C$; proper using concentration was 3wt%; sodium acetate was the best catalyst for water-repellenting agents among the used, and proper concentration was 0.6wt%. From the results of reaction mechanism of cellulosic fiber with water-repellenting agent and washability of the fibers treated with water-repellenting agents the prepared water-repellenting agent proved to be durable. Surface structures of cotton fabrics treated with water-repellenting agent were investigated by SEM.

• Corrosion Science and Technology
• /
• v.9 no.4
• /
• pp.147-152
• /
• 2010

Conventional paints for conversion coating applications in steel production derived mainly from water-based polymer dispersions containing several additives actually show good general performance, but suffer from poor scratch and abrasion resistance during use. The reason for this is because the relatively soft organic binder matrix dominates the mechanical surface properties. In order to maintain the high quality and decorative function of coated steel sheets, the mechanical performance of the surface needs to be improved significantly. In fact the wear resistance should be enhanced without affecting the optical appearance of the coatings by using appropriate nanoparticulate additives. In this direction, nanocomposite coating compositions (Nanomer$^{(R)}$) have been derived from water-based polymer dispersions with an increasing amount of surface-modified nanoparticles in aqueous dispersion in order to monitor the effect of degree of filling with rigid nanoparticles. The surface of nanoparticles has been modified for optimum compatibility with the polymer matrix in order to achieve homogeneous nanoparticle dispersion over the matrix. This approach has been extended in such a way that a more expanded hybrid network has been condensed on the nanoparticle surface by a hydrolytic condensation reaction in addition to the quasi-monolayer type small molecular surface modification. It was expected that this additional modification will lead to more intensive cross-linking in coating systems resulting in further improved scratch-resistance compared to simple addition of nanoparticles with quasi-monolayer surface modification. The resulting compositions have been coated on zinc-galvanized steel and cured. The wear resistance and the corrosion protection of the modified coating systems have been tested in dependence on the compositional change, the type of surface modification as well as the mixing conditions with different shear forces. It has been found out that for loading levels up to 50 wt.-% nanoparticles, the mechanical wear resistance remains almost unaffected compared to the unmodified resin. In addition, the corrosion resistance remained unaffected even after $180^{\circ}$ bending test showing that the flexibility of coating was not decreased by nanoparticle addition. Electron microscopy showed that the inorganic nanoparticles do not penetrate into the organic resin droplets during the mixing process but rather formed agglomerates outside the polymer droplet phase resulting in quite moderate cross linking while curing, because of viscosity. The proposed mechanisms of composite formation and cross linking could explain the poor effect regarding improvement of mechanical wear resistance and help to set up new synthesis strategies for improved nanocomposite morphologies, which should provide increased wear resistance.

• Polymer(Korea)
• /
• v.30 no.6
• /
• pp.538-544
• /
• 2006

Two kinds of novel bifunctional methacrylated prepolymers (170-2MA and 631-2MA) which have similar structure with 2,2-bis[4- (2'-hynroxy-3'-methacryloyloxypropoxy)phenyl] propane (Bis-GMA) was synthesized for dental applications as an alternative to Bis-GMA containing bisphenol A that is doubtful as an endocrine disrupter. The organic matrices were prepared by mixing a diluent and/or a monomer with the synthesized methacrylated prepolymers. The yield, viscosity, and chemical structures of the prepolymers and the physical and methanical properties of the organic matrices were evaluated. The yields of the prepolymers synthesized through a ring-opening reaction of epoxy compound and methacrylic acid were above 90% and the viscosities of the prepolymers were much lower than that of the Bis-GMA control. From the results of $^1H-NMR$ and FTIR analyses, the chemical structures of the prepolymers were similar to that of Bis-GMA. In addition, the curing time, poly-merization shrinkage, photoconversion, polymerization depth, and compressive strength of the organic matrices formulated with 170-2MA and 631-2MA prepolymers exhibited comparable to or better than those of the existing Bis-GMA-based one. These results suggest that the novel methacrylated prepolymers which have no endocrine disrupter can be an alternative to Bis-GMA and be applicable to dental polymer materials.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.1
• /
• pp.15-20
• /
• 2014

In this research, the geopolymer was fabricated using municipal solid waste incineration ash (denoted as MSWIA) slag and alkali activator, NaOH and its properties were analyzed. Particularly, the effects of NaOH molarity, particle size of MSWIA, and liquid/solids ratio on the compressive strength of geopolymers were investigated. The compressive strength of geopolymers fabricated increased with finer grain size of MSWIA, and optimum value of the liquid/solids ratio was identified as 0.13. As the molarity of the NaOH increased, the compressive strength of geopolymers was increased. Even more the 20 M of NaOH, but the strength was not increased. The calcium aluminum silicate and calcium aluminum silicate hydrate zeolites were generated in the geopolymer fabricated with more than 20 M of NaOH, with some unreacted silica and unknown crystals remained. The highest compressive strength, 163 MPa, of geopolymer was appeared at conditions of curing temperature $70^{\circ}C$, and 20 M of NaOH, indicating that the high concentration of NaOH accelerates the geopolymer reaction and dense microstructure. The high-strength geopolymer fabricated in the present study is expected to contribute significantly to develop the field of cement alternative substances and to improve the recycling rate of MSWIA slag.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2017.05a
• /
• pp.915-922
• /
• 2017

The study on the thermal and oil resistance rubber composite, 2016. [6] predicted the lifetime of Fluorocarbon Rubber by accelerating aging at high temperature ($150^{\circ}C$, $175^{\circ}C$, $200^{\circ}C$). general rubber products are likely to exhibit different properties depending on the degradation factors such as temperature, humidity, ozone, light, emulsion, mechanical and electrical stress. To solve these problems, We compared the rate of change about tensile strength, elongation rate, volume change rate, weight change rate, thickness change rate, thermal conductivity in low temperature promoting aging on the basis of predictive lifetime of high temperature promoting aging. As a result of the review, the required life expectancy was satisfied, but there was a slight difference in the rate of change between the high-temperature promoted aging life result and the low temperature promoted aging life result. The cause was a reduction in "tensile strength / elongation" and an increase in "volume / weight / thickness" caused by the main chain decomposition of fluorine rubber due to aging at high temperature promoting aging. However, the low temperature promoting aging was caused by the curing reaction of fluorine rubber at $80^{\circ}C$. The tensile strength / elongation and volume / weight / thickness changes were small.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.2
• /
• pp.154-160
• /
• 2018

Cement industries are considered key industries for reducing carbon emissions, and efforts are off the ground to reduce the use of cement in the concrete sector. As a part of this effort, research is off the ground to utilize a large amount of industrial by-products that can be used as a substitute for a part of cement. Concrete using industrial by-products has advantages such as durability, environment friendliness and economical efficiency, but there are problems such as retarding and early-age strength deterioration. Therefore, this study aimed to reduce the use of cement and solve the problem of early-age strength deterioration while using fly ash, which is an industrial by-product. Accordingly, it was confirmed that the strength was improved at all ages irrespective of curing temperature by accelerating the hydration reaction by using high fineness cement. Subsequently, high fineness cement was partially replaced with fly ash and the strength development characteristics were examined. As a result, it was possible to exhibit strength equal to or higher than ordinary portland cement even at the early age. Also, it was confirmed that even when the fly ash is replaced by 30%, it is possible to shorten the time for dismantling the forms of vertical and horizontal members.

• Resources Recycling
• /
• v.19 no.6
• /
• pp.36-42
• /
• 2010

Researches on resources recycling in the field of construction have made an extensive progress such as recycled aggregate of waste concrete and recycling of asphalt. On the other hand, there are almost never researches on pavement method with used waste frying oil. In South Korea, 0.2 million ton used waste frying oil is discharged every year. It is guessed that about 0.1 million ton used waste frying oil can be collected. If used waste frying oil is recycled, it is expected that disuse cost will be reduced and water pollution of rivers will be prevented. Therefore, the purpose of the study was to evaluate on mechanical features (strength, water resistance, chemical resistance, abrasion resistance, freezing and thawing resistance and permeable coefficient) whether dense graded permeable concrete mixing silica sand with flexible alkyd resin manufactured by making ester reaction with collected used waste frying oil to make alkyd resin could be applied to road pavement for non-roadway. The results of the study were as follows. In flexural strength, it had 1.6 times as much as road design standard 4.5MPa. In water resistance, chemistry resistance and freezing and thawing resistance, they had lack of strength in early age. As age went by, they didn't have large changes. And curing temperature had phenomenon of increase in strength at rather low temperature than high temperature by glass transition temperature of resin. Therefore, considering workability, strength and durability when it was applied to road pavement, it was reasonable that the mixing ratio of flexible alkyd resin was 10~15% in comparison with silica sand weight.

• Polymer(Korea)
• /
• v.33 no.1
• /
• pp.39-44
• /
• 2009

Polymer substrates were fabricated by using poly (phenylene ether) as a base resin, N,N'-m-phenylenedimaleimide (PDMI) as a crosslinking agent and decabromodiphenylethane as a flame retardant. The effects of crosslinking agent and flame retardant on physical properties such as dielectric property of the substrate were investigated. Thermal curing feature of PDMI with or without an initiator was analyzed by DSC, and then, PPE-PDMI test compositions were designed based on this result. Composite sheets were cast by film coater, laminated under vacuum and pressure, and then, the changes of dielectric constant, dielectric loss, peel strength, solder heat resistance and inflammability according to increasing amount of PDMI and flame retardant were evaluated, Dielectric constant and dielectric loss showed increasing trend with increasing amount of PDMI and flame retardant, but solder heat resistance and inflammability were improved. Peel strength was obtained higher than 1 kN/m when PDMI above 10 wt% was added, but slightly decreased as the amount of flame retardant increased. From the measured gel contents, the reaction mechanism of PPE-PDMI system was deduced to the formation of network structure by crosslinking PDMI with PPE rather than the formation of semi-IPN structure. In conclusion, the polymer composite substrate materials with dielectric constant of 2.52$\sim$2.65 and dielectric loss below 0.002 at 1 GHz were obtained and they will be proper for high frequency applications.

• Journal of the Korean Geosynthetics Society
• /
• v.22 no.3
• /
• pp.87-95
• /
• 2023

Recently, redevelopment of the original downtown area is underway, the necessity of construction in adjacent location is increasing. However, excavations in dense urban areas are prone to ground problems due to various causes, so it is necessary to use materials and methods that can minimize such problems. As a general earth retaining method, various methods such as diaphragm wall and CIP method are applied using cement. However, since a large amount of cement is used for the installation of earth retaining method, it is necessary to conduct research on the development of new cement substitute materials to significantly reduce greenhouse gas emissions. In this study, we utilized the hardening reaction of blast furnace slag powder, desulfurized gypsum and high calcium fly ash by alkali activation and applied it to the SCW method. As a result, it was analyzed that the compressive strength of solidified soil using development solidification material was 96.2 ~ 106.3% of OPC at 28 days of curing. In addition, the strength increment ratio was 2.06 for sandy soil and 2.41 for clayey soil, which was higher than 1.85 of OPC. It seems an advantageous in terms of long-term strength. In addition, from the environmental point of view, it was analyzed that there is no elution of heavy metals and that greenhouse gas emissions can be dramatically reduced. Therefore, if further studies are conducted, it can be applied to the SCW method.

• Clean Technology
• /
• v.29 no.2
• /
• pp.102-108
• /
• 2023

This study applied a hydrothermal carbonization (HTC) method to carbonize sewage sludge in order to satisfy the criteria of the Waste Management Act for recycled products and to explore the possibility of recycling sludge into modification blocks. Cement was mixed with carbonized sludge generated at the optimal temperature and reaction time during HTC. After that, the compressive strengths of the modification blocks were measured by conducting both a performance and leaching test. The results of the leaching test showed that heavy metals were not detected, and the specific gravity and absorption rates were less than 1.7 and 10%, respectively, indicating that all species satisfied the criteria. The results of the compressive strength test showed that a mixing ratio of 5% and 7% with cement cured for 28 days satisfied the criteria of A, B, and C type blocks but a mixing ratio of 3% with cement did not satisfy the criteria of A type blocks after 28 days. However, after additional curing for 42 days, the mixing ratio of 3% also satisfied the A type block criteria. Therefore, the optimal mixing ratio of carbonized sludge and cement was considered to be between 3% and 5% and confirmed that the modified blocks could be utilized as aggregates.