• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2004년도 춘계 학술발표대회 개요집
• /
• pp.84-86
• /
• 2004

기존의 전자산업에서는 Sn-37Pb 공정솔더를 사용하였으나, 최근 납의 환경적인 문제로 인하여 무연 솔더에 관한 연구와 적용이 세계적으로 진행되고 있다. 무연 솔더의 실용화와 관련하여 Sn-37Pb 솔더와 같은 만능의 솔더는 없지만, 그 중 도입이 가장 유력시 되는 것으로 Sn-Ag-Cu계 솔더가 있다. (중략)

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년 추계학술발표대회 개요집
• /
• pp.181-183
• /
• 2006

This paper studies the mechanical behaviors of Sn-3.5Ag solder joint against substrate(such as Au/Ni/Cu, Au/cu, Ni/Cu and Cu pad) after induction heating, a new soldering method. It was found that the solder bump formation depends on the time and current of the induction heating system. Also the heating value of the solder bump were found to vary with respect to the thermal conductivity of the pads on the substrate. In case of Au/Ni/Cu pad and Au/Cu pad, solder bump's shear strength were high for the heating time of $1.5{\sim}2sec$. For Ni/Cu pad, solder bump's shear strength were found to increase with time increment.

• 한국마이크로전자및패키징학회:학술대회논문집
• /
• 한국마이크로전자및패키징학회 2002년도 추계기술심포지움논문집
• /
• pp.33-37
• /
• 2002

본 연구에서는 전해도금법을 이용하여 플립칩용 Ni, Ni-Cu 합금 UBM (Under Bump Metallurgy) 및 Sn-Ag 무연 솔더 범프를 형성하였다. 솔더 범프의 전해도금시 고속도금 방법으로 균일한 범프 높이를 갖도록 하는 도금 조건 및 도금 기판의 역할로서의 UBM의 영향을 조사하였다. Cu/Ni-Cu 합금/Cu UBM을 적용한 경우 음극시편의 전극 접점수를 증가시켰을 때 비교적 균일한 솔더 범프를 형성시킬 수 있었던 반면, Ni UBM의 경우는 접점수를 증가시켜도 다소 불균일한 솔더 범프를 형성하였다. 리플로 시간을 변화하여 범프 전단 강도 및 파단 특성을 조사하였는데 Ni UBM의 경우 Cu/Ni-Cu 합금/Cu UBM에 비해 전단강도가 다소 낮은 값을 가졌고 금속막이 웨이퍼에서 분리되는 파괴 거동이 관찰되었다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 춘계학술발표대회
• /
• pp.42.1-42.1
• /
• 2011

높은 광흡수 계수를 갖는Cu(In,Ga) $Se_2$ (CIGS) 화합물 박막 소재는 고효율 태양전지 양산을 위해 가장 전도유망한 재료이나 상대적으로 매장량이 적은 In 및 Ga을 사용한다는 소재적 한계가 있다. $Cu_2ZnSnSe_4$ (CZTSe) 혹은 $Cu_2ZnSnS_4$(CZTS)와 같은 Cu-Zn-Sn-Se계 화합물 반도체는 CIGS 내 희소원소인 In과 Ga이 범용원소인 Zn 및 Sn으로 대체된 소재로써 미래형 저가 태양전지 개발을 위해 활발히 연구되고 있는데, 그 화합물 조합에 따라 0.8 eV부터 1.5 eV까지의 에너지 밴드갭을 갖는 것으로 알려져 있다. 스퍼터링법에 기반한 2단계 공정에 의해 3.2%의 CZTSe 및 6.7%의 CZTS 태양전지 효율 달성이 보고된 바 있으며, 최근 비진공 방식을 이용하여 제조된 $Cu_2ZnSn(S,Se)_4$ (CZTSSe) 태양전지가 9.6%의 변환효율을 생산하여 세계 최고기록을 갱신한 바 있다. 반면, 동시진공증발법에 의한 Cu-Zn-Sn-Se계 연구는 박막 조성 조절이 상대적으로 용이하다는 장점에도 불구하고, 상대적으로 공개된 연구결과의 양이 적으며 그 효율에 대한 보고는 특히 미미하다. 본 연구에서는 동시진공증발법에 의한 CZTSe 박막 연구 결과를 바탕으로 Sn 손실을 최소화하기 위한 진공증발 공정을 최적화하였으며, 이를 통해 CZTSe 박막 태양전지를 제조하고 그 특성분석을 통해 5% 이상의 변환효율을 달성하였다.

• 마이크로전자및패키징학회지
• /
• 제14권2호
• /
• pp.35-40
• /
• 2007

Sn-8Zn-3Bi 무연 솔더 페이스트의 접합부신뢰성 및 적합성을 평가하기 위해 유(SnPb) 무연(Sn, SnBi)도금된 Cu 리드프레임 QFP(Quad Flat Packager)를 사용하여 열충격 조건 하에서의 인장 강도의 변화 및 파괴 기구에 대한 분석을 실시하였다. 리드 도금의 종류에 상관없이 모든 시험 시편에서 열충격 사이클 수의 증가에 비례하여 접합부의 취성 특성이 강화되어 인장 강도가 감소하는 것을 확인하였다. 하지만, 접합부에는 열팽창 계수의 차이에 의해 야기될 수 있는 미세 균열은 발견되지 않았다. 단면 관찰 및 변위 이력 곡선 분석을 통하여 열충격 사이클 수의 증가에 따른 인강 강도의 감소는 접합부의 파괴 기구의 변화에 기인되었음을 확인하였다. 본 실험을 통해 Sn-3Zn-3Bi 솔더의 유 무연 도금 Cu 리드프레임과의 우수한 작업 특성과 열충격 환경 하에서도 우수한 기계적 접합 특성을 유지하는 것을 확인할 수 있었다.

• 한국자기학회지
• /
• 제1권2호
• /
• pp.15-21
• /
• 1991

고온초전도체 $Y_{1}Ba_{2}Cu_{3-x}Sn_{x}O_{7-y}$에서 Cu 대신에 Sn 을 치환하면서 이들의 조성변화에 따른 자기적 특성을 vibrating sample magnetometer(VSM)와 torque magnetometer를 이용 하여 측정하였다. Cu 대신에 Fe, Ni 등의 원소를 치환했을 때와는 달리 x=0.36 까지 되어도 초전도 전이온도가 90 K 이상을 나타냄을 알 수 있었다. 온도와 외부자기장에 따른 자기 모우먼트 측정을 통하여 각 조성에 따른 lower critical field ($H_{c1}(T)$)과 upper critical field ($H_{c2}(T)$)를 측정하였다. 이 결과를 이용해 $H_{c1}(0)$과 $H_{c2}(0)$를 계산했으며, 간섭길이 (${\varepsilon}_{0}$), 침투깊이 (${\lambda}_{0}$), Ginzburg-Landau 상수 k등을 얻을 수 있었으며, 시료의 flux pinning 효과도 확인할 수 있었다.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2009년 추계학술발표대회
• /
• pp.66-66
• /
• 2009

Various alloy system, such as Cu-Sn-Ti, Cu-Ag-Ti, and Ni-B-Cr-based alloy are used for the brazing of diamond grits. However, the problem of the adhesion strength between the diamond grits and the brazed alloy is presented. The adhesion strength between the diamond grits and the melting filler alloy is predicted by the contact angle, thereby, instead of diamond grit, the study on the wettability between the graphite and the brazing alloy has been indirectly executed. In this study, Cu-13Sn-12Ti filler alloy was manufactured, and the contact angles, the shear strengths and the interfacial area between the graphites(diamond grits) and braze matrix were investigated. The contact angle was decreased on increasing holding time and temperature. The results of shear strength of the graphite joints brazed filler alloys were observed that the joints applied Cu-13Sn-12Ti alloy at brazing temperature 940 $^{\circ}C$ was very sound condition indicating the shear tensile value of 23.8 MPa because of existing the widest carbide(TiC) reaction layers. The micrograph of wettability of the diamond grit brazed filler alloys were observed that the brazement applied Cu-13Sn-12Ti alloy at brazing temperature $990^{\circ}C$ was very sound condition because of existing a few TiC grains in the vicinity of the TiC layers.

• Journal of Welding and Joining
• /
• 제28권3호
• /
• pp.49-58
• /
• 2010

Various alloy system, such as Cu-Sn-Ti, Cu-Ag-Ti, and Ni-B-Cr-based alloy are used for the brazing of diamond grits. However, the problem of the adhesion strength between the diamond grits and the brazed alloy is presented. The adhesion strength between the diamond grits and the melting filler alloy is predicted by the contact angle, thereby, instead of diamond grit, the study on the wettability between the graphite and the brazing alloy has been indirectly executed. In this study, Cu-13Sn-12Ti filler alloy was manufactured, and the contact angles, the shear strengths and the interfacial area between the graphites (diamond grits) and braze matrix were investigated. The contact angle was decreased on increasing holding time and temperature. The results of shear strength of the graphite joints brazed filler alloys were observed that the joints applied Cu-13Sn-12Ti alloy at brazing temperature $940^{\circ}C$ was very sound condition indicating the shear tensile value of 23.8 MPa because of existing the widest carbide(TiC) reaction layers. The micrograph of wettability of the diamond grit brazed filler alloys were observed that the brazement applied Cu-13Sn-12Ti alloy at brazing temperature $990^{\circ}C$ was very sound condition because of existing a few TiC grains in the vicinity of the TiC layers.

• 열처리공학회지
• /
• 제26권5호
• /
• pp.225-232
• /
• 2013

The influence of aging treatment, addition elements and rolling reduction ratio on the microstructure, mechanical, electrical and bendability properties of Cu-Ni-Si-P-x (x = Fe, Sn, Zn) alloys for connector material application was investigated. SEM/EDS analysis exhibited that Ni2-Si precipitates with a size of 20~100 nm were distributed in grains. Fe, Sn, Zn elemnets in Cu-Ni-Si-P alloy imporved the mechanical strength but it was not favor in increasing of electrical conductivity. As higher final rolling reduction ratio, the strength and electrical conductivity is increased after aging treatment, but it indicated excellent bendability. Especially, Cu-2Ni-0.4Si-0.5Sn-0.1Fe-0.03P alloy show the tensile strength value of 700MPa and the electrical conductivity was observed to reach a maximum of 40%IACS. It is optimal for lead frame and connector.

• 한국표면공학회지
• /
• 제44권5호
• /
• pp.185-189
• /
• 2011

$Cu_2ZnSnSe_4$ thin films for solar absorber application were prepared by pulsed laser deposition of a synthesized $Cu_2ZnSnSe_4$ compound target. The film's composition revealed that the deposited films possess an identical composition with the target material. Further film compositional control toward a stoichiometric composition was performed by optimizing substrate temperature, deposition time and target rotational speed. At the optimum condition, X-ray diffraction patterns of films showed that the films demonstrated polycrystalline stannite single phase with a high degree of (112) preferred orientation. The absorption coefficient of $Cu_2ZnSnSe_4$ thin films were above 104 cm.1 with a band gap of 1.45 eV. At an optimum condition, films were identified as a p type semiconductor characteristic with a resistivity as low as $10^{-1}{\Omega}cm$ and a carrier concentration in the order of $10^{17}cm^{-3}$.