• Asian-Australasian Journal of Animal Sciences
• /
• 제16권12호
• /
• pp.1804-1808
• /
• 2003

A layer experiment was conducted to determine the effects of supplementary methionine chelates (Cu, Zn and Mn), individual or in combination, on laying performance, eggshell quality, gizzard erosion, and IgG level of serum for 8 weeks. Five hundred 96-wk-old force molted ISA Brown layers were assigned to five dietary treatments. Basal diet was formulated to meet or exceed the nutrients requirements listed in NRC (1994). Five experimental diets were control, Zn-methionine chelate (Zn-Met) supplemented, Cumethionine chelate (Cu-Met) supplemented, Zn-Mn-methionine chelate (Zn-Mn-Met) supplemented and Zn-Mn-Cu-Met supplemented diet. Each treated diet was supplemented with respective mineral(s) at the level of 100 ppm in the form of methionine chelate. Egg production was increased by Cu-Met supplementation but decreased by Zn-Met supplementation. Egg weight was significantly (p<0.05) lower in Cu-Met treatment than those of the control and Zn-Met treatment. Specific gravity of eggs and eggshell strength were highest and soft egg production was lowest in Cu-Met treatment. Gizzard erosion index was significantly increased by supplementation of Cu-Met, Zn-Mn-Met or Zn-Mn-Cu-Met. Zinc content in liver significantly increased by Zn-Met, but not by Zn-Mn-Cu-Met treatment. In conclusion, 100 ppm Cu in Cu-Met chelate improved laying performance and eggshell quality but also increased gizzard erosion index. Supplementation of Zn-Met or its combination with other mineral chelates had no beneficial effects on laying performance and eggshell quality.

• 한국재료학회지
• /
• 제14권8호
• /
• pp.595-599
• /
• 2004

We investigated the structural, electrical and magnetic properties of Mn-doped $CuAlO_2$ delafossite ceramics ($CuAl_{1-x}Mn_{x}O_2,\;0\le\;x\;\le0.05$), synthesized by solid-state reaction method in an air atmosphere at a sintering temperature of $1150^{\circ}C$. The solubility limit of Mn ions in delafossite $CuAlO_2$ was found to be as low as about 3 $mol\%$. Positive Hall coefficient and the temperature dependence of conductivity established that non-doped $CuAlO_2$ ceramic is a variable-range hopping p-type semiconductor. It was found that the Mn-doping in $CuAlO_2$ rapidly reduced the hole concentration and conductivity, indicating compensation of free holes. The analysis of the magnetization data provided an evidence that antiferromagnetic superexchange interaction is the dominant mechanism of the exchange coupling between Mn ions in $CuAl_{1-x}Mn_{x}O$ alloy, leading to an almost paramagnetic behavior in this alloy.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.713-716
• /
• 2001

In many papers, the electrochemical analysis of LiMn$_2$O$_4$shows the transition results of Mn$^{3+}$ ion. Charge ordering is accompanied by simultaneous orbital ordering due to the Jahn-Teller effect in Mnl$^{3+}$ ions. To analyze the cycle performance of LiMn$_{2-x}$Cu$_{x}$ O$_4$as the cathode of 4 V class lithium secondary batteries, XRD, TGA analysis were conducted. Although the cycle performance of the LiMn$_{2-x}$Cu$_{x}$ O$_4$was improved from pure LiMn$_2$O$_4$, the discharge capacity was significantly lower than LiCoO$_2$. In this paper, We study the Electrochemical characterization and enhanced stability of Cu-doped spinels in the LiMn$_{2-x}$Cu$_{x}$ O$_4$upon initial cycling.l cycling.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2010년도 하계학술대회 논문집
• /
• pp.141-141
• /
• 2010

ZnS:Mn yellow phosphors doped with Cu for white light emitting diodes were synthesized by solid state reaction method. Photoluminescence excitation spectra originated from $Mn^{2+}$ were ranged from 450 nm to 500 nm. The yellow emission at around 580 nm was associated with $^4T_1{\rightarrow}^6A_1$ transition of $Mn^{2+}$ ions in ZnS:Mn,Cu phosphors. The highest photoluminescence intensity of the phosphors under 405 nm excitation was obtained at Cu concentration of 0.02 mol%.

• 한국반도체및디스플레이장비학회:학술대회논문집
• /
• 한국반도체및디스플레이장비학회 2006년도 춘계학술대회
• /
• pp.225-231
• /
• 2006

.고상반응법 (solid state reaction)합성된 ZnS:Mn,Cu,Cl 형광체는 약 $20^{\sim}25{\mu}m$ 의 구형이고, Cubic/hexagonal 구조를 보였다. Electroluminescent device(ELD)는 실크 스크린된 형광층(ZnS:Mn,Cu,Cl)/유전체층 ($BaTiO_3$)으로 구성되었으며, 각층은 $30^{\sim}50{\mu}m,\;50^{\sim}60{\mu}m$ 정도로 도포 하였다. 100 V-400 Hz 의 구동조건에서, ELD 의 백색 발광은 450 nm, 480 nm 픽에서 각각 $Cl_s{\to}Cu^{+}\;_{Zn},\;Cl_s{\to}Cu^{2+}\;_{Zn}$ 전이에 의해 중첩된 청색, 녹색 밴드의 발광과, 580 nm 픽에서 Mn 의 $^{4}T_1{\to}^{6}A_1$ 전이에 의한 황색 밴드의 발광으로 이루어진다. Cu 농도의 증가에 따라 450 nm 의 발광 밴드의 휘도는 감소하며 580 nm 의 발광 밴드의 휘도가 증가하였고 발광 휘도가 향상되었다. 즉, 색온도가 높은 cold white(10000 K)에서 색온도가 낮은 Warm white(3000 K) 로 변한다. 이것은 450 nm 의 발광 밴드가 580 nm 의 발광 밴드에 흡수되는 에너지 전이 (Energy transfer) 현상에 기인한다. ZnS:Mn,Cu,Cl 의 Mn 1.5 wt %, Cu 2.5 wt.% 에서 최적 발광 휘도를 보이며, 100 V-400 Hz 에서 약 $12cd/cm^2$이였다.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.782-785
• /
• 1995

In this paper, $Mn^{2+}$ ion was doped in Y-Ba-Cu-O as an EPR probe. The following samples were prepared by conventional solid-state reaction method : $YBa_{2}Cu_{2.96}Mn_{0.04}O_{7-\delta}$ (MN-I), annealed $YBa_{2}Cu_{2.96}Mn_{0.04}O_{7-\delta}$ (AMN) and $YBa_{2}Cu_{2.94}Mn_{0.06}O_{7-\delta}$ (MN-II). AMN sample was obtained from MN-I by annealing for 1 hr under the Ar gas atmosphere at $600^{\circ}C$. X-band (~9.05 GHz) EPR spectra were measured from 103 K to room temperature by employing a JES-RE3X spectroscopy with a $TE_{0.11}$ cylindrical cavity and 100 kHz modulation frequency. In MN-I we have observed only the $Cu^{2+}$ signal. The fact that no $Mn^{2+}$ signal was observed, in spite of $Mn^{2+}$ being a very sensitive EPR probe, indicates that most likely isolated $Mn^{2+}$ ions don't exist in the MN-I sample. Most probably $Mn^{2+}$ ions in the MN-I sample interact antiferromagnetically and hence are EPR silent. The AMN spectra of at room temperature and 103 K indicate not only the $Cu^{2+}$ signal but also an extra signal, which increases with decreasing temperature. It is suggested that the extra signal originates from Mn ions that were antiferromagnetically coupled before the annealing process. In MN-II, from 103 K to room temperature, also, the extra signal was observed together with the $Cu^{2+}$ signal. The extra signal in MN-II, however, decreases with decreasing temperature and nearly disappears at 103 K. The signal originates from Mn ions in impurity phases that include $Mn^{2+}$ ions. We suppose that there exist at least two $Mn^{2+}$ doped phases in Y-Ba-Cu-O. The $Mn^{2+}$ signal of one phase is undectable at all temperature and that of another phase decreases with decreasing temperature and disappears around 103 K.

• 대한화학회지
• /
• 제20권5호
• /
• pp.431-437
• /
• 1976

연탄 연소가스중의 일산화탄소와 산소 사이의 반응을 몇가지 촉매에 대해 조사했다. 이산화망간, 산화 동 및 그 혼합촉매를 사용하였으며, 그 실효반응 온도(effective reaction temperature)는 각각 다음과 같다. 즉, $MnO_2$ 단독촉매 및 30% $MnO_2$-70% CuO 혼합촉매는 $250^{\circ}C,\;CuO$는 $450^{\circ}C$, 50% $MnO_2$-50% CuO는$200^{\circ}C$, 70% $MnO_2$-30% CuO는$180^{\circ}C$였다. 실효반응온도 이하에서 일산화탄소의 산화율은 일산화 탄소의 농도가 증가함에 따라 감소하는 경향을 보였으며, 실효반응 온도 이상에서는 변화가 없었다. 반응기 내 체재시간은 0.9 ∼ 1.8초의 범위 내에서는 일산화탄소 산화반응에 조금도 영향을 주지 않았다.

• 공업화학
• /
• 제33권5호
• /
• pp.466-470
• /
• 2022

최근 촉매 소각 공정은 휘발성 유기 화합물을 저온(< 450 ℃)에서 고효율(> 95%)로 산화 및 분해하기 위해 상당한 주목을 받고 있다. 많은 귀금속 촉매 물질이 잘 연구되어 사용되고 있으나 단가가 비싸고 위험하다. 본연구에서는 Cu와 Mn 전구체의 공침법을 활용하여 간단하고 손쉬운 합성 방법을 개발함으로써 고활성 및 저비용의 Cu-Mn 바이메탈 촉매를 제조하였다. 촉매 합성은 Cu와 Mn의 조성비를 조절하여 최적화하였다. 최적화된 촉매는 메조포러스 구조로 230.8 m²/g의 넓은 표면적을 나타냈다. 촉매 성능을 입증하기 위해 에틸 아세테이트의 산화 반응에 대해 Cu-Mn 촉매를 테스트했으며, 250 ℃의 저온에서 100%의 높은 전환 효율을 나타내었다.

• 한국응용과학기술학회지
• /
• 제33권1호
• /
• pp.129-135
• /
• 2016

Cu-Mn과 Cu-Zn 촉매를 침전제로 다르게 하거나, 금속의 몰비율, 소성온도를 다르게 하여 공침법으로 제조하였고 CO산화반응을 수행하여 혼합산화물 촉매에서 Cu, Mn 과 Zn의 영향 및 소성온도가 미치는 영향을 조사하였다. 촉매의 물리 화학적 특성을 알아보기 위하여 XRD, $N_2$ 흡착 및 SEM의 분석을 수행하였다. $Na_2CO_3$로 침전시켜 $270^{\circ}C$로 소성하여 제조한 2Cu-1Mn 산화물 촉매가 저온에서 CO 산화반응 활성이 가장 좋았으며 2Cu-1Mn 산화물 촉매는 $43m^2/g$으로 가장 높은 비표면적과 촉매 활성을 나타내었다. XRD로 촉매의 결정구조를 분석하였을 때 $Cu_{0.5}Mn_{2.5}O_4$의 결정구조를 갖는 촉매는 낮은 활성을 보였다. $270^{\circ}C$에서 소성한 촉매가 좋은 활성을 나타냈으며 Pt 촉매와 비교하여도 저온에서 CO산화반응이 더욱 우수함을 알 수 있었다.

• 한국재료학회지
• /
• 제6권1호
• /
• pp.90-98
• /
• 1996

Mn((Cu0.66AI0.34)1-x(Bi0.3Sb0.7)x) 및 Mn((Fe0.66AI0.34)1-x(Bi0.3Sb0.7)x) 합금계의 상의 변화와 자기적 특성을 조사하였다. Mn((Cu, SI)(Bi, Sb)) 합금계는 Bi상, MnSb상, MnBi상, k-상, Heuser상, Mn2Sb 및 $\beta$-Mn상의 혼합상으로 이루어졌으며 x가 증가함에 따라 Bi상과 Mn2Sb상이 증가하고 K-상, Heusler상 및 $\beta$-Mn상이 줄어들거나 사라졌다. 자기적 성질은 자성을 띄는 MnSb상, MnBi상, Mn2Sb상, k-상 및 Hseusler상과 비자성인 Bi상과 $\beta$-Mn상의 상대적 분율에 의해 결정됨을 알 수 있었고, 150K-200K 부근에서 그 이하로 온도가 감소함에 따라 자화값이 급격히 감소하는 현상이 나타났다. Mn((Fe, AI)(Bi, Sb))합금계는 Bi상, MnSb상, MnBi상, MnBi상,$\beta$-Mn상, k-상 및 Mn2Sb상의 혼합상으로 나타났으며, 자기적 성질은 조사한 전 조성에서 강자성을 띄고 있음을 알 수 있었다.