• Korean Journal of Materials Research
• /
• v.25 no.12
• /
• pp.708-712
• /
• 2015

This study reports the effects of $H_2S$ gas concentration on the properties of $Cu_2ZnSnS_4(CZTS)$ thin films. Specifically, sulfurization process with low $H_2S$ concentrations of 0.05% and 0.1%, along with 5% $H_2S$ gas, was studied. CZTS films were directly synthesized on Mo/Si substrates by chemical bath deposition method using copper sulfate, zinc sulfate heptahydrate, tin chloride dihydrate, and sodium thiosulfate pentahydrate. Smooth CZTS films were grown on substrates at optimized chemical bath deposition condition. The CZTS films sulfurized at low $H_2S$ concentrations of 0.05 % and 0.1% showed very rough and porous film morphology, whereas the film sulfurized at 5% $H_2S$ yielded a very smooth and dense film morphology. The CZTS films were fully crystallized in kesterite crystal form when they were sulfurized at $500^{\circ}C$ for 1 h. The kesterite CZTS film showed a reasonably good room-temperature photoluminescence spectrum that peaked in a range of 1.4 eV to 1.5 eV, consistent with the optimal bandgap for CZTS solar cell applications.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.4
• /
• pp.9-12
• /
• 2004

We report a successful fabrication of high-$J_C$ $NdBa_2Cu_3O_{7-{\delta}}$ (NdBCO) films on (100) $SrTiO_3$ substrates by pulsed laser deposition (PLD) in high oxygen pressures ranging from 400 to 800 mTorr. Fabricated NdBCO films exhibited only c-axis orientation, good out-of-plane and in-plane textures, and also excellent superconducting properties, including critical temperature ($T_C$) and critical current density ($J_C$) of above 90 K and the highest of $3.1MA/cm^2$ at 77 K in self-field, implying that NdBCO is a perspective alternative to YBCO for coated conductor. In low oxygen pressures ranging from 100 to 200 mTorr, however, the films showed a-, c-mixed orientation and degraded $T_{C,zero}$ values due to the formation of $Nd_{1+x}Ba_{2-x}Cu_3O_{7-{\delta}}$-type solid solutions with an excessive substitution of $Nd^{3+}$ ions for the $Ba^{2+}$ sites.

• Progress in Superconductivity
• /
• v.4 no.1
• /
• pp.10-13
• /
• 2002

We report the effect of Ca doping in $YBa_2Cu_3O_{7-\delta}$ (YBCO) thin films grown on the Rolling- Assisted, Biaxially Textured Substrates (RABiTS) with the architecture of $CeO_2/YSZ/CeO_2/Ni$. Critical currents of bilayer and trilayer structures of $YBCO/Y_{0.7}Ca_{0.3}Ba_2Cu_3O_{7-\delta}$/(YCaBCO) as well as undoped YBCO for comparison have been measured in a wide range of temperatures and fields. For $6-8^{\circ}$ grain boundaries, 30% Ca-doping in bilayer structure enhances $J_c$ as high as 35%. The enhancement is larger at low temperatures and at magnetic fields. On the other hand, 30% Ca-doping in trilayer structure reduces $J_c$ as high as 60%. Combined with slightly lower $T_c$, this indicates that Ca is overdoped in this structure and degrades GBs.

• 한국초전도학회:학술대회논문집
• /
• v.15
• /
• pp.2-2
• /
• 2005

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.06a
• /
• pp.326-329
• /
• 2007

$CuInS_{2}$ thin films were synthesized by sulpurization of Cu/In Stacked elemental layer deposited onto glass Substrates by vacuum furnace annealing at temperature 200[$^{\circ}C$]. And structural and electrical properties were measured in order to certify optimum conditions for growth of the ternary compound semiconductor $CuInS_{2}$ thin films with non-stoichiometry composition. $CuInS_{2}$ thin film was well made at the heat treatment 200[$^{\circ}C$] of SLG/Cu/ln/S stacked elemental layer which was prepared by thermal evaporator, and chemical composition of the thin film was analyzed nearly as the proportion of 1 : 1 : 2. Physical properties of the thin film were investigated at various fabrication conditions substrate temperature, annealing and temperature, annealing time by XRD, FE-SEM and Hall measurement system. At the same time, carrier concentration, hall mobility and resistivity of the thin films was $9.10568{\times}10^{17}$ [$cm^{-3}$], 312.502 [$cm^{2}/V{\cdot}s$] and $2.36{\times}10^{-2}$ [${\Omega}{\cdot}cm$], respectively.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.5
• /
• pp.379-385
• /
• 1996

Adhesion of Cu/Cr and Cu/$Cu_xCr_{1-x}$ thin films onto polyimide substrates has been studied. For an adhesion layer, Cr or Cu-Cr alloy films were deposited onto polyimide using DC magnetron sputtering machine. Then Cu was sputter-deposited and finally, Cu was electroplated. Adhesion was evaluated using $90^{\circ}C$ peel test or T-peel test. Plastic deformation of the peeled metal layer was qualitatively measured using XRD technique. It is confirmed that high interfacial fracture energy and large plastic deformation are important to enhance the peel adhesion strength. High peel strength is obtained when the interface is strongly bonded. More ductile film has higher peel strength. In Cu-Cr alloy films, opposite effects of the Cr addition in the alloy film on the peel strength are operative: a beneficial effect of strong interfacial bonding and a negative effect of smaller plastic deformation.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.4
• /
• pp.342-347
• /
• 2007

$Bi_6Mg_2Nb_4O_{21}(BMN)$ thin films were deposited at various substrates by sputtering system for embedded capacitor applications. BMN thin films deposited at room temperature are manufactured as MIM(Metal/Insulator/Metal) structures. Dielectric properties and leakage current density were investigated as a function of various substrates and thickness of BMN thin films. Leakage current density of BMN thin films deposited on CCL(Copper Clad Laminates) showed relatively high value ($1{\times}10^{-3}A/cm^2$) at an applied field of 300 kV/cm on substrates, possibly due to relatively high value of roughness(rms $50{\AA}$) of CCL substrates. 100 nm-thick BMN thin films deposited on Cu/Ti/Si substrates showed the capacitance density of $300 nF/cm^2$, a dielectric constant of 32, a dielectric loss of 2 % at 100 kHz and the leakage current density of $1{\times}10^{-6}A/cm^2$ at an applied field of 300 kV/cm. BMN capacitors are expected to be promising candidates as embedded capacitors for printed circuit board(PCB).

• Journal of Electrochemical Science and Technology
• /
• v.8 no.3
• /
• pp.206-214
• /
• 2017

SnS films have been prepared by electrodeposition technique onto Cu and ITO substrates using acidic solutions containing tin chloride and sodium thiosulfate with sodium citrate as an additive. The effects of sodium citrate on the electrochemical behavior of electrolyte bath containing tin chloride and sodium thiosulfate were investigated by cyclic voltammetry and chronoamperometry techniques. Deposited films were characterized by XRD, FTIR, SEM, optical, photoelectrochemical, and electrical measurements. XRD data showed that deposited SnS with sodium citrate on both substrates were polycrystalline with orthorhombic structures and preferential orientations along (111) directions. However, SnS films with sodium citrate on Cu substrate exhibited a good crystalline structure if compared with that deposited on ITO substrates. FTIR results confirmed the presence of SnS films at peaks 1384 and $560cm^{-1}$. SEM images revealed that SnS with sodium citrate on Cu substrate are well covered with a smooth and uniform surface morphology than deposited on ITO substrate. The direct band gap of the films is about 1.3 eV. p-type semiconductor conduction of SnS was confirmed by photoelectrochemical and Hall Effect measurements. Electrical properties of SnS films showed a low electrical resistivity of $30{\Omega}cm$, carrier concentration of $2.6{\times}10^{15}cm^{-3}$ and mobility of $80cm^2V^{-1}s^{-1}$.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.30 no.4
• /
• pp.350-356
• /
• 1994

We have prepared superconducting Bi-Pb-Sr-Ca.Cu-O thin films by RF magnetron sputtering technique, on heated MgO(100) substrates. Sputtering was carried out in a mixture of argon and oxygen(10%) and the pressure was maintained at 5 mTorr during deposition. The substrate temperature was maintained $400^{\circ}C$ during deposition. The films sputtered were amorphous and insulating. All the films became superconducting by annealing, The films annealed at $880^{\circ}C$ for 30 minutes in air showed high-Tc phase with zero resistivity of 93K. These results indicate that the growth of the high-Tc phase is promoted by the presence of Pb at annealing temperature.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.56 no.1
• /
• pp.128-131
• /
• 2007

YBaCuO superconducting ceramic thick films were fabricated by chemical process. YBaCuO films have been successfully grown on $SrTiO_3$ substrates without a template layer. The films show poor or non superconductivity although they have excellent crystalline properties. ion channeling measurement made it clear that the strain in the films due to strong chemical bonding between the substrate and epilayer remains, resulting in the poor superconductivity. The X ray diffraction pattern of the YBaCuO thick films contained 90K phase. The self template method have resolved this problem. We obtained high-Jc as-grown YBaCuO on $SrTiO_3$ (100).