• Korean Journal of Materials Research
• /
• v.9 no.7
• /
• pp.747-752
• /
• 1999

The interfacial reaction and joint properties of Sn-3.5Ag/Cu and Sn-3.5Ag-1Zn/Cu joint were studied. Modified double lap shear solder joints of Sn-3.5Ag and Sn-3.5Ag- lZn solder were aged for 60days at $100^{\circ}C$ and $150^{\circ}C$ and then loaded to failure in shear. The Sn-3.5Ag/Cu had a fast growth rate of the reaction layer in comparison with the Sn-3.5Ag-lZn at the aging temperature of $150^{\circ}C$ Through the SEM/EDS analysis of solder joint, it was proved that intermatallic layer was $Cu_{6}Sn_5$ phase and aged specimens showed that intermatallic layer grew in proportion to $t_{1/2}$, and the precipitate of $Ag_3Sn$ occur to both inner layer and interface of layer and solder. In case of Zn-containing composite solder, $Cu_{6}Sn_{5}$ phase formed at the side of substrate and $Cu_{5}Zn_{8}$ phase formed at the other side in double layer. The shear strength of the Sn-3.5Ag/Cu joint improved by addition of IZn. The strength of the joint increases with strain rate and decreases with aging temperature

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.3
• /
• pp.55-61
• /
• 2000

Sn-37Pb and Sn-3.5Ag-0.7Cu solder balls of 0.3 mm diameter were reflow soldered with the variation of soldering peak temperature and conveyer speed of reflow machine. The peak temperatures far soldering were changed in the range of 220~$240^{\circ}C$ for Sn-37Pb and 230~$260^{\circ}C$ for Sn-3.5Ag-0.7Cu. As the results of experiments, optimum soldering condition for Sn-37Pb was $230^{\circ}C$ of soldering temp., 0.7~0.8 m/min of conveyer speed. The optimum condition for the Sn-3.5Ag-0.7Cu was $250^{\circ}C$ and 0.6 m/min. The maximum shear strength for the soldered joints of Sn-37Pb was 555 gf and of Sn-3.5Ag-0.7Cu was 617 gf. Thickness of the intermetallic compound Cu6Sn5 on the soldered interface was 1.13~1.45 $\mu\textrm{m}$ for Sn-37Pb and 2.5~4.3 $\mu\textrm{m}$ for Sn-3.5Ag-0.7Cu.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.11a
• /
• pp.55-58
• /
• 2002

The possibility of SnCuX Solder as alternative for Pb-free Solder have been investigated in this study. SnCuX Solder balls(500${\mu}{\textrm}{m}$) were placed on Si-wafer which is Al/Ni/Cu(500nm/$4{\mu}{\textrm}{m}$/$4{\mu}{\textrm}{m}$)UBM layer. After reflow soldering at $250^{\circ}C$, shear strength and microstructure were analyzed. The results showed that the shear strength(500gf) of SnCuX was higher than that of SnCuX at $230^{\circ}C$ and $Cu_6Sn_5$ intermetallic compounds were formed between Cu and SnCuX Solder layers

• Journal of the Korean institute of surface engineering
• /
• v.22 no.1
• /
• pp.3-9
• /
• 1989

The intermetallic compount formation, growth rections, and growth kinetices as functions of the aging temperaturess, time, and the condition of substarte have invedtigted in the Sn/Cu and Sn/Ni bimetal couples. The η'-phase (Cu6Sn5) and $\delta$-phase (Ni3Sn4) were only found to grow at 20 and $70^{\circ}C$in the Sn/Cu and Sn/Ni bimetallic coples repectively. Above that temperatures, all other compounds were formed in sequence of high Sn content plase and the metastable Cu41Sn11 was formed at agend $200^{\circ}C$. The ectivation energy for the growth of intermetallic compounds was 14.7Kxal/mole in the Sn/Cu interface and 26.7Kcal/mole in the Sn/Ni interface.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.1
• /
• pp.19-24
• /
• 2000

To make stacked chip packages far high-density packaging of memory chips used in workstations or PC severs, several lead-frames are to be connected vertically. Fer this purpose. Sn or Sn/Ag were electrochemically deposited on Cu lead-frames and their microstructures were examined by XRD and SEM. Then, two specimens were annealed at $250^{\circ}C$ for 10 min. and pressed to be joined. The shear stresses of joined lead-frames were measured fur comparison. In the case of Sn only, $Cu_3Sn$ was formed by the reaction of Sn and Cu lead-frames. In the case of Sn/Ag, besides $Cu_3Sn$. $Ag_3Sn$ was formed by the reaction of Sn and Ag. Compared to joined specimens made from Sn only, those made from Sn/Ag showed 1.2 times higher shear stress. This was attributed to the $Ag_3Sn$ phase formed at the joined interface.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.265-269
• /
• 2003

Sn(또는 SnAg)/Ni(P)와 Sn/Cu 계의 열사이클동안 형성되는 금속간화합물에 의해 유기되는 응력의 변화를 in-situ로 관찰하였다. Sn(또는 SnAg)/Ni(11.7P) 박막은 계면반응으로 인해 $Ni_3P$와 $Ni_3Sn_4$ 상이 형성되고 이때 인장응력이 발생하였으며, 한편, Sn(또는 SnAg)/Ni(3P) 박막의 계면반응에 의해서는 동일한 $Ni_3P$와 $Ni_3Sn_4$ 상이 형성됨에도 불구하고 압축응력이 발생하였다. SmAg를 사용할 때 형성되는 $Ag_3Sn$이 응력에 미치는 영향은 거의 없었다. Sn/Cu 박막의 경우는 계면반응 초기에는 인장응력이 발생하였고 어느 정도 이상 반응이 진전됨에 따라 압축응력이 발생하였고 최종적으로 $Cu_3Sn$ 상이 형성되었다. 초기의 인장응력은 계면에서 원자들의 intermixing 베 의한 것이고 압축응력은 Sn 방향으로 일방향 성장하는 금속간화합물 형성에 기인한다.

• Electronic Materials Letters
• /
• v.14 no.6
• /
• pp.678-688
• /
• 2018

The repeated-bending properties of Sn-0.7Cu, Sn-0.3Ag-0.7Cu (SAC0307), and Sn-3.0Ag-0.5Cu (SAC305) solders mounted on flexible substrates were studied using highly accelerated stress testing (HAST), followed by repeated-bending testing. In the Sn-0.7Cu joints, the $Cu_6Sn_5$ intermetallic compound (IMC) coarsened as the HAST time increased. For the SAC0307 and SAC305 joints, the $Ag_3Sn$ and $Cu_6Sn_5$ IMCs coarsened mainly along the grain boundary as the HAST time increased. The Sn-0.7Cu solder had a high contact angle, compared to the SAC0307 and SAC305 solders; consequently, the SAC0307 and SAC305 solder joints displayed smoother fillet shapes than the Sn-0.7Cu solder joint. The repeated-bending for the Sn-0.7Cu solder produced the crack initiated from the interface between the Cu lead wire and the solder, and that for the SAC solders indicated the cracks initiated at the surface, but away from the interface between the Cu lead wire and the solder. Furthermore, the oxide layer was thickest for Sn-0.7Cu and thinnest for SAC305, regardless of the HAST time. For the SAC solders, the crack initiation rate increased as the oxide layer thickened and roughened. $Cu_6Sn_5$ precipitated and grew along the grain and subgrain boundaries as the HAST time increased, embrittling the grain boundary at the crack propagation site.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.5
• /
• pp.386-392
• /
• 2003

The electroplating process for a solder bump which can be applied for a flip chip was studied. Si-wafer was used for an experimental substrate, and the substrate were coated with UBM (Under Bump Metallization) of Al(400 nm)/Cu(300 nm)Ni(400 nm)/Au(20 nm) subsequently. The compositions of the bump were Sn-Cu and eutectic Sn-Pb, and characteristics of two bumps were compared. Experimental results showed that the electroplated thickness of the solders were increased with time, and the increasing rates were TEX>$0.45 <\mu\textrm{m}$/min for the Sn-Cu and $ 0.35\mu\textrm{m}$/min for the Sn-Pb. In the case of Sn-Cu, electroplating rate increased from 0.25 to $2.7\mu\textrm{m}$/min with increasing current density from 1 to 8.5 $A/dm^2$. In the case of Sn-Pb the rate increased until the current density became $4 A/dm^2$, and after that current density the rate maintains constant value of $0.62\mu\textrm{m}$/min. The electro plated bumps were air reflowed to form spherical bumps, and their bonded shear strengths were evaluated. The shear strength reached at the reflow time of 10 sec, and the strength was of 113 gf for Sn-Cu and 120 gf for Sn-Pb.

• Journal of Electrochemical Science and Technology
• /
• v.10 no.3
• /
• pp.329-334
• /
• 2019

Sn-Cu alloy powders were prepared via a simple chemical reduction method for the negative electrode materials in lithiumion batteries. The addition of Cu can suppress the growth of Sn particles during synthetic process. Furthermore, the Cu also acts as a matrix phase against the volume change during cycling. With increasing amount of the Cu, a stable $Cu_6Sn_5$ phase formed in the Sn-Cu alloy and its cycle performance greatly enhanced depending on the Cu content. To promote the generation of the $Cu_6Sn_5$ phase, the synthesis temperature is raised to $60-100^{\circ}C$ from the ambient temperature. The Sn-Cu alloy powders prepared at elevated temperatures showed remarkable cycle performances. The Sn-Cu alloy powder obtained at $60^{\circ}C$ exhibited a significantly high volumetric capacity of over 2,000 mAh/cc at the 50th cycle.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.953-954
• /
• 2006

Ti-Cu-Ni-Sn quaternary amorphous alloys of $Ti_{50}Cu_{32}Ni_{15}Sn_3$, $Ti_{50}Cu_{25}Ni_{20}Sn_5$, and $Ti_{50}Cu_{23}Ni_{20}Sn_7$ composition were prepared by mechanical alloying in a planetary high-energy ball-mill (AGO-2). The amorphization of all three alloys was found to set in after milling at 300rpm speed for 2h. A complete amorphization was observed for $Ti_{50}Cu_{32}Ni_{15}Sn_3$ and $Ti_{50}Cu_{25}Ni_{20}Sn_5$ after 30h and 20h of milling, respectively. Differential scanning calorimetry analyses revealed that the thermal stability increased in the order of $Ti_{50}Cu_{32}Ni_{15}Sn_3$, $Ti_{50}Cu_{25}Ni_{20}Sn_5$, and $Ti_{50}Cu_{23}Ni_{20}Sn_7$.