• The Journal of Advanced Prosthodontics
• /
• v.6 no.3
• /
• pp.215-223
• /
• 2014

PURPOSE. This study aimed to develop a copper-aluminium-nickel alloy which has properties comparable to that of dental alloys used for dental post and core applications with the reasonable cost. MATERIALS AND METHODS. Sixteen groups of experimental copper alloys with variants of 3, 6, 9, 12 wt% Al and 0, 2, 4, 6 wt% Ni were prepared and casted. Their properties were tested and evaluated. The data of thermal, physical, and mechanical properties were analyzed using the two-way ANOVA and Tukey's test (${\alpha}$=0.05). The alloy toxicity was evaluated according to the ISO standard. RESULTS. The solidus and liquidus points of experimental alloys ranged from $1023^{\circ}C$ to $1113^{\circ}C$ and increased as the nickel content increased. The highest ultimate tensile strength ($595.9{\pm}14.2$ MPa) was shown in the Cu-12Al-4Ni alloy. The tensile strength was increased as the both elements increased. Alloys with 3-6 wt% Al exhibited a small amount of 0.2% proof strength. Accordingly, the Cu-9Al-2Ni and Cu-9Al-4Ni alloys not only demonstrated an appropriate modulus of elasticity ($113.9{\pm}8.0$ and $122.8{\pm}11.3$ GPa, respectively), but also had a value of 0.2% proof strength ($190.8{\pm}4.8$ and $198.2{\pm}3.4$ MPa, respectively), which complied with the ISO standard requirement (>180 MPa). Alloys with the highest contents of nickel (6 wt% Ni) revealed a widespread decolourisation zone (5.0-5.9 mm), which correspondingly produced the largest cell response, equating positive control. CONCLUSION. The copper alloys fused with 9 wt% Al and 2-4 wt% Ni can be considered for a potential use as dental post and core applications.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.05a
• /
• pp.38-46
• /
• 1999

Dispersion strengthened Cu alloys have been manufactured by spray forming and also by reactive spray forming, followed by hot extrusion of the spray deposited billets. The size of dispersed particles in the reactive spray formed alloy was much finer than that in the spray formed alloy. That was because the dominant chemical reaction between Ti and B had occurred in Cu-Ti-B alloy melt in spray forming while it had occurred after deposition of droplets in reactive spray forming. The yield strength of the reactive spray formed alloy was greater than that of the spray formed alloy. To understand the mechanism responsible for this observed strengthening, the yield strength of two Cu alloys were analyzed using the dislocation pile-up model and Orowan mechanism, which were fairly consistent with the experimental results. Increase in yield strength of reactive spray formed alloy relative to spray formed alloy was largely attributed to nano-scale TiB dispersoids.

• Journal of Korea Foundry Society
• /
• v.16 no.6
• /
• pp.556-564
• /
• 1996

Variation of shape and size of solid particles and solute redistribution in Mg-9wt.%Al, AI-4.5wt.% Cu, and AI-7wt.%Si alloys were investigated when they were heated to semi-solid temperatures and held without stirring. In the case of Mg-9wt.% Al and Al-4.5wt.%Cu alloys, the polygonal shaped solid particles were agglomerated with non-uniform distribution, and there were no disappearance of the solid/solid boundary until the end of melting. But in the case of an Al-7wt.%Si alloys, two or three spherical shaped particles were coalesced or separated individually, and the coalesced particles had no solid/solid interface on the contrary to the prevous case. The maximum size of solid particles during isothermal heating at high temperature was smaller than that at lower temperature, but the time required to reach the maximum size at high temperature was shorter than that at lower temperature. The concentrations of main solute atom whose distribution coefficient is lower than 1, decreased in the primary solid particles as the liquid fraction increased, and the gradient of solute concentration was steeper in Mg-9wt.%Al alloy and Al-4.5wt.%Cu alloy than that of Al-7wt.%Si alloy.

• Korean Journal of Materials Research
• /
• v.11 no.4
• /
• pp.266-271
• /
• 2001

Effect of Cd addition on the stress corrosion cracking(SCC) resistance of Al-Cu-Mn cast alloy was investigated by C-ring test and electrical conductivity measurement. With increasing Cd contents, the electrical conductivity and the SCC resistance were increased. The PFZ and coarse precipitates along the grain boundary were observed from TEM micrographs. The fracture made of the alloys was confirmed as intergranular type and showed brittle fracture surface. As a result, it was concluded that the SCC mechanism of these alloys is the anodic dissolution model. The maximum hardness was increased from 127Hv in the Cd-free alloy to 138∼145Hv in the Cd addition alloys.

• Korean Journal of Metals and Materials
• /
• v.46 no.1
• /
• pp.26-32
• /
• 2008

Examination of two bronze vessels supposedly from the Koryo dynasty revealed that they consist of bowls and stands that are fixed together using rivet joints made of Cu-Ag alloys. The bowls and stands were forged out of unleaded bronze alloys of approximately 22 weight % Sn before being quenched from the ${\alpha}+{\beta}$ region of the Cu-Sn phase diagram. This specific alloy and the thermo-mechanical treatment constitute two key elements of the unique technical tradition called Bangcha (방짜) that has long been established in Korea. The high Sn content ensures better casting and the thermal treatment causes the brittle ${\delta}$ phase to be avoided in forging as well as in services. The experiment on the laboratory Cu-Ag alloys of varying Ag contents suggested that the Cu-Ag system was the best choice of materials for the rivets at the time in view of their color, availability, ductility and low melting points.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.271-272
• /
• 2012

Bulk Metallic Glasses (BMGs or amorphous alloy) exhibit high strength and good corrosion resistance. Applications of thin films and micro parts of BMGs have been used a lot since its inception in the research of BMGs. However, Application and fabrication of BMGs are limited to make structural materials. Thin films of BMGs which is sputtered on the surface of structural materials by sputtering process is used to improve limits about application of BMGs. In order to investigate the difference of properties between designed alloys and thin films, we identified that thin films deposited on the surface that have the characteristic of the amorphous films and the composition of designed alloys. Zr-Cu (Cu=30, 35, 38, 40, 50 at.%) and Zr-Cu-Al (Al=10 at.% fixed, Cu=26, 30, 34, 38 at.%) alloys were fabricated with Zr (99.7% purity), Cu (99.997% purity), and Al (99.99% purity) as melting 5 times by arc melting method before rods 2mm in diameter was manufactured. In order to analyze GFA (Glass Forming Ability), rods were observed by Optical Microscopy and SEM and $T_g$, $T_x$, ($T_x$ is crystallization temperature and $T_g$ is the glass transition temperature) and Tm were measured by DTA and DSC. Powder was manufactured by Gas Atomizer and target was sintered using powder in large supercooled liquid region ($=T_x-T_g$) by SPS(Spark Plasma Sintering). Amorphous foil was prepared by RSP process with 5 gram alloy button. The composition of the foil and sputtered thin film was analyzed by EDS and EPMA. In the result of DSC curve, binary alloys ($Zr_{62}Cu_{38}$, $Zr_{60}Cu_{40}$, $Zr_{50}Cu_{50}$) and ternary alloys ($Zr_{64}Al_{10}Cu_{26}$, $Zr_{56}Al_{10}Cu_{34}$, $Zr_{52}Al_{10}Cu_{38}$) have $T_g$ except for $Zr_{70}Cu_{30}$ and $Zr_{60}Al_{10}Cu_{30}$. The compositions with $T_g$ made into powders. Figure shows XRD data of thin film showed similar hollow peak.

• Journal of Korea Foundry Society
• /
• v.33 no.4
• /
• pp.171-180
• /
• 2013

The effects of alloying elements on the solidification characteristics, microstructure, thermal conductivity, and tensile strength of Al-Zn-Mg-Fe alloys were investigated for the development of high strength and high thermal conductivity aluminium alloy for die casting. The amounts of Zn and Mg in Al-Zn-Mg-Fe alloys had little effect on the liquidus/solidus temperature, the latent heat for solidification, the energy release for solidification and the fluidity of Al-Zn-Mg-Fe alloys. Thermo-physical modelling of Al-Zn-Mg-Fe alloys by the JMatPro program showed $MgZn_2$, AlCuMgZn and $Al_3Fe$ phases in the microstructure of the alloys. Increased amounts of Mg in Al-Zn-Mg-Fe alloys resulted in phase transformation, such as $MgZn_2{\Rightarrow}MgZn_2+AlCuMgZn{\Rightarrow}AlCuMgZn$ in the microstructure of the alloys. Increased amounts of Zn and Mg in Al-Zn-Mg-Fe alloys resulted in a gradual reduction of the thermal conductivity of the alloys. Increased amounts of Zn and Mg in Al-Zn-Mg-Fe alloys had little effect on the tensile strength of the alloys.

• Korean Journal of Materials Research
• /
• v.10 no.6
• /
• pp.422-429
• /
• 2000

To investigate the effect of annealing temperature and time on the recrystallization behavior and microstructure of Zr-based alloys, the specimens of Zr-0.8Sn-0.4Nb-0.4Fe-0.2Cu, Zr-1Nb, Zircaloy-4, and unalloyed Zr were cold-worked and annealed at 400, 500, 600, 700, 800, $900^{\circ}C$ for 30 to 5000 minutes. The hardness, microstructure and precipitate of the specimens were investigated by using micro-hardness tester, optical microscope and transmission electron microscope, respectively. The recrystallization of Zr-based alloys occurred between $400^{\circ}C$ and $600^{\circ}C$. As the content of alloying elements increased, the hardness and recrystallization temperature of the alloys increased though the grain sizes after recrystallization decreased. It was supposed that the hardness of Zr-based alloy with Fe or Cu increased during recovery by the formation of Fe or Cu precipitates.

• Journal of the Korean Society for Heat Treatment
• /
• v.24 no.5
• /
• pp.243-250
• /
• 2011

When alloys are vacuum-deposited on cooled substrates, super-rapidly cooled alloy films in the unequilibrium state can be obtained. As an application of this method, Ag-Cu, Ag-Ni and Ag-C alloys were successfully produced, and their mechanical properties with tempering temperature were investigated. The following results were obtained : (1) In case of Ag-Cu alloys, the solid solution was hardened by tempering at $150^{\circ}C$. The hardening is considered to occur when the solid solution begins to decompose into ${\alpha}$ and ${\beta}$ phases. The Knoop hardness number of a 40 at.%Ag-Cu alloy film deposited on a cooled glass substrate was 390 $kg/mm^2$. The as-deposited films were generally very hard but fractured under stresses below their elastic limits. (2) In case of Ag-Ni and Ag-C alloys, after the tempering of 4 at.%Ni-Ag alloy at $400^{\circ}C$ and of 1 and 2 at.%C-Ag alloys at $200^{\circ}C$, they were hardened by the precipitation of fine nickel and carbon particles. The linear relationship between proof stress vs. $(grain\;diameter)^{-l/2}$ for bulk silver polycrystals can be applied to vacuum-deposited films up to about 0.1 ${\mu}m$ grain diameter, but the proof stress of ultra-fine grained silver with grain diameters of less than 0.1 ${\mu}m$ was smaller than the value expected from the Petch's relation.

• Korean Journal of Materials Research
• /
• v.23 no.7
• /
• pp.385-391
• /
• 2013

The influence of Cu and Ni on the ductile-brittle transition behavior of metastable austenitic Fe-18Cr-10Mn-N alloys with N contents below 0.5 wt.% was investigated in terms of austenite stability and microstructure. All the metastable austenitic Fe-18Cr-10Mn-N alloys exhibited a ductile-brittle transition behavior by unusual low-temperature brittle fracture, irrespective of Cu and/or Ni addition, and deformation-induced martensitic transformation occasionally occurred during Charpy impact testing at lower temperatures due to reduced austenite stability resulting from insufficient N content. The formation of deformation-induced martensite substantially increased the ductile-brittle transition temperature(DBTT) by deteriorating low-temperature toughness because the martensite was more brittle than the parent austenite phase beyond the energy absorbed during transformation, and its volume fraction was too small. On the other hand, the Cu addition to the metastable austenitic Fe-18Cr-10Mn-N alloy increased DBTT because the presence of ${\delta}$-ferrite had a negative effect on low-temperature toughness. However, the combined addition of Cu and Ni to the metastable austenitic Fe-18Cr-10Mn-N alloy decreased DBTT, compared to the sole addtion of Ni or Cu. This could be explained by the fact that the combined addition of Cu and Ni largely enhanced austenite stability, and suppressed the formation of deformation-induced martensite and ${\delta}$-ferrite in conjunction with the beneficial effect of Cu which may increase stacking fault energy, so that it allows cross-slip to occur and thus reduces the planarity of the deformation mechanism.