• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.33 no.3
• /
• pp.97-103
• /
• 2023

Barrier films for transparent packaging materials with excellent moisture barrier properties are prepared, utilizing a nanoclay dispersion coating layer formed after a pretreatment process of plasma activation surface treatment process under vacuum at room temperature. Attention is paid on optimizing the coupling additive through the appropriate crosslinking process and optimal dispersion process of the coating process to enhance adhesion. Analysis of the functional coating thin film shows that the water vapor transmission rate is less than 10 g/m²/24 hrs (ASTM F-1249) and the oxygen transmission rate is less than 30 cc/m²/24 hrs (ASTM D3985). It is shown that water barrier properties of coating thin film prepared in this study are greater than conventional untreated films by 10 times or more. The thickness of the transparent gas barrier film is within 0.1 mm, and the transparent gas barrier complex is implemented in two layers. In the study of PET thin film interface characteristics, FT-IR experimental analysis shows the reaction activity was optimized at RDS 1.125 %.

• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.4
• /
• pp.9-14
• /
• 2022

Silica aerogel is a porous material with a very low density and high specific surface area. Still, its application is limited due to its weak mechanical properties due to structural features. To solve this problem, a method of complexing it with various polymers has been proposed. We synthesized polyimide cross-linked silica aerogel by the sol-gel process to obtain high mechanical properties. Tetraethyl orthosilicate (TEOS) was used as a precursor to make silica aerogel, and 3- aminopropyltriethoxysilane (APTES) was used as a coupling agent for cross-linking polyimide. Polyimide was synthesized using pyromellitic dianhydride and 3,5-diaminobenzoic acid, and mechanical properties were improved by crosslinking polyimide with 10 repeating units in the polyimide chain using the reaction formula ${\frac{n_1}{n_2}}={\frac{n}{n+1}}$ To realize silica aerogel, polyimide having various weight ratios was added before gelation, resulting in a 19-fold or greater increase in maximum compressive strength compared to pure silica aerogel. From this study, an enhancement of silica aerogel could be enhanced through polymer cross-linking bonds.

• Korean Chemical Engineering Research
• /
• v.58 no.4
• /
• pp.541-549
• /
• 2020

The Drug Delivery System (DDS) is defined as a technology for designing existing or new drug formulations and optimizing drug treatment. DDS is designed to efficiently deliver drugs for the care of diseases, minimize the side effects of drug, and maximize drug efficacy. In this study, the optimization of tripolyphosphate (TPP) concentration on the size of Chitosan nanoparticles (CNPs) produced by crosslinking with chitosan was measured. In addition, the characteristics of Fe₃O₄-CNPs according to the amount of iron oxide (Fe₃O₄) were measured, and it was confirmed that the higher the amount of Fe₃O₄, the better the characteristics as a magnetic drug carrier were displayed. Through the ninhydrin reaction, a calibration curve was obtained according to the concentration of γ-aminobutyric acid (GABA) of Y = 0.00373exp(179.729X)-0.0114 (R² = 0.989) in the low concentration (0.004 to 0.02 wt%) and Y = 21.680X-0.290 (R² = 0.999) in the high concentration (0.02 to 0.1 wt%). Absorption was constant at about 62.5% above 0.04 g of initial GABA. In addition, the amount of GABA released from GABA-Fe₃O₄-CNPs over time was measured to confirm that drug release was terminated after about 24 hr. Finally, GABA-Fe₃O₄-CNPs performed under the optimal conditions were spherical particles of about 150 nm, and it was confirmed that the properties of the particles appear well, indicating that GABA-Fe₃O₄-CNPs were suitable as drug carriers.

• Journal of Korean Society of Environmental Engineers
• /
• v.35 no.9
• /
• pp.636-642
• /
• 2013

In order to overcome drawbacks (i.e., filtration and recovery) of conventional powder type photocatalysts, nano-ZnO/Laponite/PVA (ZLP) photocatalyzed adsorption balls were developed by using in situ mixing of nanoscale ZnO as a photocatalyst, and Laponite as both adsorbent and supporting media in deionized water, followed by the poly vinyl alcohol polymerization with boric acid. The optimum mixing ratio of nano-ZnO:Laponite:PVA:deionized water was found to be 3:1:1:16 (by weight), and the mesh and film produced by PVA polymerization with boric acid might inhibit both swelling of Laponite and detachment of nanoscale ZnO from ZLP balls. Drying ZLP balls with microwave (600 watt) was found to produce ZLP balls with stable structure in water, and various sizes (55~500 ${\mu}m$) of pore were found to be distributed based on SEM and TEM results. In the initial period of reaction (i. e., 40 min), adsorption through ionic interaction between methylene blue and Laponite was the main removal mechanism. After the saturation of methylene blue to available adsorption sites for Laponite, the photocatalytic degradation of methylene blue occurred. The effective removal of methylene blue was attributed to adsorption and photocatalytic degradation. Based on the results from this study, synthesized ZLP photocatalyzed adsorption balls were expected to remove recalcitrant organic compounds effectively through both adsorption and photocatalytic degradation, and the risks of environmental receptors caused by detachment of nanoscale photocatalysts can be reduced.