• Macromolecular Research
• /
• 제14권1호
• /
• pp.34-37
• /
• 2006

Attaching the organosilyl groups to macromolecular chains of 2-hydroxyethyl methacrylate (HEMA) should lead to important modifications of polymer properties. t-$BuMe_{2}Si$ and cubane-l, 4-dicarboxylic acid (CDA) were covalently linked with 2-hydroxyethyl methacrylate (HEMA). The silyl-linked HEMA is abbreviated as TSMA, while cubane-l ,4-dicarboxylic acid (CDA) linked to two HEMA groups is the cross-linking agent (CA). Free radical cross-linking copolymerization of TSMA and HEMA with various ratios of CA as the cross-linking agent was carried out at 60-70$^{circ}C$. The compositions of the cross-linked, three-dimensional polymers were determined by FTIR spectroscopy. The glass transition temperature ($T_{g}$) of the network polymers was determined calorimetrically. The $T_{g}$ of the network polymer increased with increasing cross-linking degree.

• 폴리머
• /
• 제39권3호
• /
• pp.499-505
• /
• 2015

Dimethyldimethoxysilane(DMDMS), methyltrimethoxysilane(MTMS)과 phenyltrimethoxysilane(PTMS)을 이용하여 폴리유기실록산 열 경화성 코팅액을 제조하고 가교도와 페닐기 함량이 코팅액과 도막 물성에 미치는 영향을 살펴보았다. Si-NMR 측정에서 얻어진 D $T^{Me}$ $T^{Ph}$ 구조 코팅액 조성비가 사용된 DMDMS, MTMS, PTMS의 몰 비로부터 얻어진 이론치와 일치함을 확인할 수 있었다. 가교밀도가 높을수록 그리고 페닐 함량이 낮을수록 실록산 결합의 증가에 의하여 코팅액 분자량이 증가됨을 알 수 있으며 페닐기 증가는 코팅액 굴절률 증가에 매우 큰 영향을 미침을 알 수 있었다. 가교밀도가 높을수록, 페닐기 함량이 감소할수록 코팅도막 경도는 증가되었으며 내열특성 또한 우수해짐을 확인할 수 있었다. 이상의 결과로부터 같은 실록산 결합을 갖는 폴리유기실록산 코팅제라도 치환도에 따른 가교도 조절과 페닐기 함량에 따라 코팅액 물성이 달라짐을 확인할 수 있었다.

• 멤브레인
• /
• 제28권3호
• /
• pp.205-213
• /
• 2018

본 연구에서는 가교막을 poly(2,6-dimethyl-1,4-phenylene oxide)(PPO)에 브롬화반응을 통해 제조한 Br-PPO를 주사슬로 성공적으로 제조하였고, 키토산과 4차암모늄이 포함된 키토산을 가교제로 사용하였다. 제조된 가교막은 트리메틸아민 용액에 함침하여 후처리를 진행하였다. 그리고 가교도는 가교제 비율을 이용하여 조절하였다. 이렇게 제조된 A-PPO + chitosan 가교막과 A-PPO + QA-chitosan 가교막의 이온교환막으로써의 가능성을 여러 특성평가로 확인하였다. Chitosan을 사용한 가교막보다 QA-chitosan을 사용한 가교막이 가교가 더 잘 이루어졌으며, QA-chitosan의 함량이 증가할수록 이온교환용량이 1.18 meq/g에서 1.53 meq/g까지 증가하는 경향, 함수율이 21.6%에서 42.2%까지 증가하는 경향을 나타내었다.

• Korean Membrane Journal
• /
• 제10권1호
• /
• pp.13-19
• /
• 2008

Water softening is a very promising field for membranes and especially ultra low pressure membranes. Nanofiltration membranes based on pore-filling technology was prepared by using a new technique: the in-situ cross-linking. This route involves introducing a pre-formed polymer into the pores of a host membrane and then locking the polymer in the pores by in-situ cross-linking with an appropriate reagent. By this way, it is possible to make robust and competitive, pore-filled, anion-exchange membranes with excellent control over the properties of the incorporated gel without affecting the host membrane. In this paper, the possibilities of tuning such membranes for ultra low pressure water softening was examined by altering pore-filling chemistry (by changing cross-linking and aminating reagents). The results showed that tuning the chemistry of the pore-filling has important effects. In particularly, it had been shown that the correct selection of cross-linking reagent was not only essential to get pore-filled membranes but it could control their properties. Moreover, the aminating reagent could improve membrane performance. It was found that an increase in hydrophobicity could improve the Darcy permeability.

• Fibers and Polymers
• /
• 제7권4호
• /
• pp.328-332
• /
• 2006

Poly(ethylene terephthalate) (PET) and poly(ethylene glycol) (PEG) copolymers cross-linked with pentaerythritol, a four-way cross-linker, are prepared to compare their mechanical and shape memory properties with the one cross-linked by glycerol. Composition of PEG and pentaerythritol is varied to search for the one with the best mechanical and shape memory properties. The highest shape recovery rate is observed for the copolymer composed of 30 mol% PEG-200 and 2.5 mol% pentaerythritol. Four-way cross-linking by pentaerythritol significantly improves shape recovery rate and retention of high shape recovery rate after repeated use compared to the one cross-linked by glycerol, a three-way cross-linker, and difference and advantage of additional cross-linking point are discussed.

• Biomaterials and Biomechanics in Bioengineering
• /
• 제1권3호
• /
• pp.163-174
• /
• 2014

The objective of this study is to prepare an artificial extracellular matrix (ECM) for cell culture by using polymer hydrogels. The polymer used is a cytocompatible water-soluble phospholipid polymer: poly[2-methacryloyloxyethyl phosphorylcholine (MPC)-n-butyl methacrylate-p-nitrophenyloxycarbonyl poly(ethylene oxide) methacrylate (MEONP)] (PMBN). The hydrogels are prepared using a cross-linking reaction between PMBN and diamine compounds, which can easily react to the MEONP moiety under mild conditions. The most favorable diamine is the bis(3-aminopropyl) poly(ethylene oxide) (APEO). The effects of cross-linking density and the chemical structure of cross-linking molecules on the mechanical properties of the hydrogel are evaluated. The storage modulus of the hydrogel is tailored by tuning the PMBN concentration and the MEONP/amino group ratio. The porous structure of the hydrogel networks depends not only on these parameters but also on the reaction temperature. We prepare a hydrogel with $40-50{\mu}m$ diameter pores and more than 90 wt% swelling. The permeation of proteins through the hydrogel increases dramatically with an increase in pore size. To induce cell adhesion, the cell-attaching oligopeptide, RGDS, is immobilized onto the hydrogel using MEONP residue. Bovine pulmonary artery endothelial cells (BPAECs) are cultured on the hydrogel matrix and are able to migrate into the artificial matrix. Hence, the RGDS-modified PMBN hydrogel matrix with cross-linked APEO functions as an artificial ECM for growing cells for applications in tissue engineering.

• Macromolecular Research
• /
• 제17권10호
• /
• pp.791-796
• /
• 2009

An electrochemically and photochemically polymerizable monomer, 2-((2,3-dihydrothieno[3,4-b] [1,4]dioxin-2-yl)methoxy)ethyl methacrylate (EDOT-EMA), was explored for patterning of poly(3,4-ethylenedioxythiophene) (PEDOT) via side chain cross-linking. The polymer from EDOT-EMA was deposited electrochemically to produce polymeric EDOT (PEDOT-EMA), which was directly photo-patterned by UV light as the side EMA groups of PEDOT-EMA were polymerized to give cross-linked EMA (PEDOT-PEMA). Absorption and FTIR studies of the UV-exposed film (PEDOT-PEMA) indicated that the photo-patterning mainly originated from the photo cross-linking of the methacrylates in the side-chain. After irradiation of the film, the conductivity of the irradiated area decreased from $5.6{\times}10^{-3}$ S/cm to $7.2{\times}10^{-4}$ S/cm, possibly due to bending of the conductive PEDOT channel as a result of the side chain cross-linking. The patterned film was applied to a solid state electrochromic (EC) cell to obtain micro-patterned EC cells with lines up to 5 ${\mu}m$ wide.

• Macromolecular Research
• /
• 제17권11호
• /
• pp.926-930
• /
• 2009

A new method for encapsulating nanomaterials within intermediary layer cross-linked (ILCL) polymeric micelles using a bifunctional photo-cross-linking agent was developed. For ILCL polymeric micelles, an amphiphilic triblock copolymer of poly(ethylene glycol)-b-poly(2-hydroxyethyl methacrylate)-b-poly(methyl methacrylate) (PEG-PHEMA-PMMA) was synthesized via consecutive atom transfer radical polymerization (ATRP), Di(4-hydroxyl benzophenone) dodecanedioate (BPD) was used as a bifunctional photo-cross-linking agent. The PMMA-tethered Au nanoparticles and BPD, or pyrene and BPD were encapsulated in the PEG-PHEMA-PMMA micelles, and their intermediary layers were photo-cross-linked by UV irradiation for 1 h. The HEMA units donated labile hydrogens to the excited-state benzophenone groups in BPD, and they were subsequently cross-linked by BPD through radical-radical combination. The spherical structures of the PEG-PHEMA-PMMA micelles containing the Au nanoparticles or pyrene were unaffected by the photo-cross-linking process.

• Transactions on Electrical and Electronic Materials
• /
• 제10권1호
• /
• pp.9-15
• /
• 2009

There is a growing demand for a high voltage silicone rubber composite with high mechanical property and high electrical property. The effect of modified cross-linking agent on the mechanical, electrical properties, and short-circuit test performance of silicone rubber insulators have been investigated. To use base polymer, the various silicone polymers were prepared by the equilibrium polymerization. Aluminum trihydrate surface was treated by vinyl silane. Liquid silicone rubber nanocomposite was prepared from the compounding of VPMPS, HPDMS, catalyst, and alumina trihydrate modified with 1,3,5-trivinyl-l,3,5-trimethylcyclotrisiloxane. The mechanical property and electrical property for insulation materials were measured, indicating the high tensile strength and the good short-circuit property.

• The Korean Journal of Ceramics
• /
• 제5권3호
• /
• pp.278-283
• /
• 1999

Formaldehyde has widely been used for the cross-linking of polyvinyl alcohol polyvinyl alcohol polymer. The effects of formaldehyde on the water resistance of MDF cement composites were investigated as a function of types of catalyst, base or acid, and the amount of formaldehyde. The acetalization, reaction of OH group of PVA with aldehyde, was ended incompletely under base atmosphere. However, by addition of citric acid, the cross-linking of PVA polymer could be acheved through acetalization of PVA and formaldehyde. The effects of these different patterne according to the types of catalyst on the water resistance of MDF cement were studied by the preparation of PVA films and MDF composites. Thanks to the cross-linking reaction of PVA polymer chains by formaldehyde, the modified PVA films and MDF composites showed a good water-resistant propety. The modified MDF cement composite to which 3 wt% formaldehyde and 1 wt% cirtic acid were added showed 80% of initial flexural strength and good interfacial state between cement grain and polymer matrix. However, 4 wt% formaldehyde deteriorted the processing conditions, microstructures and eventually the flexural strength, causing sharp increase in the viscosity of sample dough during the mixing process. To study the relatins of flexural strength and interface of cement grain and polymer matrix, SEM and MIP measurement were performed.