• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.11a
• /
• pp.40-41
• /
• 2018

The purpose of this study is to compare the amount of critical chloride of rebar embedded in concrete according to the substitution rate of admixture. In order to determine the starting point of corrosion of rebar, electrodes were embedded in concrete, chloride was supplied, and OCP of rebar was observed in real time. The amount of the contaminants in the concrete surrounding the rebar was judged to be the critical corrosion chloride contents of the rebar at the start of the corrosion. As a result of the comparative evaluation, it was confirmed that the critical chloride contents of the rebar decreased with increasing the substitution ratio of the admixture.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.50 no.6
• /
• pp.49-60
• /
• 2008

This study were predicted the corrosion threshold reached at steel reinforcement in latex modified concrete(LMC) which were applied the agricultural hydraulic concrete structures. Accelerated testing was accomplished to the evaluate the diffusion coefficient of LMC mix, and the time dependent constants of diffusion. Also, the average chloride diffusion coefficient was estimated. From the average chloride ion diffusion coefficient, the time which critical chloride contents at depth of reinforcement steel was estimated. Test results indicated that the corrosion threshold reached at reinforcement in LMC were effected on the mix proportion factor including cement contents, latex content, and water-cement ratio. Especially, the average chloride diffusion coefficient, the corrosion threshold reached at reinforcement in LMC were affected by the all mix proportion factor.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1994.10a
• /
• pp.87-92
• /
• 1994

The main objective of this study is to determine the critical chloride ion concentrations in the pore solutions causing depassivation of steel reinforcement in concrete made with cements of different $C_3A$ contents. Cement pastes with water-ratio of 0.5 were prepared using four cements with $C_3A$ contents of 0.46, 5.97, 9.14, and 9.65 percent. The pastes were allowed to hydrate in sealed containers for 28days and then objected to pore solution expression. The expressed pore fluids were analyzed for chloride and hydroxyl ion concentrations. It was found that the free cholride concentration in the pore solution decreases significantly with an increase in the $C_3A$ content of the cement. With increasing level of chloride addition, although the alsolute amount of bound chloride increase, the ratio of bound to total chlorides decreases.

• Journal of the Korea Concrete Institute
• /
• v.20 no.4
• /
• pp.415-421
• /
• 2008

Reinforced concrete starts to corrode when the chloride ion concentration which is the sum of included in concrete and penetrated from environments exceeds a certain level of critical chloride concentration. Therefore each country regulates the upper bounds of chloride amount in concrete and the regulations are different for each country due to its circumstances. In this study, the critical threshold chloride content according to unit cement amount is empirically calculated to propose a reasonable regulation method on the chloride amount. As a result, the critical threshold chloride content increases considerably according to cement content and it agrees with the established theories. The present regulations on total chloride amount 0.3 or 0.6 kg chloride ions per $1\;m^3$ of concrete does not reflect the influences of mix design, environmental conditions and etc. So it can be said that it is more reasonable to regulate the critical threshold chloride content by the ratio of chloride amount per unit cement content than by the total chloride content in $1\;m^3$ of concrete.

• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.44 no.2
• /
• pp.163-165
• /
• 1999

The study was conducted to find the critical concentrations of zinc toxicity and to determine the changes of the contents of free proline and organic acids with treatment of different zinc chloride concentrations during rice germination and seedlings grown for seven days. The concentration of zinc chloride, 140 ppm, inhibited root elongation as much as 46 times compared with the control, and the germination rate was also decreased in all treatments of zinc chloride, showing that the germination rate decreased more with increasing concentrations of zinc chloride. Its rate was only 13% with treatment of 140 ppm zinc chloride. The content of free proline with treatment of zinc chloride, 140 ppm, was highest about 4,873 $\mu$M at 3 days compared with the control. Malic acid concentration with treatment of zinc chloride, 140 ppm, increased to approximately 4 times compared to the control. Citric and succinic acid content were also slightly increased in all treatments of zinc chloride.

• Journal of the Korean Society of Safety
• /
• v.29 no.6
• /
• pp.87-93
• /
• 2014

In this study, the reinforced concrete rahmen bridge damaged by the chloride attack was investigated. According to the investigation, the degraded concretes on cantilever kerb and end part were intensively observed. Thus, the chloride content test and half-cell method were performed to evaluate the degraded parts. As a result, the contents of chloride on degraded parts were C and D grade. On the other hand, the half-cell potential values of rebar in degraded concrete were measured with the minor corrosion. This rebar corrosion is expected to progressing. Chloride content D grade is due to expansion pressure by corrosion of rebar and freeze-thaw by permeate water, could see progresses rapidly degradation. In order to prevent chloride attack to concrete deck caused by deicing salts, corresponding to the chloride critical concentration must maintain grade b or at least grade c. Chloride condition evaluation standard apply to evaluation of marine structure chloride attack with chloride attack by deicing salts.

• Geomechanics and Engineering
• /
• v.18 no.2
• /
• pp.189-203
• /
• 2019

Brine leakage is a common phenomenon during construction facilitated by artificial freezing technique, threatening the stability of frozen wall due to the continual thawing of already frozen domain. This paper takes the frequently encountered soft clay in Wujiang District as the study object, and remolded specimens were prepared by mixing calcium chloride solutions at five levels of concentration. Both the deformation and pore water pressure of frozen specimens during thawing were investigated by two-stage loading tests. Three sections were noted from the changes in the strain rate of specimens during thawing at the first-stage load, i.e., instantaneous, attenuated, and quasi-stable sections. During the second-stage loading, the deformation of post-thawed soils is closely correlated with the dissipation of pore water pressure. Two characteristic indexes were obtained including thaw-settlement coefficient and critical water content. The critical water content increases positively with salt content. The higher water content of soil leads to a larger thaw-settlement coefficient, especially at higher salt contents, based on which an empirical equation was proposed and verified. The normalized pore water pressure during thawing was found to dissipate slower at higher salt contents, with a longer duration to stabilize. Three physical indexes were experimentally determined such as freezing point, heat conductivity and water permeability. The freezing point decreases at higher salt contents, especially as more water is involved, like the changes in heat conductivity. The water permeability maintains within the same order at the considered range of salt contents, like the development of the coefficient of consolidation. The variation of the pore volume distribution also accounts for this.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.375-381
• /
• 2017

Recently, due to the increasing of interest about the eco-friendly concrete, it is being increased to use concretes containing by-products of industry such as fly ash, ground granulated blast furnace slag, silica fume, and etc. Especially, these are well known for improving the resistance to reinforcement corrosion in concrete and decreasing chloride ion penetration. The purpose of this experimental research is to evaluate the resistance to corrosion of reinforcement and critical chloride content of high volume fly ash concrete(HVFAC) which is replaced with fly ash for approximately 50% cement content. For this purpose, corrosion monitoring of reinforcement by half cell potential method was carried out for the cylindrical test specimens that the upper of reinforcement in concrete was exposed to detect the time of corrosion initiation for reinforcement. It was observed from the test result that the the time of corrosion initiation for reinforcement of HVFAC by the accelerated corrosion tests increased 1.2~1.3 times than plain concrete and the critical chloride contents of plain concrete and HVFAC were found to range $0.80{\sim}1.20kg/m^3$, $0.89{\sim}1.60kg/m^3$, respectively.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.5
• /
• pp.30-36
• /
• 2019

In order to evaluate service life of RC (Reinforced Concrete) structures exposed to chloride attack, chloride penetration analysis is required referred to the chloride diffusion coefficient from the actual mix proportions. In this work, accelerated diffusion coefficients are obtained from NT BUILD 492 and ASTM C 1202 and the related apparent diffusion coefficients are derived via the previously proposed relationship for RC structures near to sea shore. Considering the properties of the mix proportions and the most conservative analysis conditions like critical and surface chloride contents, service lifes in column and exterior wall member are evaluated through conventional program LIFE 365 ver.2. The different built-up period of 10 and 15 years has no significant effect on service life. The results from mix proportions with slag show longer than 75 years of service life with the help of higher time dependent parameter and lower initial diffusion coefficient.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.409-412
• /
• 2008

This study were evaluated the corrosion threshold reached at steel reinforcement in latex modified concrete(LMC). Accelerated testing was accomplished to the evalate the diffusion coefficient of LMC mix, and the time dependent constants of diffusion. Also, average chloride diffusion coefficient was estimated. From the average chloride ion diffusion coefficient, the time which critical chloride contents at depth of reinforcement steel was estimated. Test results indicated that the corrosion threshold reached at reinforcement in LMC are effected on the mix proportion factor including latex content, and water-cement ratio.