• Proceedings of the Korean Nuclear Society Conference
• /
• 2002.10a
• /
• pp.282.1-282
• /
• 2002

• Journal of the Korean Society for Heat Treatment
• /
• v.11 no.1
• /
• pp.54-61
• /
• 1998

Since Cr-Mo-V steel has excellent fracture and creep properties at elevated temperature, they are extensively used as steam turbine components such as the turbine rotor. However, the turbine rotor steel used to suffer material degradation during long term service. Therefore, the assessment of the safety and residual life of the turbine rotor is periodically required during service. One of the most convenient techniques for that is the hardness method mainly due to its simplicity and nondestructive characteristics. In this research, six specimens with different aging times of turbine rotor steel were artificially prepared by an isothermal heat treatment at $630^{\circ}C$. The micro Vickers hardnesses of specimens were measured at room temperature. The relationships between the fracture properties and the hardness ratio were investigated. And also an indirect method to evaluate the residual life of degraded turbine rotor was proposed based on the micro Vickers hardness measurement.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.445-450
• /
• 2000

The integrity of the turbine rotors can be assessed by measuring reversible permeability and Vickers hardness of the aged rotors at service temperature. The measurement system of reversible permeability, which measured by applied alternating perturbing magnetic field, was constructed in order to evaluate material degradation, nondestructively. The test specimen was 1Cr-1Mo-0.25V steel used widely for turbine rotor material, and the specimens were prepared by the isothermal heat treatment at $630\;^{\circ}C$. The reversible permeability of the test materials were measured at room temperature. The peak interval of reversible permeability and Vickers hardness decreased with the increase of degradation. The degradation of test material may be determined nondestructively by the lineality of Vickers hardness and the peak interval of reversible permeability.

• Journal of the Korean Society for Heat Treatment
• /
• v.35 no.3
• /
• pp.121-129
• /
• 2022

Recently the growth of the renewable energy production has caused the flexible operation in LNG combined cycle power plant. Due to the rapid start and stop operations, large CrMoV castings used for turbine casings and valve bodies could be distorted and lead to replacement or welding repair. This study was performed to find out the characteristics of the repair welding for a damaged CrMoV casting steel. A typical field repair method (arc & TIG welding) was applied to making specimens. The degraded N2 packing head sample from the steam turbine was used. The evaluations of weldments were carried out in terms of microstructural characterization, microhardness measurements, tensile, creep-rupture and fatigue tests. Color etching was also applied for better understanding of welding microstructures. As the boundary between HAZ and base material was deteriorated by welding, it caused microstructural changes formed during PWHT and the shortening of the remaining residual life. By comparing the properties according to repair welding method, it was possible to derive what important welding factors were. As a result, arc welding method is more suitable for repair welding on CrMoV castings.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.231-236
• /
• 2001

A newly developed Advanced Indentation System (AIS), which is a portable and nondestructive system for evaluating tensile properties, was used to measure mechanical behavior of materials used under high temperature and pressure conditions. This test measures indentation load-depth curve during indentation and analyzes the mechanical properties related to deformation and fracture. Aging effects of Cr-Mo and Cr-Mo-V steel at high temperature were simulated. Tensile properties including yield strength and tensile strength at various temperature are obtained from the test. For all test materials and conditions, the AIS-derived results were in good agreement with those from conventional standard test method. Examples of the test results ate given and potential applications of the AIS to assess the integrity of aging structures are briefly discussed.

• Korean Journal of Materials Research
• /
• v.17 no.8
• /
• pp.425-432
• /
• 2007

The microstructural evolution of ferritic 9Cr-1Mo-V-Nb steel, subjected to creep-fatigue at $550^{\circ}C$, was evaluated nondestructively by measuring the ultrasonic velocity. The variation of the ultrasonic velocity with the fatigue life fraction exhibited three regions. In the first region ($N/N_f$<0.2), a significant increase in the velocity was observed, followed by a slight increase between the fatigue life fractions of $0.2N_f$ and $0.8N_f$, and then a decrease in the final region. The change of the ultrasonic velocity during creep-fatigue was interpreted in relation to the microstructural properties. This study proposes an ultrasonic nondestructive evaluation method of quantifying the level of damage and microstructural change during the creep-fatigue of ferritic 9Cr-1Mo-V-Nb steel.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.12
• /
• pp.2116-2124
• /
• 2001

It's required mechanical properties of in-service facilities to maintain safety operation in power plants as well as chemical plants. In this studdy the four classes of the thermally aged 1Cr-lMo-0.25V specimens were prepared using an artificially accelerated aging method at 630$\^{C}$. Ultrasonic tests, tensile tests, K$\_$IC/ tests and hardness tests were performed in order to evaluate the degree of degradation of the material. The mechanical properties were decreased as degraded, but the attenuation coefficient and the harmonic generation level of a ultrasonic signal were increased. Expecially the nonlinear parameter derived from the harmonic generation level is sensitive and will be a good parameter to evaluate the material degradation.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.27 no.5
• /
• pp.417-425
• /
• 2007

The ferritic 9Cr-1Mo-V-Nb heat-resisting steel was experimentally studied in order to characterize its microstructural evolution during creep-fatigue by coercivity measurement. The creep-fatigue test was conducted at $550\;^{\circ}C$ with the tensile holding time of 60s and 600s, respectively. The coercivity decreased until the failure and the hardness monotonously decreased for the whole fatigue life. As the life fraction of creep-fatigue increased, the $M_{23}C_6$ carbide coarsened following the Ostwald ripening mechanism. However, the MX carbonitrides did not grow during creep-fatigue due to so stable at $550\;^{\circ}C$. The width of martensite lath increased because of the dislocation recovery at the lath boundaries. The magnetic coercivity has an influence on the microstructural properties such as dislocation, precipitates and martensite lath boundaries, which interpreted in relation to microstructural changes. Consequently, this study proposes a magnetic coercivity to quantify the level of damage and microstructural change during the creep-fatigue of ferritic 9Cr-1Mo-V-Nb steel.

• Journal of Korea Foundry Society
• /
• v.33 no.1
• /
• pp.1-7
• /
• 2013

The effect of the Mo addition on the high temperature creep properties of the 9Cr-3W steel was also evaluated. Two experimental steels, (9Cr-3W and 9Cr-3W-0.5Mo), were prepared using a vacuum induction melting process, followed by hot rolling and heat treatment processes. Three types of precipitates, ($M_{23}C_6$, Nb-rich MX and V-rich MX) were observed in a typical tempered martensitic matrix. Significant effects of the Mo addition on the tensile properties were not observed. However, the creep properties at $650^{\circ}C$ under applied stresses of 140 and 150 MPa were considerably enhanced by the Mo addition. The microstructural observation after the creep test indicated that the addition of Mo could function to retain the recovery of the martensitic matrix, thus resulting in the enhanced creep properties of the 9Cr-3W-0.5Mo steel. Furthermore coarsening of the $M_{23}C_6$ carbides and formation of Laves phases were observed in both samples after the creep tests.

• Journal of Welding and Joining
• /
• v.13 no.1
• /
• pp.89-102
• /
• 1995

The evaluation of reheat cracking susceptibility in CrMoV turbine rotor steel was performed using thermally simulated heat affected zones. The examinations were carried out in terms of microstructural characterization, microhardness measurement and a Charpy type notch opening three point bend test. It was found that reheat cracking susceptibility increased as the peak temperature increased. This effect was due to the combined effects of the carbide dissolution and unrestricted grain growth at 1350.deg. C peak temperature. Reheat cracking susceptibility was estimated based on microhardness measurement and prior austenite grain size. It was established that for this particular material, reheat cracking in coarse grained heat affected zone can be eliminated if the microhardness is below about 360DPH and the grain size is below about 30.mu.m. It is evident that reheat cracking susceptibility can be eliminated or reduced by carefully controlling the welding parameters such that a refined structure is produced in the coarse grained heat affected zone.