• 한국재료학회지
• /
• 제32권11호
• /
• pp.466-473
• /
• 2022

The effect of Cr and Mo contents on the hydrogen embrittlement of tempered martensitic steels was investigated in this study. After the steels with different Cr and Mo contents were austenitized at 820 ℃ for 90 min, they were tempered at 630 ℃ for 120 min. The steels were composed of fully tempered martensite with a lath-type microstructure, but the characteristics of the carbides were dependent on the Cr and Mo contents. As the Cr and Mo contents increased, the volume fraction of film-like cementite and prior austenite grain size decreased. After hydrogen was introduced into tensile specimens by electrochemical charging, a slow strain-rate test (SSRT) was conducted to investigate hydrogen embrittlement behavior. The SSRT results revealed that the steel with lower Cr or lower Mo content showed relatively poor hydrogen embrittlement resistance. The hydrogen embrittlement resistance of the tempered martensitic steels increased with increasing Mo content, because the reduction in the film-like cementite and prior austenite grain size plays an important role in improving hydrogen embrittlement resistance. The results indicate that controlling the Cr and Mo contents is essential to achieving a tempered martensitic steel with a combination of high strength and excellent hydrogen embrittlement resistance.

• 열처리공학회지
• /
• 제25권4호
• /
• pp.196-205
• /
• 2012

The purpose of this study is to enhance the hardenability and the mechanical properties by the addition of alloying elements such as Ni, Cr, Mo and B for the development of Cr-Mo plastic mold steel with uniform hardness and microstructure. The ingots were prepared by vacuum induction melting and forged to ${\Phi}35mm$ round bar. Forged bars were quenched and tempered at $200{\sim}600^{\circ}C$ for 1.5 hour. Jominy test, boron distribution observation, microstructual observation, tensile test and charpy impact test were conducted. It was confirmed that the hardenablity of these steels was improved by increasing of alloying elements and further promoted by the addition of boron. The critical rate of cooling required to obtain the bainitic structure for 0.27C-1.23Cr-0.28Mo-B steel was $0.5^{\circ}C/sec$. Hardness and strength of Cr-Mo steels decreased with increasing tempering temperature, but elongation and reduction of area increased with increasing tempering temperature. However, impact energy tempered at $400^{\circ}C$ showed the lowest value in the range $200{\sim}600^{\circ}C$ due to the temper embrittlement.

• 한국해양공학회지
• /
• 제1권2호
• /
• pp.101-112
• /
• 1987

Fracture toughness characterization in the transition region is examined for heat-treated and ionnitrided Ni-Cr-Mo steel. After heat treatment for the specimens of Ni-Cr-Mo steel, organizations of specimens-specimens which are heat-treated and ion-nitrided for 4 hours at 500 .deg. C and 5 torr in 25%N/dub 2/-75%H/sub 2/mixed gas-, hardness variety, and X-ray diffraction pattern of the ion-nitriding compound layer are observed. Fracture toughenss test of unloading compliance method were conducted over the regions from room trmperature to -70.deg. C. The compound layer was consisted of r'=Fe/sub 4/N phase and ion-nitrided layer's depth was 200mm from surface. The transition regions of heat-treated and ion-nitrided specimens were about -30.deg. C and -50.deg. C, respectively. The transition region of ion-nitrided specimens is estimated less than that of heat-treated one, and this is the effect of ion-nitriding.

• 대한기계학회논문집A
• /
• 제26권1호
• /
• pp.55-60
• /
• 2002

For the development of a new creep test technique, the availability of SP-Creep test is discussed for 1Cr-0.5Mo boiler header material. And some results are also compared with those of 2.25Cr- 1Mo steel which widely uses as boiler superheater tube. The results can be summarized as follows. The load exponents(n) obtained by SP-Creep test for 1Cr-0.5Mo steel are decreased with increasing creep temperature and the values are 15.67, 13.89, and 17.13 at 550$^{circ}C$ ,575$^{circ}C$ and 600$^{circ}C$, respectively. The temperature dependence of the load exponent is given by n = 107.19 - 0.1108T. This reason that load exponents show the extensive range of 10∼16 is attributed to the fine carbide such as M$_{23}$C$_{6}$ in lath tempered martensitic structures. At the same creep condition, the secondary creep rate of 1Cr-0.5Mo steel is lower than the 2.25Cr-1Mo steel1 due to the strengthening microstructure composed by normalizing and tempering treatments. Through a SEM observation, it can be summarized that the primary, secondary, and tertiary creep regions of SP-Creep specimen are corresponding to plastic bending, plastic membrane stretching, and plastic instability regions among the deformation behavior of four steps in SP test, respectively.y.

• 대한금속재료학회지
• /
• 제49권2호
• /
• pp.153-160
• /
• 2011

The AISI 216L stainless steel with a composition of Fe-16Cr-6Ni-6Mn-1.7Mo (wt.%) was oxidized at $700{\sim}900^{\circ}C$ in air for 100 h. At $700^{\circ}C$, a thin $Mn_{1.5}Cr_{1.5}O_4$ oxide layer with a thickness of $0.4{\mu}m$ formed. At $800^{\circ}C$, an outer thin $Fe_2O_3$ oxide layer and a thick inner $FeCr_2O_4$ oxide layer with a total thickness of $30{\mu}m$ formed. The non-adherent scale formed at $800^{\circ}C$ was susceptible to cracking. At $900^{\circ}C$, an outer thin $Fe_2O_3$ oxide layer and a thick inner $Mn_{1.5}Cr_{1.5}O_4$ oxide layer formed, whose total thickness was $10{\sim}15{\mu}m$. The scales formed at $900^{\circ}C$ were non-adherent and susceptible to cracking. 216 L stainless steel oxidized faster than 316 L stainless steel, owing to the increment of the Mn content and the decrement of Ni content.

• 비파괴검사학회지
• /
• 제22권3호
• /
• pp.284-291
• /
• 2002

전기비저항법을 이용하여 2.25Cr-1Mo 강의 경년열화도를 평가하고자 하였다. 2.25Cr-1Mo 강이 $540^{\circ}C$에서 장시간 노출되었을 때 일어나는 미세조직 변화를 모사하기 위해 인공 열화를 실시하였으며 열화에 따른 미세조직 인자 (고용원소의 함량), 기계적 성질 (연성-취성 천이온도 ), 전기비저항을 측정하여 이들간의 상호관계를 구하고자 하였다. 열화재에서는 기지내의 고용 원소 (Mo 와 Cr)의 고갈이 나타났다. 연성-취성 천이온도는 열화 초반부에 급격히 증가 후 포화되는 경향을 보인 반면 전기비저항은 열화 초반부에 급격히 감소 후 포화되는 경향을 보였다. 즉, 열화 시간에 따른 연성-취성 천이온도의 변화 경향과 전기비저항의 변화는 서로 반대적으로 변화하는 관계를 나타내었다.

• 한국재료학회지
• /
• 제21권11호
• /
• pp.592-595
• /
• 2011

It is well known that modified 9Cr-1Mo steel has a low thermal expansion and high thermal conductivity with excellent high temperature properties compared to austenitic stainless steel. For these advantages, the steel is very popular for the boiler tube of thermal power plants. Normalizing is commonly utilized to obtain martensite in this steel, which shows an unusual toughness for martensite. However, some accidents related to this steel have been reported recently, opening the necessity for further study. As a particular behavior of the steel, an abrupt drop of the impact value has been identified upon tempering at 750$^{\circ}C$ for about 1 hour. It is well known that $Fe_3C$ forms during autotempering and turns to $Cr_2C$ at an early stage and then transforms to $Cr_{23}C_6$. In this study, the cause of the abrupt drop of the impact value was investigated with an impact test, microstructural observation, nanodiffraction and phase analyses using instruments such as optical and transmission electron microscopes (TEM) with an extraction carbon replica of the carbides. The analyses revealed that the $M_2C$ that formed when retained for about 1 hour at 750$^{\circ}C$ causes a drastic decrease in the mechanical properties. The sharp drop in mechanical properties, however, disappeared as the $M_2C$ transformed into $M_{23}C_6$ with longer retention.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1997년도 특별강연 및 춘계학술발표 개요집
• /
• pp.65-68
• /
• 1997

Fracture behavior of ex-serviced 1Cr-0.5Mo steel was measured at room(24$^{\circ}C$) and elevated(538$^{\circ}C$) temperature and compared with that measured with virgin 1Cr-0.5Mo steel. Compact C(T) specimens were machined from the base and welded test materials. In case of the C(T) specimens of the weld, fatigue precrack was introduced along the fusion line so that a crack growth should occur along the region of heat affected zone. It was observed that the J-R curve of the serviced material was significantly lower than that of the virgin material at room temperature. Brittle fracture was observed in the serviced material. On the other hand at elevated temperature no noticeable difference was found between the J-R curves of the virgin and the serviced material. The measured J-R curves were also compared with those of the 1.25Cr-0.5Mo steel from other literatures. Optical microscopy and SEM examination of the serviced material reveal the carbide in/along the grain boundary which shows material degradation due to long-term usage.

• 한국안전학회지
• /
• 제12권2호
• /
• pp.45-56
• /
• 1997

Fracture behavior of ex-serviced 1Cr-0.5Mo steel was measured at room($24^{\circ}C$) and elevated($538^{\circ}C$) temperature and compared with that measured with virgin 1Cr-0.5Mo steel. Compact C(T) specimens were machined from the base and welded test materials. In case of the C(T) specimens of the weld, fatigue precrack was introduced along the fusion line so that following crack growth should occurs along the region of heat affected zone. It was observed that the J-R curve of the serviced material was significantly lower than that of the virgin material at room temperature. Brittle fracture was observed in the serviced material. On the other hand, at elevated temperature no noticeable difference was found between the J-R curves of the virgin and the serviced material. The measured J-R curves were also compared with those of the 1.25Cr-0.5Mo steel obtained from the other literatures. Optical microscopy and SEM examination of the serviced material reveal the carbide in/along the grain boundary which shows material degradation due to long-term usage. An example of application of the measured J-R curves is shown.

• Corrosion Science and Technology
• /
• 제19권1호
• /
• pp.43-50
• /
• 2020

In this study, the effects of KCl(s) and K₂SO₄(s) on the oxidation characteristics of 2.25Cr-1Mo steel were investigated for 500 h in 10O₂ + 10CO₂ (vol%) gas environmen at 650 ℃. Oxidation kinetics were characterized by weight gain, oxide layer thickness, and fitted models for the experiment data were proposed. The fitted models presented considerable agreement with the experimental data. The oxide layer was analyzed using the scanning electron microscope, optical microscope, and energy dispersive X-ray spectroscopy. The oxidation kinetics of 2.25Cr-1Mo steel with KCl and K₂SO₄ coatings showed significantly different oxidation kinetics. KCl accelerated the oxidation rate very much and had linear oxidation behavior. In contrast, K₂SO₄ had no significant effect, which had parabolic kinetics. The oxide layer was commonly composed of Fe₂O₃, Fe₃O₄, and FeCr₂O₄ spinel. KCl strongly accelerated the oxidation rates of 2.25Cr-1Mo steel in the high-temperature oxidation environment. Conversely, K₂SO₄ had little effect on the oxidation rates.