• Journal of Ceramic Processing Research
• /
• 제19권6호
• /
• pp.455-460
• /
• 2018

Chromium plating is a common surface treatment technique extensively applied in industry due its excellent properties which include substantial hardness, abrasion resistance, corrosion resistance, surface color, and luster. In this study, the effect of PTFE on corrosion behavior of Cr-P plating, low carbon steel substrates are electroplated in Cr(III) baths without and with PTFE. Trivalent chromium carbon plating was electroplated from trivalent chromium sulfate-based baths with different PTFE dispersion contents. The study focused on the microstructure, PTFE content, roughness, and corrosion resistance of the Cr-P-PTFE composite plating. Scanning electron microscopy and atomic force microscopy images showed a smoother plating and a decrease in the surface roughness of the electrodeposited. The results demonstrate that PTFE eliminates the cracks within plating by reducing internal stress. Therefore, the corrosion resistance of Cr-P-PTFE composite platings were better than that of Cr-P alloy platings.

• Tribology and Lubricants
• /
• 제19권4호
• /
• pp.211-216
• /
• 2003

This paper was studied on the corrosion and corrosion-wear behavior of chromium (Cr) plating in the acidic environments. In the various pH of acidic solutions, the electrochemical polarization test and wear-corrosion test of Cr plating were carried out. And thus potential, corrosion current density and corrosion-wear loss behaviour of Cr plating are investigated.

• 수산해양기술연구
• /
• 제39권3호
• /
• pp.211-217
• /
• 2003

해양환경의 비저항 변화에 따른 모재, Ni도금 및 Cr도금의 분극저항, 부식전류밀도, 부식억제율 및 분극지배기구에 관하여 연구한 결과 다음과 같은 결론을 얻었다. 1) Cr도금 및 Ni도금의 분극저항은 모재의 분극저항보다 더 높게 나타나고, 이들 재료의 분극저항은 비저항이 감소함에 따라 낮아진다. 2) 비저항이 낮아질수록 Cr도금 및 Ni도금의 부식전류밀도는 모재의 부식전류보다 더 억제됨에 따라 Ni 및 Cr도금의 부식억제율은 더 높게 된다. 3) 해양환경의 비정항에 따른 모재, Ni도금 및 Cr 도금의 부식반응은 음극지배로 판단된다.(이 논문의 결론부분임)

• Journal of Welding and Joining
• /
• 제14권3호
• /
• pp.66-74
• /
• 1996

In this study, friction and wear properties of flame sprayed specimens and hard Cr plating specimens were tested, and their properties were compared each other in dry and lubrication condition. Ni-Cr powder and steel powder were used as the spray powder and sprayed on the steel(S45C) substrate by flame sprayed method. Each wear surface was observed with SEM after friction and wear test. The friction coefficient of the as-forged steel specimens was the highest among surface treatment specimens, and the other specimens appeared in order as follows ; hard Cr-plating specimens, Ni-Cr powder sprayed specimens, steel powder sprayed specimens. Comparing the wear volumes in dry condition, as forged steel specimens appeared the greatest wear volume, and the other specimens appeared wear volume in order as follows ; Ni-Cr powder sprayed specimens, steel powder sprayed specimens, hard Cr plating specimens. In friction and wear test, the hard Cr plating specimens were worn by the abrasive phenomenon, involving the cracks. The wear volume of steel powder sprayed specimens was lower than that of Ni-Cr powder sprayed specimens. Comparing the tensile strength of both sprayed coating layers, the steel powder sprayed coating layer was better than Ni-Cr powder sprayed coating layer.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2009년도 제33회 추계학술대회논문집
• /
• pp.603-607
• /
• 2009

액체로켓엔진 연소기의 내벽에 사용하기 위한 니켈/크롬 도금 공정 개발을 수행하였다. 열충격 시험을 통해 니켈 도금 조건을 선별하였고 니켈/크롬 도금이 수행된 축소형 연소기의 연소시험을 통해 도금 층의 내구성 검증을 수행하였다. 시험결과 도금 층의 균열 및 박리는 발견되지 않았고, 이 결과로부터 현재 사용중인 대기 플라즈마 용사된 세라믹 코팅의 대안으로 니켈/크롬 도금을 액체로켓엔진 연소기에 사용할 수 있으리라 사료된다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.722-727
• /
• 2004

This paper includes the comparative study between Cr plating and nitriding process with an aim at improving corrosion, wear and maintainability for KNR(Korean Next Generation Rifle) 5.56mm barrel. The endurance test was conducted to compare the performance of standard barrel, Cr plating barrel and nitriding barrel. Main activities are described as follows; optimal Cr plating and nitriding process set-up for KNR 5.56mm barrel; durability test of each barrel(20,000 rounds); salt water immersion test; dispersion, initial velocity, inner diameter data acquisition. According to the results of this firing test, Cr plating barrel is superior to standard barrel and nitriding barrel in view of corrosion, wear and maintainability

• 한국군사과학기술학회지
• /
• 제7권1호
• /
• pp.5-12
• /
• 2004

This paper includes the comparative study between Cr plating and nitriding process with an aim at improving corrosion, wear and maintainability for KNR(Korean Next Generation Rifle) 5.5mm barrel. The endurance test was conducted to compare the performance of standard barrel, Cr plating barrel and nitriding barrel. Main activities are described as follows; optimal Cr plating and nitriding process set-up for KNR 5.56mm barrel; durability test of each barrel(20,000 rounds); salt water immersion test; dispersion, initial velocity, inner diameter data acquisition. According to the results of this firing test, Cr plating barrel is superior to standard barrel and nitriding barrel in view of corrosion, wear and maintainability.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2009년도 춘계학술대회 논문집
• /
• pp.192-193
• /
• 2009

CrN 코팅막은 고온에서 치밀한 Cr2O3 확산방지막을 형성함으로 $800^{\circ}C$까지 기계적성질을 유지할 수 있다. 본 실험에서는 Ar, N2, 그리고 $O_2$ 가스 분위기에서 AIP(Arc Ion Plating) 기법에 의해 다양한 조성의 Cr-O-N 박막을 Si(200)과 AISI 304 기판 위에 증착되었다. Cr-O-N 코팅막은 47.4at% 미만의 산소함량을 포함 할 때까지 B1구조를 유지하였고 코팅막 내 산소함량 24.6at%에서는 강한 XRD peak intensification을 나타내었다. 47.4at%에서는 결정상을 전혀 찾아볼 수 없는 전이구조를 나타내었고, 그 이상의 산소함량에서는 Cr22O3 결정상을 나타내었다. Cr-O(17at%)-N 조성의 코팅막에서는 (200)배향의 Grain 크기 증가 및 압축잔류응력이 증가하였으나, 그 이상의 산소함량에서는 점차 감소하였다. Cr-O(24.6at%)-N 조성의 코팅막이 가장 높은 경도를 나타내었고, 산소함량이 증가할수록 점차 향상된 마찰특성을 보였다.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2017년도 제48회 춘계학술대회논문집
• /
• pp.857-863
• /
• 2017

본 논문은 다단연소사이클 엔진의 연소실 내벽을 고온, 고압의 환경으로부터 보호하기 위한 열차폐 코팅 공정 개발에 관한 내용이다. 기존 연소기 내벽에는 열차폐 특성이 우수한 Zr 기반의 세라믹용사코팅을 적용했지만, 세라믹의 특성상 연소실 내벽(금속)과 열팽창계수 차이로 인해 박리가 발생할 수 있다. 때문에 로켓 선진국에서는 열차폐 효과를 다소 희생 하더라도 밀착력 향상을 위하여 금속계 코팅인 Ni-Cr 도금을 적용하고 있다. 본 연구에서는 연소기에 적용 가능한 상향 순환식 유동셀을 적용한 도금조를 개발했으며, 반복적인 공정 개선을 통해 도금 두께 $100{\mu}m$이상, ${\pm}10%$의 두께 균일도를 만족하는 Ni, Cr 도금 공정조건을 확립했다.

• 한국표면공학회지
• /
• 제24권1호
• /
• pp.24-24
• /
• 1991

Cr-N films were deposited on low-carbon steel sheets by the reactive arc-induced ion plating (AIIP). The influence of the deposition conditions (nitrogen pressure and substrate bias voltage) on the crystal orientation, morphology and microhardness of the Cr-N films has been investigated using x-ray diffractometer and scanning electron microscope. The impurities and contaminations on the surface and at the interface, and the layer-by-layer compositions of the film have been analyzed using scanning Auger multiprobe (SAM) and glow discharge spectroscope (GDS). The mixed state of Cr and Cr2N turned out to have a fine fibrous structure. The Cr2N films were deposited at a wide range of nitrogen flow rates. The orientations of Cr2N films were mainly (110) and (111), and the intensity of the (111) peak increased as the substrate bias voltage increased. The micorstructure of the Cr2N film was dense and no columnar structure was observed. The films in the mixed state of Cr2N and CrN were also dense without columnar structure. The maximum microhardness of the Cr-N films was 2400 kg/$\textrm{mm}^2$ at 10gf load.