• Journal of Ceramic Processing Research
• /
• v.19 no.6
• /
• pp.455-460
• /
• 2018

Chromium plating is a common surface treatment technique extensively applied in industry due its excellent properties which include substantial hardness, abrasion resistance, corrosion resistance, surface color, and luster. In this study, the effect of PTFE on corrosion behavior of Cr-P plating, low carbon steel substrates are electroplated in Cr(III) baths without and with PTFE. Trivalent chromium carbon plating was electroplated from trivalent chromium sulfate-based baths with different PTFE dispersion contents. The study focused on the microstructure, PTFE content, roughness, and corrosion resistance of the Cr-P-PTFE composite plating. Scanning electron microscopy and atomic force microscopy images showed a smoother plating and a decrease in the surface roughness of the electrodeposited. The results demonstrate that PTFE eliminates the cracks within plating by reducing internal stress. Therefore, the corrosion resistance of Cr-P-PTFE composite platings were better than that of Cr-P alloy platings.

• Tribology and Lubricants
• /
• v.19 no.4
• /
• pp.211-216
• /
• 2003

This paper was studied on the corrosion and corrosion-wear behavior of chromium (Cr) plating in the acidic environments. In the various pH of acidic solutions, the electrochemical polarization test and wear-corrosion test of Cr plating were carried out. And thus potential, corrosion current density and corrosion-wear loss behaviour of Cr plating are investigated.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.39 no.3
• /
• pp.211-217
• /
• 2003

Recently, with rapid development in marine and shipbuilding industries such as marine structures, ships and chemical plants for ship, there occurs much interest in the study on corrosion characteristics played an important role in mechanical design. This paper was studies on the corrosion characteristics of chromium plating in the marine environment. Under the various specific resistance, the electrochemical polarization test of chromium plating was carried out. And thus corrosion potential, polarization resistance, corrosion current density, control efficiency of corrosion and polarization control behavior of chromium plating are investigated. The main results are as the followed : 1. The polarization resistance of Cr plating and Ni become higher than that of base metal, also and these material become low with decrease of the specific resistance. 2. As the specific resistance decreases, the corrosion current density of Cr and Ni plating is lower than that of base metal. 3. The corrosion reaction of Cr plating, Ni plating and base metal vs. specific resistance is cathodic control.

• Journal of Welding and Joining
• /
• v.14 no.3
• /
• pp.66-74
• /
• 1996

In this study, friction and wear properties of flame sprayed specimens and hard Cr plating specimens were tested, and their properties were compared each other in dry and lubrication condition. Ni-Cr powder and steel powder were used as the spray powder and sprayed on the steel(S45C) substrate by flame sprayed method. Each wear surface was observed with SEM after friction and wear test. The friction coefficient of the as-forged steel specimens was the highest among surface treatment specimens, and the other specimens appeared in order as follows ; hard Cr-plating specimens, Ni-Cr powder sprayed specimens, steel powder sprayed specimens. Comparing the wear volumes in dry condition, as forged steel specimens appeared the greatest wear volume, and the other specimens appeared wear volume in order as follows ; Ni-Cr powder sprayed specimens, steel powder sprayed specimens, hard Cr plating specimens. In friction and wear test, the hard Cr plating specimens were worn by the abrasive phenomenon, involving the cracks. The wear volume of steel powder sprayed specimens was lower than that of Ni-Cr powder sprayed specimens. Comparing the tensile strength of both sprayed coating layers, the steel powder sprayed coating layer was better than Ni-Cr powder sprayed coating layer.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2009.11a
• /
• pp.603-607
• /
• 2009

A Ni/Cr plating process has been developed for applying to inner wall of liquid rocket engine(LRE) thrust chamber. Ni plating conditions were selected through thermal shock test and endurance verification of the plating layers was performed through hot firing test of a subscale thrust chamber with Ni/Cr plating. Test results showed that a crack or separation of the plating layers was not found. Judging from the results, Ni/Cr plating could be applied to LRE thrust chamber as a substitute of air plasma sprayed ceramic coating which is presently being used.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.722-727
• /
• 2004

This paper includes the comparative study between Cr plating and nitriding process with an aim at improving corrosion, wear and maintainability for KNR(Korean Next Generation Rifle) 5.56mm barrel. The endurance test was conducted to compare the performance of standard barrel, Cr plating barrel and nitriding barrel. Main activities are described as follows; optimal Cr plating and nitriding process set-up for KNR 5.56mm barrel; durability test of each barrel(20,000 rounds); salt water immersion test; dispersion, initial velocity, inner diameter data acquisition. According to the results of this firing test, Cr plating barrel is superior to standard barrel and nitriding barrel in view of corrosion, wear and maintainability

• Journal of the Korea Institute of Military Science and Technology
• /
• v.7 no.1
• /
• pp.5-12
• /
• 2004

This paper includes the comparative study between Cr plating and nitriding process with an aim at improving corrosion, wear and maintainability for KNR(Korean Next Generation Rifle) 5.5mm barrel. The endurance test was conducted to compare the performance of standard barrel, Cr plating barrel and nitriding barrel. Main activities are described as follows; optimal Cr plating and nitriding process set-up for KNR 5.56mm barrel; durability test of each barrel(20,000 rounds); salt water immersion test; dispersion, initial velocity, inner diameter data acquisition. According to the results of this firing test, Cr plating barrel is superior to standard barrel and nitriding barrel in view of corrosion, wear and maintainability.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.192-193
• /
• 2009

CrN 코팅막은 고온에서 치밀한 Cr2O3 확산방지막을 형성함으로 $800^{\circ}C$까지 기계적성질을 유지할 수 있다. 본 실험에서는 Ar, N2, 그리고 $O_2$ 가스 분위기에서 AIP(Arc Ion Plating) 기법에 의해 다양한 조성의 Cr-O-N 박막을 Si(200)과 AISI 304 기판 위에 증착되었다. Cr-O-N 코팅막은 47.4at% 미만의 산소함량을 포함 할 때까지 B1구조를 유지하였고 코팅막 내 산소함량 24.6at%에서는 강한 XRD peak intensification을 나타내었다. 47.4at%에서는 결정상을 전혀 찾아볼 수 없는 전이구조를 나타내었고, 그 이상의 산소함량에서는 Cr22O3 결정상을 나타내었다. Cr-O(17at%)-N 조성의 코팅막에서는 (200)배향의 Grain 크기 증가 및 압축잔류응력이 증가하였으나, 그 이상의 산소함량에서는 점차 감소하였다. Cr-O(24.6at%)-N 조성의 코팅막이 가장 높은 경도를 나타내었고, 산소함량이 증가할수록 점차 향상된 마찰특성을 보였다.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2017.05a
• /
• pp.857-863
• /
• 2017

In this paper, the process of electro Ni and electro Cr plating is studied for the purpose of thermal barrier to protect the inner wall combustion chamber. The chamber is under the environment of very high temperature and high pressure when propellants burn in there. As one of the thermal barrier coatings, Zr-based thermal spray coating has been applied to the chamber. However, peeling of coating layer can occur under such a hard condition because of the difference of thermal expansion coefficients between the ceramic and the metallic wall. We study the characteristics of Ni-Cr coating and establish its process. It is found that the thickness of over $100{\mu}m$ of Ni and Cr coating layers with the uniformity of ${\pm}10%$ can be obtained with the used of as-developed plating bath.

• Journal of the Korean institute of surface engineering
• /
• v.24 no.1
• /
• pp.24-24
• /
• 1991

Cr-N films were deposited on low-carbon steel sheets by the reactive arc-induced ion plating (AIIP). The influence of the deposition conditions (nitrogen pressure and substrate bias voltage) on the crystal orientation, morphology and microhardness of the Cr-N films has been investigated using x-ray diffractometer and scanning electron microscope. The impurities and contaminations on the surface and at the interface, and the layer-by-layer compositions of the film have been analyzed using scanning Auger multiprobe (SAM) and glow discharge spectroscope (GDS). The mixed state of Cr and Cr2N turned out to have a fine fibrous structure. The Cr2N films were deposited at a wide range of nitrogen flow rates. The orientations of Cr2N films were mainly (110) and (111), and the intensity of the (111) peak increased as the substrate bias voltage increased. The micorstructure of the Cr2N film was dense and no columnar structure was observed. The films in the mixed state of Cr2N and CrN were also dense without columnar structure. The maximum microhardness of the Cr-N films was 2400 kg/$\textrm{mm}^2$ at 10gf load.