• Journal of the Korea Concrete Institute
• /
• v.17 no.2 s.86
• /
• pp.213-220
• /
• 2005

Carbon fiber reinforced polymer (CFRP) sheets are becoming increasingly popular for strengthening deteriorated concrete bridges due to their excellent strength and stiffness-to-weight ratio, corrosion resistance, and convenience of construction work. The purpose of this study is to compare the performance of CFRP-strengthened reinforced concrete (RC) beams and to develop a new design formula. Simple beams with 3 m span length were tested to investigate the effect of reinforcing steel ratio and CFRP-reinforcing ratio on the flexural behavior of strengthened RC beams. The test results were analyzed with the special emphasis on the failure mode, the maximum load, and the strain distribution in the section. It is shown that the strain of the strengthened beams is not linearly distributed in the section. A new design formula based on the non-linear distribution of the strain has been derived and showed that it has a good agreement with the various domestic and foreign test results.

• Journal of the Korea Concrete Institute
• /
• v.14 no.1
• /
• pp.76-82
• /
• 2002

The rapid-set cement concrete causes high hydration temperature and nay result in a high drying shrinkage and shrinkage-induced cracking. This problem may be fixed by incorporating polypropylene fibers in rapid-set cement concrete, because of increased toughness, resistance to impact, corrosion, fatigue, and durability. A series of concrete drving shrinkage tests was peformed in order to investigate the shrinkage properties of polypropylene fiber reinforced concrete with experimental variables such as concrete types, fiber reinforcement, W/C ratio, with and without restraint. Uni-axially restrained bar specimens were used for the restrained shrinkage tests. The results were as follows; The dry shrinkage of rapid-set cement concrete was much lessor than that oi OPC, probably because of smaller weight reduction rate by early hydration and strength development. The constraint and bridging effects caused by polypropylene fibers were great for the rapid-setting cement concrete when compared with that of plain concrete, and this resulted In increased resistance against tensile stress and cracking.

• Journal of Sensor Science and Technology
• /
• v.10 no.1
• /
• pp.33-41
• /
• 2001

Wire ropes have been widely used in industrial applications, wherever heavy weight should be carried safely or mechanical energy should be transmitted fast. Especially, wire rope failures in operating elevator may lead to extensive property damage and serious injury to nearby personnel. Hence, it is very important to inspect wire rope periodically. Failure defection of wire rope requires fundamental knowledge of wire rope construction, rope behavior, properties of fault, sensing and signal processing method. In this research, the development of a new fault detecting system incorporating Hall-effect sensors to detect flaws such as abrasion, broken wire, corrosion and deformation for aged wire ropes in elevator, is described. For using a detector as a portable instrument, several performances for implementing sensing part with Hall-effect sensor, analog signal processing unit and programs are described. Experiments and field testing results for the implemented detecting system are also given. As a result, it is verified that the detecting system has good efficiency for inspecting faults of aged wire ropes in service.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.2
• /
• pp.18-25
• /
• 2016

Bascule bridge, with its use to help vessels ply, has a several examples overseas of being serviced for more than decades years by careful maintenance, admitted its significance as landmarks for its rareness. Yeongdo Bridge, the sole bascule bridge in Korea was reconstructed in 2013 after being demolished because of its corrosion and aging, and now operates once in a day. Recently, safety inspections are executed thanks to demands getting higher for maintenance and safety of bridges, but measurement and analysis about bascule bridges are scarce. This study includes the analysis of the bascule bridge's behavior such as stress, vibration and reaction in normal condition and while it lifts up, based on measurement. We expect that this study will be used as an initial data to compare and confirm bridge's changes as service year and the number of operation increase.

• Journal of the Korean Society for Heat Treatment
• /
• v.8 no.1
• /
• pp.32-43
• /
• 1995

Ti-6Al-4V alloy are widely used in chemical and aircraft industries for their good corrosion resistance and high strength to weight ratio. Surface alloying of Ti alloy by $CO_2$ laser is able to produce few hundred micrometers thick TiN surface-alloyed layer with high hardness on the substrate very simplely by injecting reaction gas($N_2$) into a laser-generated melt pool and adjust the hardness to the specific requirements of the individual application by changing of laser processing parameters. This research has been investigated the effect of such parameters on TiN surface-alloying of Ti-6Al-4V alloy by $CO_2$ laser. The maximum hardness of TiN surface-alloyed zone waw obtained by injecting 100% $N_2$ gas and it was decreased as the amount of $N_2$ gas in Ar and $N_2$ gas mixture was decreased. As scanning speed was increased, the hardness and depth of TiN surface-alloyed zone was decreased at constant laser power. The surface hardness after double scanning laser treatment is higher than that of single scanning. At constant laser power, the surface roughness is increased after the surface alloying if laser scanning speed is decreased.

• Structural Engineering and Mechanics
• /
• v.67 no.2
• /
• pp.207-217
• /
• 2018

In past years, numerous problems have vexed engineers with regard to buckling, corrosion, bending, and overloading in damaged steel structures. This article sets out to investigate the possible effects of carbon fiber reinforced polymer (CFRP) and steel plates for retrofitting deficient steel square hollow section (SHS) columns. The effects of axial loading, stiffness, axial displacement, the position and shape of deficient region on the length of steel SHS columns, and slenderness ratio are examined through a detailed parametric study. A total of 14 specimens was tested for failure under axial compression in a laboratory and simulated using finite element (FE) analysis based on a numerical approach. The results indicate that the application of CFRP sheets and steel plates also caused a reduction in stress in the damaged region and prevented or retarded local deformation around the deficiency. The findings showed that a deficiency leads to reduced load-carrying capacity of steel SHS columns and the retrofitting method is responsible for the increase in the load-bearing capacity of the steel columns. Finally, this research showed that the CFRP performed better than steel plates in compensating the axial force caused by the cross-section reduction due to the problems associated with the use of steel plates, such as in welding, increased weight, thermal stress around the welding location, and the possibility of creating another deficiency by welding.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.18 no.1
• /
• pp.24-30
• /
• 2019

The deck floor of a the cargo truck becomesis damaged and aged due to the continuous loading of the loading cargo and external environmental factors. Floor boards made of wood and metal are often used. In the case of wood, the cost is high due to the use of imported wood, and the strength is easily deterioratesd due to environmental factors. In the case of metal materials, the durability is higher than that of wood, but problems are raised due to the effect of major factors that hinder the weight reduction, and the effects of corrosion. In order to replace this stucturestructural design, this study proposed a wood fiber composite using natural raw materials. Woody composites are being used as environmentally and friendly exterior materials with the combined advantages of plastic, and wood,; low cost and low density. However, due to the nature of the woody composites, the properties are differentdiffer depending on the contents of the matrix, reinforcing agent, additives, compatibilizer, etc. In this study, we investigate these problems through analysis of the microstructure and mechanical properties according to proper content and injection molding conditions. As a result, it is considered that the wood deck composite can replaced the current Deck Floor Boardreplace current deck floor boards through continuous continued research and results of this study.

• Journal of Korea Foundry Society
• /
• v.41 no.6
• /
• pp.543-549
• /
• 2021

Aluminum cast iron has excellent oxidation resistance and good resistance to sulfide and corrosion. Compared to Ti and Ni alloys, it is expected to be a substitute material for structural materials and stainless steels because it is relatively inexpensive to use Fe, which is a non-strategic element. This results in a weight reduction effect of about 30% as compared to the use of stainless steel. With regard to aluminum as an alloying material, it is an element that has been widely used for the alloying of cast iron in recent years. Practical use has been delayed owing to the resulting lack of ductility at room temperature and the sharp decrease in the strength above 600℃ of this alloy, however. The cause of the weak room temperature ductility is known to be environmental embrittlement by hydrogen, and the addition of various alloying elements has been attempted in order to mitigate these shortcomings. Although alloying elements such as vanadium, chromium, and manganese are mainly used to increase the hardness and wear resistance of gray cast iron, the price of finished products containing these elements and the problems associated with alloys with this material impose many limitations.

• Structural Monitoring and Maintenance
• /
• v.9 no.1
• /
• pp.29-42
• /
• 2022

In mountainous areas of China, concrete poles with connectors are widely employed in power transmission due to its convenience of manufacture and transportation. The bearing capacity of the poles must have degenerated over time, and most of the steel connectors have been corroded. Carbon fiber reinforced polymer (CFRP) offers a durable, light-weight alternative in strengthening those poles that have served for many years. In this paper, the bearing capacity and failure mechanism of CFRP sheet strengthened existing reinforced concrete poles with corrosion steel connectors were investigated. Four poles were selected to conduct flexural capacity test. Two poles were strengthened by single-layer longitudinal CFRP sheet, one pole was strengthened by double-layer longitudinal CFRP sheets and the last specimen was not strengthened. Results indicate that the failure is mainly bond failure between concrete and the external CFRP sheet, and the specimens fail in a brittle pattern. The cross-sectional strains of specimens approximately follow the plane section assumption in the early stage of loading, but the strain in the tensile zone no longer conforms to this assumption when the load approaches the failure load. Also, bearing capacity and stiffness of the strengthened specimens are much larger than those without CFRP sheet. The bearing capacity, initial stiffness and elastic-plastic stiffness of specimen strengthened by double-layer CFRP are larger than those strengthened by single-layer CFRP. Weighting the cost-effective effect, it is more economical and reasonable to strengthen with single-layer CFRP sheet. The results can provide a reference to the same type of poles for strengthening design.

• Journal of Urban Science
• /
• v.11 no.2
• /
• pp.19-24
• /
• 2022

Conventional RC beams for crossing small and medium-sized rivers do not have a cross-sectional area, so the floating debris is accumulated and disasters such as damage to bridges occur. To improve this, the PSC method was invented. However, this also had problems such as transverse curvature, increase in dead weight due to cross-sectional shape, and negative moment generated during serialization, so it was necessary to develop a new type of girder. Therefore, it was intended to propose a LIT(Leton Interaction Thrust) girder bridge that is safer and has better performance than the conventional PSC girder with improved section efficiency. Unlike existing girder bridges, the LIT girder has the feature that the change in the strands of the entire girder occurs only in the vertical direction when the first tension is applied because the tendon arrangement is symmetrical by applying the raised portion. In addition, slab continuation generates a secondary moment that is advantageous to the continuous point, effectively controlling the negative moment and preventing the corrosion of the tendon. The dimensions of the cross section were determined, and the arrangement of the strands was designed to conduct structural analysis and detailed analysis. As a result of the structural analysis, the stress of the girder showed results within the allowable compressive stress, and the deflection showed the result within the allowable deflection. showed results. In addition, a detailed analysis was performed to examine the stress distribution around the girder body and the anchorage area and the stress distribution of the embossed portion, and as a result, the stress of the girder body due to the tension force showed a stable level.