• Journal of Welding and Joining
• /
• v.14 no.2
• /
• pp.36-45
• /
• 1996

Fatigue strength of the spot welded lap joint is considerably influenced by corrosive environments. Particularly, the chloride and the sulfide are most injurious to strength of the spot welded lap joint. Therefore, there is a need to evaluate its effect to corrosion fatigue strength for safe life design of spot welded structures. In order to evaluate their corrosion fatigue strength, corrosion fatigue tests on the spot welded lap joints of the uncoated and the coated high strength steel sheets were conducted in air and in 10% NaCl solution. Corrosion fatigue strength of the uncoated specimens were entirely lower than the coated one in NaCl solution, but those of the coated specimens in NaCl solution were lower than in air. And stress distribution in single spon welded lap joint subjected to tension-shear load was investigated by the finite element method. Using these results, we tried to evaluate corrosion fatgue strength of the various spot welded lap joints with maximum stress $\sigma_{max}$ at edge on loading side of the spot welded lap joint. We could find that corrosion fatigue strength could be quantitatively and systematically rearranged by $\sigma_{max}$.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.241-246
• /
• 2003

In order to develop a method of corrosion fatigue design and estimate reliability of TMCP steel using as the material of heavy industries and plants, its corrosion susceptibilities, corrosion fatigue strength, and determination of fatigue design criterion considering corrosion degradation were investigated. From the results, the corrosion characteristic of TMCP steel is very susceptible in 3.5wt.% NaCl solution. Its susceptibility was linearly increased with the solution temperature increase. The corrosion fatigue strength in $25${\circ}$, 3.5wt.% NaCl solution is very lower than that of in air. And also, it was decreased with the frequency decrease in the same environment. It is expected that the developed corrosion fatigue design method for TMCP steel is useful. However, it is necessary to verify its reliability for actual application.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.2
• /
• pp.28-38
• /
• 1997

The corrosion fatigue test was conducted in air to investigate the corrosion fatigue strength of SM 30 C steel by which was corroded in the under sea and surface in the conditions of 3.0% NaCl salt solution. The fatigue tests were carried out on a rotary bending testing machine of cantilever type. The corrosion effect of the sea surface conditionwas served more than that of the under sea condition which was due ti the periodic contact of air thus accelerate the corrosion. The difference of the fatgue strength between sea surface and under sea conditions decreased with increase of stree level and corroded period. Inthe case of the solid shaft and thickness 2mm of hollow shaft, the difference of corrosion fatigue strength decreased as stress level and corrosion periodic increasing. Onthe contrary in the case of thickness 1mm of hollow sgaft, the difference of it increased as stress level, corrosionn periooodic increasing and also the condition of corrosion chaanged. The main factors affecting the degradation of fatigue strength due to corrosion were the reduction of sectional area and the increase of surface roughness. The interference phenomenon increase with stress level got higher.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.8 no.5
• /
• pp.181-187
• /
• 2000

Fatigue tests under acid fog environment were carried out to investigate the effect of acid fog on the corrosion fatigue strength of SM55C in comparison with distilled water. Main results obtained are as follows. The fatigue strength of SM55C under acid fog environment are remarkably decreased as compared with that of distilled water specimen. The corrosive effect of acid fog on fatigue strength are more serious under low stress amplitude level than under high stress amplitude level, and this leads to continuous reduction of fatigue strength. Under acid fog environment in early stage of crack growth. because the corrosive components dissolve the crack face offensively. the unstable fracture surface appears. But, the stable corrosion precipitation and products layer are formed on the fracture surface in accordance with the time pass.

• Corrosion Science and Technology
• /
• v.17 no.2
• /
• pp.81-89
• /
• 2018

In this study, the effect of Nb alloying element on the corrosion fatigue properties of high strength steel is investigated by conducting fatigue experiments under corrosive condition and hydrogen induced condition, potentiodynamic polarization test, tensile test and surface analyses. Nb element is added to enhance the mechanical property of medium carbon steel. This element forms MX-type phases such as carbides and nitrides which are playing an important role in the grain refinement. The grain refinement is one of the effective way to improve mechanical property because both tensile strength and toughness can be improved at the same time. However, MX-type phase precipitates can be a susceptible site to localized corrosion in corrosive environment due to the potential difference between matrix and precipitate. The obtained results showed that Nb-added steel improved corrosion fatigue property by grain refinement. However, it is degraded for hydrogen-induced fatigue property due to Nb, Ti-inclusions acting as a stronger trap.

• Journal of Ocean Engineering and Technology
• /
• v.12 no.1
• /
• pp.32-38
• /
• 1998

This paper is to investigate of microhardness, adhesive strength, tensile strength, and fatigue strength of ceramic sprayed steel. Rotary bending fatigue tests have been conducted at room temperature in air and 3% NaCl solution using specimens of carbon steel(S45C) with sprayed coating layers of Ni-4.5% Al(under coating) and $TiO_2$ (top coating). The microhardness has been improved at $800^{\circ}C$ heat treatment and 150mm spraying distance. Tensile strength of the sprayed steel is dependent on the substrate strength. The fatigue strength of the sprayed steel is larger than that of substrate due to blasting and constraint surface of plastic deformation effect. In low stress level, the corrosion fatigue strength of the sprayed steel were lower than that of fatigue strength in air by corrosion.

• Journal of the Korean Society for Railway
• /
• v.8 no.4
• /
• pp.299-307
• /
• 2005

In general, structural integrity of rolling stock structures should last more than 25 years. During the lifetime corrosive degradation occurs. For structural design and diagnosis, quantitative relationship between corrosive degradation and variation of mechanical properties such as tensile strength and fatigue strength is needed. In this study, first of all we established the atmospheric corrosion test procedure. At regular intervals using specimens of SM490A and SS400 on the atmospheric corrosion test bed, we carried out tensile and fatigue tests. The fatigue strength decreases as the atmospheric corrosion period increases. In addition we studied the effect of post-weld heat treatment on the tensile and fatigue behaviour and performed electrochemical corrosion tests.

• Journal of Advanced Marine Engineering and Technology
• /
• v.19 no.3
• /
• pp.62-69
• /
• 1995

In order to investigate the effect of TiN coating on corrosion fatigue behavior of metal, the rotary bending corrosion fatigue tests were carried out in 3% NaCl solution by using the round bar specimens of high-speed steel, SKH-9, coated with TiN by PVD method. From the experimental results, fatigue strength of TiN coating steel in air was obvious improvement as compared with that of the substrate because of the restriction of dislocation movement in near surface of the substrate by hard thin film. In 3% NaCl solution, corrosion fatigue life of TiN coating specimen in high stress level was improvement same as in air. But in low stress level, corrosion fatigue life of TiN coating one was equivalent to that without coating, due to much crack initiated from corrosion pits formed at the substrate by failure of coating layer.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1997.04a
• /
• pp.143-149
• /
• 1997

the horizontal corrosion fatigue tester has been developed for investigating environmental strength. Using this tester, we investigated about corrosion fatigue caracteristic for A106 GrB steel weldments in 3.5% synthetic seawater and room temperature. Considered parameter is only frequency of 1,3 and 5Hz. and Corrosion fatigue crack length was measured by DC potential difference method. From the results, we could find that the horizontal corrosion fatiued tester could be well applied to estimation of fatigue strength. and In case of 5Hz, corrosion fatigue crack growth path of A106 GrB steel weldment was transgranular, and of 1 and 3Hz showed that transgranular and intergranular was mixed. Also, Corrosion fatigue crack growth caracteristic values estimated in each frequency were C=9.33 x 10-9 and m=2.93 in 1Hz, C=9.77x10-10 and m=3.47 in 3Hz, C=1.02x10-10 and m=4.05 in 1Hz

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.1787-1791
• /
• 2007

For structural design and diagnosis, quantitative relationship between corrosive degradation and variation of mechanical properties such as tensile strength and fatigue strength is needed. But it is difficult to find data associated with corrosive degradation of structural structures. In this study, first of all we established the atmospheric corrosion test procedure. And using specimens of SM490A and SS400 on the atmospheric corrosion test bed, we carried out tensile and fatigue tests at regular intervals. And we studied the effect of post-weld heat treatment on the tensile and fatigue behaviour. It is found fatigue strength decreases as the atmospheric corrosion period increases.