• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.222-227
• /
• 2004

The failure assessment for corroded pipeline has been considered with the full scale burst test and the finite element analysis. The burst tests were conducted on 762 mm diameter, 17.5 mm wall thickness and API 5L X65 pipe that contained specially manufactured rectangular corrosion defect. The failure pressure for corroded pipeline was measured by burst testing and classified with respect to corrosion sizes and corroded regions - the body, the girth weld and the seam weld of pipe. Finite element analysis was carried out to derive failure criteria of corrosion defect on the pipe. A series of finite element analyses were performed to obtain a limit load solution for corrosion defects on the basis of burst test. As a result, the criteria for failure assessment of corrosion defect within the body, the girth weld and the seam weld of API 5L X65 gas pipeline were proposed.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.453-458
• /
• 2001

Pipelines have the highest capacity and are the safest and the least environmentally disruptive way for gas or oil transmission. Recently, failures due to corrosion defects have become of major concern in maintaining pipeline integrity. A number of solutions have been developed for the assessment of remaining strength of corroded pipelines. However, these solutions are known to be dependent on material properties and pipeline geometries. In this paper, a Fitness-For-Purpose type limit load solution for corroded gas pipelines made of the X65 steel is proposed. For this purpose, a series of burst tests with various types of corrosion defects are performed. Finite element simulations are carried out to derive an appropriate failure criterion. And then, further, extensive finite element analyses are performed to obtain the FFP type limit load solution for corroded X65 gas pipelines as a function of defect depth, length and pipeline geometry. And also, a window based computer program far the assessment of corrosion defect, which is named as COPAP(COrroded Pipeline Assessment Program) has been developed on the basis of proposed limit load solution.

• Corrosion Science and Technology
• /
• 제4권4호
• /
• pp.164-170
• /
• 2005

Pipelines have the highest capacity and are the safest and the least environmentally disruptive means for transmitting gas or oil. Recently, failures due to corrosion defects have become a major concern in maintaining pipeline integrity. A number of solutions have been developed for the assessment of remaining strength of corroded pipelines. In this paper, a Fitness-For-Purpose(FFP) type limit load solution for corroded city gas pipelines is proposed. For this purpose, a series of burst tests with various types of machined defects were performed. Finite element simulations were carried out to derive an appropriate failure criterion. Based on such solution along with existing solutions, an integrity evaluation program for corroded city gas pipeline, COPAP-CITY, has been developed.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.339-344
• /
• 2001

The transmission pipeline industry spends many millions of dollars annually performing inline inspections, excavating sites of possible corrosion, and repairing or replacing damaged sections of pipe. New criteria for evaluation the integrity of corroded pipe have been developed in recent years to help in controlling these costs. These new criteria vary widely in their estimates of integrity and the most appropriate criterion for a given pipeline is not always clear. This paper presents an overview, comparison and evaluation of acceptability criteria for corrosion defects in pipelines. By full scale burst tests, this paper have assessed the relative accuracy of each of theses criteria in predicting failure and remaining strength. Many of the criteria appear to be excessively conservative and indicate that defects must be repaired when none is needed, based upon burst test data.

• International Journal of Precision Engineering and Manufacturing
• /
• 제1권2호
• /
• pp.48-54
• /
• 2000

This paper presents the effect of shape of external corrosion in pipeline on failure prediction by using a numerical simulation. The numerical study for the pipeline failure analysis is based on the FEM(Finite Element Method)with an elastic-plstic and large-deformation analysis. Corrosion pits and narrow corrosion grooves in pressurized pipeline were analysed. A failure criterion, based on the local stress state at the corrosion and a plastic collapse failure mechanism, is proposed. The predicted failure stress assessed for the simulated corrosion defects having different corroded shapes along the pipeline axis compared with those by methods specified in ANSI/ASME B31G code and a modified B31G code. It is concluded the corrosion geometry significantly affects the failure behavior of corroded pipeline and categorisation of pipeline corrosion should be considered in the development of new guidance for integrity assessment.

• 대한기계학회논문집A
• /
• 제26권1호
• /
• pp.203-210
• /
• 2002

The transmission pipeline industry spends many millions of dollars annually performing inline inspections, excavating sites of possible corrosion, and repairing or replacing damaged sections of pipe. New criteria fur evaluation of the integrity of corroded pipe have been developed in recent years to help in controlling these costs. These new criteria vary widely in their estimates of integrity and the most appropriate criterion fur a given pipeline is net always clear. This paper presents an overview, comparison and evaluation of acceptability criteria for corrosion deflects in pipelines. By full scale burst tests, this paper has assessed the relative accuracy of each of theses criteria in predicting burst pressure. Many of the criteria appear to be excessively conservative and indicate that deflects must be repaired when none is needed, based upon burst test data.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2004년도 추계학술발표대회 개요집
• /
• pp.165-167
• /
• 2004

The failure pressure for corroded pipeline was measured by burst testing and classified with respect to corrosion sizes and corroded regions - the body, the girth weld and the seam weld of pipe. A series of finite element analyses were performed to obtain a limit load solution for corrosion defects on the basis of burst test. As a result, the criteria for failure assessment of corrosion defect within the body, the girth weld and the seam weld of API 5L X65 gas pipeline were proposed.

• 한국산업융합학회 논문집
• /
• 제7권4호
• /
• pp.411-417
• /
• 2004

Recently, researchers and engineers from, the development of reliability engineering and probability fracture mechanics, have begun to take seriously the reliability analysis and the integrity for a corroded pipeline. Pressurized pipelines containing active corrosion defects increase gradually both in extent, and depth with increased periods of exposure. This causes a reduction of the remaining strength and the carrying capacity of a pipeline; and creates uncertainty about the future capacity. The steps that are necessary in order to assess the integrity of corroded pipelines will be discussed in this paper utilizing results from an actual model.

• International Journal of Precision Engineering and Manufacturing
• /
• 제7권3호
• /
• pp.24-29
• /
• 2006

Pressurized gas pipelines are subject to harmful effects from both the surrounding environment and the materials passing through them. Reliable assessment procedures, including fracture mechanics analyses, are required to maintain their integrity. Currently, integrity assessments are performed using conventional deterministic approaches, even though there are many uncertainties to hinder rational evaluations. Therefore, in this study, a probabilistic approach was considered for gas pipeline evaluations. The objectives were to estimate the failure probability of a corroded pipeline in the gas and oil industries and to propose limited operating conditions for different types of loadings. To achieve these objectives, a probabilistic assessment program was developed using a reliability index and simulation techniques, and applied to evaluate the failure probabilities of a corroded API-5L-X52 gas pipeline subjected to internal pressures, bending moments, and combined loadings. The results demonstrated the potential of the probabilistic integrity assessment program.

• 한국산업안전학회:학술대회논문집
• /
• 한국안전학회 1998년도 추계 학술논문발표회 논문집
• /
• pp.261-266
• /
• 1998

This paper presents a numerical simulation of the failure behaviour for the pipeline which has external corroded parts along the axis. The numerical study for the pipeline failure analysis is based on an FEM with an elastic-plastic and large-deformation. The predicted failure assessments for the simulated corrosion defects are compared with ANSI/ASME B31G code and a modified B31G method.