• 대한치과기공학회지
• /
• 제35권2호
• /
• pp.121-126
• /
• 2013

Purpose: The aim of this research was to investigate difference in shear bond strengths of full-contour zirconia layered with porcelain. Methods: Disk-shaped (diameter: 12.0 mm; height: 3.0 mm) zirconia were randomly divided into six groups according to the surface conditioning method to be applied (N=90, n=15 per group): group 1-contol group(ZC); group 2-airborne particle abrasion with $50-{\mu}m\;Al_2O_3(5A)$; group $3-50-{\mu}m\;Al_2O_3$ + liner(5AL), group $4-110-{\mu}m\;Al_2O_3(1A)$; group $5-110-{\mu}m\;Al_2O_3$ + liner(1AL); group 6-liner(LC). On each block, zirconia porcelain was build up according to manufacturer's instructions. All samples were fixed with measuring jigs and shear bond strength were measured with Universal testing machine. Collected data were analyzed using SPSS(Statistical Package for Social Sciences) Win 12.0 statistics program. Results: LC showed the highest value($29.92{\pm}2.55$ MPa) and ZC showed the lowest value($13.22{\pm}1.37$ MPa). Zirconia liner and Alumina oxide groups was significantly higher shear bond strength than control(p<0.05). 5A (without liner $22.18{\pm}2.37$, with liner $22.84{\pm}1.74$ MPa) was higher shear bond strength than $110{\mu}m$ (without liner $20.18{\pm}2.38$, with $20.71{\pm}2.67$). Conclusion: Surface treatments may have advantage in bond strength improvement for full-contour zirconia layered with porcelain.

• 대한치과기공학회지
• /
• 제36권2호
• /
• pp.83-89
• /
• 2014

Purpose: This study is to evaluate the effect of modeling liquid on the shear-bond strength between zirconia core and veneering ceramic. Methods: Disk-shaped (diameter: 12.0mm; height: 3.0mm) zirconia were randomly divided into six groups according to the surface conditioning method and whether modeling liquid is used or not to be applied (N=60, n=10 per group): group 1-control group with distilled water(ZD); group 2-control group with modeling liquid(ZM); group 3-airborne particle abrasion with $110-{\mu}m$ $Al_2O_3$(AD) with distilled water; group 4-airborne particle abrasion with $110-{\mu}m$ $Al_2O_3$ with modeling liquid(AM); group 5-liner with distilled water(LD); group $6{\pounds}{\neq}liner$ with modeling liquid(LM). Contact angles were determined by the sessile drop method at room temperature using a contact angle measurement apparatus. The specimens were prepared using dentin veneering ceramics, veneered, 3mm high and 2.8mm in diameter, over the cores. The shear bond strength test was performed in a Shear bond test machine. Load was applied at a cross-head speed of 0.50mm/min until failure. The fractured zirconia surfaces were evaluated by using stereomicroscope (${\times}30$). Collected data were analyzed using SPSS(Statistical Package for Social Sciences) Win 12.0 statistics program. Results: ZD showed the highest contact angle($50.6{\pm}5.4^{\circ}$) and LD showed the lowest value($6.7{\pm}1.3^{\circ}$). Control groups and zirconia liner groups were significantly higher contact angle than liner groups(p<0.05). LD was the highest shear bond strength($43.9{\pm}3.8MPa$) and ZD was the lowest shear bond strength($24.8{\pm}4.9MPa$). Shear bond strengths of control groups and contact angle of liner groups were not significantly different((p>0.05). Liner groups presented adhesive failures. The others groups showed cohesive and adhesive failures. Conclusion: Modeling liquid groups showed lower contact angles and lower shear bond strength compared to those of distilled water groups.

• 대한치과보철학회지
• /
• 제51권2호
• /
• pp.73-81
• /
• 2013

연구 목적: 이 연구의 목적은 지르코니아 표면처리에 따른 3종의 레진시멘트와 지르코니아의 전단결합강도를 평가하기 위함이다. 연구 재료 및 방법: 총 143개의 디스크 모양의 지르코니아 블록(HASS Co., Gangneung, Korea) 시편을 제작하고 총 13개군(n=11)으로 나누었다. 그중9개군은 표면처리 방식(1. 알루미나 분사, 2. 알루미나 분사와 지르코니아 라이너의 도포, 3.알루미나 분사와 Rocatec (3M ESPE, Seefeld, Germany) 처리) 및 사용한 3종류의 레진시멘트(Bistite II (Tokuyama Dental Co., Japan), Panavia F2.0 (Kuraray Medical, Japan), Super-bond C&B (Sun Medical, Japan))에 따라 나누어 열순환처리 전 접착강도 실험을 시행하였다. 열순환처리 전 접착강도 실험은 위 3종류의 레진시멘트를 3가지 방법으로 표면처리한 지르코니아 시편에 접착하고, 상온의 증류수에 24시간 동안 보관한 후, 전단결합강도를 측정하였다. 열순환처리 후 접착강도 실험은, 열순환처리 전 접착강도 실험에서 우수한 전단결합강도를 보인 지르코니아 표면처리군(알루미나 분사와 Rocatec 처리를 하고 3종류의 레진시멘트를 접착한 3개의 군)과 대조군으로 알루미나만으로 표면처리 후 Super-bond C&B를 접착한 1개의 군을 대상으로 $5^{\circ}C$와 $55^{\circ}C$사이에서 5,000회 열순환처리를 시행하고 전단결합강도를 측정하였다. 결과: 열순환처리 전 접착강도 실험에서는 알루미나 분사와 Rocatec 처리를 한 지르코니아 표면에 Super-bond C&B를 접착한 군이 가장 높은 전단결합강도를 보였다. Super-bond C&B를 사용한 군이 다른 시멘트 군보다 유의성 있게 높은 전단결합강도를 보였으며, 지르코니아 표면에 Rocatec 처리를 한 군이 다른 표면처리를 한 군보다 유의성 있게 높은 전단결합강도를 보였다. 열순환처리를 한 후에는, Rocatec 처리를 한 지르코니아 표면에 Super-bond C&B를 접착한 군만이 유일하게 전단결합강도가 증가하였으며, 다른 모든 군에서는 전단결합강도가 감소하였다. 결론: 본 실험에서는 Super-bond C&B 시멘트가 가장 높은 전단결합강도를 보였으며, Rocatec 시스템은 레진시멘트와 지르코니아의 전단결합강도를 향상시키는 방법이 될 것이라고 사료된다.