• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.26 no.3
• /
• pp.126-130
• /
• 2016

Ti alloys have been used for orthopedic devices, automobile and aircraft because it has several beneficial properties such as a low density, a low modulus of elasticity, excellent high-temperature strength, excellent corrosion resistance and biocompatibility. In this study, Ti-64 composition (6 wt% Al, 4 wt% V) is investigated as a representative Ti-alloy system on the crystallographic characteristics and microstructure. We investigated crystal structure of the Ti-64 sample by XRD, and analyzed microstructure by compositional differences measured using FE-SEM and EDX.

• Journal of Technologic Dentistry
• /
• v.23 no.1
• /
• pp.31-43
• /
• 2001

This study was performed to observe the micro-structure change of surface, behavior of oxide change of element, the component transformation of the alloy and the bonding strength between the porcelain interface in order to investigate effects of indium, tin on interfacial properties of porcelain fused to low gold alloy. Hardness of castings was measured with a micro-Vicker's hardness tester. The compositional change of the surface of heat-treated specimen was analyzed with an EDS and an EPMA. The interfacial shear bonding strength between alloy specimen and fused porcelain was measured with a mechanical testing system(MTS 858.20). The results were as follows: 1) The hardness value of alloy increased as increasing amount of indium addition. 2) The formation of oxidation increased as increasing indium and tin contents after heat treatment. 3) Diffusion of indium and tin elements increased as increasing indium and tin contents in metal-porcelain surface after porcelain fused to metal firing. 4) The most interfacial shear bonding strength was increased as increasing a composition of adding elements, and a heat-treatment time, and an oxygen partial pressure. From the results of this study it was found that the addition of alloying elements such as indium and tin increase hardness of as-cast alloy, produce surface oxide layer of adding elements by heat-treatment which may improve interfacial bonding strength between alloy and porcelain.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.8
• /
• pp.622-626
• /
• 2011

Lead-free piezoelectric ceramics with the composition of $(Na_{0.54}K_{0.46})_{0.96}Li_{0.04}(Nb_{1-0.10-x}Ta_{0.10}Sb_x)O_{3}$ (x= 0~8 mol%) were fabricated by nomal sintering at $1,090^{\circ}C$ for 5 h. the phase structure, microstructure and electrical properties were investigated with a emphasis on the influence of the Sb content. All samples exhibit a single perovskite phase over the whole compositional range. For the ceramics with x= 4 [mol%], two phase transitions are observed at $75^{\circ}C$ and $366^{\circ}C$, corresponding to the phase transitions of orthorhombic to tetragonal (To-t) and tetragonal to cubic (Tc), respectively. high electrical properties of $d_{33}$= 210.83 pC/N, kp= 40%, ${\varepsilon}_r$= 1,091.35, $\rho$= 4.54 g/$cm^2$ were obtained from the specimen with x= 4 [mol%], which suggests that the composition ceramics is a promising lead-free piezoelectric material.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.271-271
• /
• 2006

The structural, dielectric and piezoelectric properties of $[Bi_{1-x}(Na_{0.7-x}K_{0.2}Li_{0.1})]_{0.5}BaxTiO_3$ (BNKLBxT) ceramics were studied for the compositional range, x = 0-0.08. The samples were prepared by conventional sintering technique. The result of X-ray diffraction (XRD) suggest that $Ba^{2+}$ diffuse into the $[Bi(Na_{0.7}K_{0.2}Li_{0.1})]_{0.5}TiO_3$ (BNKLT) lattices to form a solid solution with a single phase perovskite structure. The ceramic show excellent piezoelectric and ferroelectric properties, and optimum properties measured are as follows: piezoelectric constant $d_{33}=230pC/N$, planar electromechanical coupling factor $k_p\;=\;40.3%$, remanent polarization $P_r\;=\;30\;{\mu}C/cm^2$, and coercive field $E_c\; =\;2.5\;kV/mm$, respectively.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.277-277
• /
• 2010

The capacity of the carbonaceous materials reached ca. $350\;mAhg^{-1}$ which is close to theorestical value of the carbon intercalation composition $LiC_6$, resulting in a relatively low volumetric Li capacity. Notwithstanding the capacities of carbon, it will not adjust well to the need so future devices. Silicon shows the highest gravimetric capacities (up to $4000\;mAhg^{-1}$ for $Li_{21}Si_5$). Although Si is the most promising of the next generation anodes, it undergoes a large volume change during lithium insertion and extraction. It results in pulverization of the Si and loss of electrical contact between the Si and the current collector during the lithiation and delithiation. Thus, its capacity fades rapidly during cycling. We focused on electrode materials in the multiphase form which were composed of two metal compounds to reduce the volume change in material design. A combination of electrochemically amorphous active material in an inert matrix (Si-M) has been investigated for use as negative electrode materials in lithium ion batteries. The matrix composited of Si-M alloys system that; active material (Si)-inactive material (M) with Li; M is a transition metal that does not alloy with Li with Li such as Ti, V or Mo. We fabricated and tested a broad range of Si-M compositions. The electrodes were sputter-deposited on rough Cu foil. Electrochemical, structural, and compositional characterization was performed using various techniques. The structure of Si-M alloys was investigated using X-ray Diffractometer (XRD) and transmission electron microscopy (TEM). Surface morphologies of the electrodes are observed using a field emission scanning electron microscopy (FESEM). The electrochemical properties of the electrodes are studied using the cycling test and electrochemical impedance spectroscopy (EIS). It is found that the capacity is strongly dependent on Si content and cycle retention is also changed according to M contents. It may be beneficial to find materials with high capacity, low irreversible capacity and that do not pulverize, and that combine Si-M to improve capacity retention.

• Journal of the Korean Applied Science and Technology
• /
• v.25 no.2
• /
• pp.211-218
• /
• 2008

The performance of positive plates depends on the structure of the lead dioxide active mass. The positive active materials (PAM) consists of a skeleton, built up of agglomerates and macropores. Agglomerates, in their turn, comprise particles and micropores. This paper described a study conducted to determine the effects of different soaking times between the acid fill and formation stages of the tubular plate production. For the positive plates a lead oxide were filled into tubular bag with a red lead. After filling the positive plates were soaked in $H_2SO_4$ solution. X-ray diffraction(XRD), scanning electron microscopy(SEM) and electrical testing had been used to study the compositional and morphological aspects of the positive active material(PAM) just prior and after formation. Results indicate that PAM compositions were effected by the soaking time and acid density of $H_2SO_4$ solution. It can be seen that as the soaking time duration increases, $\alpha$-PbO, $Pb_3O_4$, and Pb were all gradually sulphating. Composition of 3BS reached a maximum at around 3 h duration and $H_2SO_4$ of sp. gr. 1.10 on soaking. This results would suggest that the most beneficial conditions for soaking were the $H_2SO_4$ of sp. gr. 1.10 and 2 to 6 h of soaking.

• Korean Journal of Optics and Photonics
• /
• v.14 no.6
• /
• pp.594-599
• /
• 2003

By using the spectroscopic ellipsometry, we have measured and analyzed the optical characteristics of P $r^3$$^{+}$-doped selenide glasses of Ge-Sb-Se system, a strong candidate material for U band fiber amplifiers. The ellipsometric spectra measured in the transparent wavelengths range of the material were all fitted to a model consisting of ambient/roughness/thin fil $m_strate structures to obtain simultaneously the optical properties such as refractive index, in terms of Sellmeier parameters and film structure of P $r^3$$^{+}$-doped selenide glasses. Repeated measurements on different positions in both polished faces rendered to verify positional dependence of measured spectre-ellipsometric data. Hence, the model made possible the analysis of the optical characteristics of the glasses. Even though surface roughness was mainly responsible for the position dependencies, the averaged refractive indexes were as precise as to reflect the minute compositional change tantamount to 1 mol%. The measured refractive indexes are useful for design of core and clad compositions of single-mode selenide optical fibers.

• Korean Journal of Metals and Materials
• /
• v.47 no.1
• /
• pp.13-20
• /
• 2009

This work presents functionally graded coatings (FGC) of hydroxyapatite (HA) and metallic powders on Ti-6Al-4V implants using plasma spray coating method. HA has been the most frequently used coating material due to its excellent compatibility with human bones. However, because of the abrupt changes in thermomechanical properties between HA and the metallic implant across an interface, and residual stress induced on cooling from coating temperture to room temperature, debonding at the interface occurs in use sometimes. In this work, FGC of HA and Ti or Ti-alloy powders is made to mitigate the abrupt property changes at the interface and the effect of FGC on residual stress release is investigated by evaluating the mechanical bond strength between the implant and the HA coating layers. Thermal annealing is done after coating in order to crystallize the HA coating layer which tends to have amorphous structure during thermal spray coating. The effects of types and compositional ratio of metallic powders in FGC and annealing conditions on the bond strength are also evaluated by strength tests and the microstructure analysis of coating layers and interfaces. Finally, biocompatibility of the coating layers are tested under ISO 10993-5.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.5
• /
• pp.435-444
• /
• 2001

WC-( $Ti_{1-x}$ A $l_{x}$) N coatings of constant changing Al concentration were deposited on S45C substrates by high-ionization sputtered PVD method. The Al concentration could be controlled by using evaporation source for Al and fixing the evaporation rate of the metals (i.e, WC- $Ti_{0.86}$A $l_{0.14}$N, WC- $Ti_{0.72}$A $l_{0.28}$N, and WC- $Ti_{0.58}$A $l_{0.42}$N). The corrosion behavior of WC-( $Ti_{1-x}$ A $l_{x}$)N coatings in a deaerated 3.5% NaCl solution was investigated by electrochemical corrosion tests and surface analyses. The measured galvanic corrosion currents between coating and substrate indicated that WC- $Ti_{0.72}$A $l_{0.28}$N coating showed the best resistance of the coating tested. The results of potentiodynamic polarization tests showed that the WC- $Ti_{0.72}$A $l_{0.28}$N coating deposited with 32W/c $m^2$ of Al target revealed higher corrosion resistance. This indicated that the WC- $Ti_{0.72}$A $l_{0.28}$N coating is effective in improving corrosion resistance. In EIS, the WC- $Ti_{0.72}$A $l_{0.28}$N coating showed one time constant loop and increased a polarization resistance of coating ( $R_{coat}$) relative to other samples. Compositional variations of WC-( $Ti_{1-x}$ A $l_{x}$)N coatings were analyzed by EDS and XRD analysis was performed to evaluate the crystal structure and compounds formation behavior. Surface morphologies of the films were observed using SEM and AFM. Scratch test was performed to measure film adhesion strength.strength. adhesion strength.strength.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.2
• /
• pp.82-89
• /
• 2007

Glass-ceramics were fabricated by heat-treating a glass at $700^{\circ}C$/10hr which was obtained by melting a glass frit mixed with $40{\sim}80 wt%$ EAF dust at $1300^{\circ}C$/1hr. Dependence of crystal phase and bonding state change upon a compositional change and heat treatment condition were studied and the results was connected to the toxic characterization leaching procedure (TCLP) test data to investigate a chemical durability of the specimens. Increasing dust in a glass shifted the peak around $1000cm^{-1}$ to the lower frequency which was composed of two vibration peaks for the nonbridging oxygen at $960cm^{-1}$ and the bridging oxygen at $1050{\sim}1060cm^{-1}$. Also, the $B_2O_3$ structure of boroxol ring changed to a tetrhedral-, trigonal- and di-borate with dust addition. The Fe-O peaks in the glass-ceramics were observed which is consitent with XRD results of spinel formation. The surface of glass after TCLP test was severely cracked while there was no cracks on a glass-ceramics after TCLP test so the chemical durability of the glass-ceramics is superior than that of glass. The leaching concentration of Fe for the glass-ceramics containing EAF dust 80 wt% is 1/15 times lower than that of glass. The Zn leaching concentration fur the glass-ceramics containing dust < 70 wt% was higher than that of glass but its trend was reversed for the specimen of dust content > 80 wt% which could be concluded as correlated with occurrence of willemite phase.