• Journal of the Korean Ceramic Society
• /
• v.43 no.5 s.288
• /
• pp.299-303
• /
• 2006

In this paper, anode supported SOFC with columnar structured YSZ electrolyte was fabricated via Electron Beam Physical Vapor Deposition (EBPVD) method. Liquid condensation process was employed for the preparation of NiO-YSZ substrate and the high power electron beam deposition method was used for the deposition of YSZ electrolyte film. Double layered cathode with LSM-YSZ and LSM was printed on electrolyte via screen-printing method and fired at $1150^{\circ}C$ in air atmosphere for 3 h. The electrochemical performance and the long-term stability of $5{\times}5cm^2$ single cell were investigated with DC current-voltage characteristics and AC-impedance spectroscopy. According to the investigation, $5{\times}5cm^2$ sized unit cell showed the maximum power density of around $0.76W/cm^2$ at $800^{\circ}C$ and maintained the stable performance over 400 h.

• The Korean Journal of Malacology
• /
• v.31 no.1
• /
• pp.27-34
• /
• 2015

The anatomy and ultrastructure of the digestive diverticulum of Tegillarca granosa were described using light and electron microscopy. The digestive diverticulum was situated on the gonad and connected to stomach by a primary duct. Digestive diverticulum is composed of numerous digestive tubules. The epithelial layer of digestive tubule, which is simple, is composed of basophilic cells and digestive cells. Basophilic cells are columnar in shape, and the electron density is higher than that of the digestive cell. The cytoplasm has a well-developed endoplasmic reticulum, tubular mitochondria, Golgi complex and of membrane-bounded granules of high electron density. Digestive cells were classified into three types. According to cell shape, electron density and cell organelles. However, three types of epithelia was same that striated border was observed in free surface and lysosome was observed in cytoplasm. The results of this study suggest that basophilic cells and digestive cells in the digestive tubule are specialized in the extracellular and intracellular digestions, respectively.

• Journal of Plant Biology
• /
• v.17 no.3
• /
• pp.118-126
• /
• 1974

Mulberry plants cultivated in mid-Korea were studied on the growth habitat, canopy type, productive structure and vertical light intensity in relation to the quality of mulberry leaves for sericulture. The growth in length of new branch of summer cut mulberry in spring was vigorous on the uppermost of old shoot. Numbers of leaves on a branch were barely 4 leaves on lower than 20th branch from base, but those were 13 leaves on higher than 24th branch. Area of leaves completely expanded was broad on high branch, but narrow on low one. The form of canopy, the type of productive structure and the vertical light distribution depend upon varieties of cultivated mulberry plants were classified according to characteristic of each variety in two groups, respectively; globular and columnar form in canopy, broad leaves and narrow leaves types in productive structure, and seriously obstructured the light and fairly transmitted the light into lower leaf stratum invertical light distribution. Out of varieties of mulberry investigated, Suwon No. 4 and Rosang were belong to the former characters, but Illchiroe and Kaeryangsubun were to the latters. The values of leaf dry matter index and dry matter production produced by leaves were increased in direct proportion to the height of leaf stratum; the leaf dry matter index of the uppermost leaf was twice as much that of the lowest, and the dry matter production by the highest leaf was 17 times compared with that by the lowest leaf. It is assumed that the meagre leaves occurred in the lower leaf stratum of Suwon No. 4 and Rosang were caused to diminished the dry matter index and dry matter production in the under leaves of plant, which were affected by receiving the weak light.

• Corrosion Science and Technology
• /
• v.7 no.3
• /
• pp.139-144
• /
• 2008

The results of microstructure observations of the $Al_2O_3$ scale formed on a Fe-Cr-Al steel during high temperature oxidation in the $SO_2$ atmosphere are presented. Morphology of the scale has been studied by SEM and TEM techniques. Phase and chemical compositions have been studied by EDX and XRD techniques. The alumina oxide is a primary component of the scale. TEM observations showed that the scale was multilayer. The entire surface of the scale is covered with "whiskers", which look like very thin platelets and have random orientation. The cross section of a sample shows, that the "whiskers" are approximately $2{\mu}m$ high, however the compact scale layer on which they reside is $0.2{\mu}m$ thick. The scale layer was composed mainly of small equiaxial grains and a residual amount of small columnar grains. EDX analysis of the scale surface showed that the any sulfides were found in the formed outer and thin inner scale layer. A phase analysis of the scale formed revealed that it is composed mainly of the $\theta-Al_2O_3$ phase and a residual amount of $\alpha-Al_2O_3$.

• Corrosion Science and Technology
• /
• v.3 no.4
• /
• pp.140-147
• /
• 2004

High temperature oxidation of Fe-19Cr and Fe-19Cr-0.2Ti alloys is studied at 1173-1373 K in 16.5 kPa $O_2$ - balances $N_2$ atmosphere aimed at clarifying the effect of titanium addition. Oxidation rate of Fe-19Cr alloy was accelerated with titanium. For both alloys chromium rich $(Fe,\;Cr)_2O_3$ was formed as a major oxidation product. On Fe-19Cr-0.2Ti alloy, a thin layer composed of spinel type oxide and titanium oxide was also formed and an internal oxidation of titanium was observed. Titanium was concentrated at the oxide surface and internal oxidation zone but a small amount of titanium was also found in the intermediate corundum type $(Fe,\;Cr)_2O_3$ layer. Crystals of corundum type $(Fe,\;Cr)_2O_3$ formed on Fe-19Cr alloy are coarse but that formed on Fe-19Cr -0.2Ti alloys were fine and columnar. Reason for the difference in oxidation kinetics and crystal structure will be discussed relating to the distribution of aliovalent titanium in corundum type $(Fe,\;Cr)_2O_3$ oxide layer.

• Korean Journal of Materials Research
• /
• v.12 no.3
• /
• pp.211-214
• /
• 2002

Properties of 52/48 PZT films with various thicknesses for piezoelectric micro-electro mechanical systems (MEMS) devices fabricated by multi-coating method on $Pt(3500{\AA})/Ti(400{\AA})/SiO_2(3000{\AA})/Si$(525$\mu\textrm{m}$) substrates were investigated. PZT films were deposited by spin-coating process at 3500 rpm for 30 sec, followed by pyrolysis at 45$0^{\circ}C$ for 10 min producing the thickness of about 120nm. These processes were repeated 4, 8, 12, 16 and 20 times in order to have various thicknesses, respectively. Finally, they were crystallized at $650^{\circ}C$ for 30 min. All thick PZT films showed dense and homogeneous surface microstructures. Thick PZT films showed crystalline structures of random orientations with increasing thickness. Dielectric constants of thick PZT films were increased with increasing film thickness and reached 800 at 100kHz for 2.3$\mu\textrm{m}$ thick PZT film. $P_r\; and\; E_c$ of 2.3$\mu\textrm{m}$ thick PZT films were about 20$\mu$C/$\textrm{cm}^2$ and 63kV/cm. Depth profile analysis by Auger Electron Spectroscopy (AES) of 4800 $\AA$ thick PZT film showed the formation of the perovskite phase on Pt layer by Pb diffusion behavior. It was considered that Pb-Pt intermediate layer promoted PZT (111) columnar structures.

• Korean Journal of Materials Research
• /
• v.24 no.8
• /
• pp.407-412
• /
• 2014

Currently, diopside ($MgCaSi_2O_6$) crystal glaze is used frequently for pottery works or in earthen wares, though the process is not straightforward. However, to create and control the positions and sizes of the crystals in desired amounts when making pottery is difficult. To solve this problem, a diopside crystal seed was created at a temperature of $1450^{\circ}C$. After planting this seed in the glaze, a glaze combination and firing process which allows a user to create crystals with the desired position and at the desired size were established. In addition, in order to investigate the creation process of the crystals, the growth patterns of the crystals were observed and examined using Raman spectrography and XRD and SEM analyses. As a result, the optimum synthesis condition of the diopside seed was created by mixing 1 mole of $CaCo_3$, 0.2 mole of $(MgCo_3)_4(MgCoH)_2{\cdot}5H_2O$ and 2 moles of $SiO_2$ and then applying a firing process to the mixture at $1,450^{\circ}C$ for 30 minutes. The optimum glaze content of the seed was 70 % feldspar, 20 % limestone and 10 % $MgCo_3$. For the firing process, it was confirmed that the size of crystal is larger with a longer firing time at $1100^{\circ}C$ by completing a two-hour process at $1280^{\circ}C$. In addition, the diopside crystal has columnar structure and is less than $1{\mu}m$ in size.

• Journal of Magnetics
• /
• v.21 no.1
• /
• pp.12-19
• /
• 2016

The <100> oriented $Fe_{83}Ga_{17}$ alloys with various contents of NbC or B were prepared by directionally solidification method at the growth rate of $720mm{\cdot}h^{-1}$. With a small amount of precipitates, the columnar grains grew with cellular mode during directional solidification process, while like-dendrite mode of grains growth was observed in the alloys with higher contents of 0.5 at% due to the dragging effect of precipitates on the boundaries. The NbC precipitates disperse both inside grains and along the boundaries of $Fe_{83}Ga_{17}$ alloys with NbC addition, and the Fe2B secondary phase particles preferentially distribute along the grain boundaries in B-doped alloys. Precipitates could affect grain growth and improved the <100> orientation during directional solidification process. Small amount of precipitate element addition slightly increased the magnetostrictive strain, and a high value of 335 ppm under pre-stress of 15 MPa was achieved in the alloys with 0.1 at% NbC. Despite the fact that the effect on magnetic induction density of small amount of precipitates could be negligible, the coercivity markedly increased with addition of precipitate element for $Fe_{83}Ga_{17}$ alloy due to the retarded domain motion resulted by precipitates.

• Journal of Veterinary Clinics
• /
• v.28 no.3
• /
• pp.332-335
• /
• 2011

A 6-year-old castrated male domestic short hair cat with the clinical signs of anorexia and vomiting was admitted to the local animal hospital. Abdominal radiography and ultrasonography revealed renomegaly and severe hydronephrosis in the right kidney. Surgically excised right kidney was submitted for diagnosis. On the cut surface, two milky white masses and severe dilation of renal pelvis were observed. Most of the neoplastic masses were composed of uniform well differentiated tubules lined by a single layer of cuboidal to columnar cells and projected papillae into the lumen. The neoplastic cells were strong positive for cytokeratin (CK) MNF116, but negative for CK 7. Based on the clinical and gross findings, histopathology and immunohistochemistry, this case was diagnosed as papillary renal adenoma with hydronephrosis.

• Korean Journal of Veterinary Research
• /
• v.49 no.1
• /
• pp.67-71
• /
• 2009

A 10-year old female Yorkshire terrier with nasal discharge and swelling was referred to the local animal hospital. Abnormal mass of right nasal cavity was detected in physical examination and radiography. According to the radiographs of the head, there was an evidence of bony destruction in right nose. Oronasal fistula was detected in right maxillary canine teeth. After surgical excision, the sample of nasal mass was refereed to Pathology Department of Veterinary Medicine in Jeju National University. Grossly, the enlarged mass was soft and 3 ${\times}$ 3 cm in size. Histopathologically, the neoplastic mass was composed of tubular to tubulopapillary structures which were lined by single to 6~7 layers of cuboidal to ciliated columnar cells. These neoplastic cells showed invasive tendency to adjacent normal parenchyma. They had uniform, round to oval nuclei, cytoplasm with small vacuoles and indistinct cellular margin. The number of mitotic figures was varied in different areas, ranged from 0 to 4 per high power field. Necrotic foci and infiltration of inflammatory cells including neutrophils, lymphocytes, and plasma cells also presented in the mass. Immunohistochemically, the neoplastic cells demonstrated strong positive reaction for cytokeratin (CK) 18 but were negative for CK 7 and 8. Based on the gross, histopathology and immunohistochemistry, this mass was diagnosed as nasal adenocarcinoma originated from respiratory epithelium.