• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.1
• /
• pp.38-49
• /
• 2000

The purpose of this study was to evaluate the effects of thermocycling on the shear bond strength of Co-Cr alloy to denture base resin. PMMA denture base resin such as heat-cured $Vertex-RS^{(R)}$, self-cured $Vertex-SC^{(R)}$ and 4-META denture base resin such as heat-cured $Meta-Dent^{(R)}$, self-cured $Meta-Fast^{(R)}$ was bonded to Co-Cr alloy. Samples were divided into 3 groups : no thermocycling group as control, thermocycling between $5^{\circ}C\;and\;55^{\circ}C$ with 15 second dwell time as group 1, thermocycling with 1 minute dwell time as group 2. The shear bond strength was measured and the interface between metal and resin was observed by SEM. The results were as follows. 1. The shear bond strength decreased significantly according to thermocycling and dwell time(P<0.001). 2. The bond strength of Co-Cr alloy and 4-META denture base resin was significantly higher than that of Co-Cr alloy and PMMA denture base resin(P<0.001) 3. In SEM, there was no gap in control group, but there was much and large gap in group 1, 2. The longer dwell times, the lower bond strength. PMMA denture base resin had more gap than 4-META denture base resin in the interface. These results revealed that thermocycling decreased the bond strength between Co-Cr alloy and denture base resin and dwell time of thermocycling changed the effect of thermocycling. The results suggested that oral temperature change affect the bond strength of prosthesis.

• Biomaterials Research
• /
• v.22 no.4
• /
• pp.259-270
• /
• 2018

Background: Total hip arthroplasty (THA) is probably one of the most successful surgical interventions performed in medicine. Through the revolution of hip arthroplasty by principles of low friction arthroplasty was introduced by Sir John Charnley in 1960s. Thereafter, new bearing materials, fixation methods, and new designs has been improved. The main concern regarding failure of THA has been the biological response to particulate polyethylene debris generated by conventional metal on polyethylene bearing surfaces leading to osteolysis and aseptic loosening of the prosthesis. To resolve these problems, the materials of the modern THA were developed since then. Methods: A literature search strategy was conducted using various search terms in PUBMED. The highest quality articles that met the inclusion criteria and best answered the topics of focus of this review were selected. Key search terms included 'total hip arthroplasty', 'biomaterials', 'stainless steel', 'cobalt-chromium', 'titanium', 'polyethylene', and 'ceramic'. Results: The initial search retrieved 6921 articles. Thirty-two articles were selected and used in the review. Conclusion: This article introduces biomaterials used in THA and discusses various bearing materials in currentclinical use in THA as well as the newer biomaterials which may even further decrease wear and improve THA survivorship.

• Transactions of the Korean hydrogen and new energy society
• /
• v.5 no.1
• /
• pp.1-8
• /
• 1994

Lattice structure, hydrogen absorption characteristics, discharge capacity and cycle life of $V_{22}Ti_{16}Zr_{16}Ni_{39}X_7$(X= Cr, Co, Fe, Mn, Al) alloys were investigated. The matrix phases of these alloys were the C14 Laves phase. Chromium-containing alloy had a vanadium-rich phase in addition to the Laves phase. The chromium, maganese, or aluminum-containing alloys had lower hydrogen equilibrium pressure and larger hydrogen absorption content than the cobalt or iron-containing alloys. The discharge capacities of these alloys were 270~330mAh/g. The discharge capacity according to the alloying element X decreased in the order of Mn>Cr>Co, Al)Fe. The charge/discharge cycle lives of the chromium, cobalt or iron-containing alloys were longer than those of maganese or aluminum-containing alloys due to the lower vanadium dissolution rate.

• Journal of Technologic Dentistry
• /
• v.18 no.1
• /
• pp.15-25
• /
• 1996

This study is to measure and compare the hardness and tensile strength of each time after we recast seven times continually only with and metal alloy Chromium-Cobalt alloy used in the production of partial denture frame work. The result of the experiment were as follow; 1) The result of the hardness measurement The result of the first casting was $490.48{\pm}38.38$ and that of the second recasting was $455.18{\pm}35.61$ and form the third recasting. the result were $518.38{\pm}37.68$ and over. The change of the hardness difference between each recasting was as follow; The hardness difference between the first casting and the second recasting was $35.25{\pm}31.93$ and that between the second recasting and the third recasting was $63.20{\pm}54.02$. There was a statistically significant difference(P<0.01) in the above hardness, however, there was little difference on the whole. And after the third recasting, the hardness grew high a little bit. That is why low-melting metals such as Cr, Mn, Cu of alloy ingredient was evaporated or there was an effect of changes in metal crystal structure, I suppose. 2) The result of the tensile strength measurement. There was a statistically significant difference(P<0.01) between the first casting and the second, the fourth recasting, however. there was little difference in general.

• Applied Chemistry for Engineering
• /
• v.17 no.2
• /
• pp.150-157
• /
• 2006

The alternate plating method was suggested by a tin-cobalt alloy plating process which has excellent mechanical characteristics and also favorable to environment. Tin-cobalt alloy plating has many advantages such as nontoxicity, variable color-tone, and no post-treatment process. In this study, the plating conditions such as temperature, pH, current density, plating time, and amount of additive (glycine) were determined in the tin-cobalt alloy plating process through Hull-cell test and surface analysis. As the result of Hull-cell analysis, brightness became superior as the amount of glycine increased. It was found that the optimum alloy ratio was 0.03 M of $SnCl_{2}{\cdot}2H_{2}O$ and 0.05 M of $CoSO_{4}{\cdot}7H_{2}O$ at $50^{\circ}C$, pH 8.5, and $0.5A/dm^2$. The optimum amount of additive was 15 g/L of glycine and 0.1 g/L of organic acid. Then, the solution including glycine was recommended as an optimum plating solution for a chromium plating process.

• The Journal of Korean Academy of Prosthodontics
• /
• v.43 no.2
• /
• pp.218-231
• /
• 2005

Statement of problem. In the partially edentulous patients, removable partial dentures have been working as a important treatment modality. Clasps, a kind of direct retainers, received some amount of stresses during the insertion and removal of partial denture on the abutment tooth. Purpose. The study is to investigate stresses of the different clasps. Material and methods. In order to investigate the degree of stresses, maxillary partial edentulism (Kennedy Class II modification I) was assumed and removable partial dentures were designed on it with three kinds of metallic materials; cobalt-chromium alloy, type IV gold alloy and commercially pure (c.p.) titanium. Aker's clasp was applied on the left second molar. RPA (mesial rest-proximal plate-Aker's) clasp was on the left first premolar and wrought wire clasp was on the right first premolar. Three dimensional, non-linear, dynamic finite element analysis method was run to solve this process. Results. 1. Cobalt-chromium alloy had the highest von Mises stress value and c.p. titanium had the lowest one irrespective of the types of clasps. 2. In the Aker's clasps, stress on the retentive tips was shown shortly after the appearance of stresses of the middle and minor connector areas. These time lag was much shorter in the RPA clasps than in the Aker's clasp. 3. In general. retentive tips of wrought wire clasps had much less amount of stress than other clasps. Conclusion. The amount of stress was the highest in the RPA clasp and the lowest in the wrought wire clasp, in general.

• Journal of Technologic Dentistry
• /
• v.45 no.4
• /
• pp.87-94
• /
• 2023

Purpose: This study aimed to observed changes in the shape of dental barrels based on application time. Machinability measures the angle of alloy specimens. Polishing performance measures the surface roughness of alloy specimens. Methods: The dental barrel polishing equipment used in this study was a Snow Barrel (DK Mungyo). Three types of cobalt-chromium alloys for partial dentures were used as specimens (BC CAST R [BP]; Bukwang, Vera PDI [VP]; Aalbadent, and GM 800+ [GP]; Dentaurum). Specimens were prepared in the form of plates (10 mmx10 mmx2 mm). Dental barrel polishing was performed at 450 rpm for 60 minutes with intervals of 5 minutes. The processing angle was measured using a microscope (SZ61; Olympus). Results: For the angle measurement, the VPC specimen was measured at 78.64°, 36.00° for the VP60 specimen, 79.57° for the BP control (BPC) specimen, 28.07° for the BP60 specimen, 75.01° for the GPC specimen, and 39.92° for the GP60 specimen. For the surface roughness measurements, the average surface roughness of the VPC and VP15 specimens were 1.09 ㎛ and 0.26 ㎛, respectively. The average surface roughness of the BPC and BP20 specimens were 1.77 ㎛ and 0.29 ㎛, respectively. The average surface roughness of the GPC and GP15 specimens were 1.08 ㎛ and 0.27 ㎛. Conclusion: The results were excellent after about 20 minutes of dental barrel polishing conditions presented in this study.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.4
• /
• pp.510-525
• /
• 2000

The effects of pretreatment of Co-Cr alloy, including two adhesive primers that contain either MDP or MAC-10, and silicoating on the bond The result sobtained as follows; o Strength of 4-META/MMA-TBB resin were investigated using FT-IR, SEM, and EDAX. o In the SEM observation of surface morphologies, the sandblasted specimen exibited a very rough surface, whereas the surfaces of the two groups primed with either MDP or MAC-10 were covered with a layer of primer, and the surface morphology of the silicoated specimen remained almost the same after sandblasting. o Before the thermocycling tests, the group treated with MDP demonstrated the highest mean tensile bond strength and the sandblasted group showed the lowest bond strength. o After 20,000 thermocyling, the mean tensile bond strength of the sandblasted group exhibited a 50% reduction in bond strength, while the others showed a $20\sim30%$ reduction. o Observation of the metal-resin interface revealed that in all groups the resin permeated the rough surface formed by sandblasting thereby producing a mechanical bond between the metal and the resin. It was also found that thermocycling resulted in a gap formation at the metal-resin interface of the specimens, and the sandblasted group exhibited a larger gap width than the other groups. o In fracture mode, all specimens indicated a cohesive fracture within the resin before thermocycling. However, thermocyling produced adhesive failure at the edge of the resin-metal interface in most specimens. The sandblasted group, which exhibited the lowest bond strength after thormocycling, also demonstrated the largest area of adhesive failure.

• Korean Journal of Materials Research
• /
• v.10 no.12
• /
• pp.831-837
• /
• 2000

To improve the catalytic activity of platinum on polymer electrolyte fuel cell(PEFC), platinum was alloyed with cobalt and nickel at various temperature. By XRD, it was observed the crystal structure of alloy catalysts were the ordered face centered cubic(f.c.c) due to the superlattice line at $33^{\circ}$. As heat-treatment temperature was increased, the particle size of alloys also were increased and the crystalline lattice parameters were decreased. According to the results from mass activity, specific activity and Tafel slope measured by cell performance test and cyclic voltammogram, the catalyst activities of alloys are higher than that pure platinum.

• Journal of the Korean Society of Radiology
• /
• v.17 no.1
• /
• pp.25-30
• /
• 2023

As 3D printing technology is used in the medical field, interest in metal materials is increasing. The Department of Radiation Oncology uses a shielding block to shield the patient's normal tissue from unnecessary exposure during electron beam therapy. However, problems such as handling of heavy metal materials such as lead and cadmium, reproducibility according to skill level and uncertainty of arrangement have been reported. In this study, candidate materials that can be used for metal 3D printing are selected, and the physical properties and radiation dose of each material are analyzed to develop a customized shielding block that can be used in electron beam therapy. As candidate materials, aluminum alloy (d = 2.68 g/cm³), titanium alloy (d = 4.42 g/cm³), and cobalt chromium alloy (d = 8.3 g/cm³) were selected. The thickness of the 95% shielding rate point was derived using the Monte Carlo Simulation with the irradiation surface and 6, 9, 12, and 16 energies. As a result of the simulation, among the metal 3D printing materials, cobalt chromium alloy (d = 8.3 g/cm³) was similar to the existing shielding block (d = 9.4 g/cm³) in shielding thickness for each energy. In a follow-on study, it is necessary to evaluate the usefulness in clinical practice using customized shielding blocks made by metal 3D printing and to verify experiments through various radiation treatment plan conditions.