• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05a
• /
• pp.38-41
• /
• 2003

상업용 Ag 판재 위에 cyclic 전위와 일정 전위를 인가하는 전기증착법으로 Tl-1223상 precursor 막을 증착하는 연구를 수행한 다음, 이를 이영역 전기로를 사용하여 열처리함으로써 고온초전도 coated conductors를 제조하는 연구를 수행하였다. 전기증착법으로 비교적 균질하고 치밀한 precursor막을 증착할 수 있었으며, 이 막을 $870^{\circ}C$에서 20분 동안 열처리하여 임계온도가 114 K이고 자속고정능력도 비교적 우수한 50%의 Tl-1223상과 50%의 Tl-1212상으로 구성된 고온초전도 도체를 제조할 수 있었다. 이로부터 아주 값싼 증착법인 전기증착법을 이용하여 후막의 고온초전도 도체를 제조할 수 있음을 증명하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.236-237
• /
• 2007

Lamination of coated conductor is important to commercialize for electrical stabilizer and mechanical support. It should be known the properties of soldering interface and the variation of superconductivity on coated conductor with various kinds of solders. $SmBa_2Cu_O_x$ thin films were deposited by co-evaporation method (EDDC, Evaporation using Drum in Dual Chambers). 4 kinds of solders were used to investigate interface properties of SmBCO conductors. In-Bi solder could maintain good connection.

• Progress in Superconductivity and Cryogenics
• /
• v.9 no.1
• /
• pp.47-52
• /
• 2007

This paper presents characteristics analysis of persistent current switch(PCS) system on a small scale by using YBCO coated conductor(CC). A high temperature superconductor(HTS) PCS system mainly consists of a PCS, a HTS magnet load and a magnet power supply(MPS). To design the optimal heater triggering switch. the three-dimensional heat conduction model was analyzed by finite element method(FEM). The electrical equivalent model considering the n-value of CC was applied to analyze current decay during persistent current mode. In the experiment and simulation, the heater was applied with a current of 0.43A and the current was ramped up to 10A and 20A with 0.2A/s. Finally, experimental results of the HTS PCS system have been compared with the theoretical results. It has been concluded that flux creep can not influence the results because the operating current was 40% of critical current and optimal sequential operation of the PCS system is indispensable to enhance its performance.

• Progress in Superconductivity and Cryogenics
• /
• v.9 no.3
• /
• pp.21-25
• /
• 2007

Superconducting fault current limiter (SFCL) is attractive apparatus to reduce fault current in power grid. Since it is applied to the alternating current (AC) power line, the SFCL has losses in the normal operation. Recently, coated conductor (CC) is noticeable material employed for resistive bifilar winding type SFCL in many research groups. Bifilar structure is expected to have low AC loss by magnetic field offset as compared with the single tape structure in the same length. This paper reports about characteristic of bifilar pancake type coil for SFCL application in AC loss aspect. The bifilar coil is wound using CC with facing on HTS sides each other. Transport AC loss measurement and characteristic analysis of the bifilar coil using CC have been performed at 77K. The test results are compared with the Norris equations and the test results of non-inductively wound paralleled solenoid type coil which is suggested and tested in this group at present.

• Progress in Superconductivity and Cryogenics
• /
• v.10 no.3
• /
• pp.23-26
• /
• 2008

Constructions of coated conductor which is differently from Bi-2223 is comprised multiple coatings on a base material or substrate and designed to achieve the highest degree of alignment possibility of the atoms in the superconductor material. In this study, we are measured and analyzed degradations of critical current according to diameter. In addition to study the effects of bending strain, we observed the AC loss of coated conductor and carried out analytical study for relation between Ic degradation and AC loss as well. The measurement of AC loss and numerical calculation was carried out based on Norris theory to compare with experimental results. The relationship between critical current and AC loss of HTS tapes with partial deformation by mechanical stress was studied. These results will amount the most important basis data in the of HTS cable, magnet, etc that winding work is required.

• Progress in Superconductivity and Cryogenics
• /
• v.11 no.1
• /
• pp.1-4
• /
• 2009

Mechanical and electrical properties of silver stabilizer layer of coated conductor, which as prepared with nano silver paste as starting materials, have been investigated, Nano silver paste was coated on a YBCO film by dip coating process at a diping speed of 20m/min. Coated film was dried in air and heat treated at $400{\sim}700^{\circ}C$ in an oxygen atmosphere. Adhesion strength between YBCO and silver layer was measured by a tape est(ASTM D 3359). Hardness and electrical conductivity of the samples were measured by pencil hardness test (ASTM D 3363) and volume resistance test by LORESTA-GP (MITSHUBISHD, respectively. The sample heat-treated at $500^{\circ}C$ showed poor adhesion 1B, but samples heat treated at higher than $600^{\circ}C$ showed enhanced adhesion of 5B. The silver layer heat-treated at $700^{\circ}C$ showed the high hardness value larger than 9 H, low volume resistance, surface resistance value as well as superior current carrying capacity compared to sputtered silver. SEM observations showed that a dense silver layer was formed with a thickness of about $2{\mu}m$. Dip coated silver layer prepared by using nano silver paste showed superior electrical and mechanical characteristics.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2003.02a
• /
• pp.98-100
• /
• 2003

PbTiO$_3$ films applicable to buffer layers for YBCO coated conductor have been successfully fabricated by sol-gel process. Crystallinity of grown films are heavily dependent on processing parameters such as annealing atmosphere and number of dipping. (100) oreinted PbTiO$_3$ films grown on (200) oriented Ni substrates exhibit uniform surface with small grain size(200~300nm).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.22-23
• /
• 2005

In order to increase the critical current of coated conductor, highly Bi-axially textured substrates are required. Texture uniformity of substrate is also important to fabricate high quality superconducting coated conductor because the amount of current flow along the coated conductor is limited by the defects such as bad textured area. Therefore, we need to evaluate the distribution of texture of Ni substrate along the length before buffer layer deposition on Ni tape. R2R(reel-to-reel) XRD system was used to measure the texture of long Ni substrate continuously. $\theta-2\theta$ scan of 10 m long Ni tape was measured and indicates that some of Ni(111) planes equally remain on Ni(002) textured substrate. The results of continuous Ni(220) $\Phi$-scan indicate that average FWHM is 9$^{\circ}$ within $\pm$1.

• Progress in Superconductivity
• /
• v.12 no.2
• /
• pp.118-123
• /
• 2011

The properties of $2^{nd}$ generation high temperature superconducting wire, coated conductor strongly depend on the quality of superconducting oxide layer and property of metal substrate is one of the most important factors affecting the quality of coated conductor. Good mechanical and chemical stability at high temperature are required to maintain the initial integrity during the various process steps required to deposit several layers consisting coated conductor. And substrate need to be nonmagnetic to reduce magnetization loss for ac application. Hastelloy and stainless steel are the most suitable alloys for metal substrate. One of the obstacles in using stainless steel as substrate for coated conductor is its difficulties in making smooth surface inevitable for depositing good IBAD layer. Conventional method involves several steps such as electro polishing, deposition of $Al_2O_3$ and $Y_2O_3$ before IBAD process. Chemical solution deposition method can simplify those steps into one step process having uniformity in large area. In this research, we tried to improve the surface roughness of stainless steel(SUS310). The precursor coating solution was synthesized by using yttrium complex. The viscosity of coating solution and heat treatment condition were optimized for smooth surface. A smooth amorphous $Y_2O_3$ thin film suitable for IBAD process was coated on SUS310 tape. The surface roughness was improved from 40nm to 1.8 nm by 4 coatings. The IBAD-MgO layer deposited on prepared substrate showed good in plane alignment(${\Delta}{\phi}$) of $6.2^{\circ}$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.348-348
• /
• 2009

본 논문에서는 최근 한류용 소자로 널리 이용되고 있는 여러 가지 Coated Conductor들에 대한 렌치 특성을 조사하였다. 이를 위해 전원전압을 증가시키면서 임의의 시간동안 퀜치 특성을 조사하였으며, 이는 한류소자의 한류시간별 가용전압을 산정하는데 있어 중요한 지표가 된다.