• 한국재료학회지
• /
• 제11권11호
• /
• pp.953-959
• /
• 2001

Homogeneous spherical W-Co salt powders were made by spray drying of aqueous solution of ammonium $metatungstate(NH_4)_6(H_2W_{12}O_{40}){\cdot}4H_2O,\; AMT)$ and cobalt nitrate $hexahydrate(Co(NO_3)_2{\cdot}6H_2O)$. The thermal decomposition process of spray dried W-Co salt powders was studied by TG, XRD, SEM, TEM and FT-IR. Spray dried W-Co salt powders were calcined for 1 hour in the temperature from$ 350^{\circ}C$ to $800^{\circ}C$ in atmosphere of air. At the temperatures over $600^{\circ}C$, spherical $CoWO_4/WO_3$ composite oxide powders were obtained. The primary particle size of W/Co composite oxide powders increased with increasing thermal decomposition temperature due to the particle growth. The observed crystallite size by TEM was in the range of 60nm and that of $CoWO_4$ calculated by Scherrer's formula at $800^{\circ}C$ was smaller than 55nm. The crystallite site was identified by XRD and TEM.

• 한국표면공학회지
• /
• 제39권6호
• /
• pp.276-281
• /
• 2006

In order to improve the performance of PPFs (Pre-Plated Frames), a PPF that employed a Cu-Sn alloy instead of conventionally used Ni was developed and then its properties were investigated. It was found that the electoplated Cu-Sn alloy layer was a mixture of uniformly distributed fine crystallites, resulting In better wettability and crack resistance than those of Ni PPF. Moreover, as in Cu/Ni/Pd/Au PPF, migration of copper atoms from the base metal to the top of the Cu/Cu-Sn/Pd/Au PPF surface was not found although the Cu-Sn layer itself contained considerable amount of copper. It was expected that, by using the newly developed Cu-Sn PPF, any possible heat generation and signal interrupt caused by an external electro-magnetic field could be reduced because the Cu-Sn layer was paramagnetic, i.e., nonmagnetic.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2001년도 춘계연구발표회 논문개요집
• /
• pp.110-111
• /
• 2001

• Nuclear Engineering and Technology
• /
• 제53권5호
• /
• pp.1593-1601
• /
• 2021

Oxide dispersion strengthening (ODS) tungsten alloys are highly desirable in irradiation applications. However, how to improve the properties of ODS-tungsten alloys efficiently has been worth studying for a long time. Here we report a nanostructuring approach that achieves W-La₂O₃ alloy with a high level of flexural strength and Vickers hardness at room temperature, which have the maximum value of 581 MPa and 703 Hv, respectively. This method named solution combustion synthesis (SCS) can generate 30 nm coating structures W-La₂O₃ composite powders by using Keggin-type structural polyoxometalates as raw materials in a fast and low-cost process. The composite powder can be fabricated to W-La₂O₃ alloy with an optimal microstructure of submicrometric W grains coexisting with nanometric oxide particles in the grain interior, and a stability interface structure of grain boundaries (GBs) by forming transition zones. The method can be used to prepare new ODS alloys with excellent properties in the future.

• 전기화학회지
• /
• 제6권4호
• /
• pp.236-241
• /
• 2003

Magnetic CoW thin film alloys were electrodeposited from citrate baths to investigate the resulting microstructure and magnetic properties. Deposit tungsten (W) content in the films electrodeposited at $70^{\circ}C$ were independent of current density, while coercivity decreased from hard $(H_{c,//}\~150\;Oe\;and\;H_{c.{\bot}}\;\~240\;Oe)$ to soft magnetic properties $(H_{c,//}\~20\;Oe\;and\;H_{c.{\bot}}\;\~30\;Oe)$ with increasing current densities from $10\;to\;100mA{\cdot}cm^2$, with deposit W content $(\~40\%)$ relatively unaffected by the applied current density. X-ray diffraction analysis indicated that hcp $Co_3W$ phases [(200), (201) and (220) planes] in the CoW films electrodeposited at $70^{\circ}C\;and\;10mA{\cdot}cm^{-2}$ were dominant, whereas amorphous CoW phases with small amount of hcp $Co_3W$ [(002) planes] were dominant with deposition at $70^{\circ}C\;and\;100mA{\cdot}cm^{-2}$. At intermediate current densities $(25\;and\;50mA{\cdot}cm^{-2}),\;hop\;Co_3W$ phases [(200), (002), (201) and (220)] were observed. The average grain size was measured to be 30 nm from Sheller formula. It is suggested that the change of the deposit coercivities in the CoW thin films electrodeposited at $70^{\circ}C$ is attributed to the change of microstructures with varying the current density. Nanostructured $Co_3W/amorphous-CoW$ multilayers were fabricated by alternating current density between 10 and $100 mA{\cdot}cm^{-2}$, varying the individual layer thickness. The magnetic properties of $Co_3W/amorphous-CoW$ multilayers were strongly dependent on the thickness of the alternating hard and soft magnetic thin films. The nanostructured $Co_3W/amorphous-CoW$ multilayers exhibited a shift from low to high coercivities suggesting a strong coupling effect.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2013년도 임시총회 및 하계학술연구발표회
• /
• pp.15-16
• /
• 2013

Magnetization behavior of ultra thin $Fe_xCo_{1-x}$ alloy (where x varies from 0 to 100) has been investigated as functions of composition on Cr (100) substrate by using in situ surface magneto optical Kerr effect (SMOKE). It's always show in plane uniaxial magnetic anisotropy at room temperature (RT) & Low temperature (LT). It is observed that composition dependent coercive force maximum at about 30 at % Co and 70 at % Co atomic ratio and minimum near equiatomic site. The relative magnetic moments as composition variation also show magnetization collapse near equiatomic site. The magnetization behaviors of Fe-Co alloy on Cr (100) due to composition varies are supported the order-disordering as well as structural stability bcc (ferromagnetic)/fcc (anti-ferromagnetic) phase stability magnetism.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.650-651
• /
• 2006

This paper presents a study of large grains by transmission electron microscopy in two WC-Co alloys, one W rich and one C rich. In the W rich alloy, some large grains are found in contact with the $\eta$ phase. The C content influences the morphology of large grains: they are flatter in the C rich alloy with smoother interfaces. Whatever the C content, they contain few dislocations compared to matrix grains except often in a small area. Small WC grains are often found inside the large grains. They have likely been engulfed during the growth of the large grains owing to the low boundary energy.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제50권1호
• /
• pp.11-16
• /
• 2001

CuNi alloy films are deposited by co-sputtering of dual targets (Cu and Ni, respectively). Effects of the co-sputtering conditions, such as powers applied to the targets, deposition pressures, and substrate temperatures, on the structural and electrical properties of deposited films are systematically investigated. The composition ratio of Ni/Cu is almost linearly decreased by increasing the DC power applied to the Cu target from 25.6 W to 69.7 W with the RF power applied to the Ni target unchanged(140 W). it is noted that the chamber pressure during deposition and the film thickness give rise to a change of the Ni/Cu ratio within the films deposited. The former may be due to a higher sputtering yield of Cu atom and the latter due to the re-sputtering phenomenon of Cu atoms on the surface of deposited film. The film deposited at higher pressures or at lower substrate temperatures have a smaller crystallite size, a higher electrical resistivity, and much more voids. This may be attributed to a lower surface mobility of sputtered atoms over the substrate.

• 한국자기학회지
• /
• 제10권2호
• /
• pp.54-61
• /
• 2000

마그네트론 스퍼터를 사용하여 증착한 CoNbZr 합금박막의 제조 조건 및 열처리에 따르는 구조 및 자기적 성질의 변화를 연구하였다. Ar분압 2mTorr, RF 인가전력 130 W에서 증착되어진 $Co_{87.0}$N $b_{8.5}$Z $r_{4.5}$막은 최대 비저항 3000 $\mu$Ω.cm을 나타냄으로써 가장 안정한 비정질상을 형성하였으며 100 MHz에서 1095의 최대투자율, 1.75 Oe의 최소 보자력을 나타내었다. Ar 분압이 2 mTorr 이상으로 증가할 경우 그리고 RF 인가전력이 130 W 이상으로 증가할 경우 주상정 구조의 발달과 불안정한 비정질상의 형성으로 투자율은 감소하고 보자력은 증가하는 것을 확인하였다 1 mTorr에서 증착되어진 막과 190 W에서 증착되어진 막은 결정질 상을 형성하여 100 이하의 낮은 투자율과 60 Oe의 높은 보자력을 나타내었다. 회전자장중 열처리에 의해 이방성을 제어할 수 있음을 확인하였으며, 증착상태에서 보였던 1095의 투자율은 1345로 증가하였다.증가하였다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1995년도 하계학술대회 논문집 C
• /
• pp.1165-1167
• /
• 1995

The Cu-Si alloy has been proposed as a new matrix materal for filamentary Nb-Ti wires in AC use. The Cu-Si alloy shows approprite mechanical and electrical properties, and is economically more favourable than the Cu-Ni alloy matrix used currently. Moreover, the addition of Si to Cu prevents the formation of intermetallic compounds around the filaments. After we investigated resistivity and hardness of Cu-Si alloy as matrix materal, investigated CuSi/NbTi interface reactions and superconductivities of superconducting wires that were made by various heat treatment.