We have investigated the magnetoresistance (MR) effect of the spin valve structures composed of perpendicularly magnetized Pd/Co multilayers, with changing the space layer (Pd or Cu) thickness, the stacking number of the Pd/Co multilayers, and the Co insertion-layer thickness. The Cu space layer showed larger MR ratio than the Pd space layer. The Co insertion-layer between Cu layer and pinned layer enhanced the MR ratio about three times. The maximum MR ratio of 7.4 % was established in the sample with the Co insertion-layer thickness of 0.62 and 1.01 nm.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.5
• /
• pp.421-426
• /
• 2008

The magnetic bio-sensor used the PHR (planar hall resistance) effect generated by the free layer in spin-valve giant magnetoresistance structure of Ta/NiFe/CoFe/Cu/NiFe/IrMn/Ta. The PHR element with micrometer size was fabricated through the photolithograph and dry etching process. The PHR signal with magnetic field was measured under the conditions of with and without single magnetic bead. A single magnetic bead of diameter $2.8\;{\mu}m$ was successfully detected using the PHR sensor. Therefore, the high resolution PHR sensor can be applied to bio-sensor application utilizing the output voltage variation of the PHR signals in the presence and absence of a single magnetic bead.

• Journal of the Korean Magnetics Society
• /
• v.15 no.2
• /
• pp.61-66
• /
• 2005

In order to make submicron cell for spin-injection device, lift-off method using Pt stencil and wet etching was chosen. This approach allows batch fabrication of stencil substrate with electron-beam lithography. It simplifies the process between magnetic film stack deposition and final device testing, thus enabling rapid turnaround in sample fabrication. Submicron junctions with size of $200nm{\times}300nm$ and $500nm{\times}500nm$ 500 nm and pseudo spin valve structure of $CoFe(30{\AA})/Cu(100{\AA})/CoFe(120{\AA}$) was deposited into the nanojunctions. MR ratio was 0.8 and $1.1{\%}$, respectively and spin transfer effect was confirmed with critical current of $7.65{\times}10^7A/cm^2$.

• Journal of the Korean Magnetics Society
• /
• v.27 no.3
• /
• pp.82-86
• /
• 2017

The IrMn based GMR-SV films with three different buffer layers were prepared on Corning glass by using ion beam deposition and DC magnetron sputtering method. The major and minor magnetoresistance curves for three different buffer layers beneath the structure of NiFe(15 nm)/CoFe(5 nm)/Cu(2.5 nm)/CoFe(5 nm)/NiFe(7 nm)/IrMn(10 nm)/Ta(5 nm) at room temperature have shown different magnetoresistance properties. When the samples were annealed at $250^{\circ}C$ in vacuum, the magnetoresistance ratio, the coercivity of pinned ferromagnetic layer, and the interlayer coupling field of free ferromagnetic layer were enhanced while the exchange bias coupling field did not show noticeable changes.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.23 no.4
• /
• pp.322-327
• /
• 2003

Giant magnetoresistance(GMR) NiO multilayer, which has been used to reading head of highly dense magnetic recording, was fabricated, and oxidized in an air during 80 days to study the dependence of magnetoresistance properties on residual stress in the interfaces. The magnetoresistance ratio and the exchange biasing $field(H_{ex})$ of $NiO(60nm)/Ni_{81}Fe_{19}(5nm)/Co(0.7nm)/Cu(2nm)/Co(0.7nm)/Ni_{81}Fe_{19}(7nm)$ spin valves were increased from 4.9% to 7.3%, and 110 Oe to 170 Oe after natural oxidation in the atmosphere for 80 days, respectively. The sheet resistivity ${\rho}$ decreased from $28{\mu}{\Omega}m$ to $17{\mu}{\Omega}m$, but ${\Delta}p$ did not almost change after the oxidation. Therefore, the increase of MR ratio is due to the decrease in the sheet resistivity. the reduced resistance may result from the increase in the reflection of conduction electrons at the oxidized top surface. Also, the increase in the exchange biasing field is originated from the reduction of residual stress at the interface of $NiO/Ni_{81}Fe_{19}$ according as the aging time increases.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2002.12a
• /
• pp.158-159
• /
• 2002

스핀 밸브에서는 NiFe, CoFe, Cu등 주요 금속들이 면심입방체(111)로 배향이 용이하지만, 자기 터널 접합 소자에서는 $Al_2$O$_3$ 장벽층이 비정질로서 상부 강자성 전극이 충분히 (111) 배향을 할 수 없기 때문에 top bias 방식의 사용이 거의 불가능하며, bottom bias의 경우에도 교환 바이어스의 크기는 상대적으로 작다[1]. 이를 극복하기 위해 인공 초격자를 이용한 인공 반강자성층(synthetic antiferromagnet - SAF)을 이용하여 높은 교환 바이어스 효과를 구현하고자 하였다. (중략)

• Journal of the Korean Magnetics Society
• /
• v.10 no.2
• /
• pp.62-66
• /
• 2000

Annealing cycle number and nonmagnetic layer thickness dependences of interlayer coupling field ( $H_{inf}$ ) and coercivity ( $H_{cf}$ ) of free magnetic layer on NiMn alloy-spin valve films (SVF) were investigated. The SVF is Glass (7059)/N $i_{81}$F $e_{l9}$(70 $\AA$)/Co(10 $\AA$)/Cu(t $\AA$)/Co(15 $\AA$)N $i_{81}$$Fe_{19}$(35 $\AA$)/N $i_{25}$M $n_{75}$(250 $\AA$)Ta(50 $\AA$) films, it were fabricated using the dc sputtering method at different pinning layer thickness and nonmagnetic spacer thickness (Cu thickness; 30 $\AA$, 35 $\AA$, 40 $\AA$) of NiMn alloy with 25 at.%. Ni In case that Cu thickness of SVF is 35 $\AA$ and peak exchange coupling field ( $H_{ex}$) was 620 Oe, while coercivity $H_{c}$ = 280 Oe and MR ratio showed 2.5%. As for $H_{inf}$ and $H_{cf}$ , every SVF increased up to the stabilized values with the increase of annealing cycle number 15, which were $H_{inf}$ of 120 Oe and $H_{cf}$ of 75 Oe. The increase of $H_{cf}$ with the annealing cycle number seems to be caused by the effective reduction of Cu layer thickness due to the increase of interfacial mixing of Cu layer and Co layer. In addition, the $H_{inf}$ and $H_{cf}$ dependences of free NiFe layer by the interfacial mixing effect were appeared the different aspects when Cu layer becomes more thinner and thicker than Cu layer thickness of 35 $\AA$, respectively.ively....