• Journal of the Korea Institute of Building Construction
• /
• v.24 no.1
• /
• pp.11-21
• /
• 2024

This research elucidates the fundamental properties of carbon dioxide (CO₂)-cured mortar as influenced by varying substitution rates of blast furnace slag fine powder. The findings indicate that CO₂ curing enhances the formation of calcium carbonate (CaCO₃), contributing to pore reduction and the early development of strength. While calcium hydroxide (Ca(OH)₂) plays a more pivotal role in the primary development of strength compared to CaCO₃, an increase in the substitution rate of blast furnace slag fine powder results in reduced production of Ca(OH)₂. Nonetheless, the maintenance of strength through CaCO₃ formation is observed even after the depletion of Ca(OH)₂, suggesting that the required performance can be sustained post-exposure to the atmosphere following CO₂ curing. It is noted that substitution rates exceeding 50% lead to performance deterioration due to CO₂, highlighting the necessity for careful adjustment of the substitution ratio.

• Journal of the Korean Ceramic Society
• /
• v.49 no.1
• /
• pp.118-123
• /
• 2012

GDC20($Ce_{0.8}Gd_{0.2}O_{1.9}$) powder was synthesized from Ce and Gd nitrate solutions using ammonium carbonate($(NH_4)_2CO_3$) as a precipitant. Attrition-milling of the powder, which had been calcined at $700^{\circ}C$ for 4 h, decreased an average particle size of 2.2 ${\mu}m$ to 0.5 ${\mu}m$. The milled powder consisted of nano-sized spherical primary particles. Due to the excellent sinterability of the powder, sintering of the powder compacts for 4 h showed relative densities of 80% at 1000 $^{\circ}C$ and 96.5% at $1200^{\circ}C$, respectively. Densification was found to almost complete at $1300^{\circ}C$, resulting in a dense and homogeneous microstructure with a relative density of 99.5%. The grains of ~0.2 ${\mu}m$ in size at $1200^{\circ}C$ grew to ~1 ${\mu}m$ in size at $1300^{\circ}C$ as a result of a rapid grain growth.

• Journal of Korea Foundry Society
• /
• v.23 no.5
• /
• pp.235-243
• /
• 2003

The collapsibility of sodium silicate-bonded sands mixed with the L.D converter slag powder to form a hardener were investigated. Five to six percent sodium silicate on the basis of silica sand and 30-40% L.D converter slag powder on the basis of sodium silicate, were mixed and the compressive strength, surface stability index(SSI), bench time, retained strength of the standard sand specimens were measured. The properties were similar to those of general inorganic bonded self-setting molds. The compressive strength and surface stability index were increased and the retained strength and bench time were decreased with increased amount of the L.D converter slag powder. The retained strength of sodium silicate-bonded self-setting molds with the L.D converter slag powder were decreased than $CO_2$ sand molds. The collapsibility of sodium silicate-bonded self-setting molds with the L.D converter slag powder were superior in comparison with $CO_2$ sand molds. The L.D converter slag powder could be used as hardener and collapse agent for the sodium silicate-bonded self-setting molds.

• Bulletin of the Korean Chemical Society
• /
• v.20 no.5
• /
• pp.508-516
• /
• 1999

Polycrystalline powder of LixNi0.85Co0.15O2 was synthesized by pyrolyzing a powder precursor obtained by the PVA-precursor method. Coin cells of lithium-ion rechargeable battery were assembled, whose the cathodes were fabricated from the crystalline powders of LixNi0.85Co0.15O2 synthesized by the method. The effect of synthetic variation on the property of the cell was tested by carrying out 100 consecutive cycles of charge-dis-charge on the cells. The property of the cell was largely influenced by the pyrolysis conditions applied for the synthesis of the LixNi0.85Co0.15O2. Depending on whether the pyrolysis was carried out in standing air or in the flow of dry air, the discharge capacity and cycle-reversibility of the cell varied in large extent. When the powder precursor was pyrolyzed in standing air, a minor phase of lithium carbonate was remained in the LixNi0.85Co0.15O2. The carbon containing powder precursor had to be pyrolyzed in the flow of dry air to eliminate the minor phase. In the flow of dry air, the lithium carbonate in the precursor was eliminated over 500-700。C without any prominent heat event. By controlling the flow of air over the precursor during its pyrolysis, particle size could also be altered. The effect of flowing dry air, during first step pyrolysis or during second step heat treatment, on the property of the cell was discussed.

• International Journal of Industrial Entomology and Biomaterials
• /
• v.48 no.2
• /
• pp.59-66
• /
• 2024

The mature Bombyx mori silkworm is recognized as a rich source of several nutrients. A unique steaming process has been developed to enhance the palatability of Bombyx mori silkworm and make it more convenient to consume. Additionally, it has also been freeze-dried into a powder form, which is recognized as a nutritional supplement with many health benefits. Steamed and Freeze-dried Mature Silkworm Powder (SMSP) is said to offer a wide range of benefits, including longevity, improved athletic performance, prevention of alcohol-induced liver fibrosis or tumors, amelioration of fatty liver, prevention of peptic ulcers, regulation of melanin production, and mitigation of Parkinson's and Alzheimer's diseases by improving cognitive function. The nutritional composition of SMSP is particularly high in glycine, alanine and serine. This review aims to summarize the molecular mechanisms underlying the diverse effects induced by these key components of SMSP. Such elucidation will enhance the credibility of future studies on SMSP, which will require more comprehensive analyses. It appears that SMSP represents a natural health supplement that could have a positive impact on global human health while increasing income.

• Journal of Powder Materials
• /
• v.10 no.1
• /
• pp.6-14
• /
• 2003

The purpose of the present study is to investigate the method decreasing debinding time as well as lowering operation condition than pure supercritical $CO_2$ debinding by using cosolvent or binary mixture of propane + $CO_2$. First method is to add cosolvent, such as n-hexane, DCM, methanol, 1-butanol, in supercritical $CO_2$. In case of adding cosolvent, we were found the addition of non-polar cosolvent (n-hexane) improves dramatically the binder removal rate (more than 2 times) compared with pure supercritical $CO_2$ debinding, second method is to use mixture of supercritical propane + $CO_2$, as solvent. In case of using mixture of supercritical propane + $CO_2$, the rate of debinding speeded up with increasing of pressure and concentration of propane at 348.15 K. It was found that addition of cosolvent (e.g., n-hexane, DCM) and binary mixture propane + $CO_2$ for supercritical solvent remarkably improved binder removal rate for the paraffin wax-based binder system, in comparison with using pure supercritical $CO_2$.

• Journal of Powder Materials
• /
• v.5 no.4
• /
• pp.334-339
• /
• 1998

In purpose of introducing the inverse magnetostrictive properties into the structural ceramics, $Al_2O_3$ based nanocomposites dispersed with nano-sized Ni-Co particles were studied. The composites were fabricated by the hydrogen reduction and hot-pressing of $Al_2O_3$ and NiO-CoO mixed powders. The mixtures were prepared by using Ni- and Co-nitrate $(Ni(NO_3)_2\;{\cdot}\;6H_2O\;and\;Co(NO_3)_2\;{\cdot}\6H_2O)$ as source materials for the Ni-Co particles. Microstructural observations revealed that nano-sized Ni-Co particles were dispersed homogeneously at $Al_2O_3$ grain boundaries. High strength above 1 GPa was obtained for the $Al_2O_3/10$ wt% Ni-Co nanocomposite fabricated by a controlled powder preparation process. The inverse magnetostrictive response to applied stress was obtained due to the presence of dispersed Ni-Co particles, which indicates a possibility to incorporate new functions into the structural ceramics without loosing the mechanical properties.

• Journal of Powder Materials
• /
• v.9 no.3
• /
• pp.167-173
• /
• 2002

A new approach to produce nanostructured WC/Co composite powders by a mechanochemical process was made to improve the mechanical properties of advanced hardmetals. Homogeneous spherical W-Co salt powders were made by spray drying of aqueous solution from ammonium metatungstate($(NH_4)_6(H_2W_{12}O_{40})\cdo4H_2O$,AMT) and cobalt nitrate hexahydrate (Co(NO$_3$)$_2$.6$H_2O$). spray dried W-Co salt powders were calcined for 1 hr at $700^{\circ}C$ in atmosphere of air. The oxide powder was mixed with carbon black by ball milling and this mixture was heated with various temperatures and times in $H_2$. The $WO_3/CoWO_4$ composite oxide powders were obtained by calcinations at $700^{\circ}C$. The primary particle size of W/Co composite oxide powders by SEM was 100 nm. The reduction/carburization time decreased with increasing temperatures and carbon additions. The average size of WC particle carburized at $800^{\circ}C$ by TEM was smaller than 50 nm.

• Journal of Powder Materials
• /
• v.11 no.2
• /
• pp.124-129
• /
• 2004

Nanosized WC and WC-Co powders were synthesised by chemical vapor condensation(CVC) process using the pyrolysis of tungsten hexacarbonyl(W(CO)$_6$) and cobalt octacarbonyl(Co$_2$(CO)$_8$). The microstructural changes and phase evolution of the CVC powders during post heat-treatment were studied using the XRD, FE-SEM, TEM, and ICP-MS. CVC powders were consisted of the loosely agglomerated sub-stoichimetric WC$_{1-x}$ and the long-chain Co nanopowders. The sub-stochiometric CVC WC and WC-Co powders were carburized using the mixture gas of CH$_4$-H$_2$ in the temperature range of 730-85$0^{\circ}C$. Carbon content of CVC powder controlled by the gas phase carburization at 85$0^{\circ}C$ was well matched with the theoretical carbon sioichiometry of WC, 6.13 wt％. During the gas phase carburization, the particle size of WC increased from 20 nm to 40 nm and the long chain structure of Co powders disappeared.

• Journal of Powder Materials
• /
• v.4 no.2
• /
• pp.90-99
• /
• 1997

Densification behavior and grain growth of tool steel powder compacts during pressureless sintering, sinter forging, and hot isostatic pressing were investigated. Experimental data were compared with results of finite element calculations by using the constitutive model of Abouaf and co-workers and that of McMeeking and co-workers. Densification and deformation of tool steel powder compacts were studied by implementing power-law creep, diffusional creep, and grain growth into the finite element analysis. The shape change of a powder compact in the container during hot isostatic pressing was also studied. The theoretical models did not agree well with experimental data in sinter forging, however, agreed well with experimental data in hot isostatic pressing.