• Journal of Welding and Joining
• /
• 제16권2호
• /
• pp.73-83
• /
• 1998

This study investigated the relationships between the microstructure and the wear resistance of hardfaced iron/chromium alloys to examine the low stress abrasive wear mechanism. The effects of volume fraction of reinforcing phases(chromium carbide and eutectic phase) were studied. The alloys were deposited once or twice on a mild steel plate using a self-shielding flux cored arc welding process. The low stress abrasion resistance of he alloys against dry sands was measured by the Dry Sand/Ruber Wheel Abrasion Tester (RWAT). The wear resistance of hypoeutectic alloys, below 0.36 volume fraction of chromium-carbide phase (VFC), behaved as Equal Pressure Mode (EPM) for the inverse rule of mixture whereas the wear resistance of hypereutectic alloys, above 0.36 VFC, represented Equal Wear Mode (EWM) for the linear rule of mixture.

• Journal of Welding and Joining
• /
• 제16권2호
• /
• pp.64-72
• /
• 1998

This study aims a investigating the effect of volume fraction of chromium carbide phase(VFC) of hardfaced iron/chromium alloys on fracture toughness. The alloys were deposited twice on a mild steel plate using self-shielding flux cored arc welding process. In order to examine VFC effect, different VFC (0.28∼0.62) were employed by changing the Cr and C content, while the ratio of Cr/C was fixed in the range of 5.7∼6.6. Fracture toughness was constant as increasing VFC because fracture surface was developed in the eutectic phase which was growing parallel with introduced sharp notch in the hypoeutectic alloys, but fracture toughness did not decreased in spite of increasing volume fraction of coarse primary chromium carbide phase which was easily craced at the low stress because the growth direction of chromium carbide phase were more irregular as increasing VFC in the hypereutectic alloys.

• 대한치과보철학회지
• /
• 제34권3호
• /
• pp.475-488
• /
• 1996

The opaque porcelain layer of porcelain-fused-to-metal(PFM) restoration is critical for the success of PFM restoration because it is the first layer placed over the treated alloy. But, the methods of opaquing technique have not been confirmed. Usually, the one layer method and two layer method have been used for the application of opaque porcelain. In the past, alloys with porcelain veneers which have been used successfully have contained various precious metals. Recent increase in the cost of precious metals stimulates considerable interest in nonprecious alloys. Although nickel-chromium alloys and nickel-chromium-beryllium alloys have been widely used, the use of cobalt-chromium alloys would be gradually increased with elimination of any potential risk of nickel-related allergic responses and/or beryllium-related toxic responses. This investigation examined one- and two-layer opaque porcelain applications to determine the effect on the bond strength of titanium added cobalt-chromium metal ceramic alloy. Bond strength of Ceramco II porcelain to titanium added cobalt-chromium alloy(2Dentitan) and gold-platinum-palladium alloy(Degudent H) were evaluated by direct shear bond strength test with Instron universal testing machine. The results were as follows; 1. When the mean shear bond strength of each experimental group were compared in $0.25cm^2$ unit area, the titanium added cobalt-chromium alloy/two layer method exhibited the greatest strength(79.7kg), followed by titanium added cobalt-chromium alloy/one layer method(76.2kg), gold-platinum-palladium alloy/two layer method(71.4kg), gold-platinum-palladium alloy/one layer method(64.2kg). 2. No significant differences in bond strength were recorded between the two opaquing techniques for gold-platinum-palladium alloy and titanium added cobalt-chromium alloy. 3. No significant differences in bond strength were recorded between the gold-platinum-palladium alloy and the titanium added cobalt-chromium alloy.

• 대한치과기공학회지
• /
• 제32권3호
• /
• pp.195-207
• /
• 2010

Purpose: The purpose of this study was to observe the microstructural changes of surface in the specimens, performing the shear bond strength testing. The currently most used non-precious alloys are nickel-chromium based alloys with or without beryllium. However, their biocompatibility has been questioned concerning possible damages to the health of the patient and professionals involved in the fabrication of prosthesis caused by long exposure to Ni and Be. An option to nickel-chromium alloys is the cobalt-chromium alloy, an alternative that does not sacrifice the physical properties of the metal porcelain systems. Studies in the animals substantially show that the cobalt-chromium alloys are relatively well tolerated, being therefore more biocompatible than the nickel-chromium alloys. Methods: Non-addition Be to nickel-chromium based alloy(Bellabond plus) and cobalt-chromium alloy which has been widely used(Wirobond C) fused with ZEO light porcelain classified control group and cobalt-chromium alloy which is developing alloy of Alphadent company in Korea(Alphadent alloy) fused with ZEO light porcelain classified experimental group. The specimens of $4mm{\times}4mm{\times}0.5mm$ were prepared as-cast and as-opaque to cast body to analyze the mechanical characteristic change, the microstructure of alloy surface. The phase change was used to observe through XRD analysis and OM/SEM was used to observe the surface of specimens as-cast and as-opaque to cast body. Chemical formation of their elements was measured with EDS. Then hardness was measured with Micro Vicker's hardness tester. Shear bond strength test thirty specimens of $10mm{\times}10mm{\times}2mm$ was prepared, veneered, 3mm high and 3mm in diameter, over the alloy specimens. The shear bond strength test was performed in a universal testing machine(UTM) with a cross head speed of 0.5mm/min. Ultimate shear bond strength data were analyzed with one-way ANOVA and the Scheffe's test (P<0.05). Within the limits of this study, the following conclusions were drawn: The X-ray diffraction analysis results for the as-cast and as-opaque specimens showed that the major relative intensity of Bellabond plus alloy were changed smaller than Wirobond C and Alphadent Co-Cr based alloys. Results: Microstructural analysis results for the opaque specimens showed all the alloys increased carbides and precipitation(PPT). Alphadent Co-Cr based alloy showed the carbides of lamellar type. The Vickers hardness results for the opaque specimens showed Wirobond C and Alphadent Co-Cr based alloys were increaser than before ascast, but Bellabond plus alloy relatively decreased. The mean shear bond strengths (MPa) were: 33.11 for Wirobond C/ZEO light; 25.00 for Alphadent Co-Cr alloy/ZEO light; 18.02 for Bellabond plus/ZEO light. Conclusion: The mean shear bond strengths for Co-Cr and Ni-Cr based alloy were significantly different. But the all groups showed metal-metal oxide modes in shear bond strengths test at the interface.

• 대한치과보철학회지
• /
• 제23권1호
• /
• pp.39-59
• /
• 1985

The purpose of this study was to investigate how gap distances of 0.13mm, 0.15mm, 0.20mm, and 0.30mm affects solder joint strength from gold alloys and nickel-chromium base alloys and to examine the composition of solder gold, the solder joint of gold alloys and nickel-chromium base alloys. The tensile test specimens were prepared in the split stainless steel mold with a half dumbbell shape 2.5mm in diameter and l2mm in length. 6 pairs of specimens of each gap distance group of gold alloys and nickel-chromium base alloys were made and 48 pairs of all specimens were soldered with solder gold of 666 fineness. All soldered specimens were machined to a uniform diameter and then a tensile load was applied at a cross-head speed of 0.10mm/min using Instron Universal Testing Machine, Model 1115. The fractured specimens at solder gold of solder joint fracture with each gap distance of 0.13mm, 0.15mm, 0.20mm, and 0.30mm were examined under the Scanning Electron Microscope, JSM-35c and the composition of solder gold, the solder joint of gold alloys and nickel-chromium base alloys was analyzed by Electron Probe Micro Analyzer. The results of this study were obtained as follows: 1. In case of soldering of gold alloys, the tensile strength between gold alloys showed $37.33{\pm}2.52kg/mm^2$ at 0.13, $39.14{\pm}3.35kg/mm^2$ at 0.15mm, $43.76{\pm}2.97kg/mm^2$ at 0.20mm, and $49.18{\pm}4.60kg/mm^2$ at 0.30mm. There was statistically significant difference at each gap distance, and so the greater increase of gap distance showed the greater tensile strength. 2. In case of soldering of nickel-chromium base alloys, the tensile strength between nickel-chromium base alloys showed $34.84{\pm}4.26kg/mm^2$ at 0.13mm, $37.25{\pm}2.49kg/mm^2$ at 0.15mm, $42.91{\pm}4.32kg/mm^2$ at 0.20mm, and $46.93{\pm}4.21kg/mm^2$ at 0.30mm. There was not statistically significant difference only between 0.13mm and 0.15mm and bet ween 0.20 mm and 0.30mm, but generally the greater increase of gap distance showed the greater tensile strength. 3. The greater increase of gap distance shoed less porosities in solder gold at solder joint fracture. 4. In solder gold Au, Cu, Ag, Zn, and Sn were composed and Au and Cu were mostly distributed uniformly. 5. In solder joints of solder gold and gold alloys Au, Cu, Ag, Zn, and Sn were composed in solder gold and Au, Cu, Ag, Pt, and Pd were composed in gold alloys. Au and Cu of solder gold and gold alloys were mostly distributed uniformly and the diffusion of other elements except Pt and Pd around the solder joint was not almost found. In solder joints of solder gold and nickel-chromium base alloys Au, Cu, Ag, Zn, and Sn were composed in solder gold and Ni, Cr, and Al were composed in nickel-chromium base alloys. Au and Cu of solder gold and Ni and Cr of nickel-chromium base alloys were mostly distributed uniformly and the diffusion of other elements except Cr around the solder joint was not almost found.

• The Journal of Advanced Prosthodontics
• /
• 제6권2호
• /
• pp.138-145
• /
• 2014

Cobalt-Chromium (Co-Cr) alloys are classified as predominantly base-metal alloys and are widely known for their biomedical applications in the orthopedic and dental fields. In dentistry, Co-Cr alloys are commonly used for the fabrication of metallic frameworks of removable partial dentures and recently have been used as metallic substructures for the fabrication of porcelain-fused-to-metal restorations and implant frameworks. The increased worldwide interest in utilizing Co-Cr alloys for dental applications is related to their low cost and adequate physico-mechanical properties. Additionally, among base-metal alloys, Co-Cr alloys are used more frequently in many countries to replace Nickel-Chromium (Ni-Cr) alloys. This is mainly due to the increased concern regarding the toxic effects of Ni on the human body when alloys containing Ni are exposed to the oral cavity. This review article describes dental applications, metallurgical characterization, and physico-mechanical properties of Co-Cr alloys and also addresses their clinical and laboratory behavior in relation to those properties.

• 한국수소및신에너지학회논문집
• /
• 제5권1호
• /
• pp.1-8
• /
• 1994

Lattice structure, hydrogen absorption characteristics, discharge capacity and cycle life of $V_{22}Ti_{16}Zr_{16}Ni_{39}X_7$(X= Cr, Co, Fe, Mn, Al) alloys were investigated. The matrix phases of these alloys were the C14 Laves phase. Chromium-containing alloy had a vanadium-rich phase in addition to the Laves phase. The chromium, maganese, or aluminum-containing alloys had lower hydrogen equilibrium pressure and larger hydrogen absorption content than the cobalt or iron-containing alloys. The discharge capacities of these alloys were 270~330mAh/g. The discharge capacity according to the alloying element X decreased in the order of Mn>Cr>Co, Al)Fe. The charge/discharge cycle lives of the chromium, cobalt or iron-containing alloys were longer than those of maganese or aluminum-containing alloys due to the lower vanadium dissolution rate.

• Advances in materials Research
• /
• 제7권1호
• /
• pp.17-28
• /
• 2018

Niobium is a candidate base for new alloys devoted to applications at especially elevated temperatures. Elaborating and shaping niobium-based alloys by conventional foundry may lead to mechanically interesting microstructures. In this work a series of charges constituted of pure elements were subjected to high frequency induction melting in cold crucible to try obtaining cast highly refractory Nb-xCr and Nb-xCr-0.4 wt.%Calloys(x=27, 34 and 37 wt.%). Melting and solidification were successfully achieved. The as-cast microstructures of the obtained alloys were characterized by electron microscopy and X-ray diffraction and their hardness were specified by Vickers macro-indentation. The obtained as-cast microstructures are composed of a body centered cubic (bcc) niobium dendritic matrix and of an interdendritic eutectic compound involving the bcc Nb phase and a $NbCr_2$ Laves phase. The obtained alloys are hard to cut and particularly brittle at room temperature. Hardness is of a high level (higher than 600Hv) and is directly driven by the chromium content or the amount of {bcc Nb - $NbCr_2$} eutectic compound. Adding 0.4 wt.% of carbon did not lead to carbides but tends to increase hardness.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.134-135
• /
• 2006

Ancorsteel 4300, a high performance Cr-Si-Ni-Mo steel, was unveiled two years ago as the first in a series of powder metallurgy alloys that will simulate wrought steel compositions. Advantages of this alloy include good compressibility, high hardenability, and excellent dimensional stability. More important, however, is that this alloy has the ability to be effectively sintered at $1120^{\circ}C$ and maintain oxygen contents below 500 ppm. This unique blend of performance and processing capabilities provides static and dynamic properties that exceed those of conventional powder metallurgy alloys and approach wrought gearing materials. A second Cr-Si-Ni-Mo alloy has now been developed that offers complimentary performance levels at a lower Mo content. This manuscript reviews properties of the two chromium steels with comparisons to traditional sinter-hardened and heat-treated powder metallurgy alloys.

• Journal of Welding and Joining
• /
• 제16권1호
• /
• pp.125-133
• /
• 1998

The effect of volume fraction of Cr carbide phase (Cr CVF) on the low stress abrasion resistance in the chromium-carbide-type high Cr white iron hardfacing weld deposits has been investigated. In order to examine Cr CVF, a series of alloys with varying Cr CVF by changing chromium and carbon contents and the ratio of Cr/C were employed. The alloys were deposited once or twice on a mild steel plate using the self-shielding flux cored arc welding process. The low stress abrasion resistance of the alloys against sands was measured by the Dry Sand/Rubber Wheel Abrasion Test (RWAT). It was shown that hardness and abrasion resistance increased with increasing Cr CVF within the whole test range (Cr CVF : 0.23-0.64). Both primary Cr carbide and eutectic Cr carbide were particularly effective in resisting wear due to their high hardness.