• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.303-303
• /
• 2007

Photo-imageable thick-film lithography technology was developed for the fabrication of embedded passives such as inductors and capacitors. In this study, photo-imageable dielectric and conductor pastes have apoted a negative type. Sodalime glass wafer, alumina substrate and zero-shrinkage LTCC green tapes were used as substrates. In result, The lithographic patterns were designed as lines and spaces for conductor material, or via-holes for ceramic, LTCC, materials. The scattering and reflection of UV-beam on the substrate had negative effects on fine patterning. The patterning performance was varied with the exposing and developing process conditions, and also varied with the substrate materials. Fine resolution of less then $50/50{\mu}m$ in line and space was obtained, which is difficult in screen printing method.

• Journal of the Korean Society of Industry Convergence
• /
• v.21 no.6
• /
• pp.355-360
• /
• 2018

The product developed in this study is a ceramic catalyst filter for 1 ton heavy-oil boiler that can simultaneously process dust and nitrogen oxides. This has been developed for simultaneous processing of nitrogen oxides and dust at high efficiency of hot exhaust gas (approximately $300^{\circ}C$) generated after burning 1 ton heavy oil boiler. Ceramic catalytic filters for 1 tonne heavy-duty glass display are technologies that remove 90% of dust and 85% or more of nitrogen oxides. This is an improved new technology to integrate exhaust ventilation and desiccation devices into one, thereby reducing the production process and improving the economy. To this end, the performance test of the catalytic filter for heavy oil boilers was carried out, and the durability of the PLC circuit was constructed.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.1
• /
• pp.14-24
• /
• 2001

The purpose of this study was to compare the fracture strengths and the fracture patterns of several hybrid-ceramic crowns and metal-ceramic crown. Ten crowns were constructed for each group according to the manufacturer's instruction. Removable template of silicone rubber impression material was used for standardization of each crowns. Each crown was cemented on a metal die with hybrid glass ionomer cement. All crowns cemented were stored in distilled water, $36^{\circ}C$ for 24 hours prior to loading in an universal testing machine. The load was directed at 130 degrees the long axis of metal die. The fracture strengths were measured and the fracture patterns were observed. The following results were obtained from this study 1. The mean fracture strengths of $Artglass^{(R)}$, $Sculpture^{(R)}$ and $Targis^{(R)}$ were $57.5{\pm}9.5Kgf,\;62.7{\pm}12.2Kgf$ and $60.2{\pm}10.1Kgf$ respectively. There was no significant difference among each hybrid ceramic crown group. 2. The toad required to fracture hybrid-ceramic crowns was significantly smaller than metal-ceramic crowns($131.7{\pm}22.0Kgf$). 3. In the metal-ceramic crowns, labial porcelain detached partially from porcelain-metal junction of proximal side by load. 4. Hybrid-ceramic crowns showed a simple fracture pattern that fracture line began at the loading area and extended through proximal surface, perpendicular to the margin. The crown was separated into two parts of labial side and lingual side. Above results revealed that three kinds of the hybrid-ceramic crowns used in this study must have careful application in clinical use since the strength of hybrid-ceramic crown was lower(about 1/2) than that of metal-ceramic crown.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.342-342
• /
• 2008

The low temperature sintering and microwave dielectric properties of ceramic/glass composites which were composed of ceramics in the $Bi_2(Zn_{1/3}Nb_{2/3})_2O_7$ and zinc borosilicate glass/bismuth-zinc borosilicate glass were investigated with a view to applying the microwave dielectrics to low temperature co-fired ceramics. The $Bi_2(Zn_{1/3}Nb_{2/3})_2O_7$ addition of 5 wt% ZBS and BZBS glass ensured a successful sintering below $900^{\circ}C$. In addition, pyrochlore phase was observed in the all composition. $Bi_2(Zn_{1/3}Nb_{2/3})_2O_7$ with 5 wt% BZBS glasss demonstrated 70 as the dielectric constant ($\varepsilon_r$), 2,500 GHz as the Q$\times$f value, and -40 ppm/$^{\circ}C$ as TCF.

• The Journal of Korean Academy of Prosthodontics
• /
• v.26 no.1
• /
• pp.51-61
• /
• 1988

The recently introduced castable glass ceramics incorporate properties characteristic of natural teeth and they are regarded as an ideal material to restore lost tooth structure. The purpose of this study was to compare the marginal fit of castable ceramic crown with that of the metal-ceramic crown in the process of heat treatment. Two master dies for castable ceramic crowns and metal-ceramic crowns were fabricated from being cast with the base metal. Each master die was duplicated with addition silicone and hard stone. Ten castable ceramic crowns were made on each hard stone die and their marginal openings were measured three times first, after casting; second, after ceramming; third, after shading. The other ten metal-ceramic crowns were made on each hard stone die and their marginal openings were measured three times : first, after casting; second, after degassing; third, after porcelain veneering. Each crown was seated on its master die with the constant force delivered by loading jig. And then, marginal openings were measured on four locations by optical projector at X50 magnification. The results were as follows: 1. The mean marginal openings of castable ceramic crowns were $31.1{\pm}12.7{\mu}m$ after casting; $44.6{\pm}12.8{\mu}m$ after ceramming; $51.2{\pm}16.8{\mu}m$ after shading. 2. The mean marginal openings of the metal-ceramic crowns were $26.2{\pm}13.8{\mu}m$ after casting; $29.8{\pm}10.3{\mu}m$ after degassing; $38.0{\pm}14.5{\mu}m$ after porcelain veneering. 3. There was significant increase in the marginal opening of castable ceramic crowns after ceramming, while metal-ceramic crowns sho(wed significant increase after porcelain veneering (p<0.05). 4. Marginal fit of metal-ceramic crown was better than that of castable ceramic crown (p<0.01).

• Journal of the Korean Ceramic Society
• /
• v.39 no.6
• /
• pp.598-603
• /
• 2002

The effects of alumine borosilicate glass composition on the densification and the microwave properties of (M $g_{0.93}$C $a_{0.07}$)Ti $O_3$ ceramics were studied. As the amount of glass increase, the density of ceramics increases and grain growth enhances. When 20 ~30 wt% of glass added, it was densified to over 95% of (M $g_{0.93}$C $a_{0.07}$)Ti $O_3$ theoretical density. (M $g_{0.93}$C $a_{0.07}$)Ti $O_3$ ceramic sintered at 95$0^{\circ}C$ exhibits dielectric constants of 15~16, quality factor of 8000 and temperature coefficient of resonant frequency of -45 ppm/$^{\circ}C$ by adding 20 wt% alumine borosilicate glass.

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.145-152
• /
• 2002

Four commercial alumina powders having different particle size of $0.5{\mu}m,\;2.8{\mu}m,\;12{\mu}m,\;and\;45{\mu}m$ were presintered at 1120$^{\circ}C$ for 2h and then lanthanum aluminosilicate glass was infiltrated at 1100$^{\circ}C$ for 2h in the interval of 0.1h to investigate the penetration kinetic of the glass into the alumina preforms. The infiltration distance is parabolic with respect to time as described by the Washburn equation and the penetration rate constant, K, increases with raising the alumina particle size. The strength of glass-alumina composites increases as the alumina particle size reaches to 2.8${\mu}m$ due to the increase in packing, however, decreases with further increasing the alumina particle size. The fracture toughness of the composites rises with increasing the alumina particle size due to the crack bowing and the interaction between crack and alumina particles.

• Journal of the Korean Ceramic Society
• /
• v.45 no.8
• /
• pp.459-463
• /
• 2008

$P_2O_5-SnO_2$ system $0.5SnO_2-xP_2O_5-(0.5-x)B_2O_3$(x=0.1, 0.2, 0.3, 0.4, 0.5) glasses have been prepared for Pb-free low temperature glass frit. A investigation about the effect of $B_2O_3$ substitution on properties of $P_2O_5$ glasses, including glass structure properties, thermal properties, and mechanical properties was presented. Substance that is responsible for in moisture absorption existing circumstances supposes by phosphate, and excess moisture tolerance that state funeral's structure is improved breaking does not affect in state funeral bond that only most single bond remains, and can know that does not suffer big impact in boric oxide anomaly present state. This phenomenon estimates that connect with structure change. It is thought according to link this result the phosphoric acid happened structural change. $B_2O_3$ displacement quantity 0.3 mole put out $BO_4$ structures, but above 0.3 mole it changed with the case $BO_3$ structure which it displaces.

• Korean Journal of Materials Research
• /
• v.10 no.5
• /
• pp.328-334
• /
• 2000

The photocatalyst of $TiO_2$coated on glass bead was prepared from sol-gel method to remove the VOC (vola-tile organic compounds) by the photocatalytic reaction. The coated films were characterized by X-ray diffraction(XRD), specific surface area(BET), and scanning electron microscopy observation (SEM), The gas-phase photocatalytic degradation of trichloroethylene(TCE) and benzene with coated titanium dioxide on glass beads was in-vestigated using a fixed bed reactor. The degradation was calculated by the concentration difference with the retained on the reactor with aid of gas chromatography. At steady state, conversion yields were obtained for 80% of trichloroeth-vlene in 400 ppmv concentration and 65% on benzene in the range of concentration from 50 to 300 ppmv, respectively.

• The Journal of the Korea Contents Association
• /
• v.15 no.9
• /
• pp.384-394
• /
• 2015

The purpose of this study was to evaluate the push-shear bond strength between five commercial zirconia veneering ceramics and zirconia core cylinder, and to investigate the effect of biaxial flexural strength and zirconia liner glass treatments. The biaxial flexural strengths of the veneering ceramics were evaluated by a piston-on-three-ball test. The bond strengths between the Y-TZP cylinder and zirconia veneering ceramics were evaluated using the push-shear bond strength test. The data was analyzed using two-way ANOVA and Scheffe's test. The biaxial flexural strength of Cercon ceram kiss (CE) was higher than those of the other groups. The glass-treated and Triceram zirconia groups showed the highest value and the Creation ZI(CR) showed the lowest. In all groups, the liner glass treatment groups showed significantly higher push-shear bond strength than those without(P<0.05). The liner glass treatments of zirconia can improve the bond strength between the zirconia ceramic core and veneering ceramics.