In this study we aims to examine the co-doping effects of 1/3 mol% $Mn_3O_4+Co_3O_4$ (1:1) on the reaction, microstructure, and electrical properties such as the bulk defects and grain boundary properties of $ZnO-Bi_2O_3-Sb_2O_3$ (ZBS; Sb/Bi=0.5, 1.0, and 2.0) varistors. The sintering and electrical properties of Mn,Co-doped ZBS, ZBS(MCo) varistors were controlled by Sb/Bi ratio. Pyrochlore ($Zn_2Bi_3Sb_3O_{14}$) was decomposed and promoted densification at lower temperature on heating in Sb/Bi=1.0 by Mn rather than Co. Pyrochlore on cooling was reproduced in all systems however, spinel (${\alpha}$- or ${\beta}$-polymorph) did not formed in Sb/Bi=0.5. More homogeneous microstructure was obtained in $Sb/Bi{\geq}1.0$ In ZBS(MCo), the varistor characteristics were improved drastically (non-linear coefficient, ${\alpha}$=30~49), and seemed to form $Zn_i^{..}$(0.17 eV) and $V_o^{\bullet}$(0.33 eV) as dominant defects. From impedance and modulus spectroscopy (IS & MS), the grain boundaries have divided into two types, i.e. the one is tentatively assign to $ZnO/Bi_2O_3(Mn,Co)/ZnO$ (0.47 eV) and the other ZnO/ZnO (0.80~0.89 eV) homojunctions.

• 한국결정성장학회지
• /
• 제32권4호
• /
• pp.151-158
• /
• 2022

본 연구에서는 폐콘크리트 분쇄물의 탄산화 가능성 검토를 위해 폐콘크리트 분쇄물의 기초물성 측정 및 탄산화를 실시하였으며, 탄산화 시료의 CaCO₃ 생성량, 결정성 분석 및 미세구조를 관찰하였다. 폐콘크리트 분쇄물의 탄산화 전 CaCO₃ 함량은 14.51 %이었으며, 24시간 탄산화 시 CaCO₃ 함량은 28.52 %, 미분쇄 후 24시간 탄산화 시의 CaCO₃ 함량은 32.73 %이었다. 탄산화 시간에 따른 폐콘크리트 분쇄물의 탄산화는 초기 6시간까지 급격히 이루어졌으나, 12시간 이후 24시간까지의 탄산화는 서서히 진행되었다. 특히 12시간 이후 24시간까지의 CaCO₃ 생성량은 2.32 % 수준에 불과하였다. 폐콘크리트 탄산화 후 미세구조 관찰 시 calcite 형상의 CaCO₃ 결정을 발견할 수 있었으며, 또한 XRD 패턴에서도 동일 결정 피크를 검출할 수 있었다. 따라서 본 연구에서 생성된 CaCO₃ 결정은 calcite라는 것을 확인할 수 있었다.

• 한국세라믹학회지
• /
• 제53권1호
• /
• pp.105-109
• /
• 2016

We prepared a working electrode (WE) with a blocking layer (BL) containing 0 ~ 0.5 wt% Ag nano powders to improve the energy conversion efficiency (ECE) of dye sensitized solar cell (DSSC). FESEM and micro-Raman were used to characterize the microstructure and phase. UV-VIS-NIR spectroscopy was employed to determine the adsorption of the WE with Ag nano powders. A solar simulator and a potentiostat were used to confirm the photovoltaic properties of the DSSC with Ag nano powders. From the results of the microstructural analysis, we confirmed that Ag nano powders with particle size of less than 150 nm were dispersed uniformly on the BL. Based on the phase and adsorption analysis, we identified the existence of Ag and found that the adsorption increased when the amount of Ag increased. The photovoltaic results show that the ECE became 4.80% with 0.3 wt%-Ag addition compared to 4.31% without Ag addition. This improvement was due to the increase of the localized surface plasmon resonance (LSPR) of the BL resulting from the addition of Ag. Our results imply that we might be able to improve the efficiency of a DSSC by proper addition of Ag nano powder to the BL.

• 한국세라믹학회지
• /
• 제51권5호
• /
• pp.406-412
• /
• 2014

In this study, flat-tubular-type alumina filters were manufactured using alumina powder of two sizes ($2.4{\mu}m$ ALM-44 and $0.4{\mu}m$ AP 400) by an extrusion process. The manufactured alumina filter was sintered at $1200-1600^{\circ}C$ for 1 h. As particle size increased, the largest pore size, average pore size and porosity increased; but density and linear shrinkage decreased. The alumina filter fabricated using ALM-44 powder sintered at $1500^{\circ}C$ was confirmed as the best water treatment filter after investigation of the bending strength, water permeability and impurity-removal efficiency of the experimental filters. This flat-tubular-type alumina filter is expected to be useful not only for direct water treatment, but also for use as a support filter during coating processes, to control pore size.

• 한국세라믹학회지
• /
• 제51권5호
• /
• pp.466-471
• /
• 2014

Hydrous zirconia particles were prepared from $ZrOCl_2$ aqueous solution using an electro-dialysis [ED] process. For the preparation of $(Zr,Y)(OH)_4$ precipitates, 3 mol% $YCl_3$ was added into $ZrOCl_2$ aqueous solution. During the hydrolysis of 0.5 mol/L $(Zr,Y)OCl_2$ solution at $90^{\circ}C$ a slurry solution was obtained. The ED process was used for the removal of chlorine from the slurry solution. Two kinds of slurry solution were sampled at the beginning and end of the ED process. The morphology of hydrous zirconia particles in the solution was observed using an inverted optical microscope and an FE-SEM. The hydrous zirconia particles were nano-crystalline, and easily coagulated with drying. Yttrium stabilized zirconia [YSZ] powder could be obtained by the calcination of $(Zr,Y)(OH)_4$ precipitates prepared from a $(Zr,Y)OCl_2$ solution by the ED process. The coagulated dry powders were shaped and sintered at $1500^{\circ}C$ for 2 h. The sintered body showed a dense microstructure with uniform grain morphology.

• 한국세라믹학회지
• /
• 제51권5호
• /
• pp.481-486
• /
• 2014

Environmental barrier coatings (EBCs) are used to protect SiC-based ceramics or composites from oxidation and corrosion due to reaction with oxygen and water vapour at high temperatures above $1000^{\circ}C$. Mullite ceramics have been studied for environmental barrier coatings for Si-based ceramics. More recently, rare earth silicate ceramics have been identified as more water vapour-resistant materials than mullite for environmental barrier coatings. In this study, we fabricate mullite and yttrium silicate ceramics by an atmospheric plasma spray coating method using spherical granules fabricated by spray drying. As a result, EBCs with thicknesses in the range of $200-300{\mu}m$ are successfully fabricated without any macroscopic cracks or interfacial delamination. Phase and microstructure analysis are conducted, and the basic mechanical properties, such as hardness and indentation load-displacement curves are evaluated.

• 한국세라믹학회지
• /
• 제49권3호
• /
• pp.221-225
• /
• 2012

It is possible to enhance the color of the natural diamond with a high pressure high temperature(HPHT) process. We employed a pyrophyllite tube cell and cubic press apparatus for HPHT treatment on the brown colored Type II (5.6 GPa/ $1700^{\circ}C$/ 52 min), and Type I aB(5.6 GPa/ $1650^{\circ}C$/ 30 min) diamond samples. We investigated the microstructure, Types, fluorescence, properties of the diamonds with an optical microscopy, FT-IR, photoluminescence(PL) spectroscopy, Diamond-View, and micro-Raman spectroscopy. Two tinted brown diamonds changed into colorless just after the HPHT process. Optical microscopy showed that no crack and significant inclusion evolution occurred during the HPHT process except the small graphite spot appeared in Type I aB sample. FTIR spectrum confirmed that no Type, amber center, and platelet defect change with the HPHT treatment. Diamond-View could not distinguish the HPHT treated diamonds from the naturals. PL spectroscopy showed that N3 and H3 color centers remained even after HPHT process. Consequently, we successfully changed the color of diamonds into colorless by 5.6 GPa HPHT process.

• 한국세라믹학회지
• /
• 제55권3호
• /
• pp.239-243
• /
• 2018

Up to now, microstructure changes of photocatalysts have been studied to improve photocatalytic activity. Especially, to improve the adsorption of reactants and reactive sites, porous and fine crystal structures have received much attention because of their large specific surface area. In this study, $TiO_2$ nanotubes were synthesized by hydrothermal method using $TiO_2$ nanoparticles; nanotubes were evaluated by oxidized methylene blue reduction test. Using synthesized $TiO_2$ nanotubes, results of TEM showed that the $TiO_2$ nanoparticles were changed into folding sheets and nanotubes. XRD results showed that the peaks of the nanoparticles almost disappeared and only the rutile (110) and anatase (200) peaks were observed. Comparison of photocatalytic properties of nanoparticles and nanotube structures was performed by measuring the UV-vis absorbance with reducing oxidized methylene blue. As a result, the reduction rate of nanotubes was found to be $0.24{\mu}mol/s$, which was 2.6 times higher than the rate of reduction of nanoparticles.

• 한국세라믹학회지
• /
• 제55권6호
• /
• pp.576-580
• /
• 2018

In this study, a small amount of CoO was added to commercial Gd-doped $CeO_2$ (GDC) powder. The CoO addition greatly enhanced sinterability at low temperatures, i.e., more than 98% of relative density was achieved at $1,000^{\circ}C$. When GDC/8YSZ (8 mol% yttrium stabilized zirconia) bilayers were sintered, Co-doped GDC showed excellent adhesion to the YSZ electrolyte. Transmission electron microscope (TEM) analysis showed that there were no traces of liquid films at the grain boundaries of GDC, whereas liquid films were observed in the Co-doped GDC sample. Because liquid films facilitate particle rearrangement and migration during sintering, mechanical stresses at the interface of a bilayer, which are developed based on different densification rates between the layers, might be reduced. In spite of $Co^{2+}$ doping in GDC, the electrical conductivity was not significantly changed, relative to GDC.

• 한국세라믹학회지
• /
• 제55권6호
• /
• pp.527-555
• /
• 2018

High-temperature thermal insulation materials challenge extensive oxide candidates such as porus $SiO_2$, $Al_2O_3$, yttria-stabilized zirconia, and mullite, due to the needs of good mechanical, thermal, and chemical reliabilities at high temperatures simultaneously. Recently, porous rare earth (RE) silicates have been revealed to be excellent thermal insulators in harsh environments. These materials display attractive properties, including high porosity, moderately high compressive strength, low processing shrinkage (near-net-shaping), and very low thermal conductivity. The current critical challenge is to balance the excellent thermal insulation property (extremely high porosity) with their good mechanical properties, especially at high temperatures. Herein, we review the recent developments in processing techniques to achieve extremely high porosity and multiscale strengthening strategy, including solid solution strengthening and fiber reinforcement methods, for enhancing the mechanical properties of porous RE silicate ceramics. Highly porous RE silicates are highlighted as emerging high-temperature thermal insulators for extreme environments.