• Journal of Ceramic Processing Research
• /
• v.13 no.spc1
• /
• pp.59-63
• /
• 2012

Ga2O3-core/CdO-shell nanowires were synthesized by a two step process comprising thermal evaporation of GaN powders and sputter-deposition of CdO. Transmission electron microscopy (TEM) and X-ray diffraction (XRD) analyses revealed that the cores and the shells of the annealed coaxial nanowires were single crystal of monoclinic Ga2O3 and FCC CdO, respectively. As-synthesized Ga2O3 nanowires showed a broad emission band at approximately 460 nm in the blue region. The blue emission intensity of the Ga2O3 nanowires was slightly decreased by CdO coating, but it was significantly increased by subsequent thermal annealing in a reducing atmosphere. The major emission peak was also shifted from ~500 nm by annealing in a reducing atmosphere, which is attributed to the increases in the Cd interstitial and O vacancy concentrations in the cores.

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.338-346
• /
• 1991

The alumina-titania composite powders coated with Al2O3 were prepared by the method of hydrolysis-deposition of mixed aluminium salt solution of Al2(SO)4-Al(NO3)3-Urea. The effects of coating-process parameters on the characteristics of coated composite powders were also investigated. As the content of TiO2 dispersed in deionized water increased, the coated composite powders were found to be more uniform in size and unagglomerated. When TiO2 powders were coated for 30 min, the optimum TiO2 content in the coating process was 400 mg/ι. The size of TiO2 particle was increased approximately from 0.7${\mu}{\textrm}{m}$ to 1.0${\mu}{\textrm}{m}$ through coating of Al2O3. The IEP of coated composite powders was pH=8.3 identical to the value of aluminium hydroxides and the zeta-potential showed nearly similar values each other. When heat treating coated composite powders at 130$0^{\circ}C$, only two phases of TiO2(rutile) and Al2TiO5 were observed. These results showed that the suface of TiO2 could be uniformly coated with the aluminium hydroxide.

• Composites Research
• /
• v.29 no.6
• /
• pp.375-378
• /
• 2016

Characteristics of nanocrystalline materials are known substantially dependent on the microstructure such as grain size, crystal orientation, and grain boundary. Thus it is desired to have systematic characterization methods on the various nanomaterials with complex geometries, especially in low dimensional nature. One of the interested nanomaterials would be a pure two-dimensional material, graphene, with superior mechanical, thermal, and electrical properties. In this study, mechanical properties of "polycrystalline" graphene were numerically investigated by molecular dynamics simulations. Subdomains with various sizes would be generated in the polycrystalline graphene during the fabrication such as chemical vapor deposition process. The atomic models of polycrystalline graphene were generated using Voronoi tessellation method. Stress strain curves for tensile deformation were obtained for various grain sizes (5~40 nm) and their mechanical properties were determined. It was found that, as the grain size increases, Young's modulus increases showing the reverse Hall-Petch effect. However, the fracture strain decreases in the same region, while the ultimate tensile strength (UTS) rather shows slight increasing behavior. We found that the polycrystalline graphene shows the reverse Hall-Petch effect over the simulated domain of grain size (< 40 nm).

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.18 no.3
• /
• pp.337-346
• /
• 2020

Two commonly used ceramics in molten salt research are alumina and mullite. The two ceramics were exposed to a combination of rare earth chlorides (YCl₃, SmCl₃, NdCl₃, PrCl₃, and CeCl₃; each rare earth chloride of 1.8 weight percent) in LiCl-KCl at 773 K for approximately 13 days. Scanning electron microscopy with wave dispersion spectra was utilized to investigate a formation layer or deposition of rare earths onto the ceramic. Only the major constituents of the ceramics (Al, Si, and O₂) were observed during the wave dispersion spectra. X-ray fluorescence was used as well to determine concentration changes in the molten salt as a function of ceramic exposure time. This study shows no evidence of ionic exchange or layer formation between the ceramics and molten chloride salt mixture. There are signs of surface tension effects of molten salt moving out of the tantalum crucible into secondary containment.

• Journal of the Korean Ceramic Society
• /
• v.29 no.8
• /
• pp.667-673
• /
• 1992

The alumina-zirconia composite powders of core particle ZrO2 coated with Al2O3 were prepared by the hydrolysis-deposition of the mixed aluminum salt solution of Al2(SO4)3-Al(NO3)3-Urea. The effects of hydrolysis reaction and coating parameters on characteristics of coated powders and composites were also investigated. The degree of coating could be estimated from the ratio of tetra-/mono-ZrO2 present at the room temperature after heat-treating coated powders at 120$0^{\circ}C$ and the result of TEM observations. When the content of ZrO2 in the dispersed coating system, the coating time, and the volume ratio of water/solution were 50 mg/g, 180 min, and 5, respectively the coating efficiency was maximum (the ratio of tetra-/mono-ZrO2 was 87/13). The relative densities of coated Al2O3-ZrO2 composites sintered at 1$650^{\circ}C$ for 4 hrs were about 91~98% and the maximum ratio of tetra-/mono-ZrO2 in Al2O3-20wt% ZrO2 composites was 62/38.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.533-534
• /
• 2006

1mm-thick BLT ceramics were sintered in accordance with a bulk ceramic fabrication process. All XRD peaks detected in the sintered ceramics were indexed as the Bi-layered perovskite structure without secondary phases. Density was increased with increasing the sintering temperature up to $1050\;^{\circ}C$ and the maximum value was about 98% of the theoretical density. The remanent polarization (2Pr) value of BLT ceramic sintered at $1050\;^{\circ}C$ was approximately $6.5\;{\mu}C/cm^2$ at the applied voltage of 4.5kV. From these results, a BLT ceramic target for plused laser deposition (PLD) system was successfully fabricated.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.276-277
• /
• 2006

1mm-thick BLT ceramics were sintered in accordance with a bulk ceramic fabrication process. AII XRD peaks detected in the sintered ceramics were indexed as the Bi-layered perovskite structure without secondary phases. Density was increased with increasing the sintering temperature up to $1050^{\circ}C$ and the maximum value was about 98% of the theoretical density. The remanent polarization (2Pr) value of BLT ceramic sintered at $1050^{\circ}C$ was approximately $6.5\;{\mu}C/cm^2$ at the applied voltage of 4.5 kV. The calculated electromechanical coupling factor ($k_t$) of it was about 5% and the mechanical quality factor (Qm) was about 2200. From these results, a BLT ceramic target for pulsed laser deposition (PLD) system was successfully fabricated.

• Proceedings of the Korea Crystallographic Association Conference
• /
• 2007.11a
• /
• pp.14-14
• /
• 2007

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.10a
• /
• pp.141-143
• /
• 2001

Ceramic fiber-reinforced composites have good mechanical properties in hardness and durability. In this study, we studied the formation of SiC/C composites from methyltrichlorosilane and hydrogen by the Pulse-chemical vapor infiltration(PCVI) to deposit silicon carbide around the changes of the amount of deposit. SiC/C composites formed at $950^{\circ}C$, 20torr, Pulse-times (5s/60s). SEM of the cross sectional area of semple showed deposited silicon carbide around fibers.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2004.10a
• /
• pp.79.2-79.2
• /
• 2004