• The Journal of Korean Academy of Prosthodontics
• /
• v.32 no.2
• /
• pp.195-211
• /
• 1994

The purpose of this study was to evaluate the fracture resistance of the four kinds of dental porcelains for the all-ceramic crown(Vita In-Ceram, Vita Hi-Ceram, IPS-Empress, Vitadur-N) and one kind for the metal-ceramic non(Vita VMK 68) was used as the control group. In order to determine the fracture resistance, the hi-axial flexure strength was measured at a crosshead speed of 0.5mm/min, and the Vickers hadrness was measured at an indentation load of 1kg for 20 seconds. The results obtained were summarized as follows ; 1. The maximum Weibull modulus of 24.61 for Vitadur-N and the minimum one of 852 for IPS-Empress were observed ; the maximum characteristic strength of 353.26MPa for Vita In-Ceram and the minimum that of 63.20MPa for Vitadur-N were also observed. 2. The maximum mean bi-axial flexure strength of 339.12MPa for Vita In-Ceram and thd minimum one of 61.99MPa for Vitadur-N were calculated. Results of the Scheffe test indicated that the statistically significant difference(P<0.05) existed between Vita In-Ceram or Vita Hi-Ceram and the others ; also between IPS-Empress and Vitadur-N. 3. The maximum mean hardness of $980.55kg/mm^2$ for Vita VMK 68 appeared. Results of the Scheffe test indicated that statistically significant difference(P<0.05) existed between Vita In-Ceram or Vita Hi-Ceram and the others ; also between IPS-Empress and Vita VMK 68.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.2
• /
• pp.92-97
• /
• 2013

PURPOSE. All-ceramic crowns are subject to fracture during function. To minimize this common clinical complication, zirconium oxide has been used as the framework for all-ceramic crowns. The aim of this study was to compare the fracture strengths of two computer-aided design/computer-aided manufacturing (CAD/CAM) zirconia crown systems: Lava and Digident. MATERIALS AND METHODS. Twenty Lava CAD/CAM zirconia crowns and twenty Digident CAD/CAM zirconia crowns were fabricated. A metal die was also duplicated from the original prepared tooth for fracture testing. A universal testing machine was used to determine the fracture strength of the crowns. RESULTS. The mean fracture strengths were as follows: $54.9{\pm}15.6$ N for the Lava CAD/CAM zirconia crowns and $87.0{\pm}16.0$ N for the Digident CAD/CAM zirconia crowns. The difference between the mean fracture strengths of the Lava and Digident crowns was statistically significant (P<.001). Lava CAD/CAM zirconia crowns showed a complete fracture of both the veneering porcelain and the core whereas the Digident CAD/CAM zirconia crowns showed fracture only of the veneering porcelain. CONCLUSION. The fracture strengths of CAD/CAM zirconia crowns differ depending on the compatibility of the core material and the veneering porcelain.

• 대한치과보철학회:학술대회논문집
• /
• 2001.11a
• /
• pp.42-42
• /
• 2001

• The Journal of Advanced Prosthodontics
• /
• v.8 no.2
• /
• pp.131-136
• /
• 2016

PURPOSE. The aim of this study was to observe stress concentration in the implant, the surrounding bone, and other components under the pull-out force during the crown removal. MATERIALS AND METHODS. Two 3-dimensional models of implant-supported conventional metal ceramic crowns were digitally constructed. One model was designed as a vertically placed implant ($3.7mm{\times}10mm$) with a straight abutment, and the other model was designed as a 30-degree inclined implant ($3.7mm{\times}10mm$) with an angled abutment. A pull-out force of 40 N was applied to the crown. The stress values were calculated within the dental implant, the abutment, the abutment screw, and the surrounding bone. RESULTS. The highest stress concentration was observed at the coronal portion of the straight implant (9.29 MPa). The stress concentrations at the cortical bone were lower than at the implants, and maximum stress concentration in bone structure was 1.73 MPa. At the abutment screws, the stress concentration levels were similiar (3.09 MPa and 3.44 MPa), but the localizations were different. The stress at the angled abutment was higher than the stress at the straight abutment. CONCLUSION. The pull-out force, applied during a crown removal, did not show an evident effect in bone structure. The higher stress concentrations were mostly observed at the implant and the abutment collar. In addition, the abutment screw, which is the weakest part of an implant system, also showed stress concentrations. Implant angulation affected the stress concentration levels and localizations. CLINICAL IMPLICATIONS. These results will help clinicians understand the mechanical behavior of cement-retained implant-supported crowns during crown retrieval.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.25 no.1
• /
• pp.1-12
• /
• 2009

The objective of this study was to test the effects of crown material, cement type, the direction in which stress is applied and distribution of luting cement that might lead to cement microfracture using 2D Finite Element Method. Twenty three finite element models with a chamfer margin configuration were generated for a mandibular first molar. Crown models exhibited four crown materials: type 3 gold alloy, Ni-Cr alloy, ceramic and composite resin, and two luting cements: zinc phosphate and glass ionomer cements with a thicknesses of $70{\mu}m$. Modeled crowns were loaded axially or obliquely at unit load of 1 N. Areas and levels of stress concentrations within the cement were determined. Stress in the cement layer at the margins of crowns were higher than those in the area away from the margin. Stress under oblique loads were much higher than under axial load. The stiffer crown material produced higher stress and similarly, higher stress were found in cements with the greater Young's modulus.

• Journal of dental hygiene science
• /
• v.14 no.3
• /
• pp.405-410
• /
• 2014

The purpose of this study in vitro investigation was to compare the marginal and internal fit of Ni-Cr alloy metal ceramic crown before and after porcelain veneering. Furthermore, this study evaluated whether the influence of the porcelain firing on the precision of fit of dental prostheses. The maxillary right incisor was selected as an abutment for experiments. Ten working models were prepared. Ni-Cr alloy cores appropriate for each abutment were prepared by lost wax technique. The marginal area and four internal areas of the crowns were measured at two stages: before veneering process and after upper porcelain firing. Silicone replica techniques were used. The data were statistically analyzed with the paired t-test (${\alpha}=0.05$). $Mean{\pm}SD$ marginal and internal gap were $67.1{\pm}23.3{\mu}m$ for the nickle chrome alloy core group and $74.4{\pm}21.9{\mu}m$ for the metal ceramic crown group. There were statistically significant differences in all investigated areas (p<0.05). Within the limitations of this study, none of the Ni-Cr alloy metal crown values measured after porcelain firing process exceeded $120{\mu}m$, which is the clinically acceptable threshold.

• Journal of Technologic Dentistry
• /
• v.25 no.1
• /
• pp.63-70
• /
• 2003

The microstructure and hardness of a porcelain fused Au-Pt-Cu-In alloy was investigated using optical microscopy, secondary electron microscopy, electron probe microanalyzer, transmission electron microscope, and vickers hardness. The hardness of the heat-treated Au-Pt-Cu-In quartenary alloy reached a maximum value in 30 min at 550$^{\circ}C$ in the range of 150 to 950$^{\circ}C$. In the aged Au-Pt-Cu-0.5In alloy at 550$^{\circ}C$, the hardness of the alloy rapidly increased until 30min with increasing aging time and after that it was remained nearly constant value. Based on above results, glazing and final aging of the porcelain fused Au-Pt-Cu-0.5In alloy were performed at 920 and 550$^{\circ}C$, respectively. The hardness of Au-Pt-Cu-0.5In alloy glazed at 920$^{\circ}C$ was 90 Hv and that of the alloy aged for 30 min at 550$^{\circ}C$ increased to 160 Hv. This indicates that a ceramic-metal crown with high strength can be manufactured using the glazing at 920$^{\circ}C$ and followed final aging at 550$^{\circ}C$ for 30 min.

• Restorative Dentistry and Endodontics
• /
• v.34 no.4
• /
• pp.324-332
• /
• 2009

The purpose of this study was to investigate the effect of rigidity of post core systems on stress distribution by the theoretical technique, finite element stress-analysis method. Three-dimensional finite element models simulating an endodontically treated maxillary central incisor restored with a zirconia ceramic crown were prepared and 1.5 mm ferrule height was provided. Each model contained cortical bone, trabecular bone, periodontal ligament, 4 mm apical root canal filling, and post-and-core. Six combinations of three parallel type post (zirconia ceramic, glass fiber, and stainless steel) and two core (Paracore and Tetric ceram) materials were evaluated, respectively. A 50 N static occlusal load was applied to the palatal surface of the crown with a $60^{\circ}$angle to the long axis of the tooth. The differences in stress transfer characteristics of the models were analyzed. von Mises stresses were chosen for presentation of results and maximum displacement and hydrostatic pressure were also calculated. An increase of the elastic modulus of the post material increased the stress, but shifted the maximum stress location from the dentin surface to the post material. Buccal side of cervical region (junction of core and crown) of the glass fiber post restored tooth was subjected to the highest stress concentration. Maximum von Mises stress in the remaining radicular tooth structure for low elastic modulus resin core (29.21 MPa) was slightly higher than that for high elastic modulus resin core (29.14 MPa) in case of glass fiber post. Maximum displacement of glass fiber post restored tooth was higher than that of zirconia ceramic or stainless steel post restored tooth.

• Journal of dental hygiene science
• /
• v.11 no.4
• /
• pp.299-303
• /
• 2011

The purpose of this case report was to present an example of an esthetic and functional rehabilitation of anterior teeth with tetracycline discoloration and minor morphological abnormality of a 39-year old female. A chairside computer-aided design/computer-aided manufacturing (CAD/CAM) system with CEREC AC was applied for the prosthetic procedure and all ceramic crowns made with lithum disilicate (IPS e.max CAD) restored the esthetic and functional features of sixteen anterior teeth successfully.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.2
• /
• pp.265-276
• /
• 1997

The effect of thermocycling and surface finishing on the marginal fidelity of copings for a metal ceramic crown was examined. Methods for minimizing the loss of marginal fidelity were evaluated. The results were as follows ; 1. Thermocycling of ceramic metal copings resulted in increased marginal gap. 2. The greatest marginal gap occurred during the first thermocycling of the copings. 3. No additional distortion of marginal fidelity occurred when surface finishing and second thermocycling were completed after initial thermocycling. 4. The gap increases according to various treatment methods showed group 1 to be the highest values. 5. There was no significant difference between group 2 and group 3(p>0.05) 6. There was significant difference between group 1 and group 2, 3(p<0.05). 7. There was no significant difference among the measurement sites.