Journal of Dental Rehabilitation and Applied Science
/
v.25
no.4
/
pp.403-415
/
2009
The purpose of the study is to establish the effect of different abutment shapes and types of cements on the retention of the full veneer casted gold crowns. Metal dies that has the similar shape with the implant abutment were manufactured using a short(5mm) and long(10mm) dies with different convergence angles. Metal dies and gold crowns, which were made from the metal dies, were cemented with Temp-bond, Temp-bond mixed with petroleum jelly, ZPC and Premier implant cement. After that, these were tested for tensile force at the point of separation. The effect of convergence angle changes of different cement types on the retention was studied as well as the effects of the cement type changes with different convergence angles on the retention. In addition, study about the marginal gap of Premier implant cement used for this experiment was conducted. The results are as followed under the in-vitro experimental limits; 1. The retention of the Temp-bond mixed with petroleum jelly decreased as the convergence angle increased, and the retention was weakest among the cements. 2. The retention of ZPC decreased as convergence angle increased. When convergence angle was 5 degrees, ZPC showed stronger retention than Premier implant cement. 3. Premier implant cement had the weakest retention when the convergence angle was 5 degrees but when the convergence angle was 10 degrees, it had the strongest retention. As the angle increased more than 10 degrees, the retention decreased. 4. Premier implant cement showed bigger marginal gap when the convergence angle was 5 degrees than 10 degrees under the experimental condition.
Recently as the esthetic concerns about dental prosthesis have been increased, the nonmetallic post and core systems have been introduced clinically to improve the color and the low optical transmittance of conventional casting metal post and core systems. The purpose of this study was to compare and analyze the optical transmittance and the shade changes of all-ceramic crowns with two nonmetallic post and core systems. The experimental groups were classified as follows : Total 27 specimens(9 samples in each group) were evaluated. Group I : Natural teeth as a control group Group II : CosmoPost and $Empress^{(R)}$ core (Ivoclar-Vivadent, Liechtenstein) Group III : $LIGHT-POST^{TM}$ and $LIGHT-CORE^{TM}$ (Bisco, U.S.A.) In all group, all-ceramic crowns were fabricated with the same shade of IPS $Empress^{(R)}$ II (Ivoclar-Vivadent, Liechtenstein) after abutment preparation, and then two kinds of spectrophotometers, UV 3101 PC (Shimadzu, Japan) and CM 503i (Minolta Co. Ltd. Japan), were used to measure the optical transmittance and the color value. The following results were obtained : 1. The optical transmittance of each group without all-ceramic crowns, was siginificantly decreased in order of Group III, I and II (p<0.05). 2. The optical transmittance of each group with all-ceramic crowns cemented, were siginificantly decreased in order of Group I, II and III (p<0.05). 3. In comparison with the shade of all-ceramic crowns, there were no significant differences between groups regardless of the cementation. 4. In comparison with the shade changes in each group after the cementation of all-ceramic crowns, there were no significant differences between groups. From the above results, it is thought that the selection among materials used in this study doesn't influence greatly the esthetic restoration, because the differences of optical transmittance were so small that those were clinically insignificant.
The purpose of this study is to evaluate the color differences in the In-Ceram according to coping thickness and various abutment core materials ; amalgam, precious alloy, composite resin, non-precious alloy. After the porcelain was built up on the In-Ceram coping at the thicknes of 0.3mm and 0.5mm then it was cemented with glass ionomer cement to the post & core materials. The following results were obtained. 1. There were significant differences in the $L^*$ values $a^*$ and $b^*$ values in the cementation of different cores, to the In-Ceram(P<0.01). $L^*$ values were not significantly different between the composite resin to the In-Ceram and the $a^*\;b^*$ values were not significantly different between the amalgam and the non-precious alloy. 2. All of cementations of In-Ceram to the core materisal had color difference(${\Delta}E^*ab$) compared to the In-Ceram. In the 0.3mm thickness of the In-Ceram copping non-precious alloy indicated the greatest value, while the composite resin core showed the lowest value with a thickness of 0.5mm In-Ceram copping. 3. By controlloing the In-Ceram coping thickness $L^*$ value was significatly different(P<0.01), but not in $a^*$ and $b^*$ values. 4. In an amalgam, precious & non-prcious alloys there was a 1,74 to 3.06 range color difference in the controlled thickness of In-Ceram coping at the thickness of 0.3mm and 0.5mm. The above results suggest that the requirement of the sufficient thickness of In-Ceram coping and the suitable core material in order to get an estheti restoration by In-Ceram and also to intercept the original core color.
Ha, Jeong-Wan;Kim, Su-Gwan;Kim, Hak-Hyun;Moon, Seong-Yong;Lim, Sung-Chul
Journal of the Korean Association of Oral and Maxillofacial Surgeons
/
v.34
no.1
/
pp.90-94
/
2008
The purpose of this study was to investigate the effects of immediate non-functional loading by analyzing histomorphology around the implant tissues in dogs. Five eight- to nine-month-old full-grown dogs weighing around 12 kg were used in the study. Group I (control group) comprised those in which delayed loading was applied to the right side of the mandible, and Group II (experimental group) consisted of dogs in which immediate loading was performed on the left side of the mandible. Resorbable blast media (RBM)-treated double-threaded US III implants measuring 3.5 mm in diameter and 11 mm long were used in the study. Each animal received four implants in each group, for a total of 40 implants. Cemented type abutments were used after implantation. An 8-week period was allowed for bone healing and an abutment was placed after exposing the periosteum for loading. An implant sample was obtained from bone blocks taken when the dogs were killed at 16 weeks after loading. A Mann-Whitney U-test was performed to evaluate statistical significance. Student's t-test was used for the histological evaluation. The bone formation ratio in Groups 1 and 2 was 88.23 and 86.41%, respectively. No significant difference in new bone formation was observed in the two groups. As no significant difference was seen in new bone formation between the delayed and immediate loading groups, early loading might be possible after implant placement.
Kim, Hae-Young;Yang, Jin-Yong;Chung, Bo-Yoon;Kim, Jeong Chan;Yeo, In-Sung
Journal of Periodontal and Implant Science
/
v.43
no.2
/
pp.58-63
/
2013
Purpose: The aim of this study was to measure the peri-implant bone length surrounding implants that penetrate the sinus membrane at the posterior maxilla and to evaluate the survival rate of these implants. Methods: Treatment records and orthopantomographs of 39 patients were reviewed and analyzed. The patients had partial edentulism at the posterior maxilla and limited vertical bone height below the maxillary sinus. Implants were inserted into the posterior maxilla, penetrating the sinus membrane. Four months after implant insertion, provisional resin restorations were temporarily cemented to the abutments and used for one month. Then, a final impression was taken at the abutment level, and final cement-retained restorations were delivered with mutually protected occlusion. The complications from the implant surgery were examined, the number of failed implants was counted, and the survival rate was calculated. The periimplant bone lengths were measured using radiographs. The changes in initial and final peri-implant bone lengths were statistically analyzed. Results: Nasal bleeding occurred after implant surgery in three patients. No other complications were found. There were no failures of the investigated implants, resulting in a survival rate of 100%. Significantly more bone gain around the implants (estimated difference=-0.6 mm, P=0.025) occurred when the initial residual bone height was less than 5 mm compared to the >5 mm groups. No significant change in peri-implant bone length was detected when the initial residual bone height was 5 mm or larger. Conclusions: This study suggests that implants penetrating the sinus membrane at the posterior maxilla in patients with limited vertical bone height may be safe and functional.
Journal of Dental Rehabilitation and Applied Science
/
v.18
no.4
/
pp.321-329
/
2002
Bending moments results from offset overloading of dental implant, which may cause stress concentrations to exceed the physiological capacity of cortical bone and lead to various kinds of mechanical failures. The purpose of this study was to compare the distributing pattern of stress on the finite element models with the different angulated placement of dental implant in mandibular posterior missing areas. The three kinds of finite element model, were designed according to 3 main configurations: Model 1(parallel typed placement of 2 fixtures), Model 2(15. distal angulated placement of one fixture on second molar area), Model 3(15. mesial angulated placement of one fixture on second molar area). The cemented crowns for mandibular first and second molars were made on the two fixtures (4mm 11.5). Three-dimensional finite element models by two fixtures were constructed with the components of the implant and surrounding bone. A 200N vertical static load were applied to the center of central fossa and the point 2mm apart from the center of central fossa on each model. The preprocessing, solving and postprocessing procedures were done by using FEM analysis software NISA/DISPLAY IV Version 10.0((Engineering Mechanics Research Corporation, USA). Von Mises stresses were evaluated and compared in the supporting bone, fixtures, and abutment. The results were as following : (1) Under the point loading at the central fossa, the direction of angulated fixture affected the stress pattern of implants. (2) Under the offset loading, the position of loading affected more on the stress concentration of implants compare to the angulated direction of implants. The results had a tendency to increase the stress on the supporting bone, fixture and screw under the offset loads when the placement angulation of implant fixture is placed toward mesial or distal direction. In designing of the occlusal scheme for angulated placement, placing the occlusal contacts axially during chewing appears to have advantages in a biomechanical viewpoint.
Oziunas, Rimantas;Sakalauskiene, Jurgina;Jegelevicius, Darius;Januzis, Gintaras
The Journal of Advanced Prosthodontics
/
v.14
no.2
/
pp.70-77
/
2022
PURPOSE. This study evaluated screw loosening and 3D crown displacement after cyclic loading of implant-supported incisor crowns cemented with original titanium bases or with three compatible, nonoriginal components. MATERIALS AND METHODS. A total of 32 dental implants were divided into four groups (n = 8 each): Group 1 used original titanium bases, while Groups 2-4 used compatible components. The reverse torque value (RTV) was evaluated prior to and after cyclic loading (1,200,000 cycles). Samples (prior to and after cyclic loading) were scanned with a microcomputed tomography (micro-CT). Preload and postload files were superimposed by 3D inspection software, and 3D crown displacement analysis was performed using root-mean-square (RMS) values. All datasets were analyzed using one-way ANOVA and Tukey's post hoc analysis. RESULTS. Significant variations were observed in the postload RTV, depending on the titanium base brand (P < .001). The mean postload RTVs were significantly higher in Groups 1 and 2 than in the other study groups. While evaluating 3D crown displacement, the lowest mean RMS value was shown in the original Group 1, with the highest RMS value occurring in Group 4. CONCLUSION. Within the limitations of this in vitro study and under the implemented conditions, it was concluded that the manufacturer brand of the titanium base significantly influenced screw loosening following the fatigue test and influenced 3D crown displacement after cyclic loading.
Statement of the problem: Under anatomical limitations on maxillary posterior region, a poor crown-to root ratio acting on dental implants can result in undesirable stress in surrounding bone, which in turn can cause bone defects and eventual failure of implants. Purpose: The purpose is to compare stress distribution due to different crown-root ratio and effect of splinting between natural teeth and implants in maxillary molar area under different loads. Material and methods: Analysis of stress arising supporting bone of the natural teeth and the implant was made with 3-dimensional finite element method. The model simulated naturel teeth was made with 2nd premolar and 1st molar in the maxillary molar region (Model T). The model simulated implants placed on same positions with two parallel implants of Straumann Dental Implant cemented abutment (Model I). Each model was designed in different crown-root ratio (0.7:1, 1:1, 1.25:1) and set cement type gold crown to make it non-splinted or splinted. After that, 300 N force was loaded to each model in five ways (Load 1: middle of occlusal table, Load 2: middle of buccal cusp, Load 3: middle of lingual cusp, Load 4: horizontal load to buccal cusp of anterior abutment only, Load 5: horizontal load to middle of buccal cusp of each abutment), and stress distribution was analyzed. Results and conclusion: On all occasions, stress was concentrated at the cervical region of the implant. Under load 1, 2 and 3, stress was not increased even when crown-root ratio increases, but under load 4 and 5, when crown-root ratio increases, stress also increased. There was difference in stress values between natural teeth and implants when crown-root ratio gradually increases; In case of natural teeth, splinting decreased stress under vertical and horizontal loads. In case of implants, splinting decreased stress under vertical loads 1,2 and 3, but increased maximal stress under loads 2 and 3. Under horizontal loads, splinting decreased stress, however the effect of splinting decreased under load 5 than load 4. Furthermore, the stress was increased, when crown-root ratio is 1.25:1. Clinical implications: This limited finite element study suggests that the stress on supporting bone may be increased under non-axial loads and poor crown-root ratio. Under poor crown-root ratio, excessive stress was generated at the cervical region of the implant, and decreased splinting effect for stress distribution, which can be related to clinical failure.
Purpose: The purpose of this study was to measure and compare the strain value exerted on the cervical area using different screw tightening protocols in implant-supported, screw-retained 3-unit prostheses. Materials and methods: Strain gauges were attached to four implants: two external and two internal. Thereafter, two study model were designed each type using acrylic resin. CAD-CAM was used to design hex and nonhex abutments for each group (EH, ENH, IH, and INH group) and Screw-cement-retained prostheses were also designed using a nonprecious base metal. Abutment was fixed with 10 Ncm torque, and the prosthesis was cemented. Screws were fixed with 30 Ncm torque using different three protocols. After 5 min, the strain gauge level was measured, and group analysis was performed (α=.05). Results: External group showed significantly lower strain values than internal group and the EH group showed significantly lower strain values than the ENH group (P<.05). There was no difference in strain value based on the types of screw tightening protocols in same group (P>.05). The IH group exhibited significantly higher strain values than the INH group and the IH group showed a significant difference in strain values based on the types of screw tightening protocols used (P<.05). Conclusion: There was no significant effect on the external type in the implant-supported, screw-retained prostheses. However, strain values were high in the internal type, and the types of screw tightening protocol significantly affected these implants.
The major influencing factors on the strength of all-ceramic crowns are types of dental ceramics, fabrication techniques, methods of abutment preparation and cementation modes of all-ceramic restorations. Zinc phosphate cement and glass-ionomer cement were used as an early lot-ing media for all-ceramic crowns. Recently many studies have reported that resin cements have more advantages in increasing the fracture strength of restorations comparing with zincphosphate cement and glass-ionomer cement. The purpose of this study is to investigate the effect of etching, silane treatment, sandblasting and dentin bonding agents on fracture strengths of dental ceramics. 40 flat dentin specimens and 40 ceramic discs of 1.5mm thickness and 8mm diameter were fabricated, and divided into 4 groups according to surface treatments. Surface treatments before cementation were as follows Group I : (ceramic) : HF etching - silane treatment - application of bonding resin (dentin) : application of dentin bonding agent Group II : (ceramic) : sandblasting - application of bonding resin (dentin) : application of dentin bonding agent Group III : (ceramic) : application of bonding resin (dentin) : application of dentin bonding agent Group IV : (ceramic) : HF etching - silane treatment - application of bonding resin (dentin) : no dentin bonding procedure Dentin specimens and ceramic discs were cemented with dual cure resin cement, and went through thermocycling. Compressive stress es were loaded on the centers of ceramic discs with Instron test-ing machine, and fracture strengths resistance for catastrophic fracture were measured The results were as follows. 1. The group I showed the highest fracture resistance. The next was group II And group III, IV followed. 2. There was a significant difference in the mean value of fracture strengths between group I and group III (p<0.05), but no significant differences between group I and group II, and group II and group III (p>0.05). 3. There was a significant difference in the mean value of fracture strengths between group I and group IV (p<0.05).
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.