• 대한금속재료학회지
• /
• 제48권3호
• /
• pp.262-267
• /
• 2010

$LiNi_{1-x}Mg_xO_2$(x=0, 0.025, 0.05, 0.075, 0.1) samples were synthesized by the solid-state reaction method. The crystal structure was analyzed by X-ray powder diffraction and Rietveld refinement. $LiNi_{1-x}Mg_xO_2$samples give single phases of hexagonal layered structures with a space group of R-3m. The calculated cation-anion distances and angles from the Rietveld refinement were changed with Mg contents in $LiNi_{1-x}Mg_xO_2$. The thicknesses of $NiO_2$ slabs were increased and the distances between the $NiO_2$ slabs were decreased with the increase in Mg contents in the samples. The electrical conductivities of sintered $LiNi_{1-x}Mg_xO_2$ samples were around $10^{-2}$ S/cm at room temperature. The electrochemical performances of $LiNi_{1-x}Mg_xO_2$were evaluated by coin cell test. Compared to $LiNiO_2$, $LiNi_{0.95}Mg_{0.05}O_2$ exhibited improved high-rate capability and cyclability due to the well-ordered layered structure by doping of Mg ion.

• 대한화학회지
• /
• 제60권6호
• /
• pp.402-409
• /
• 2016

3-Mecaptopropionic acid (MPA) 리간드와 하이브리드 타입 리간드($MPA+CdCl_2$)로 각각 부동화(passivation) 된 2.8 nm 크기의 황화납 콜로이드 양자점 박막을 제작하고, 각각을 대기 중, 질소 분위기에서 열처리, 오존 처리 하였을 때 나타나는 두 양자점 박막의 전자 구조와 조성 원소의 변화를 광전자 분광법을 이용하여 연구하였다. 대기에서 열처리는 리간드 종류와 관계없이 황화납 양자점의 가전자대 시작점이 공통적으로 약한 p-도핑 효과가 있음을 직접적으로 확인할 수 있었다. 또한, 오존처리 후 두 황화납 양자점 표면에 공통적으로 $Pb(OH)_2$, $PbSO_x$, PbO를 형성하는 것을 확인하였다. 하지만, 오존에 의해 형성된 산화물 중 PbO 성분은 특별히 하이브리드 타입 리간드로 부동화 된 양자점에서 형성된 양이 MPA 리간드만으로 부동화 된 양자점과 비교했을 때 감소한 것을 확인할 수 있었다. 이것은 PbS(111) 격자면에 있는 과량의 Pb 표면이 $Cl_2$으로 부동화되면서, Pb 양이온과 오존의 반응을 차단함으로써 PbO의 형성을 어렵게 했기 때문으로 추정된다.