• Applied Chemistry for Engineering
• /
• v.23 no.2
• /
• pp.190-194
• /
• 2012

10 wt% Mn supported on various commercial $TiO_2$ catalysts were prepared by wet-impregnation method for the low temperature selective catalytic reduction (SCR) of NO with $NH_3$. A combination of various physico-chemical techniques such as BET, XRD, XPS and TPR were used to characterize these catalysts. MnOx surface densities on MnOx/$TiO_2$ catalyst were related to surface area. As MnOx surface density lowered with high dispersion, the SCR activity for low temperature was increased and the reduction temperature ($MnO_2$ ${\rightarrow}$ $Mn_2O_3$) of surface MnOx was lower. For a high SCR, MnOx could be supported on a high surface area of $TiO_2$ and should be existed a high dispersion of non-crystalline species.

• Applied Chemistry for Engineering
• /
• v.17 no.5
• /
• pp.451-457
• /
• 2006

We synthesized phase pure CrN having surface areas up to $47m^2/g$ starting from $CrCl_{3}$ with $NH_{3}$. Thermal Gravimetric Analysis coupled with X-ray diffraction was carried out to identify solid state transition temperatures and the phase after each transition. In addition, the BET surface areas, pore size distributions, and crystalline diameters for the synthesized materials were analyzed. Space velocity influenced a little to the surface areas of the prepared materials, while heating rate did not. We believe it is due to the fast removal of reaction by-products from the system. Temperature programmed reduction results revealed that the CrN was hardly passivated by 1% $O_{2}$. Molecular nitrogen was detected from CrN at 700 and $950^{\circ}C$, which may be from lattice nitrogen. In temperature programmed oxidation with heating rate of 10 K/min in flowing air, oxidation started at or higher than $300^{\circ}C$ and resulting $Cr_{2}O_{3}$ phase was observed with XRD at around $800^{\circ}C$. However the oxidation was not completed even at $900^{\circ}C$. CrN catalysts were highly active for n-butane dehydrogenation reaction. Their activity is even higher than that of a commercial $Pt-Sn/Al_{2}O_{3}$ dehydrogenation catalyst in terms of volumetric reaction rate. However, CrN was not active in pyridine hydrodenitrogenation.

• Applied Chemistry for Engineering
• /
• v.9 no.3
• /
• pp.355-360
• /
• 1998

Reduction activity of precious metal-loaded HZSM-5 for NO has been studied and was compared to that of Cu-HZSM-5 in the presence of excess oxygen. It was found that among the catalysts used in this study, Ru-HZSM-5 was the most active catalyst for the reduction of NO to $N_2$ in the absence of hydrocarbon reductant. The highest conversion obtained was 45%. No severe inhibition of water vapor to the reduction was observed. It is suggested that the higher catalytic activity of Ru-HZSM-5 may result from the better ability to oxidize NO to $NO_2$ in the presence of excess oxygen. A proposed reaction mechanism for the reduction of NO to $N_2$ in the presence of excess oxygen is that NO is oxidized to $NO_2$ on the surface of Ru-HZSM-5 catalyst and the adsorbed $NO_2$ on the surface is then decomposed to $N_2$. $NO_2$ is supposed to the reaction.

• Korean Chemical Engineering Research
• /
• v.51 no.4
• /
• pp.443-454
• /
• 2013

Various metal ions (transition and base metals) incorporated MCM-41 catalysts can be synthesized using colloidal and soluble silica with non-sodium involved process. Transition metal ion-typically $V^{5+}$, $Co^{2+}$, and $Ni^{2+}$-incorporated MCM-41 catalysts were synthesized by isomorphous substitution of Si ions in the framework. Each incorporated metal ion created a single species in the silica framework, single-site solid catalyst, showing a substantial stability in reduction and catalytic activity. Radius of pore curvature effect was investigated with Co-MCM-41 by temperature programmed reduction (TPR). The size of metallic Co clusters, sub-nanometer, could be controlled by a proper reduction treatment of Co-MCM-41 having different pore size and the initial pH adjustment of the Co-MCM-41 synthesis solution. These small metallic clusters showed a high stability under a harsh reaction condition without serious migration, resulting from a direct anchoring of small metallic clusters to the partially or unreduced metal ions on the surface. After a complete reduction, partial occlusion of the metallic cluster surface by amorphous silica stabilized the particles against aggregations. As a probe reaction of particle size sensitivity, carbon single wall nanotubes (SWNT) were synthesized using Co-MCM-41. A metallic cluster stability test was performed by CO methanation using Co- and Ni-MCM-41. Methanol and methane partial oxidations were carried out with V-MCM-41, and the radius of pore curvature effect on the catalytic activity was investigated.

• Journal of Korean Society for Atmospheric Environment
• /
• v.18 no.E1
• /
• pp.29-36
• /
• 2002

The selective catalytic reduction (SCR) reaction of promoter catalysts was investigated in this study. A pure anatase type of TiO$_2$ was used as support. Activation measurement of prepared catalysts was practiced on a fixed reactor packing by the glass bead after filling up catalysts in 1/4 inch stainless tube. The reaction temperature was measured by K-type thermocouple and catalyst was heated by electric furnace. The standard compositions of the simulated flue gas mixture in this study were as follows: NO 1,780ppm, NH$_3$1,780ppm, $O_2$1% and $N_2$ as balance gas. In this study, gas analyzer was used to measure the outgassing gas. Catalyst bed was handled for 1hr at 45$0^{\circ}C$, and the reactivity of the various catalyst was determined in a wide temperature range. Conversion of NH$_3$/NO ratio and of $O_2$ concentration was practiced at 1,1.5 and 2, respectively. The respective space velocity were as follows . 10,000, 15,000 and 17,000 hr-1. It was found that the maximum conversion temperature range was in a 5$0^{\circ}C$. It was also found toi be very sensitive at space velocity, $O_2$ concentration, and NH$_3$/NO ratio. We also noticed that the maximum conversion temperature of (W, Mo, Sn) -V$_2$O$_{5}$/TiO$_2$ catalysts was broad. Specially WO$_3$-V$_2$O$_{5}$TiO$_2$2 catalyst appeared nearly 100% conversion at not only above 30$0^{\circ}C$ ut also below 25$0^{\circ}C$. At over 30$0^{\circ}C$, NH$_3$ oxidation decreased with decrease of surface excess oxygen. In addition, WO$_3$-V$_2$O$_{5}$TiO$_2$ catalyst did not appear to affect space velocity, $O_2$ concentration, and NH$_3$/NO ratio.ratio.

• Bulletin of the Korean Chemical Society
• /
• v.25 no.5
• /
• pp.681-686
• /
• 2004

Ti-ZSM-5 prepared by secondary synthesis, from the reaction of H-ZSM-5 with vapor phase $TiCl_4$, was characterized with several physicochemical techniques including FT-IR and UV/VIS-DRS. It was found that zeolite structure, surface area and pore volume did not change, and the framework aluminum could not be replaced by titanium atom during the secondary synthesis of Ti-ZSM-5. The incorporation of titanium into the framework might be due to reaction of $TiCl_4$with the silanol groups associated with defects or surface sites. The formation of extra-framework titanium could not be avoided, unless the samples were further treated by water vapor at 550 $^{\circ}C$ or higher temperature. High temperature steam treatment of Ti-ZSM-5 prepared by chemical vapor deposition with $TiCl_4$was efficient to prevent the formation of non-framework titanium species. Ti-ZSM-5 zeolites prepared in this work contained only framework titanium species and exhibited improved catalytic property close to TS-1 prepared by hydrothermal synthesis.

• Journal of the Korean Ceramic Society
• /
• v.41 no.11
• /
• pp.864-871
• /
• 2004

Porous pseudo-boehmite gel was prepared through the aging process of amorphous aluminum hydroxides gel precipitated by the hydrolysis reaction of dilute NaOH solution and AlCl$_3$ solution. In this study, the synthesis method was studied on porous pseudo-boehmite gel having maximum pore volume, as being investigated the changes of crystal structure, infrared rays absorption spectrum, BET surface area and pore structure when the hydrolysis reaction is controlled in the range of pH 7.6~11.6 and the aging process is hold up for 2~24 h at 60~10$0^{\circ}C$. We could find that the gel precipitates deposited in in range of pH 7.6~9.6 were developed into porous pseudo-boehmite which surface area was 250~357 $m^2$/g, pore volume was 0.4~0.7 cc/g and average pore size was 58~l14$\AA$. However, the gel precipitates deposited in range of pH 10.6~11.6 were developed into bayerite which pore volume was very little.

• Korean Journal of Materials Research
• /
• v.28 no.11
• /
• pp.646-652
• /
• 2018

During a long-term operation of polymer electrolyte membrane fuel cells(PEMFCs), the fuel cell performance may degrade due to severe agglomeration and dissolution of metal nanoparticles in the cathode. To enhance the electrochemical durability of metal catalysts and to prevent the particle agglomeration in PEMFC operation, this paper proposes a hybrid catalyst structure composed of PtCo alloy nanoparticles encapsulated by porous carbon layers. In the hybrid catalyst structure, the dissolution and migration of PtCo nanoparticles can be effectively prevented by protective carbon shells. In addition, $O_2$ can properly penetrate the porous carbon layers and react on the active Pt surface, which ensures high catalytic activity for the oxygen reduction reaction. Although the hybrid catalyst has a much smaller active surface area due to the carbon encapsulation compared to a commercial Pt catalyst without a carbon layer, it has a much higher specific activity and significantly improved durability than the Pt catalyst. Therefore, it is expected that the designed hybrid catalyst concept will provide an interesting strategy for development of high-performance fuel cell catalysts.

• Clean Technology
• /
• v.21 no.4
• /
• pp.248-256
• /
• 2015

MnO₂ was prepared by a hydrothermal process method in the range of 120-200 ℃ and 0.5-5 h, calcined at 300 ℃ after induction of precipitation using KMnO₄ and MnCl₂･4H₂O, and its catalytic activity was compared for CO oxidation. The catalysts were characterized using by X-ray diffraction, N₂-sorption, scanning electron microscopy, and temperature programmed reduction of H₂ or CO. The crystalline structure of pure α-MnO₂ or hybrid α/β-MnO₂ was controlled by the preparation conditions. The pure α-MnO₂ showed better catalytic activity and thermal stability than hybrid α/β-MnO₂. Especially, α-MnO₂ prepared at 150 ℃ for 1 h has the highest specific surface area 214 m² g^-1, reducibility and labile lattice oxygen species analyzed by H₂, CO-TPR, respectively. It also showed the best CO oxidation activity in both conditions of temperature programmed and isothermal reaction. The results came from the physicochemical properties of catalysts like the crystalline structure, specific surface area, reducibility and lattice oxygen species, and which are correlated with catalytic performance.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.383-383
• /
• 2009

Silicon is commercially prepared by the reaction of high-purity silica with wood, charcoal, and coal, in an electric arc furnace using carbon electrodes, so called the metallurgical refining process, which produces ~98% pure Si (MG-Si). This can be further purified to solar grade silicon (SoG-Si) by various techniques. The most problematic impurity elements are B and P because of their high segregation coefficients. In this study, we explored the possibility of the using Cat-CVD for Si purification. The existing hot-wire CVD was modified to accommodate the catalyzer and the heating source. Mo boat (1.5 cm ${\times}$ 1 cm ${\times}$ 0.2 cm) was used as a heating source. Commercially available Si was purchased from Nilaco corporation (~99% pure). This powder was kept in the Mo-boat and heated to the purification temperature. In addition to the purification by cat-CVD technique, other methods such as thermal CVD, plasma enhanced CVD, vacuum annealing was also tried. It is found that the impurities are reduced to a great extent when treated with cat-CVD method.