• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2008년도 춘계 학술논문 발표대회
• /
• pp.183-186
• /
• 2008

Carbonation is measured as Phenolphthalein Solution, it is possible to confirm the scope of alkali through acid and basic reaction. Then, Concrete Basic Reaction is decided according to alkali concentration depending on Potassium Hydroxide Now that Carbonation is gradually produced toward inner side from outer side, with time going by, it doesnt work, to some adequate depth, in as fast time as compulsory facilitating test. Thus, this research thesis made a comparative analysis on concrete phenomenal discoloration borderline following Phenolphthalein Solution, as part of a bid to measure Carbonation. Also, the thesis measured Concrete Alkali Concentration. The result showed that concrete coloring is classified into red and scarlet according to alkali concentration, and into borderline breakpoint of the speckle of scarlet and carbonation reaction. The higher chroma becomes with concrete decolorizing, the higher alkali concentration becomes.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 춘계 학술발표회 제20권1호
• /
• pp.569-572
• /
• 2008

본 연구에서는 한국시설안전공단에서 최근 12년 동안 실시한 297개 교량의 정밀안전진단 결과 중 내구성 평가결과를 토대로 콘크리트 부재의 내구성 현황을 분석하였다. 내구성의 중요 인자인 중성화 깊이와 염화물 함유량의 경우 주변 환경 및 교량 부재별로 비교 검토하였으며, 특히 중성화 현황 분석에서는 중성화 진행정도를 단순회귀분석(simple regression analysis)통하여 분석하였다. 주변 환경에 따른 중성화속도계수의 분석결과 도심지는 5.41로, 해상교량 3.89, 하천교량 1.91에 비해 중성화 진행속도가 빠른 것으로 나타났다. 주변 환경에 따른 평균 전염화물량의 경우 해상교량이 육상교량의 4.7배로 분석되었고, 부재별 평균 염화물량은 상부구조(슬래브)가 0.709 $kg/m^3$, 교각이 0.565 $kg/m^3$, 교대가 0.455 $kg/m^3$ 로 상부구조가 하부구조에 비해서 크게 조사되었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1996년도 가을 학술발표회 논문집
• /
• pp.218-224
• /
• 1996

The purpose of this syudy is to set up a proper repair plan and to extend the remaining lifetime of them by measuring the remaining lifetime of reinforced concrete structures quantitatively. This method is based on the actual research on age deterioration, carbonation depth and covering depth of the reinforced concrete structures. Also, it measure the remaining lifetime through quantitatively defining the probability of steel corrosion by the damage of steel corrosion. By doing that, we proceed the proper repair plan after reviewing the possibility of lifetime extension.

• 한국방재학회 논문집
• /
• 제2권1호
• /
• pp.143-152
• /
• 2002

본 연구는 서울시내 위치한 39개 콘크리트 고가차도의 중성화 깊이, 가용성 염화물량 및 철근의 자연전위 등을 측정하여 열화의 원인을 분석하기 위한 기초자료를 얻고자 하였다. 전체 조사대상 구조물 가운데 철근위치까지 중성화 깊이가 진행된 구조물은 약 25%에 해당되었으며 중성화 속도는 물-시멘트비 60%, R=1의 조건인 kishitani의 제안식 3.727 $\sqrt{t}$ 보다 5%가 빠른 3.92 $\sqrt{t}$로 나타났다. 콘크리트의 염화물량의 조사결과에서는 전체 측정부위의 24%가 임계염화물량을 초과하였으며 철근의 자연전위는 -350mV(vs. CSE)이하로 측정된 것이 약 31%에 해당되는 구조물로서 과다한 염화물량이 철근부식의 주요 원인이 되는 것으로 조사되었다. 자연전위 -350mV 이하인 구조물에 한한 철근부식의 주요요인을 추정한 결과, 약 60%에 해당하는 부위가 치대 허용염화물량을 초과하였기 때문으로 분석된다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 가을 학술발표회 논문집(I)
• /
• pp.223-228
• /
• 1998

This study is to investigate on the remaining life of reinforced concrete apartment by using the probability of a reinforcing-steel corrosion and the carbonation tendency of domestic reinforced concrete apartments by using the statistic method. The results are as follow. ·To compare with the carbonation velocity of Kishitani's formula (x=3.727{{{{ SQRT { t} }}) when water-cement ratio is w=0.6, R=1, it is founded out that the carbonation velocity is slow a little in all area investigated and inland area, and fast a bit in coastal area. ·In the influencing factors in regard to the probability of reinforcing-steel corrosion, It seems that the influence of elapsed time is more effective than that of region. Therefore, it is necessary that it makes sure of the cover depth under apartment construction in recent so far as the durability is considered.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 추계 학술발표회 제17권2호
• /
• pp.727-730
• /
• 2005

The purpose of this study evaluates possibilities of waste phosphogypsum into concerts by steam curing admixture. The waste phosphogypsum is made use of 4 forms(Dehydrate, $\beta$-Hemihydrate, III-Anhydrite and II-Anhydrite) which were changed to in low temperature of calcination. The penetration depth and compressive strength of cement mortar are investigated to evaluate the chloride ion and carbonation resistance. As a result, chloride ion and carbonation resistance of cement mortar admixed with waste phosphogypsum are more excellent than cement mortar contained OPC alone. The internal pores of cement mortar are decreased by using waste phosphogypsum, because the hydrates of ettringite which is denesified in structure is much formed in early ages at steam curing. These densified effect is concluded with improving the resistance to attack of cement mortar including waste phospogypsum.

• 콘크리트학회논문집
• /
• 제12권5호
• /
• pp.69-80
• /
• 2000

This paper presents the prediction of remaining service life of the concrete due to steel corrosion caused by the following three cases; carbonation, using sea sand and using deicing salts. The assessment of initiation period was generalized considering the existing perdiction models in the literature, corrosion experiment and field assessment. To evaluate the prediction equation of rust growth, the corrosion accelerating experiments was performed. The polarization resistance was measured by potentiostat and the conversion coefficient of polarzation resistance to corrosion rate was determined by the measurement of real mass loss. Chloride content, carbonation, cover depth, relative humidity, water-cement ratio(W/C), and the use of deicing salts were taken into account and the resulting prediction equation of rust growth was proposed on the basis of these properties. The proposed equation is to predict the rust growth during any specified period of time and be effective in particular for predicting service life of concrete in the case of using sea sand.

• 콘크리트학회논문집
• /
• 제24권3호
• /
• pp.315-322
• /
• 2012

알칼리활성고로슬래그(AAS)는 이산화탄소 배출 부하가 큰 OPC의 가장 확실한 대체 재료로써 구조재로 이용하기 위해서는 내구성 평가 및 검증이 필요하다. 내구성 평가지표의 큰 비중을 차지하고 있는 것이 탄산화 저항성인데, AAS는 OPC에 비해 탄산화 저항성이 약한 것으로 알려져 있다. 이 연구에서는 AAS의 빠른 탄산화 특성과 그 원인을 알아보기 위해 탄산화 전후 물리적 특성 변화와 탄산화에 의해 수화생성물들이 어떤 변화를 보이는지 살펴보았다. 그 결과 AAS는 OPC와 달리 수화생성물의 대부분이 CSH이며, 수산화칼슘이 거의 생성되지 않았고, AAS의 CSH는 OPC의 CSH와 다른 구조임을 알 수 있었다. AAS는 탄산화 후 CSH가 비정질의 실리카겔로 변하고, 일부 알루미나화합물은 구조가 완전 붕괴되어 탄산화 후 식별되지 않는데, 이 때문에 AAS는 탄산화 후 압축강도가 약해진 것으로 판단된다. AAS의 활성화제의 첨가량을 높이면, 빠른 반응속도로 CSH의 생성량이 많아지고 조직이 치밀해져서 압축강도와 탄산화저항성이 향상된다.

• 한국건축시공학회지
• /
• 제4권1호
• /
• pp.119-126
• /
• 2004

Generally, reinforced concrete is one of the most commonly used structural materials and it prevents corrosion of steel bar by high pH of interior, But, as time elapsed, reinforced concrete structure become deteriorated by many of combined deterioration factors and environmental conditions. And, there are large number of deteriorate mechanism of the reinforced concrete structure and it acts complexly. It is recognized that steel bar corrosion is the main distress behind the present concern regarding concrete durability. In this study, to institute combined deterioration environments, established acceleration condition and cycle for combined deterioration environments has a resemblance to environments which are real structures placed. After that to confirm corrosion properties of reinforced concrete due to permeability with covering depth and types of surface cover under combined deterioration environments, measured carbonation velocity coefficients, chloride ion diffusion coefficients, water absorption coefficients, air permeability coefficients and electric potential, corrosion area ratio, weight reduction, corrosion velocity of steel bar. The results showed that an increase in age also decrease carbonation velocity coefficients, increase Chloride ion diffusion coefficients and increases water absorption coefficients. As well, an increase in age also increases corrosion of steel bar. Data on the development of corrosion velocity of steel bar with types of surface cover made with none, organic B, organic A, inorganic B, and inorganic A is shown. As well, permeability and corrosion velocity of steel bar with covering depth is superior to 10mm than 20mm. And it is confirmed permeability and corrosion properties of steel bar are closely related.

• 해양환경안전학회지
• /
• 제20권6호
• /
• pp.730-737
• /
• 2014

본 연구에서는 남해안에 건설된 사용기간이 5~34년의 해상 콘크리트 교량의 염화물이온농도에 대한 실측데이터로부터 표면염화물이온농도를 추정하고, 기존에 제시된 시방서와 타 연구결과에서 제시한 값들의 타당성을 평가하였다. 그리고 해상 콘크리트 교량의 염해방지도장의 유무, 염화물이온농도, 탄산화 깊이 및 콘크리트 압축강도의 상관관계를 도출하여 상호 작용을 평가하였다. 연구결과에 의하면, 표면염화물이온농도는 간만대에서 KCI 2009, 물보라지역과 해상대기중에서 Cheong et al.(2005)의 제안한 값이 타당한 것으로 판단된다. 또한, 해상 콘크리트 교량의 염해방지도장은 염화물이온의 침투, 탄산화 깊이 및 압축강도 저하 대한 방지효과가 있음을 알 수 있었다. 콘크리트의 압축 강도는 탄산화 깊이와 염화물이온농도의 증가에 따라 감소하였다.